Ultraviolet excitation of photoconductivity in thin films of sol-gel SnO2

Tin dioxide (SnO2) thin film photoconductivity spectra were measured for a large temperature range using a deuterium source, the intensity of photocurrent spectra in the range 200-400 nm is temperature dependent, and the photocurrent increases in the ultraviolet even for illumination with photon energies much higher than the bandgap transition. This behavior is related to recombination of photogenerated electron-hole pairs with oxygen adsorbed at grain boundaries, which is consistent with nanoscopic crystallite size of sol-gel deposited films. (c) 2005 Elsevier Ltd. All rights reserved.

Density improvement of the sol-gel dip-coated SnO2 films by chemical surface modification

We compare the effect of organic (Tiron (R)) and inorganic (Mn(11)) additives on the low temperature (< 600 degrees C) densification of the sol-gel dip-coated SnO2 films. The structural and compositional properties of the samples were investigated by X-ray reflectometry (XRR), X-ray absorption spectroscopy (XAS) and X-ray photoelectron spectroscopy (XPS). The results suggest that the replacement of hydroxyl groups at the particle surface by Tiron (R) reduces the level of agglomeration of the sol, increasing the particles packing and the apparent density of the coatings. Undoped and Mn-doped films drawn from a Tiron (R) containing suspension show after firing at 500 degrees C a porosity reduction of 12 and 8.6%, respectively. The porosity decrease is less pronounced (4.3%) for the film without additives. Both XAS and XPS data show the presence of trivalent manganese. The formation of a non-homogeneous solid solution characterised by the presence of Mn(111) replacing tin atom near to the crystallite surface was evidenced by XAS. Additionally, XPS results reveal the presence of metallic Sn at the surface of films containing Tirono. (c) 2005 Elsevier Ltd. All rights reserved.

Characterization of nanosized ZnAl2O4 spinel synthesized by the sol-gel method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effect of fabrication conditions on I-V properties for ZnO varistor with high concentration additives by sol-gel technique

Polycrystalline nano-grain-boundary multi-doping ZnO-based nonlinear varistors with higher concentration additives have been fabricated by sol-gel and standard solid-state reaction method, of which the best sample has a very high threshold voltage of E-b = 3300 V/mm. The effect of sintering processes, sintering temperature and sintering time, and that of additive concentration of Bi2O3 on E-b of the samples are systematically investigated. The results show that the great merit of sol-gel method is its high threshold voltage obtained by a lower sintering temperature than the solid-state reaction method. The present work also shows that five phases including solid-state sintering, rich Bi liquid phase formation and ZnO as well as other additive dissolution, ZnO grain growth, the secondary phase sufficient formation and evolution have been experienced at different sintering temperatures. The hole type defect and nonhomogeneity of the microstructure will lead to the decrease of threshold voltage, i.e., the grain size and the homogeneity of the material will be important factors and directly affect the characteristic of the varistor. The sintering characteristic and the influence of Bi2O3 content on the threshold voltage are also discussed. (c) 2004 Elsevier B.V. All rights reserved.

Preparation of bioactive glass ceramic nanoparticles by combination of sol-gel and coprecipitation method

SiO2-CaO-P2O5 ternary bioactive glass ceramic nanoparticles were prepared via the combination of sol-gel and coprecipitation processes. Precursors of silicon and calcium were hydrolyzed in acidic solution and gelated in alkaline condition together with ammonium dibasic phosphate. Gel particles were separated by centrifugation, followed by freeze drying, and calcination procedure to obtain the bioactive glass ceramic nanoparticles. The investigation of the influence of synthesis temperature on the nanopartilce's properties showed that the reaction temperature played an important role in the crystallinity of nanoparticle. The glass ceramic particles synthesized at 55 degrees C included about 15% crystalline phase, while at 25 degrees C and 40 degrees C the entire amorphous nanopowder could be obtained.

COMPARATIVE-STUDY OF CA4Y6(SIO4)(6)O-A PHOSPHORS PREPARED BY SOL-GEL AND DRY METHODS (A=PB2+,EU3+, TB3+,DY3+)

Ca4Y6(SiO4)(6)O:A (A = Pb2+, Eu3+, Tb3+, Dy3+) phosphors have been prepared by two methods: the sol-gel method and the conventional dry method. The crystallization processes and the luminescence characteristics of the phosphors were studied, The sol-gel method features low-temperature formation of the phosphor, leading to successful preparation of Pb2+-activated phosphors which could not be prepared by the dry method at high temperature. The (4f)(8-)(4f)(7)(5d)(1) absorption band of Tb3+ and the charge-transfer (CT) band of Eu3+ have higher energies and narrower half-widths in the sol-gel-derived phosphors than in the phosphors prepared by the dry method, respectively. The Tb3+ and Dy3+ ions show stronger emission in the former than in the latter. Both the yellow-to-blue intensity ratio (Y:B) of Dy3+ and the red-to-orange intensity ratio (R:O) of Eu3+ in the sol-gel-derived phosphors are smaller than those for the phosphors derived by the dry method.

Development and application of a sol-gel immunosorbent-based method for the determination of isoproturon in surface water

An immunosorbent was fabricated by encapsulation Of monoclonal anti-isoproturon antibodies in sol-gel matrix. The immunosorbent-based loading, rinsing and eluting processes were optimized. Based on these optimizations, the sol-gel immunosorbent (SG-IS) selectively extracted isoproturon from an artificial mixture of 68 pesticides. In addition to this high selectivity, the SG-IS proved to be reusable. The SG-IS was combined with liquid chromatography-tandem mass spectrometry (LC-MS-MS) to determine isoproturon in surface water, and the linear range was up to 2.2 mu g/l with correlation coefficient higher than 0.99 and relative standard deviation (RSD) lower than 5% (n = 8). The limit of quantitation (LOQ) for 25-ml surface water sample was 5 ng/l. (c) 2006 Elsevier B.V. All rights reserved.

Transition metal and rare earth metal modified sol-gel titania: a versatile catalyst for organic transformations

Catalysis is a mature field with extensive practical applications in today's society.indeed,the catalysis of petroleum refining,fine chemical synthesis and emission control demands the production of catalysts in bulk quantities.Future improvement of these well established processes is likely to be incremental.On the other hand,the continuous demand for new products will require additional novel and innovative processes.The need for pollution abatement and prevention also imposes new demands on catalysis, and new processes are periodically advanced for the control of emission of gases as well as for remediation processes such as the cleaning of underground waters. The number of problems where catalysis can have a big impact is constantly growing.In general,science stimulated by the technology has enriched the field of catalysis in a way that has had broad and lasting value.The thesis"Transition metal and rare earth metal modified sol-gel titania: a versatile catalyst for organic transformations" accounts the preparation and characterization studies of both transition metals and rare earth metals modified sol-gel titania and its applications in industrially useful organic reactions.

Influence of neodymium ions on photocatalytic activity of TiO(2) synthesized by sol-gel and precipitation methods

Titanium dioxide with and without the addition of neodymium ions was prepared using sol-gel and precipitation methods. The resulting catalysts were characterized by thermal analysis, X-ray diffraction and BET specific surface area. Neodymium addition exerted a remarkable influence on the phase transition temperature and the surface properties of the TiO(2) matrix. TiO(2) samples synthesized by precipitation exhibit an exothermic event related from the amorphous to anatase phase transition at 510 degrees C, whereas in Nd-doped TiO(2) this transition occurred at 527 degrees C. A similar effect was observed in samples obtained using sol-gel method. The photocatalytic reactivity of the catalysts was evaluated by photodegradation of Remazol Black B (RB) under ultraviolet irradiation. Nd-doped TiO(2) showed enhanced photodegradation ability compared to undoped TiO(2) samples, independent of the method of synthesis. In samples obtained by sol-gel, RB decoloration was enhanced by 16% for TiO(2) doped with 0.5% neodymium ions. (C) 2010 Elsevier B.V. All rights reserved.

Sol-gel derived hydroxyapatite/titania biocoatings on titanium substrate

A simple sol–gel method was successfully developed for a hydroxyapatite (HA)/TiO₂ double layer deposition on a pure titanium substrate. Phase formation, surface morphology, and interfacial microstructure were investigated by differential scanning calorimetry analysis (DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The TiO₂ layer was coated by a spin coating method at a speed of 1500 rpm for 15 s, followed by a heat treatment at 560 °C for 20 min. The HA film was subsequently spin coated on the outer surface at the same speed and then heat-treated at difference temperatures. Results indicated that the HA phase began to crystallize after a heat treatment at 580 °C; and the crystallinity increased obviously at a temperature of 780 °C. The HA film showed a porous structure and a thickness of 5–7 μm after the heat treatment at 780 °C. SEM observations revealed no delamination and crack at the interfaces of HA/TiO₂ and TiO₂/Ti. The HA film with a porous structure is expected to be more susceptible to the natural remodeling processes when it is implanted in a living body.

Photoluminescence of Eu(3+) ion in SnO(2) obtained by sol-gel

Photoluminescence data of Eu-doped SnO(2) xerogels are presented, yielding information on the symmetry of Eu(3+) luminescent centers, which can be related to their location in the matrix: at lattice sites, substituting to Sn(4+), or segregated at particles surface. Influence of doping concentration and/or particle size on the photoluminescence spectra obtained by energy transfer from the matrix to Eu(3+) sites is investigated. Results show that a better efficiency in the energy transfer processes is obtained for high symmetry Eu(3+) sites and low doping levels. Emission intensity from (5)D(0) -> (7)F(1) transition increases as the temperature is raised from 10 to 240 K, under excitation at 266 nm laser line, because in this transition the multiphonon emission becomes significant only above 240 K. As an extension of this result, we predict high effectiveness for room temperature operation of Eu-based optical communication devices. X-ray diffraction data show that the impurity excess inhibits particle growth, which may influence the asymmetry ratio of luminescence spectra.

QEXAFS and UV/Vis Simultaneous Monitoring of the TiO2-Nanoparticles Formation by Hydrolytic Sol-Gel Route

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Er-doped silica-based waveguides prepared by different techniques: RF-sputtering, sol-gel and ion-exchange

Erbium-activated silica-based planar waveguides were prepared by three different technological routes: RF-sputtering, sol-gel and ion exchange. Various parameters of preparation were varied in order to optimize the waveguides for operation in the NIR region. Particular attention was devoted to the minimization of the losses and the increase of the luminescence efficiency of the metastable I-4(13/2) state of the Er3+ ion. Waveguide properties were determined by m-line spectroscopy and loss measurements. Waveguide Raman and luminescence spectroscopy were used to obtain information about the structure of the prepared films and about the dynamical processes related to the luminescence of the Er3+ ions.