Are there generalizable trends in the release of airborne synthetic clay nanoparticles from a jet milling process?

Despite recent efforts to assess the release of nanoparticles to the workplace during different nanotechnology activities, the existence of a generalizable trend in the particle release has yet to be identified. This study aimed to characterize the release of synthetic clay nanoparticles from a laboratory-based jet milling process by quantifying the variations arising from primary particle size and surface treatment of the material used, as well as the feed rate of the machine. A broad range of materials were used in this study, and the emitted particles mass (PM2.5) and number concentrations (PNC) were measured at the release source. Analysis of variance, followed by linear mixed-effects modeling, was applied to quantify the variations in PM2.5 and PNC of the released particles caused by the abovementioned factors. The results confirmed that using materials of different primary size and surface treatment affects the release of the particles from the same process by causing statistically-significant variations in PM2.5 and PNC. The interaction of these two factors should also be taken into account as it resulted in variations in the measured particles release properties. Furthermore, the feed rate of the milling machine was confirmed to be another influencing parameter. Although this research does not identify a specific pattern in the release of synthetic clay nanoparticles from the jet milling process generalizable to other similar settings, it emphasizes that each tested case should be handled individually in terms of exposure considerations.

What are the driving factors influencing the size distribution of airborne synthetic clay particles emitted from a jet milling process?

In the field of workplace air quality, measuring and analyzing the size distribution of airborne particles to identify their sources and apportion their contribution has become widely accepted, however, the driving factors that influence this parameter, particularly for nanoparticles (< 100 nm), have not been thoroughly determined. Identification of driving factors, and in turn, general trends in size distribution of emitted particles would facilitate the prediction of nanoparticles’ emission behavior and significantly contribute to their exposure assessment. In this study, a comprehensive analysis of the particle number size distribution data, with a particular focus on the ultrafine size range of synthetic clay particles emitted from a jet milling machine was conducted using the multi-lognormal fitting method. The results showed relatively high contribution of nanoparticles to the emissions in many of the tested cases, and also, that both surface treatment and feed rate of the machine are significant factors influencing the size distribution of the emitted particles of this size. In particular, applying surface treatments and increasing the machine feed rate have the similar effect of reducing the size of the particles, however, no general trend was found in variations of size distribution across different surface treatments and feed rates. The findings of our study demonstrate that for this process and other activities, where no general trend is found in the size distribution of the emitted airborne particles due to dissimilar effects of the driving factors, each case must be treated separately in terms of workplace exposure assessment and regulations.

Transparent organic-inorganic nanocomposites membranes based on carboxymethylcellulose and synthetic clay

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Comparison of the nanoparticles performance in the photocatalytic degradation of a styrene-butadiene rubber nanocomposite

Much has been talking about the advantages of polymeric nanocomposites, but little is known about the influence of nanoparticles on the stability of these materials. In this sense, we studied the influence of both oxides of zirconium and titanium, known to have photocatalytic properties, as well as the influence of synthetic clay Laponite on the photodegradation of styrene-butadiene rubber (SBR). SBR nanocomposites were prepared by the colloidal route by mixing commercial polymer lattices and nanometric anatase TiO2, monoclinic ZrO2 or exfoliated Laponite clays colloidal suspensions. To better understand the degradation mechanisms that occur in these nanocomposites, the efficiency of different photocatalysts under ultraviolet radiation was monitored by FT-IR and UV-vis spectroscopies and by differential scanning calorimetric. It was observed that TiO2 and ZrO2 nanoparticles undoubtedly acted as catalysts during the photodegradation process with different efficiencies and rates. However, when compared to pure SBR samples, the polymer degradation mechanism was unaffected. Unlike studies with nanocomposites montmorillonite, exfoliated laponite clay effectively acts as a photostabilizer of polymer UV photodegradation. Copyright © 2012 Wiley Periodicals, Inc.

Synthesis and stabilization of nanocrystalline zirconia with MSU mesostructure

In the presence of nonionic block-copolymer surfactant, nanocrystalline zirconia particles with MSU mesostrucmre were synthesized by a novel solid-state reaction route. The zirconia particles possess a nanocrystalline pore wall, which renders higher thermal stability compared to an amorphous framework. To further enhance its stability, laponite, a synthetic clay, was introduced. Laponite acts as an inhibitor to crystal a growth and also as a hard template for the mesostructure. High surface area and ordered pore structure were observed in the stabilized zirconia. The results show that the formation of the MSU structure is attributed to reverse hexagonal micelles, which are the products of the cooperative self-assembly of organic and inorganic species in the solid-state synthesis system with crystalline water and hygroscopic water present.

Fate of applied biosolids nitrogen in a cut and remove forage system on an alluvial clay loam soil

The fate of nitrogen (N) applied in biosolids was investigated in a forage production system on an alluvial clay loam soil in south-eastern Queensland, Australia. Biosolids were applied in October 2002 at rates of 6, 12, 36, and 54dryt/ha for aerobically digested biosolids (AE) and 8, 16, 48, and 72dryt/ha for anaerobically digested biosolids (AN). Rates were based on multiples of the Nitrogen Limited Biosolids Application rate (0.5, 1, 3, and 4.5NLBAR) for each type of biosolid. The experiment included an unfertilised control and a fertilised control that received multiple applications of synthetic fertiliser. Forage sorghum was planted 1 week after biosolids application and harvested 4 times between December 2002 and May 2003. Dry matter production was significantly greater from the biosolids-treated plots (21-27t/ha) than from the unfertilised (16t/ha) and fertilised (18t/ha) controls. The harvested plant material removed an extra 148-488kg N from the biosolids-treated plots. Partial N budgets were calculated for the 1NLBAR and 4.5NLBAR treatments for each biosolids type at the end of the crop season. Crop removal only accounted for 25-33% of the applied N in the 1NLBAR treatments and as low as 8-15% with 4.5NLBAR. Residual biosolids N was predominantly in the form of organic N (38-51% of applied biosolids N), although there was also a significant proportion (10-23%) as NO3-N, predominantly in the top 0.90m of the soil profile. From 12 to 29% of applied N was unaccounted for, and presumed to be lost as gaseous nitrogen and/or ammonia, as a consequence of volatilisation or denitrification, respectively. In-season mineralisation of organic N in biosolids was 43-59% of the applied organic N, which was much greater than the 15% (AN)-25% (AE) expected, based on current NLBAR calculation methods. Excessive biosolids application produced little additional biomass but led to high soil mineral N concentrations that were vulnerable to multiple loss pathways. Queensland Guidelines need to account for higher rates of mineralisation and losses via denitrification and volatilisation and should therefore encourage lower application rates to achieve optimal plant growth and minimise the potential for detrimental impacts on the environment.

Characterisation and fluidisation of synthetic pit latrine sludge

Half of the world’s urban population will live in informal settlements or “slums” by 2030. Affordable urban sanitation presents a unique set of challenges as the lack of space and resources to construct new latrines makes the de-sludging of existing pits necessary and is something that is currently done manually with significant associated health risks. Therefore various mechanised technologies have been developed to facilitate pit emptying, with the majority using a vacuum system to remove material from the top of the pit. However, this results in the gradual accumulation of unpumpable sludge in the pit, which eventually fills the latrine and forces it to be abandoned. This study has developed a method for fluidising unpumpable pit latrine sludge, based on laboratory experiments using a harmless synthetic sludge. Such a sludge consisting of clay and compost was developed to replicate the physical characteristics of pit latrine sludges characterised in Botswana during the 1980s. Undrained shear strength and density are identified as the critical parameters in controlling pumpability and a method of sludge characterisation based on these parameters is reported. In a series of fluidisation tests using a one fifth scale pit emptying device the reduction in sludge shear strength was found to be caused by i) dilution, which increases water content, and ii) remoulding, which involves mechanical agitation to break down the structure of the material. The tests demonstrated that even the strongest of sludges could be rendered “pumpable” by sufficient dilution. Additionally, air injection alone produced a three-fold decrease in strength of consolidated samples as a result of remoulding at constant water content. The implications for sludge treatment and disposal are discussed, and the classification of sludges according to the equipment required to remove them from the latrine is proposed. Possible field tests to estimate sludge density and shear strength are suggested. The feasibility of using low cost vacuum cleaners to replace expensive vane pumps is demonstrated. This offers great potential for the development of affordable pit emptying technologies that can remove significantly stronger sludges than current devices through fluidising the wastes at the bottom of the pit before emptying

The effect of temperature and strain rate on the deformation behaviour, structure development and properties of biaxially stretched PET-clay nanocomposites.

The inclusion of a synthetic fluoromica clay in PET affects its processability via biaxial stretching and stretching temperature (95 °C and 102 °C) and strain rate (1 s-1 and 2 s-1) influence the structuring and properties of the stretched material. The inclusion of clay has little effect on the temperature operating window for the PET–clay but it has a major effect on deformation behaviour which will necessitate the use of much higher forming forces during processing. The strain hardening behaviour of both the filled and unfilled materials is well correlated with tensile strength and tensile modulus. Increasing the stretching temperature to reduce stretching forces has a detrimental effect on clay exfoliation, mechanical and O2 barrier properties. Increasing strain rate has a lesser effect on the strain hardening behaviour of the PET–clay compared with the pure PET and this is attributed to possible adiabatic heating in the PET–clay sample at the higher strain rate. The Halpin–Tsai model is shown to accurately predict the modulus enhancement of the PET–clay materials when a modified particle modulus rather than nominal clay modulus is used.

Nanocomposites based on LbL films of polyaniline and sodium montmorillonite clay

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Investigation and development of techniques for the characterisation of the synthetic/biological interface

The purpose of this study is to increase our knowledge of the nature of the surface properties of polymeric materials and improve our understanding of how these factors influence the deposition of proteins to form a reactive biological/synthetic interface. A number of surface analytical techniques were identified as being of potential benefit to this investigation and included in a multidisciplinary research program. Cell adhesion in culture was the primary biological sensor of surface properties, and it showed that the cell response to different materials can be modified by adhesion promoting protein layers: cell adhesion is a protein-mediated event. A range of surface rugosity can be produced on polystyrene, and the results presented here show that surface rugosity does not play a major role in determining a material's cell adhesiveness. Contact angle measurements showed that surface energy (specifically the polar fraction) is important in promoting cell spreading on surfaces. The immunogold labelling technique indicated that there were small, but noticeable differences, between the distribution of proteins on a range of surfaces. This study has shown that surface analysis techniques have different sensitivities in terms of detection limits and depth probed, and these are important in determining the usefulness of the information obtained. The techniques provide information on differing aspects of the biological/synthetic interface, and the consequence of this is that a range of techniques is needed in any full study of such a complex field as the biomaterials area.

Organometallic precursors for pillared clay synthesis

The synthetic hectorite, laponite has been used within the paper industry to produce mildly conducting paper for use in electrographic printing. The aim of this research was to modify laponite in order to improve the electrical conductivity. In a continuation of a previous investigation involving organotin intercalation of laponite, the organotin precursor (p-CH3,OC6H4)4Sn was synthesised and characterised using Mass Spectroscopy, Infrared Spectroscopy and elemental analysis. Results of intercalation with this compound and a range of organobismuth and organoantimony compounds suggested that a halide content within the precursor was necessary for improvement in conductivity to be observed. Organometallic intercalation of a range of organotellurium compounds with laponite provided evidence that a hydrolysis reaction on the clay surface followed by the release of hydrochloric acid was an important first step if a reaction was to occur with the clay. Atomic Absorption Spectroscopy studies have shown that the acid protons underwent exchange with the interlayer sodium ions in the clay to varying degrees. Gas-liquid Chromatography and Infrared Spectroscopy revealed that the carbon-tellurium bond remained intact. Powder X-ray diffraction revealed that there had been no increase in the basal spacing. The a.c. conductivity of the modified clays in the form of pressed discs was studied over a frequency range of 12Hz - 100kHz using two electrode systems, silver paste and stainless steel. The a.c. conductivity consists of two components, ionic and reactive. The conductivity of laponite was increased by intercalation with organometallic compounds. The most impressive increase was gained using the organotellurium precursor (p-CH3OC6H4)2TeCl2. Conductivity investigations using the stainless steel electrode where measurements are made under pressure showed that in the case of laponite, where poor particle-particle contact exists at ambient pressure, there is a two order of magnitude increase in the measured a.c. conductivity. This significant increase was not seen in modified laponites where the particle-particle contact had already been improved upon. Investigations of the clay surface using Scanning Electron Microscopy suggested that the improvement in particle-particle contact is the largest factor in the determination of the conductivity. The other important factor is the nature and the concentration of the interlayer cations. A range of clays were synthesised in order to increase the concentration of sodium interlayer cations. A sol-gel method was employed to carry out these syntheses. A conductivity evaluation showed that increasing the concentration of the sodium cations within the clay led to an increase in the conductivity.

Efficient and Durable Vaccine against Intimin β of Diarrheagenic E. Coli Induced by Clay Nanoparticles

Improved strategies are urgently required to control infections with enterohemorrhagic Escherichia coli and enteropathogenic E. coli, two dominant zoonotic enteric pathogens responsible for a wide spectrum of illnesses as well as deaths of human being, with tremendous financial cost worldwide. The present study investigates the capacity of two clay nanoparticles (NPs) with opposite surface charges, namely synthetic layered double hydroxide (LDH) and hectorite (HEC) NPs as adjuvants to promote strong immune responses against the infections. Here both LDH and HEC NPs are showed to be able to carry an appreciable amount of Intimin β (1.1 and 4.4 mg per mg clay nanomaterials, respectively) and significantly facilitate antigen uptake by antigen-presenting cells. Remarkably, these clay NPs induce strong antibody and cell-mediated immune responses, which are much higher than that by the potent adjuvant, QuilA. Furthermore, these strong immune responses are well maintained for at least four months in the mouse model, during which there are no changes in histopathology of the animal organs. Collectively these data demonstrate the suitability of LDH and HEC NPs as useful adjuvants in new-generation vaccine formulations to control various infectious diseases.

Thermal decomposition of the synthetic hydrotalcite iowaite

The thermal stability and thermal decomposition pathways for synthetic iowaite have been determined using thermogravimetry in conjunction with evolved gas mass spectrometry. Chemical analysis showed the formula of the synthesised iowaite to be Mg6.27Fe1.73(Cl)1.07(OH)16(CO3)0.336.1H2O and X-ray diffraction confirms the layered structure. Dehydration of the iowaite occurred at 35 and 79°C. Dehydroxylation occurred at 254 and 291°C. Both steps were associated with the loss of CO2. Hydrogen chloride gas was evolved in two steps at 368 and 434°C. The products of the thermal decomposition were MgO and a spinel MgFe2O4. Experimentally it was found to be difficult to eliminate CO2 from inclusion in the interlayer during the synthesis of the iowaite compound and in this way the synthesised iowaite resembled the natural mineral.

The Behavior of Hydroxyl Units of Synthetic Goethite and its Dehydroxylated Product Hematite

The behavior of the hydroxyl units of synthetic goethite and its dehydroxylated product hematite was characterized using a combination of Fourier transform infrared (FTIR) spectroscopy and X-ray diffraction (XRD) during the thermal transformation over a temperature range of 180-270 degrees C. Hematite was detected at temperatures above 200 degrees C by XRD while goethite was not observed above 230 degrees C. Five intense OH vibrations at 3212-3194, 1687-1674, 1643-1640, 888-884 and 800-798 cm(-1), and a H2O vibration at 3450-3445 cm(-1) were observed for goethite. The intensity of hydroxyl stretching and bending vibrations decreased with the extent of dehydroxylation of goethite. Infrared absorption bands clearly show the phase transformation between goethite and hematite: in particular. the migration of excess hydroxyl units from goethite to hematite. Two bands at 536-533 and 454-452 cm(-1) are the low wavenumber vibrations of Fe-O in the hematite structure. Band component analysis data of FTIR spectra support the fact that the hydroxyl units mainly affect the a plane in goethite and the equivalent c plane in hematite.