Anelastic spectroscopy in a Ti alloy used as biomaterial

Ti and its alloys have been used thoroughly in the production of prostheses and dental implants due to their properties, such as high corrosion resistance, low elasticity modulus and high mechanical strength/density relation. Among the Ti-based alloys, the Ti-35Nb-7Zr-5Ta (TNZT) is one that presents the smallest elasticity modulus, making it an excellent alternative to be used as a biomaterial. In this paper, mechanical spectroscopy measurements were made in TNZT alloys containing several quantities of oxygen and nitrogen in solid solution. Mechanical spectroscopy measurements were made by using a torsion pendulum, operating at an oscillation frequency in the interval 4-30 Hz, temperature in the range 100-700 K, heating rate of about 1 K/min and vacuum lower than 10(-5) Torr. Complex relaxation structures and a reduction in the elasticity modulus were observed for the heat-treated and doped samples. The observed peaks were associated with the interactions of interstitial atoms and the alloy elements. (C) 2009 Elsevier B.V. All rights reserved.

Stress induced ordering due interstitials in Nb-4.7 at.%Ta

The presence of interstitial elements in metals cause strong changes in their physical, chemical or mechanical properties. These interstitial impurities interact with the metallic matrix atoms by a relaxation process known as stress induced ordering. Relaxation processes give rise to a peak in the internal friction spectrum, known as Snock effect. The presence of substitutional solutes has a strong influence on Snoek effect, particularly if the substitutional solute element is the one, which interacts with the interstitial element. Anelastic spectroscopy measurements provide information of the behavior of these impurities in the metallic matrix. In this paper, polycrystalline samples of Nb-4.7 at.%Ta alloy have been analyzed in the as-received condition. Measurements of anelastic spectroscopy were carried out using an inverted torsion pendulum, operating with frequency of 2.0-30.0 Hz and in a temperature range between 300 and 700 K. It was observed the presence of a relaxation structure that have been attributed to stress induced ordering due to interstitial atoms around atoms of the metallic matrix. The relaxation structure have been decomposed in its constituent peaks, what it allowed to identify the following relaxation processes: Ta-O, Nb-O and Nb-N. (c) 2005 Elsevier B.V. All rights reserved.

Diffusion phenomena of the oxygen and nitrogen in niobium by mechanical spectroscopy

The short-range diffusion phenomenon (Snoek Effect) was investigated by mechanical spectroscopy measurements between 300 K and 650 K, in a polycrystalline niobium sample, containing oxygen and nitrogen, using a torsion pendulum. Experimental spectra of anelastic relaxation were obtained under three conditions: as-received sample; annealed sample and subsequently annealed in an oxygen atmosphere for three hours at 1170 K in partial pressure of 5°10 -5mbar. The experimental spectra obtained were decomposed in elementary Debye peaks and the anelastic relaxation processes were identified. With anelastic relaxation parameters and the lattice parameters, the interstitial diffusion coefficients of the oxygen and nitrogen in niobium were calculated for each kind of preferential occupation (octahedral and tetrahedral). The results were compared with the literature data, and confirmed that the best adjustment is for the preferential occupation octahedral model for low concentrations of interstitial solutes, but at higher concentration of oxygen were observed deviations of experimental data for the interstitial diffusion coefficients of oxygen in niobium when compared with the literature data, this could be related to the possible occurrence of a double occupation of interstitial sites in the niobium lattice by oxygen interstitials. © (2010) Trans Tech Publications.