A solvothermal route to crystalline lithium niobate

A solvothermal route for the preparation of crystalline state lithium niobate using Li2 CO3 and Nb2 O5 is developed. Oxalic acid is employed as solvent, which coordinates with niobium oxide to stimulate the main reaction. Scanning electron microscopy images show that the as-prepared sample displays a cubic morphology. X-ray diffraction and IR spectrum of the as-prepared sample indicate that the sample is well crystalline.

Synthesis of carbon nanotube bundles with mesoporous structure by a self-assembly solvothermal route

A kind of carbon nanotube bundle has been synthesized by a simple one-step solvothermal reaction between Na and hexachlorobenzene (HCB) using NiCl2 as catalyst precursor. Before the reaction, NiCl2 was initially dispersed ultrasonically in cyclohexane then prereduced by Na at 230degreesC to produce small Ni particles in reduced state. The tubes thus-produced have a uniform outer diameter of about 20 nm, an inner diameter of 4 nm, and are highly ordered assembled as bundles which have a 2D hexagonal arrangement as proven by SAXS and TEM experiments.

Size-controlled synthesis and characterization of quantum-size SnO2 nanocrystallites by a solvothermal route

By using ethylenediamine as both an alkali and ligand, quantum size SnO2, nanocrystallites were synthesized with a solvothermal route. The transmission electron micrographs (TEM) were employed to characterize the morphologies of the products. The crystal sizes of the as-synthesized SnO2 were ranged form 2.5 to 3.6 nm. The crystal structure and optical properties of the products were investigated by X-ray diffraction, Fourier transform infrared spectroscopy, optical absorption spectra, photoluminescence and Raman spectra.

A solvothermal route to size- and shape-controlled CdSe and CdTe nanocrystals

The size- and shape-controlled CdSe and CdTe nanocrystals, which exhibit obvious quantum confinement effect, have been synthesized by a solvothermal route. It is found that initial precursor concentrations are key factors in controlling the shape of the resulting nanocrystals. Moreover, the obtained nanocrystals are all of zinc blende structure, regardless of their sizes and shapes. A possible mechanism for the formation and growth of the nanocrystals is put forward. It is inferred that the adhesion and subsequent recrystallization of nanocrystals with an assistance of remaining monomers should be a major reason for formation and growth of the elongated nanocrystals.

Solvothermal Synthesis of InP Quantum Dots

We report an efficient and fast solvothermal route to prepare highly crystalline monodispersed InP quantum dots. This solvothermal route, not only ensures inert atmosphere, which is strictly required for the synthesis of phase pure InP quantum dots but also allows a reaction temperature as high as 430 degrees C, which is otherwise impossible to achieve using a typical solution chemistry; the higher reaction temperature makes the reaction more facile. This method also has a judicious control over the size of the quantum dots and thus in tuning the bandgap.

Temperature Dependent Photoluminescence Studies in Hg0.2Cd0.8Te Nanorods Synthesized by Solvothermal Method

Hg0.2Cd0.8Te nanorods were synthesized via solvothermal route using an air-stable Na2Te-O-3. The structural and morphological studies were done by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The diameters of the nanorods were found to be 20-50 nm. The growth of the nanorods were facilitated due to the use of CTAB as surfactant. The temperature dependent photoluminescence (PL) studies between 10-300 K show three prominent PL bands in 0.5-0.7 eV and are attributed to defect centers. The features like temperature independent peak energy and quite sensitive PL intensity which shows a thermal quenching behavior indicate that the defects are related to the compositional disorder.

Uniform YVO4:Ln(3+) (Ln = Eu, Dy, and Sm) nanocrystals: Solvothermal synthesis and luminescence properties

Well-dispersed YVO4:Ln(3+) (Ln = Eu, Dy, and Sm) nanocrystals with uniform morphology and size have been synthesized via a facile solvothermal route. XRD results demonstrate that all of the three samples can be well indexed to the pure tetragonal phase Of YVO4, indicating that the Eu3+, Dy3+, and Sm3+ have been effectively doped into the host lattices of YVO4. TEM images show that the YVO4 nanocrystals exhibit ellipsoid shape and a mean size of about 20 nm, which is in good agreement with the estimation of XRD results.

Shape-Controlled Synthesis of Wurtzite ZnS Microstructures Under Mild Solvothermal Condition

Through a facile solvothermal route using zinc chloride and thiourea as reactants, wurtzite ZnS and its precursor ZnS center dot (en)(0.5) (en = ethylenediamine) with various morphologies and sizes were grown, which were characterized by XRD, SEM, TEM and N-2 adsorption and so on. The phase evolution, composition and morphologies of the products are highly dependent on the concentration of en. By keeping the en-water volume ratio at 1/2 to 1, the nanostripes-flower or nanorod-spheric wurtzite ZnS were easily obtained under 120 degrees C for 6-24 h, which possess relatively higher specific surface area and larger total pore volume.

SrF2 hierarchical flowerlike structures: Solvothermal synthesis, formation mechanism, and optical properties

We present a solvothermal route to the synthesis of SrF2 hierarchical flowerlike structures based on thermal decomposition of single source precursor (SSP) of strontium trifluoroacetate in benzylamine solvent. These flowerlike superstructures are actually composed of numerous aggregated nanoplates, and the growth process involves the initial formation of spherical nanoparticles and subsequent transformation into nanoplates. which aggregated together to form microdisks and finally flowerlike superstructures. The results demonstrate the important role of benzylamine in the formation of well-defined SrF2 superstructures, not only providing size and shape control to form nanoplates but also contributing to the self-assembly behavior of nanoplates to build into flower-like superstructures. Additionally, the photoluminescence properties of the obtained SrF2 superstructures are studied.

Luminescent CdSe and CdSe/CdS core-shell nanocrystals synthesized via a combination of solvothermal and two-phase thermal routes

A new solvothermal route has been developed for synthesizing the size-controlled CdSe nanocrystals with relatively narrow size distribution, and the photoluminescence (PL) quantum yields (QYs) of the nanocrystals can reach 5-10%. Then the obtained CdSe nanocrystals served as cores to prepare the core/shell CdSe/CdS nanocrystals via a two-phase thermal approach, which exhibited much higher PL QYs (up to 18-40%) than the CdSe core nanocrystals. The nanocrystal samples were characterized by ultraviolet-visible (UV-vis) absorption spectra, PL spectra, wide-angle Xray diffraction (WAXD), X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM).

Nanocomposites of Styrene-Butadiene Rubber and Synthetic Anatase Obtained by a Colloidal Route and Their Photooxidation

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Tailoring the Cu(In, Al)S-2 nanostructures for photonic applications

Solvent dependent and low temperature based Chalcopyrite CuIn1-xAlxS2 (CIAS) nano structures were synthesized by a simple one-pot solvothermal route. X-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible spectroscopy and micro-Raman spectroscopy were used to characterize the nanostructures structurally and optically. CIAS hollow spheres were constructed from the nanoplates. Detailed formation mechanism of the hollow spheres was explained. Tentative optical phonon vibrational modes have been discussed. Steady state room temperature IR photodectection have been demonstrated with all the CIAS nanostructures under IR lamp illumination. Photo current was amplified by two orders and one order in case of nano needle like structures and hollow spheres respectively, which was explained based upon the trap assisted space charge. Growth and decay constants lasted for few milli seconds.