Correlations between frequency of infra-red active vibrational modes and copper-oxygen distance in copper oxides. Application to superconductors

The infra-red spectra of a large number of ternary Cu(II) oxides with at least a quasi square-planar coordination of oxygen around the copper ions have been studied. The frequency of the bands with the highest frequency,v max, is found to correlate extremely well with the shortest Cu–O distance.v max increases at an impressive rate of sim20 cm–1 per 0.01 Å when the Cu–O distance becomes less than 1.97 Å, which is the Cu2+–O2– distance in square-planar CuO4 complexes as obtained from empirical ionic radii considerations. The marked sensitivity may be used as a ldquotitrationrdquo procedure not only to assign bands but also to obtain diagnostic information about local coordination in compounds derived, for example, from the YBa2Cu3O7–d structure such as LaCaBaCu3O7–d . The only example where this correlation fails is in the two-layer non-superconducting oxides derived from La2(Ca, Sr)Cu2O6. The significance of this result is discussed. The marked dependence of frequency on the bond-distance is qualitatively examined in terms of an increased electron-phonon coupling to account for the observed tendency of the superconducting transition temperature to go through a maximum as the average basal plane Cu–O distance is decreased.

Oxygen chemistry in copper oxides: evidence for O− species

Core-level spectroscopic studies suggest that cuprates nominally supposed to contain Cu3+ions are likely to have the excess positive charge on oxygen instead, giving rise to O-type species (oxygen holes)

High-temperature superconductivity in bismuth-copper oxides of the type BimMnCupOx (M=Mg, Ca, Sr, Ba, Bi)

Several oxides of the Bi m M n Cu p O x family (m=2, 3;n=2, 3, 4;p=1, 2, 3 and M=alkaline earth or Bi), possessing structures similar to the Aurivillius family of oxides, show highT c superconductivity.

Influences of acid treatments of active carbons on no reduction over carbon-supported copper oxides

Active carbon supported copper oxides were used in NO reduction. The conversions of NO reduction depends strongly on surface oxygen-containing groups on the active carbons, among them the carboxyls and lactones favored remarkably the NO reduction. However, hydrochloric acid treatment led to the decomposition of the carboxyls and lactones on C2 and C3, decreasing their reactivities for NO reduction. Concentrated HNO3 treatment of active carbon produced higher conversions of NO reduction at relatively low temperatures due to the marked increase in the amounts of the carboxyls and lactones.

Nanostructured copper oxides and phosphates from a new solid-state route

Nanostructured copper containing materials of CuO, Cu3(PO4)3 and Cu2P2O7 have been prepared by solid-state pyrolysis of molecular CuCl2·NC5H4OH (I), CuCl2·CNCH2C6H4OH (II), oligomeric [Cu(PPh3)Cl]4 (III), N3P3[OC6H4CH2CN·CuCl]6[PF6] (IV), N3P3[OC6H5]5[OC5H4N·Cu][PF6] (V), polymeric chitosan·(CuCl2)n (VI) and polystyrene-co-4-vinylpyridine PS-b-4-PVP·(CuCl2) (VII) precursors. The products strongly depend on the precursor used. The pyrolytic products from phosphorus-containing precursors (III), (IV) and (V) are Cu phosphates or pyrophosphates, while non-phosphorous-containing precursors (VI) and (VII), result in mainly CuO. The use of chitosan as a solid-state template/stabilizer induces the formation of CuO and Cu2O nanoparticles. Copper pyrophosphate (Cu2P2O7) deposited on Si using (IV) as the precursor exhibits single-crystal dots of average diameter 100 nm and heights equivalent to twice the unit cell b-axis (1.5–1.7 nm) and an areal density of 5.1–7.7 Gigadots/in.2. Cu2P2O7 deposited from precursor (VI) exhibits unique labyrinthine high surface area deposits. The morphology of CuO deposited on Si from pyrolysis of (VI) depends on the polymer/Cu meta ratio. Magnetic measurements performed using SQUID on CuO nanoparticle networks suggest superparamagnetic behavior. The results give insights into compositional, shape and morphological control of the as-formed nanostructures through the structure of the precursors.

Electropolishing of polycrystalline YBa2Cu3O7-δ to meet the need for sharp needle geometry

An electropolishing method has been developed for preparing sharp needles from polycrystalline YBa2Cu3O7-δ by modifying a recipe for TEM specimen preparation. The method is characterized by a polishing temperature of below 0°C, a non-acidic electrolyt and an even removal of the constituent phases. An approach was employed of combining I-V measurements for polishing process and microscopical observation of surface morphology in finding optimum polishing conditions. TEM evidenced that no preferential attack appeared to grain boundaries. X-ray diffractometry and electron diffraction implied that no change in oxygen content occurred during electropolishing. The sharpness of the tip was examined by field-ion microscopy.

Synthesis and properties of substituted Hg-based superconductors

This thesis is focused on studies of substituted Hg-based superconducting copper oxides ((Hg1-xMx)Ba2Can-1CunO2n+2+δ). These compounds are promising objects of investigation, not only from a fundamental point of view but also because of their high values of superconducting transition temperature (Tc) and irreversibility field (Hirr). The first part of the thesis is devoted to optimization of the synthesis procedure for Hg-based cuprates. The influence of different parameters (T, t, p(Hg), p(O2)) on the synthesis of these compounds in sealed silica tubes was studied. Optimal conditions yielded samples containing up to 95% of HgBa2Ca2Cu3O8+δ (Hg-1223). The formation of solid solutions with the formula (Hg1-xCux)Ba2Ca2Cu3O8+δ (where x <= 0.5) was also established. Another technique was developed, using LiF as a flux, for synthesis of samples containing up to 90% of the HgBa2CaCu2O6+δ (Hg-1212) phase. The second part concerns synthesis and studies of oxyfluorides using Hg-1212 and Hg-1223 as starting materials together with XeF2 as a fluorinating agent. It was found that oxyfluorides of both phases have a parabolic dependence of Tc vs. a parameter as well as enhanced Tc values (ΔT ≈ 3-4 K) in comparison with optimally doped non-fluorinated analogues. The crystal structure of Hg-1223 oxyfluoride was studied by X-ray powder and neutron diffraction methods. It is suggested that chemical modification of the crystal structure leads to a decrease in Cu-O distance without noticeable change in Cu-O-Cu angle (in the (CuO2) layers), which may be the significant factors influencing this Tc increase. Hg-1223 oxyfluoride was also studied under high pressure for first time. It was found that this compound has a record-high Tc value (≈ 166 K) at P ≈ 23 GPa. The last part describes the investigation of substituted Hg-based superconductors in the series (Hg0.9M0.1)Ba2CuO4+δ {(Hg,M)-1201}, where M = Tl, Pb, W, Mo, Nb and V. A comprehensive study of these compounds by various methods (X-ray powder diffraction, EDX, IR-, EXAFS- and XANES -spectroscopy) indicated that the change of charge carrier doping level is a crucial factor determining the irreversibility line. (Hg0.9Mo0.1)Ba2CuO4+δ showed the most improved irreversibility line position among the (Hg,M)-1201 compounds studied in this series.

Melt textured Y123 bulk and thick film

YBa2Cu3O7-δ - 25mol%Y2BaCuO5 bars and thick films have been melt textured using a stationary furnace with a temperature gradient of 3 or 6°C/cm. Samples are heated above the peritectic reaction temperature and quenched to just above the solidification temperature and then slowly cooled below the solidification temperature. All bar shaped samples consist of 2-5 mm grains though the grain orientations strongly depend on the heat treatment conditions. The bar shows the maximum Jc of above 3,000 A/cm2, whereas the maximum Jc of 200 A/cm2 and Tczero of 88K are obtained for the thick film on (100) LaAlO3 single crystal.

Microstructural studies of quenched partially-melted Y-123 materials and Y-123 with Y-211, PtO2 and CeO2 additions

The microstructure of YBa2Cu3O7-delta (Y-123) materials partially-melted in air and quenched from the temperature range 900-1100 degrees C, has been characterized using a combination of X-ray diffractometry, optical microscopy, scanning electron microscopy, electron microprobe analyses, transmission electron microscopy and energy and wave dispersive X-ray spectrometries. The microstructural studies reveal significant changes in the character of the quenched partial-melt as a function of temperature and time before quenching. BaCu2O2 and BaCuO2 are found to co-exist in stoichiometric samples quenched from the temperature range 920-960 degrees C. Under suitable cooling conditions, large pockets of melt cristallize as BaCuO2 with an exsolution of BaCu2O2 in the form of thin plates (approximate to 50-100 nm thick) along facets. Y2BaCuO5 (Y-211) additions are associated with the formation of BaCu2O2 at 1100 degrees C. Preliminary results on the effects of PtO2 and CeO2 additions to Y-123 (and Y-123 with Y-211 additions) show that these enhace the formation of BaCu2O2 at the melting temperature of 1100 degrees C. (C) 1998 Elsevier Science S.A. All rights reserved.

Bulk manufacture of YBCO powders by coprecipitation

This work presents an assessment of the coprecipitation technique for the reliable production of high-temperature superconducting (HTS) copper-oxide powders in quantities scaled up to 1 kg. This process affords precise control of cation stoichiometry (< 4% relative), occurs rapidly (almost instantaneously) and can be suitably developed for large-scale (e.g. tonne) manufacture of HTS materials. The process is based upon a simple control of the chemistry of the cation solution and precipitation with oxalic acid. This coprecipitation method is applicable to all copper-oxides and has been demonstrated in this work using over thirty separate experiments for the following compositions: YBa2Cu3O7-δ, Y2BaCuO5 and YBa2Cu4O8. The precursor powders formed via this coprecipitation process are fine-grained (∼ 5-10 nm), chemically homogeneous at the nanometer scale and reactive, Conversion to phase-pure HTS powders can therefore occur in minutes at appropriate firing temperatures. © 1995.

The formation of YBa2Cu3O7-x in melt-texture heat treatments

A study of the bulk formation of YBa2Cu3O7-x from the Y2BaCuO5 plus liquid regime reveals that phase formation occurs at appreciable rates below 950°C in air. This result has been observed for phase-pure YBa2Cu3O7-x starting material given two types of heat treatment: held at 1100°C and slow-cooled from 1030°C at 6°C/h or heat-treated isothermally. Differential thermal analysis, with a cooling rate of 10°C/min indicates that the degree of undercooling for the peritectic formation of YBa2Cu3O7-x is greater than 100°C. © 1994.

Microstructure of an artificial grain boundary weak link in an YBa2Cu3O(7-δ) thin film grown on a (100)(110), [001]-tilt Y-ZrO2 bicrystal

The microstructure of an artificial grain boundary in an YBa2Cu3O7-δ (YBCO) thin film grown on a (100)(110), [001]-tilt yttria-stabilized-zirconia (YSZ) bicrystal substrate has been studied using transmission electron microscopy (TEM). The orientation relationship between the YBCO film and the YSZ substrate was [001]YBCO∥[001]YSZ and [110]YBCO∥[100]YSZ for each half of the bicrystal film. However, the exact boundary geometry of the bicrystal substrate was not transferred to the film. The substrate boundary was straight while the film boundary was wavy. In several cases there was bending of the lattice confined within a distance of a few basal-plane lattice spacings from the boundary plane and microfaceting. No intergranular secondary phase was observed but about 25% of the boundary was covered by c-axis-tilted YBCO grains and a-axis-oriented grains, both of which were typically adjacent to CuO grains or surrounded by a thin Cu-rich amorphous layer.

Study of in situ laser deposited YBCO thin films

YBCO thin films were fabricated by laser deposition, in situ on MgO substrates, using both O2 and N2O as process gas. Films with Tc above 90 K and jc of 106 A/cm2 at 77 K were grown in oxygen at a substrate temperature of 765 °C. Using N2O, the optimum substrate temperature was 745 °C, giving a Tc of 87 K. At lower temperatures, the films made in N2O had higher Tc (79 K) than the films made in oxygen (66 K). SEM and STM investigations of the film surfaces showed the films to consist of a comparatively smooth background surface and a distribution of larger particles. Both the particle size and the distribution density depended on the substrate temperature.

Towards rational synthesis of inorganic solids

There have been major advances in the past couple of years in the rational synthesis of inorganic solids: synthesis of mercury-based superconducting cuprates showing transition temperatures up to 150 K; ZrP2-xVxO7 solid solutions showing zero or negative thermal expansion; copper oxides possessing ladder structures such as La1-xSrxCuO2.5; synthesis of mesoporous oxide materials having adjustable pore size in the range 15-100 Angstrom; and synthesis of a molecular ferromagnet showing a critical temperature of 18.6 K. Despite great advances in probing the structures of solids and measurement of their physical properties, the design and synthesis of inorganic solids possessing desired structures and properties remain a challenge today. With the availability of a variety of mild chemistry-based approaches, kinetic control of synthetic pathways is becoming increasingly possible, which, it is hoped, will eventually make rational design of inorganic solids a reality.

Solid-state chemistry of high-temperature oxide superconductors:The experimental situation

High-temperature superconductivity in oxides of the type(La, Ln)2?xBax(Sr)xCuO4, Y(Ln)Ba2Cu3O7??, La3?xBa3+xCu6O14, and related systems is discussed with emphasis on aspects related to experimental solid-state chemistry. All of these oxides possess perovskite-related structures. Oxygen-excess and La-deficient La2CuO4 also exhibit superconductivity in the 20�40 K just as La2?xBax(Srx)CuO4; these oxides are orthorhombic in the superconductivity phase. The crucial role of oxygen stoichiometry in the superconductivity ofYBa2Cu3O7?? (Tc = 95 ± 5K) is examined; this oxide remains orthorhombic up to ? ? 0.6 and becomes tetragonal and nonsuperconducting beyond this value of ?. Oxygen stoichiometry in this and related oxides has to be understood in terms of structure and disorder. The structure of La3?xBa3+xCu6O14 is related to that of YBa2Cu3O7, the orthorhombic structure manifesting itself when the population of O1 oxygens (along the Cusingle bondOsingle bondCu chains) is preponderant compared to that of O5 oxygens (along thea-axis); nearly equal populations of O1 and O5 sites give rise to the tetragonal structure. A transition from a high-Tc (95 K) superconductivity regime to a low-Tc (not, vert, similar60 K) regime occurs in YBa2Cu3O7?? accompanying a change in ?. There is no evidence for Cu3+ in these nominally mixed valent copper oxides. Instead, holes are present on oxygens giving rise to O? or O2?2 species, the concentration of these species increasing with the lowering of temperature. Certain interesting aspects of the superconducting oxides such as domain or twin boundaries, Raman spectra, microwave absorption, and anomalous high-temperature resistivity drops are presented along with the important material parameters. Preparative aspects of the superconducting oxides are briefly discussed. Phase transitions seem to occur atTc as well as at not, vert, similar240 K in YBa2Cu3O7.