Ex Situ Scanning Electrochemical Microscopy (SECM) Investigation of Bismuth- and Bismuth/Lead Alloy Film-Modified Gold Electrodes in Alkaline Medium

Scanning electrochemical microscopy (SECM) in feedback mode was employed to characterise the reactivity and microscopic peculiarities of bismuth and bismuth/lead alloys plated onto gold disk substrates in 0.1 molL(-1) NaOH solutions. Methyl viologen was used as redox mediator, while a platinum microelectrode was employed as the SECM tip. The metal films were electrodeposited ex situ from NaOH solutions containing either bismuth ions only or both bismuth and lead ions. Approach curves and SECM images indicated that the metal films were conductive and locally reactive with oxygen to provide Bi(3+) and Pb(2+) ions. The occurrence of the latter chemical reactions was verified by local anodic stripping voltammetry (ASV) at the substrate solution interface by using a mercury-coated platinum SECM tip. The latter types of measurements allowed also verifying that lead was not uniformly distributed onto the bismuth film electrode substrate. These findings were confirmed by scanning electron microscopy images. The surface heterogeneity produced during the metal deposition process, however, did not affect the analytical performance of the bismuth coated gold electrode in anodic stripping voltammetry for the determination of lead in alkaline media, even in aerated aqueous solutions. Under the latter conditions, stripping peak currents proportional to lead concentration with a satisfactory reproducibility (within 5% RSD) were obtained.

Monitoring cuprous ion transport by scanning electrochemical microscopy during the course of copper electrodeposition

Scanning electrochemical microscopy (SECM), in the substrate generation–tip collection (SG-TC) mode, has been used to detect the cuprous ion intermediate formed during the course of electrodeposition of Cu metal from aqueous solution. Addition of chloride is confirmed to strongly stabilize the ion in aqueous solution and enhance the rate of Cu electrodeposition. This SECM method in the SG-TC mode offers an alternative to the rotating ring disk electrode (RRDE) technique for in situ studies on the effect of plating bath additives in metal electrodeposition. An attractive feature of the SECM relative to the RRDE method is that it allows qualitative aspects of the electrodeposition process to be studied in close proximity to the substrate in a simple and direct fashion using an inexpensive probe, and without the need for forced convection.

Investigation of facilitated ion-transfer reactions at high driving force by scanning electrochemical Microscopy

The kinetics of facilitated ion-transfer (FIT) reactions at high driving force across the water/1,2-dichloroethane (W/DCE) interface is investigated by scanning electrochemical microscopy (SECM). The transfers of lithium and sodium ions facilitated by dibenzo-18-crown-6 (DB18C6) across the polarized W/DCE interface are chosen as model systems because they have the largest potential range that can be controlled externally. By selecting the appropriate ratios of the reactant concentrations (Kr c(M)+/c(DB18C6)) and using nanopipets as the SECM tips, we obtained a series of rate constants (k(f)) at various driving forces (Delta(O)(W) phi(ML+)(0') - Es, Delta(O)(W) phi(ML+)(0') is the formal potential of facilitated ion transfer and Es is the potential applied externally at the substrate interface) based on a three-electrode system. The FIT rate constants k(f) are found to be dependent upon the driving force. When the driving force is low, the dependence of 1n k(f) on the driving force is linear with a transfer coefficient of about 0.3. It follows the classical Butler-Volmer theory and then reaches a maximum before it decreases again when we further increase the driving forces. This indicates that there exists an inverted region, and these behaviors have been explained by Marcus theory.

Study of electron-transfer reactions across an externally polarized water/1,2-dichloroethane interface by scanning electrochemical microscopy

A novel method to study electron-transfer (ET) reactions between ferrocene in 1,2-dichloroethane (DCE) and a redox couple of K3Fe(CN)(6) and K4Fe(CN)(6) in water using scanning electrochemical microscopy (SECM) with a three-electrode setup is reported. In this work, a water droplet that adheres to the Surface of a platinum disk electrode is immersed in a DCE solution. The aqueous redox couple serves both as a reference electrode on the platinum disk and as an electron donor/acceptor at the polarized liquid/liquid inter-face. With the present experimental approach, the liquid/liquid interface can be polarized externally, while the electron-transfer reactions between the two phases can be monitored independently by SECM. The apparent heterogeneous rate constants for the ET reactions were obtained by fitting the experimental approach curves to the theoretical values. These rate constants obey the Butler-Volmer theory i.e., them, are found to be potential dependent.

Study of electron transfer across the liquid/ice-like matrix interface by scanning electrochemical microscopy

In this work, we report the findings of a study on scanning electrochemical microscopy (SECM) to investigate the interfacial electron-transfer (ET) reaction between the 7,7,8,8-tetracyanoquinodimethane radical anion (TCNQ(.-)) in 1,2-dichloroethane and ferricyanide in an ice-like matrix (a mixture of insulting ice and conductive liquid) under low temperatures. Experimental results indicate that the formed liquid/ice-like matrix interface is superficially similar in electrochemical characteristics to a liquid/liquid interface at temperatures above -20 degreesC. Furthermore, imaging data show that the surface of the ice-like matrix is microscopically flat and physically stable and can be applied as either a conductive or an insulting substrate for SECM studies. Perchlorate ion was selected as the common ion in both phases, the concentrations of which controlled the interfacial potential difference. The effect of perchlorate concentration in the DCE phase on interfacial reactions has been studied in detail. The apparent heterogeneous rate constants for TCNQ(.-) oxidation by Fe(CN)(6)(3-) in another phase under different temperatures have been calculated by a best-fit analysis, where the experimental approach curves are compared with the theoretically derived relationships. Reaction rate data obey Butler-Volmer formulation before and after the freezing point, which is similar to most other known cases of ET reactions at liquid/liquid interfaces. However, there is a sharp change observed for heterogeneous rate constants around the freezing point of the aqueous phase, which reflects the phase transition. At temperatures below -20 degreesC, surface-confined voltammograms for the reduction of ferricyanide were obtained, and the ice-like matrix became an insulating one, which indicates that the aqueous phase is really a frozen phase.

Fabrication of nanometer-sized electrodes and tips for scanning electrochemical microscopy

A novel method for fabrication of nanometer-sized electrodes and tips suitable for scanning electrochemical microscopy (SECM) is reported. A fine etched Pt wire is coated with polyimide, which was produced by polymerization on the Pt surface initiated by heat. This method can prepare electrodes with effective radii varying from a few to hundreds of nanometers. Scanning electron microscopy, cyclic voltammetry, and SECM were used to characterize these electrodes. Well-defined steady-state voltammograms could be obtained in aqueous or in 1,2-dichloroethane solutions. Ibis method produced the nanoelectrodes with exposed Pit on the apex, and they can also be employed as the nanotips for SECM investigations. Different sizes of Pt nanotips made by this method were employed to evaluate the kinetics of the redox reaction of Ru(NH3)6(3+) on the surface of a large Pt electrode by SECM, and the standard rate constant kappa (o) of this system was calculated from the best fit of the SECM approach curve. This result is similar to the values obtained by analysis of the obtained voltammetric data.

Investigation of the model compounds at 4-aminobenzoic acid modified glassy carbon electrode by scanning electrochemical microscopy

In this paper, we studied the reactions of both potassium ferricyanide and hexaammineruthenium(III) chloride at a 4-aminobenzoic acid (4-ABA) modified glassy carbon electrode (GCE) by scanning electrochemical microscopy (SECM) in different pH solutions. The surface of the modified electrode has carboxyl groups, the dissociation of which are strongly dependent upon the solution pH values. The rate constant kb of the oxidation of ferrocyanide on the modified electrode can be obtained by fitting the experimental tip current-distance (I-T-d) curves with the theoretical values. The surface pK(a) of the 4-ABA modified GCE was estimated from the plot of standard rate constant k(o) versus the solution pH and is equal to 3.2, which is in good agreement with the reported result. The SECM approach curves for Ru(NH3)(6)(3+) both on the bare and the modified electrodes show similar diffusion control processes. These results can be explained by the electrostatic interactions between the modified electrode surface and the model compounds with different charges. (C) 2001 Elsevier Science BN. All rights reserved.

Scanning electrochemical microscopy study of electron transfer across the water/1,2-dichloroethane interface induced by common ions

In this work, we report the reverse electron transfer reaction between TCNQ in 1, 2-dichloroethane (DCE) and ferrocyanide in water. This process is a thermodynamic unfavorable reaction and the reverse electron transfer reaction can only be obtained by scanning electrochemical microscopy(SECM) in the presence of suitable potential-determining ions, which govern the interfacial potential difference. In our case, the potential determining ions are tetrabutylammonium ion(TBA(+)) and tetraphenylarsonium ion (TPAs+). The effects of the concentrations of TBA(+) and TPAs+ in two phases and other parameters have been studied in detail. The apparent heterogeneous rate constants(k(i)) were obtained under different values of K-p(K-p=c(i)(w)/c(i)(o)) for both cases by fitting the SECM approach curves with theoretical ones and the results showed that they were controlled by the interfacial potential differences. The relationship between apparent heterogeneous rate constants and the interfacial potential differences obeys Butler-Volmer theory.

Probing the Enamel Topography After Acid Erosion by Scanning Electrochemical Microscopy

In this work, we present an investigation on the thickness of the eroded enamel layer in tooth samples after exposure to citric and hydrochloric acid by using Scanning Electrochemical Microscopy (SECM). Approaching curves with typical negative feedback behavior were obtained in enamel samples for evaluation of topographic changes. In a control experiment, SECM images showed no significant difference in the current monitored during the scan, implying that enamel demineralization did not occur in mineral water medium. Topographic SECM images obtained after contact with citric and hydrochloric acid for different periods of time showed a significant increase in the current relative to a previously protected surface, indicating the structural loss of enamel. The thickness of the enamel layer eroded after contact with hydrochloric acid was significantly higher when compared to the one obtained with citric acid. Hence, our results showed that the enamel acid erosion is a relatively fast process, which is strongly dependent on parameters such as pH, time, acid strength and acid concentration.

A study of localised galvanic replacement of copper and silver films with gold using scanning electrochemical microscopy

Galvanic replacement represents a highly significant process for the fabrication of bimetallic materials, but to date its application has been limited to either modification of large area metal surfaces or nanoparticles in solution. Here, the localised surface modification of copper and silver substrates with gold through the galvanic replacement process is reported. This was achieved by generation of a localised flux of AuCl4− ions from a gold ultramicroelectrode tip which interacts with the unbiased substrate of interest. The extent of modification with gold can be controlled through the tip–substrate distance and electrolysis time.

Scanning electrochemical microscopy study of the solid--solid interconversion of TCNQ to phase I and phase II CuTCNQ

The reduction of 7,7,8,8-tetracyanoquinodimethane (TCNQ) crystals attached to a glassy carbon electrode in the presence of Cu2+(aq) to form CuTCNQ(s) has been investigated using scanning electrochemical microscopy in the substrate generation tip collection mode and shown to involve a generation of soluble TCNQ−(aq). The subsequent oxidation of CuTCNQ does not involve simple expulsion of Cu+ into solution but a soluble complex attributed to Cu2+TCNQ−(aq). Mechanistic insights relative to the electrochemical conversion of CuTCNQ phase I into phase II by repetitive cycling of potential and electrochemical formation of KTCNQ have also been established

Scanning electrochemical microscopy of living cells: Different redox activities of nonmetastatic and metastatic human breast cells

Electrochemical methods have been widely used to monitor physiologically important molecules in biological systems. This report describes the first application of the scanning electrochemical microscope (SECM) to probe the redox activity of individual living cells. The possibilities of measuring the rate and investigating the pathway of transmembrane charge transfer are demonstrated. By this approach, significant differences are detected in the redox responses given by nonmotile, nontransformed human breast epithelial cells, breast cells with a high level of motility (engendered by overexpression of protein kinase Cα), and highly metastatic breast cancer cells. SECM analysis of the three cell lines reveals reproducible differences with respect to the kinetics of charge transfer by several redox mediators.