Quantifying rubber degradation using NMR

Ageing can lead to the degradation of the tensile properties of natural rubber. The ageing process causes changes in the polymer segmental motion as well as the chemical structure, both of which can be monitored using nuclear magnetic resonance (NMR) spectroscopy. This work demonstrates that NMR can quantify rubber degradation due to ageing, and also that relatively simple NMR equipment can be used. This simpler equipment can be made portable and so could give a simple and fast indication of the condition of rubber in service. The 1H NMR transverse relaxation time, T2, and the 13C NMR spectrum using cross polarization and magic angle spinning (CP MAS) for samples taken at various levels of a degraded natural rubber liner were compared. These experiments showed that, as the level of degradation increased, the 1H NMR transverse relaxation time decreased. The 13C spectra showed considerable peak broadening, indicative of decreased mobility with increased level of degradation as well as the presence of degradation products. Further investigations using lower powered NMR equipment to measure the 1H NMR transverse relaxation times of two different series of natural rubbers were also performed. This work has shown that this simpler method is also sensitive to structural and mechanical property changes in the rubber. This method of monitoring rubber degradation could lead to the non-destructive use of NMR to determine the condition of a part in service.

Surface Degradation of Silicone Rubber Nanocomposites Due to DC Corona Discharge

Corona discharge is recognized as one of the mechanisms that can influence the surface hydrophobicity of Silicone Rubber (SR) because of the chemical changes that occur on its surface. In this study SR samples were exposed to positive and negative DC corona for 25 and 50 hours using a needle-plane electrode system. Hydrophobicity changes were monitored using a sessile drop contact angle measurement facility. The physical changes on the surface were studied using Scanning Electron Microscopy (SEM) and surface roughness measurements. The effect of positive dc corona was found to be different from that of negative dc corona. Significant surface degradation and loss of hydrophobicity was found in the case of negative dc corona exposed samples. Significant improvement in the above mentioned properties were obtained by adding small quantities of nSIL into the SR matrix.

Effect of Coldfog on the Corona Induced Degradation of Silicone Rubber Samples

Corona is an unavoidable phenomena in high voltage power transmission system, in spite of suitably designed insulator accessories and transmission line hardware. It is a proven fact that the continuous occurrence of corona can subject the polymeric insulator to a severe degradation. Further, moisture in the air has a positive influence on the corona activity. This paper presents the methodology to evaluate the corona performance of the silicone rubber housing material with simultaneous application of cold fog. Analysis conducted after corona treatment by the Fourier Transform Infrared Spectroscopy (FTIR) present an interesting results showing a higher hydroxylation of sample surface under the moisture application than in the normal condition for both AC and DC excitation. FTIR spectrum also indicates the presence of nitric acid on the treated surface with coldfog application. Results obtained from SEM analysis are also presented.

Thermal Degradation of Short Nylon -6 Fiber-Reinforced Styrene Butadiene Rubber Composite

The thermal properties of short Nylon-6 fiber-reinforced Styrene butadiene rubber (SBR) composites were studied by Thermogravimetric Analysis (TGA). The effect of epoxy-based bonding agent on thermal degradation of the gum and the composites was also studied. The thermal stability of the SBR was enhanced in the presence of Nylon-6 fibers and the stability of the composites increased in the presence of bonding agent. The epoxy resin did not significantly change the thermal stability of SBR gum vulcanizate. Results of kinetic studies showed that the degradation of SBR and the short nylon fiber-reinforced composites with and without bonding agents followed first-order kinetics.

Thermal degradation of natural rubber/ZNO nanocomposites

Nanoparticies have been widely used to enhance the properties of natural rubber (NR). In the present paper a novel nanocomposite was developed by blending nano-ZnO slurry with prevulcanized NR latex, and the thermal degradation process of pure NR and NR/ZnO nanocomposites with different nano-ZnO loading was studied with a Perkin Elemer TGA-7 thermogravimetric analyzer. The thermal degradation parameters of NR/ZnO (2 parts ZnO per hundred dlY rubber) at different heating rates (Bs) were studied. The results show that the thermal degradation of pure NR and NR/ZnO nanocomposites in nitrogen is a one-step reaction. The degradation temperatures of NR/ZnO nanocomposite increase with an increasing B. The peak height (R_p) on the differential thermogravimetric curve increases with the increase of B. The degradation rates are not affected significantly by B, and the average values of thermal degradation rate C_p and C_f are 44.42 % and 81.04 %, respectively. The thermal degradation kinetic parameters are calculated with Ozawa-Flynn-Wall method. The activation energy (E) and the frequency factor (A) vary with ecomposition degree, and can be divided into three phases corresponding to the volatilization of low-molecular-weight materials, the thermal degradation ofNR main chains and the decomposition of residual carbon.

Thermal degradation kinetics and morphology of natural rubber/silica nanocomposites

A novel natural rubber/silica (NR/SiO₂) nanocomposite with a SiO₂ loading of 4 wt% is developed by incorporating latex compounding with self-assembly techniques. The SiO₂ nanoparticles are homogenouslydistributed throughout the NR matrix as spherical nano-clusters with an average size of 75 nm. In comparison with the host NR, the thermal resistance of the nanocomposite is significantly improved. The degradation temperatures (T), reaction activation energy(E), and reaction order (n) of the nanocomposite are markedly higher than those of the pure NR, due to significant retardant effect of the SiO₂ nanoparticles.

Thermal degradation kinetics and mechanism of epoxidized natural rubber

Thermal resistance is one of the most dominative properties for polymer materials. Thermal degradation mechanisms of epoxidized natural rubber (ENR) and NR are studied by thermogravimetric analysis (TGA) and differential thermal analysis (DTA). The results show that, the introduction of epoxy groups into the NR molecular main chain leads to a remarkable change in the degradation mechanism. The thermal stability of ENR is worse than that of NR. For the first thermooxidative degradation stage, the thermal decomposition mechanism of ENR is similar to that of NR, which corresponds to a mechanism involving one-dimensional diffusion. For the second stage, the thermal decomposition mechanism of ENR is a three-dimensional diffusion, which is more complex than that of NR. Kinetic analysis showed that activation energy (E?), activation entropy (?H) and activation Gibbs energy (?G) values are all positive, indicating that the thermooxidative degradation process of ENR is non-spontaneous.

A comparative study of the non-isothermal degradation of natural rubber from Mangabeira (Hancornia speciosa Gomes) and Seringueira (Hevea brasiliensis)

Due to the increasing search for alternative sources of natural rubber (NR) whose properties are similar to Hevea brasiliesis, several sources have been studied in the past few years. Among them, Mangabeira (Hancornia speciosa Gomes), which is native to Amazon rainforest and other regions of Brazil, has a potential as another viable rubber source. As a continuation of a series of comparative studies between Hancornia and Hevea (clone RRIM 600) these two species by our research team, their thermal behavior was analyzed by thermogravimetry (TG) using Flynn-Wall-Ozawa's approach in order to obtain kinetic parameters (reaction order, pre-exponential factor and activation energy) of the decomposition process. Results indicated that the thermal behavior of NR from Hancornia was comparable to Hevea with some differences observed as follows: reaction order for Hancornia was higher than for Hevea at the beginning of degradation and very close for temperatures over 350 A degrees C; activation energy and pre-exponential factor had the same trend, i.e., increased with increasing degree of conversion remaining almost constant between 20 and 70% and then increasing for higher degrees, although Hevea was slightly more thermally stable than Hancornia. These major influences in the degradation process in the early stage are attributed to differences in non-rubber constituents present in these two species.

Comparison of the nanoparticles performance in the photocatalytic degradation of a styrene-butadiene rubber nanocomposite

Much has been talking about the advantages of polymeric nanocomposites, but little is known about the influence of nanoparticles on the stability of these materials. In this sense, we studied the influence of both oxides of zirconium and titanium, known to have photocatalytic properties, as well as the influence of synthetic clay Laponite on the photodegradation of styrene-butadiene rubber (SBR). SBR nanocomposites were prepared by the colloidal route by mixing commercial polymer lattices and nanometric anatase TiO2, monoclinic ZrO2 or exfoliated Laponite clays colloidal suspensions. To better understand the degradation mechanisms that occur in these nanocomposites, the efficiency of different photocatalysts under ultraviolet radiation was monitored by FT-IR and UV-vis spectroscopies and by differential scanning calorimetric. It was observed that TiO2 and ZrO2 nanoparticles undoubtedly acted as catalysts during the photodegradation process with different efficiencies and rates. However, when compared to pure SBR samples, the polymer degradation mechanism was unaffected. Unlike studies with nanocomposites montmorillonite, exfoliated laponite clay effectively acts as a photostabilizer of polymer UV photodegradation. Copyright © 2012 Wiley Periodicals, Inc.

Studies on thermal-oxidative degradation behaviours of raw natural rubber: PRI and thermogravimetry analysis

Thermal-oxidative degradation behaviours of raw natural rubber (NR) have been investigated by using thermogravimetry analysis in inert and oxidative atmospheres and the plasticity retention index (PRI). The activation energy E a, was calculated using Horowitz-Metzger and Coats-Redfern methods and compared with PRI. The E a values obtained by each method were in good agreement with each other. The June samples are the least stable rubbers among the studied ones, whereas February samples exhibited the highest values of activation energy, therefore in agreement with the PRI behaviour, which indicates that the thermo-oxidative stability of the June samples are the poorest during the thermo-oxidative degradation reaction. Natural rubber is a product of biological origin, and thus these variations in the values of thermal behaviour and PRI might be related to the genetic differences and alterations of climatic conditions that act directly on the synthesis of non-rubber constituents, which are generally reflected in latex and rubber properties. © 2013 Institute of Materials, Minerals and Mining.

Light scattering studies on solutions of chlorinated rubber

Measurements have been made of the depolarisation factors \sigma u ,\sigma v ,\sigma h, and the intensity of scattering in the horizontal transverse direction, in the case of solutions of four different samples of chlorinated rubber in carbon tetrachloride. The size, shape and molecular weight of the micelles have been deduced by the application of the light scattering theories of Gans, Vrklajan and Katalinic and Debye. The extent to which the degradation of the rubber molecule occurs on chlorination has also been assessed.

Differing mechanisms of simple nitrile formation on glucosinolate degradation in Lepidium sativum and Nasturtium officinale seeds.

Glucosinolates are sulphur-containing glycosides found in brassicaceous plants that can be hydrolysed enzymatically by plant myrosinase or non-enzymatically to form primarily isothiocyanates and/or simple nitriles. From a human health perspective, isothiocyanates are quite important because they are major inducers of carcinogen-detoxifying enzymes. Two of the most potent inducers are benzyl isothiocyanate (BITC) present in garden cress (Lepidium sativum), and phenylethyl isothiocyanate (PEITC) present in watercress (Nasturtium officinale). Previous studies on these salad crops have indicated that significant amounts of simple nitriles are produced at the expense of the isothiocyanates. These studies also suggested that nitrile formation may occur by different pathways: (1) under the control of specifier protein in garden cress and (2) by an unspecified, non-enzymatic path in watercress. In an effort to understand more about the mechanisms involved in simple nitrile formation in these species, we analysed their seeds for specifier protein and myrosinase activities, endogenous iron content and glucosinolate degradation products after addition of different iron species, specific chelators and various heat treatments. We confirmed that simple nitrile formation was predominantly under specifier protein control (thiocyanate-forming protein) in garden cress seeds. Limited thermal degradation of the major glucosinolate, glucotropaeolin (benzyl glucosinolate), occurred when seed material was heated to >120 degrees C. In the watercress seeds, however, we show for the first time that gluconasturtiin (phenylethyl glucosinolate) undergoes a non-enzymatic, iron-dependent degradation to a simple nitrile. On heating the seeds to 120 degrees C or greater, thermal degradation of this heat-labile glucosinolate increased simple nitrile levels many fold.

Long-term Accelerated Weathering of Outdoor Silicone Rubber Insulators

Multistress aging/weathering of outdoor composite polymeric insulators has been a topic of interest for power transmission research community in the last few decades. This paper deals with the long-term accelerated weathering of full-scale distribution class silicone rubber composite insulators. To evaluate the long-term synergistic effect of electric stress, temperature and UV radiation on insulators, they were subjected to accelerated weathering in a specially designed multistress-aging chamber for 30,000 h. All the insulators were subjected to the same level of electrical and thermal stresses but different UV radiation levels. Chemical, physical and electrical changes due to degradation have been assessed using various techniques. It was found that there was a monotonous reduction of the content of low molecular weight (LMW) molecules with the duration of the weathering. Further, due to oxidation and weathering there is an appreciable increase in surface roughness and atomic percentage of oxygen. There is no change in the leakage current of new and aged insulators under both wet and dry conditions at the end of the aging. The results also indicate that there is no influence of UV radiation on the silicone rubber for the durations and conditions under which the studies were made.

Ultrasonic degradation of butadiene, styrene and their copolymers

Ultrasonic degradation of commercially important polymers, styrene-butadiene (SBR) rubber, acrylonitrile-butadiene (NBR) rubber, styrene-acrylonitrile (SAN), polybutadiene rubber and polystyrene were investigated. The molecular weight distributions were measured using gel permeation chromatography (GPC). A model based on continuous distribution kinetics approach was used to study the time evolution of molecular weight distribution for these polymers during degradation. The effect of solvent properties and ultrasound intensity on the degradation of SBR rubber was investigated using different pure solvents and mixed solvents of varying volatility and different ultrasonic intensities. (C) 2011 Elsevier B.V. All rights reserved.