A plateau detected in lead accumulation in subsurface deciduous enamel from individuals exposed to lead may be useful to identify children and regions exposed to higher levels of lead

In a previous study, we showed 4 times more lead in surface deciduous enamel (1.9-5.9 mu m) of a notoriously contaminated area (Bauru, Sao Paulo State, Brazil) in comparison to samples from a region with no lead contamination described (Ribeirao Preto, Sao Paulo State, Brazil). The samples from the more superficial enamel (1.9-3.18 mu m) showed higher amounts of lead and the highest variability, while in the subsurface enamel (3.18-5.9 mu m) a plateau in lead content was detected in children living in the contaminated environment (around 600 mu g/g). Here we expand our previous study, and use only samples obtained from subsurface enamel (Ribeirao Preto, n = 186; Bauru, n = 20). We tried to distinguish regions with more children with lead above the threshold of 600 mu g/g of lead in enamel. We tested whether differences in the percentage of children with ""high"" lead (>= 600 mu g/g) could be observed among the different Kindergartens studied in Ribeirao Preto. We also tested whether these results were different from the ones provided by conventional comparison of the data. Ribeirao Preto showed almost 4 times less lead than Bauru (p < 0.0001), and a statistically significant difference was found only in Ribeirao Preto between Kindergarten 2 and 5 (p<0.01). Twelve percent of the children from Ribeirao Preto had ""high"" lead, while 55% of the children from Bauru did so. However, when we looked at the percentages of children with ""high"" lead in each Kindergarten, and compared them, a whole new picture emerged, in which we could see children with ""high"" lead concentrated mainly in 3 Kindergartens from Ribeirao Preto, with Kindergarten 5 with 33% of the children with ""high"" lead, being statistically different from all Kindergartens, except 4 and 6. The threshold of 600 mu g/g of lead in subsurface enamel was tentatively settled here after the plateau seen in exposed children, and enabled us to identify locations with more children exposed to a higher amount of lead. (C) 2008 Elsevier Inc. All rights reserved.

Effect of a 4% titanium tetrafluoride (TiF4) varnish on demineralisation and remineralisation of bovine enamel in vitro

Objectives: This in vitro study assessed the effect of a 4% TiF4 varnish on demineralisation and remineralisation of sound enamel and artificial carious enamel lesions, respectively. Methods: Bovine sound and carious enamel (n = 110) were randomly allocated to each type of varnish: Duraphat (R))-D (NaF, 2.26%F, pH 4.5, Colgate-Brazil, n = 30), Duofluorid (R)-F (NaF, 2.71%F, pH 8.0, FGM-Brazil, n = 30), TiF4-T (2.45%F, pH 1.0, FGM-Brazil, n = 30) and no-fluoride-P (FGM-Brazil, pH 5.0, n = 20). For the formation of artificial enamel caries, half of the blocks were immersed in 32 mL buffer acetate solution (16 h), whereas the other half was maintained sound. The varnishes were applied onto the enamel surfaces. Thus, the samples were subjected to pH cycles (37 degrees C) for 7 days. The response variables tested were surface and cross-sectional hardness. Data were tested using Kruskal-Wallis test (p < 0.05). Results: All F varnishes significantly reduced demineralisation and increased remineralisation in comparison to placebo. The TiF4 did not significantly reduce the surface enamel softening when compared with the other F varnishes, but it decreased the loss of subsurface hardness to the same extent. In enamel blocks with previous artificial carious lesions, the TiF4 significantly improved the rehardening compared to the other varnishes up to 30 mu m depth. Conclusions: The TiF4 varnish was able to decrease the demineralisation and increase the remineralisation of previously sound and carious enamel, respectively. It was equally effective compared to NaF varnishes on reducing the demineralisation at subsurface, but it was more effective on improving the remineralisation at surface and subsurface. (c) 2007 Elsevier Ltd. All rights reserved.

Lead Deposition in Bovine Enamel during a pH-Cycling Regimen Simulating the Caries Process

Like fluoride, lead (Pb) accumulates on the enamel surface pre-eruptively, but it is not yet known whether it also deposits on enamel while dental caries is developing. This study evaluates Pb distribution in bovine enamel slabs submitted to a pH-cycling regimen simulating the caries process. The slabs were subjected to 8 cycles of de- and remineralizing conditions, and Pb (as acetate salt) was added to the de- and remineralized solutions at concentrations of 30 mu g/l (experimental group, E1) and 300 mu g/l (experimental group, E2). The control group (C) consisted of solutions to which Pb was not added. After the pH cycling, 100-mu m sections of the slabs were analyzed by polarizing microscopy, to observe the extent of caries-like lesions, and these sections were used for Pb estimation by Synchrotron radiation X-ray microfluorescence. Caries lesions were observed along all superficial enamel surfaces to an extent of 120 mu m. A Pb concentration gradient was observed in enamel, which decreased toward dentine. The highest Pb signals were observed for group E2, and the differences were statistically significant at enamel depths of 0 (C vs. E2; p = 0.029) and 50 mu m (C vs. E2 and E1 vs. E2; p = 0.029). In conclusion, this study suggests that if Pb is present in the oral environment, it may deposit in enamel during the caries process. Copyright (C) 2011 S. Karger AG, Basel

Analysis of enamel microbiopsies in shed primary teeth by Scanning Electron Microscopy (SEM) and Polarizing Microscopy (PM)

The aims of this study were 1) to verify how close to the theoretically presumed areas are the areas of enamel microbiopsies carried out in vivo or in exfoliated teeth; 2) to test whether the etching solution penetrates beyond the tape borders: 3) to test whether the etching solution demineralizes the enamel in depth. 24 shed upper primary central incisors were randomly divided into two groups: the Rehydrated Teeth Group and the Dry Teeth Group. An enamel microbiopsy was performed, and the enamel microbiopsies were then analyzed by Scanning Electron Microscopy (SEMI) and Polarizing Microscopy (PM). Quantitative birefringence measurements were performed. The ""true"" etched area was determined by measuring the etched enamel using the NIH Image analysis program. Enamel birefringence was compared using the paired t test. There was a statistically significant difference when the etched areas in the Rehydrated teeth were compared with those of the Dry teeth (p = 0.04). The etched areas varied from -11.6% to 73.5% of the presumed area in the Rehydrated teeth, and from 6.6% to 61.3% in the Dry teeth. The mean percentage of variation in each group could be used as a correction factor for the etched area. Analysis of PM pictures shows no evidence of in-depth enamel demineralization by the etching solution. No statistically significant differences in enamel birefringence were observed between values underneath and outside the microbiopsy area in the same tooth, showing that no mineral loss occurred below the enamel superficial layer. Our data showed no evidence of in-depth enamel demineralization by the etching solution used in the enamel microbiopsy proposed for primary enamel. This study also showed a variation in the measured diameter of the enamel microbiopsy in nineteen teeth out of twenty four, indicating that in most cases the etching solution penetrated beyond the tape borders. (C) 2009 Elsevier B.V. All rights reserved.

Bond Strength and Etching Pattern of Adhesive Systems to Enamel: Effects of Conditioning Time and Enamel Preparation

Statement of the problem: The performance of self-etch systems on enamel is controversial and seems to be dependent on the application technique and the enamel preparation. Purpose of the Study: To examine the effects of conditioning time and enamel surface preparation on bond strength and etching pattern of adhesive systems to enamel. Materials and Methods: Ninety-six teeth were divided into 16 conditions (N = 6) in function of enamel preparation and conditioning time for bond strength test. The adhesive systems OptiBond FL (Kerr, Orange, CA, USA), OptiBond SOLO Plus (Kerr), Clearfil SE Bond (Kuraray, Osaka, Japan), and Adper Prompt L-Pop (3M ESPE, St. Paul, MN, USA) were applied on unground or ground enamel following the manufacturers` directions or doubling the conditioning time. Cylinders of Filtek Flow (0.5-mm height) were applied to each bonded enamel surface using a Tygon tube (0.7 mm in diameter; Saint-Gobain Corp., Aurora, OH, USA). After storage (24 h/37 degrees C), the specimens were subjected to shear force (0.5 mm/min). The data were treated by a three-way analysis of variance and Tukey`s test (alpha = 0.05). The failure modes of the debonded interfaces and the etching pattern of adhesives were observed using scanning electron microscopy. Results: Only the main factor ""adhesive"" was statistically significant (p < 0.001). The lowest bond strength value was observed for OptiBond FL. The most defined etching pattern was observed for 35% phosphoric acid and for Adper Prompt L-Pop. Mixed failures were observed for all adhesives, but OptiBond FL showed cohesive failures in resin predominantly. Conclusions: The increase in the conditioning time as well as the enamel pretreatment did not provide an increase in the resin-enamel bond strength values for the studied adhesives. CLINICAL SIGNIFICANCE The surface enamel preparation and the conditioning time do not affect the performance of self-etch systems to enamel. (J Esthet Restor Dent 20:322-336, 2008)

Effect of a 4% titanium tetrafluoride (TiF4) varnish on demineralisation and remineralisation of bovine enamel in vitro

Objectives: This in vitro study assessed the effect of a 4% TiF4 varnish on demineralisation and remineralisation of sound enamel and artificial carious enamel lesions, respectively.Methods: Bovine sound and carious enamel (n = 110) were randomly allocated to each type of varnish: Duraphat (R))-D (NaF, 2.26%F, pH 4.5, Colgate-Brazil, n = 30), Duofluorid (R)-F (NaF, 2.71%F, pH 8.0, FGM-Brazil, n = 30), TiF4-T (2.45%F, pH 1.0, FGM-Brazil, n = 30) and no-fluoride-P (FGM-Brazil, pH 5.0, n = 20). For the formation of artificial enamel caries, half of the blocks were immersed in 32 mL buffer acetate solution (16 h), whereas the other half was maintained sound. The varnishes were applied onto the enamel surfaces. Thus, the samples were subjected to pH cycles (37 degrees C) for 7 days. The response variables tested were surface and cross-sectional hardness. Data were tested using Kruskal-Wallis test (p < 0.05).Results: All F varnishes significantly reduced demineralisation and increased remineralisation in comparison to placebo. The TiF4 did not significantly reduce the surface enamel softening when compared with the other F varnishes, but it decreased the loss of subsurface hardness to the same extent. In enamel blocks with previous artificial carious lesions, the TiF4 significantly improved the rehardening compared to the other varnishes up to 30 mu m depth.Conclusions: The TiF4 varnish was able to decrease the demineralisation and increase the remineralisation of previously sound and carious enamel, respectively. It was equally effective compared to NaF varnishes on reducing the demineralisation at subsurface, but it was more effective on improving the remineralisation at surface and subsurface. (c) 2007 Elsevier Ltd. All rights reserved.

Microhardness change of enamel due to bleaching with in-office bleaching gels of different acidity

Objective. The aim of this study was to assess the enamel microhardness treated with three in-office bleaching agents, containing 35% hydrogen peroxide with different acidity. Materials and methods. Bovine incisors were divided into three groups that received the following bleaching agents: Whiteness HP, Total Bleach and Opalescence Xtra. Three gel applications/10-min each, totaling 30-min of bleaching treatment, were made on the teeth and activated with a blue LED (1000 mW/470 nm) combined to a LASER (120 mW/795 nm) device (Easy Bleach-Clean Line). Vickers hardness (VH) was evaluated at baseline and after the bleaching procedure. The values of Hardness loss [HNL] (% reduction) were calculated. The two-sample t-test was used for comparison of the HNL of the three bleaching products (5% level of significance). Results. The Opalescence Xtra, which had the lowest pH value (pH = 4.30), showed a significant increase of HNL when compared with Total Bleach bleaching agent, which had the highest pH value (pH = 6.62). Conclusions. The 35% hydrogen peroxide bleaching agents resulted in a reduction in surface enamel microhardness and bleaching with the most acid agent resulted in a significant enamel hardness loss compared to the less acid agent (4.30 vs 6.62). Strategies proposed to reduce the enamel loss after bleaching treatment may include the use of daily fluoride therapy, mouth rinsing (fluoride, milk and sodium bicarbonate solution), fluoride/bicarbonate dentifrices without abrasives, do not toothbrush immediately after bleaching, fluorides and calcium add to bleaching agents.

OBSERVATIONS on ETCHED ENAMEL IN NON-ERUPTED DECIDUOUS MOLARS: A SCANNING ELECTRON MICROSCOPIC STUDY

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of incorporation of remineralizing agents into bleaching gels on the microhardness of bovine enamel in situ

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Enamel microabrasion: an overview of clinical and scientific considerations

Superficial stains and irregularities of the enamel are generally what prompt patients to seek dental intervention to improve their smile. These stains or defects may be due to hypoplasia, amelogenesis imperfecta, mineralized white spots, or fluorosis, for which enamel microabrasion is primarily indicated. Enamel microabrasion involves the use of acidic and abrasive agents, such as with 37% phosphoric acid and pumice or 6% hydrochloric acid and silica, applied to the altered enamel surface with mechanical pressure from a rubber cup coupled to a rotatory mandrel of a low-rotation micromotor. If necessary, this treatment can be safely combined with bleaching for better esthetic results. Recent studies show that microabrasion is a conservative treatment when the enamel wear is minimal and clinically imperceptible. The most important factor contributing to the success of enamel microabrasion is the depth of the defect, as deeper, opaque stains, such as those resulting from hypoplasia, cannot be resolved with microabrasion, and require a restorative approach. Surface enamel alterations that result from microabrasion, such as roughness and microhardness, are easily restored by saliva. Clinical studies support the efficacy and longevity of this safe and minimally invasive treatment. The present article presents the clinical and scientific aspects concerning the microabrasion technique, and discusses the indications for and effects of the treatment, including recent works describing microscopic and clinical evaluations.

Fluoride increases lead concentrations in whole blood and in calcified tissues from lead-exposed rats

Higher blood lead (BPb) levels have been reported in children living in communities that receive fluoride-treated water. Here, we examined whether fluoride co-administered with lead increases BPb and lead concentrations in calcified tissues in Wistar rats exposed to this metal from the beginning of gestation. We exposed female rats and their offspring to control water (Control Group), 100 mg/L of fluoride (F Group), 30 mg/L of lead (Pb Group), or 100 mg/L of fluoride and 30 mg/L of lead (F+ Pb Group) from 1 week prior to mating until offspring was 81 days old. Blood and calcified tissues (enamel, dentine, and bone) were harvested at day 81 for lead and fluoride analyses. Higher BPb concentrations were found in the F+ Pb Group compared with the Pb Group (76.7 +/- 11.0 mu g/dL vs. 22.6 +/- 8.5 mu g/dL, respectively: p <0.001). Two-to threefold higher lead concentrations were found in the calcified tissues in the F+ Pb Group compared with the Pb Group (all p <0.001). Fluoride concentrations were similar in the F and in the F+ Pb Groups. These findings show that fluoride consistently increases BPb and calcified tissues Pb concentrations in animals exposed to low levels of lead and suggest that a biological effect not yet recognized may underlie the epidemiological association between increased BPb lead levels in children living in water-fluoridated communities. (C) 2010 Elsevier Ireland Ltd. All rights reserved.

Lead in saliva from lead-exposed and unexposed children

Introduction: Whole blood is used for diagnosis of lead exposure. A non-invasive method to obtain samples for the biomonitoring of lead contamination has become a necessity. This study 1) compares the lead content in whole saliva samples (Pb-saliva) of children from a city with no reported lead contamination (Ribeirao Preto, Sao Paulo State, Brazil) and children of a region notoriously contaminated with lead (Bauru, Sao Paulo State, Brazil), and 2) correlates Pb-saliva with the lead content in the enamel microbiopsy samples (Pb-enamel) in the case of these two populations. Methods: From a population of our previous study that had included 247 children (4- to 6-year-old) from Ribeirao Preto, and 26 children from Bauru, Pb-saliva was analyzed in 125 children from Ribeirdo Preto and 19 children from Bauru by inductively coupled plasma mass spectrometry (ICPMS). To correlate Pb-saliva with Pb-enamel, we used Pb-enamel data obtained in our previous study. The Mann-Whitney test was employed to compare the Pb-saliva data of the two cities. Pb-saliva and Pb-enamel values were then Log(10) transformed to normalize data, and Pb-saliva and Pb-enamel were correlated using Pearson`s correlation coefficient. Results: Median Pb-saliva from the Ribeirao Preto population (1.64 mu g/L) and the Bauru population (5.85 mu g/L) were statistically different (p<0.0001). Pearson`s correlation coefficient for Log(10) Pb-saliva versus Log(10) Pb-enamel was 0.15 (p=0.08) for Ribeirao Preto and 0.38 (p=0.11) for Bauru. Conclusions: A clear relationship between Pb-saliva and environmental contamination by lead is shown. Further studies on Pb-saliva should be undertaken to elucidate the usefulness of saliva as a biomarker of lead exposure, particularly in children. (C) 2008 Elsevier B.V. All rights reserved.

Deposition of Lead and Cadmium Released by Cigarette Smoke in Dental Structures and Resin Composite

Cigarette smoke is a significant source of cadmium, lead, and toxic elements, which are absorbed into the human organism. In this context, the aim of this study was to investigate in vitro the presence of toxic elements, cadmium, and lead deriving from cigarette smoke in the resin composite, dentine, and dental enamel. Eight cylindrical specimens were fabricated from resin composite, bovine enamel, and root dentin fragments that were wet ground and polished with abrasive paper to obtain sections with 6-mm diameter and 2-mm thickness. All specimens were exposed to the smoke of 10 cigarettes/day during 8 days. After the simulation of the cigarette smoke, the specimens were examined with scanning electron microscopy (SEM) and the energy-dispersive X-ray analysis. In the photomicrographic analysis in SEM, no morphological alterations were found; however, the microanalysis identified the presence of cadmium, arsenic, and lead in the different specimens. These findings suggest that the deposition of these elements derived from cigarette smoke could be favored by dental structures and resin composite. Microsc. Res. Tech. 74:287-291, 2011. (C) 2010 Wiley-Liss, Inc.

Papel de cepas de Streptococcus mutans e Bifidobacterium spp. na etiologia ou proteção contra doenças bucais

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Erosão dentária na adolescência

Com o presente trabalho, pretende-se perceber qual a relação do estilo de vida, hábitos alimentares e doenças sistémicas dos adolescentes com a erosão dentária, e quais são as melhores formas de prevenção e tratamento. É na fase da adolescência que começa a haver uma maior preocupação com o corpo e que começam a surgir alguns extremos de consumo alimentar, que podem caracterizar-se em desordens alimentares afetando diretamente a saúde oral, podendo causar erosão dentária. É também na adolescência que a prática de atividade desportiva aumenta, podendo também ter impacto no desenvolvimento desta patologia. A erosão dentária começa com a desmineralização das camadas superficiais do esmalte, podendo evoluir para perda significativa da estrutura dentária. Os ácidos responsáveis pela erosão dentária podem ter origem extrínseca ou intrínseca. Enquanto os fatores extrínsecos estão relacionados com hábitos alimentares e estilo de vida, os fatores intrínsecos podem ser provocados por doenças sistémicas. O fator fundamental da prevenção da erosão dentária é a diminuição da frequência e da severidade do ataque ácido. No entanto, pela sua etiologia multifatorial, muitas vezes este controlo torna-se difícil. Em relação ao tratamento, existem diferentes opções dependendo do grau da lesão, mas um diagnóstico precoce é o fator chave neste processo. É importante referir que a monitorização e o controlo periódico do paciente deverão ser realizados com o objetivo de promover a sua saúde e prevenir o aparecimento de novas lesões.