Remoção de carbonatos para otimizar a biolixiviação de rejeito calcopirítico empregando consórcio de microrganismos

The bioleaching of chalcopyrite has not been applied on a commercial scale due to the low process efficiency, so this process has been extensively studied in recent years. The bioleaching of chalcopyrite tailings becomes even more difficult by the presence of higher amounts of impurities, among them are the carbonates. The presence of carbonates in the ore promotes the increase in pH of the solution and may inhibit the development of bioleaching. Therefore, this research aims to apply the acid treatment for optimization of bioleaching process, in order to recover the lost copper throughout the process besides reducing the content of this toxic metal in the tailings pond. The removal and recovery of toxic metals is very important in protecting the environment and human health. The bioleaching experiments were performed in two stages, the first made up using the pre-treated tailing with sulfuric acid in bioleaching, and the second was made using the tailing without treatment with sulfuric acid addition at the beginning of bioleaching. The acid treatment was carried out in bioreactors with three different volumes of H2SO4 96% and a control experiment. All bioleaching experiments were performed in triplicate over a control, without addition of inoculum. The results showed that acid treatment was effective in removal of carbonates and managed to promote a good performance in the bioleaching of chalcopyrite in both steps studied, it is demonstrated that circa 47% copper recovery can be achieved.

Remoção de carbonatos para otimizar a biolixiviação de rejeito calcopirítico empregando consórcio de microrganismos

The bioleaching of chalcopyrite has not been applied on a commercial scale due to the low process efficiency, so this process has been extensively studied in recent years. The bioleaching of chalcopyrite tailings becomes even more difficult by the presence of higher amounts of impurities, among them are the carbonates. The presence of carbonates in the ore promotes the increase in pH of the solution and may inhibit the development of bioleaching. Therefore, this research aims to apply the acid treatment for optimization of bioleaching process, in order to recover the lost copper throughout the process besides reducing the content of this toxic metal in the tailings pond. The removal and recovery of toxic metals is very important in protecting the environment and human health. The bioleaching experiments were performed in two stages, the first made up using the pre-treated tailing with sulfuric acid in bioleaching, and the second was made using the tailing without treatment with sulfuric acid addition at the beginning of bioleaching. The acid treatment was carried out in bioreactors with three different volumes of H2SO4 96% and a control experiment. All bioleaching experiments were performed in triplicate over a control, without addition of inoculum. The results showed that acid treatment was effective in removal of carbonates and managed to promote a good performance in the bioleaching of chalcopyrite in both steps studied, it is demonstrated that circa 47% copper recovery can be achieved.

Estudo da viabilidade de utilização do rejeito cerâmico, como agregado graúdo, na produção de concreto com características estruturais

Este trabalho tem como objetivo principal, efetuar um estudo da viabilidade da utilização do rejeito de indústrias de produtos cerâmicos (cerâmica vermelha), como substitutivo do agregado graúdo de rocha, na produção de concreto com características estruturais. O rejeito foi coletado em quatro diferentes indústrias, localizadas no município de Gravataí, região metropolitana da Grande Porto Alegre-RS, sendo posteriormente britado, para a obtenção do agregado, objeto deste estudo. Foram analisadas as principais características do agregado produzido, distribuição granulométrica, massa unitária, massa específica e absorção de água. A seguir, foi feito um estudo para estabelecer o teor de argamassa a ser utilizado nas misturas, sendo efetuado também uma avaliação da resistência à compressão em função do teor de argamassa. Uma vez fixado o teor de argamassa, foram feitos ensaios a fim de estabelecer a correlação da resistência à compressão, com a relação água/cimento, gerando, desta forma, as chamadas curvas de Abrams, vindo a possibilitar o traçado dos gráficos de dosagem. O estudo baseou-se em determinações experimentais da resistência à compressão, da resistência à tração por compressão diametral, absorção de água, o desgaste e o módulo de deformação estática, utilizando-se em referência de comparação um concreto convencional, produzido com brita basáltica. Todas as misturas foram confeccionadas com cimento Portland pozolânico (tipo IV) classe 32, areia natural de rio e água potável. Os resultados obtidos mostraram ser tecnicamente viável, o emprego do rejeito cerâmico, como agregado graúdo, na produção de concreto.

Análise comparativa entre as propriedades do gesso obtido de rejeito da produção de sal e gesso comerciais

The environmental impacts, caused by the solid residues generation, are an often quoted concern nowadays. Some of these residues, which are originated from different human activities, can be fully reused, reducing the effects of the poor waste management on the environment. During the salt production process, the first formed crystals are discarded as industrial waste. This is mainly made of gypsum that is a calcium sulfate dihydrate (CaSO4.2H2O). The gypsum in question may go through a calcination process due to the plaster (CaSO4.0,5H2O) production and then the application on the cement industry. Considering the necessity of development and application for these industrial wastes, this paper aims to analyze the plaster, called Salgesso, from the gypsum that was generated during the salt production, and its use viability on the civil construction industry in order to create environmental and economical benefits. For characterization, the following experiments were performed: X-ray Fluorescence (XRF), X-ray Diffraction (XRD), thermal analysis (TG/DTG) and Scanning Electron Microscopy (SEM) with EDS. The following tests were also performed to obtain the mechanical characteristics: Thinness Modulus, Unit Mass, Setting Time and Compressive Resistance. Three commercial plasters used on civil construction were taken as references. All of these tests were performed according to the current standards. It was noticed that although there were some conflicting findings between the salt and commercial plasters in all of the studied properties, the Salgesso has its values within the standard limits. However, there is the possibility to improve them by doing a more effective calcination process. Three commercial plasters, used in construction, were used as reference material. All tests were performed according to standards in force. It was observed that although some tests present conflicting findings between the salt and gypsum plasters commercial properties in all of the studied Salgesso have values within the limits imposed by the standard, but can be improved simply by calcination process more effective

Rejeito de xisto como adsorvente para remoção de fenol em águas produzidas na indústria de petróleo

Produced water is the main effluent linked to the activity of extraction of oil and their caring management is necessary due to the large volume involved, to ensure to minimize the negative impacts of discharges of these waters in the environment. This study aimed to analyze the use of retorted shale, which is a reject from the pyrolysis of pirobituminous shale, as adsorbent for the removal of phenols in produced water. The material was characterized by different techniques (grain sized analysis, thermal analysis, BET, FRX, FT-IR, XRD and SEM), showing the heterogeneity in their composition, showing its potential for the removal of varied compounds, as well as the phenols and their derivatives. For the analysis of the efficiency of the oil shale for the adsorption process, assays of adsorption balance were carried through, and also kinetic studies and dynamics adsorption, in the ETE of the UTPF of Petrobras, in Guamaré-RN. The balance assays shown a bigger conformity with the model of Langmuir and the kinetic model more adjusted to describe the adsorption of phenols in retorted shale was of pseudo-second order. The retorted shale presented a low capacity of adsorption of phenols (1,3mg/g), when related to others conventional adsorbents, however it is enough to the removal of these composites in concentrations presented in the produced water of the UTPF of Guamaré. The assays of dynamics adsorption in field had shown that the concentration of phenol in the effluent was null until reaching its rupture (58 hours). The results showed the possibility of use of the reject for removal of phenols in the final operations of the treatment process, removing as well, satisfactorily, the color and turbidity of the produced water, with more than 90% of removal

Estudo do aproveitamento do rejeito da mineração de esmeraldas na produção de refratários conformados isolantes

Emerald mining is an important area of the economy in Brazil, country which is in second place among the exporting nations of this gem. Due to the process of extraction, a great amount of reject is generated. Since there is no appropriate destination, the reject is abandoned around the mining industries, contributing to environment degradation. Nowadays, some of the most relevant things to an industry in general are: energy conservation, cost reduction, quality and productivity enhancement. The production of isolating, transformed refractory materials achieves the sustainability dimension when protection of the environment is incorporated to such process. This work investigates the use of emerald mining rejects in the ceramic body of refractory materials, aiming at obtaining a product whose characteristics are compatible with commercial products and, at the same time, allow the use of such rejects to solve the environmental issue caused by its disposal in nature. X-ray fluorescence analysis show that the emerald reject obtained after the flotation to extract molybdenum and mica has 70% of silica and alumina (SiO2+Al2O3) and 21% of a basic oxides and alkaline metals and earthy alkaline mixture (Na2O, K2O, CaO e MgO). Because of the significant amount of silica and alumina present in the reject, four refractory ceramic bodies were prepared. Samples with a rectangular shape and dimensions 100x50x10 mm were pressed in a steel mold at 27,5 MPa and sintered at 1200ºC for 40 min. under environment atmosphere in a resistive oven. The sintered samples were characterized in relation to the chemical composition (FRX), mineralogical composition (DRX), microstructure (MEV) and physical and mechanical properties. The results indicate that the mixture with 45% of reject, 45% of alumina and 10% of kaolin presents a refractory quality of 1420ºC, dimensional linear variation below 2.00%, apparent specific mass of 1,56 g/cm3 and porosity of 46,68%, which demonstrates the potential use of the reject as raw material for the industry of isolating transformed refractory materials

Automação de um sistema rotatório para secagem do rejeito de maracujá

The rotary dryer is one of the most used equipments in processing industries. Its automatic control mode of operation is important specially to keep the moisture content of the final product in the desired value. The classical control strategies, like PID (proportional integral derivative) control, are largely used in the industrial sector because of its robustness and because they are easy to be implemented. In this work, a data acquisition system was implemented for monitoring the most relevant process variables, like: both inlet and outlet drying air temperature, dryer rotation, outlet air speed and humidity, and mass of the final product. Openloop tests were realized to identify a mathematical model able to represent the drying process for the rotary system. From this model, a PID controller was tuned using a direct synthesis method, assuming a first order trajectory. The PID controller was implemented in the system in order to control the inlet drying air temperature. By the end, closedloop tests (operating in automatic mode) were realized to observe the controller performance, and, after setting the best tune, experiments were realized using passion fruit seeds as raw material. The experiments realized in closedloop showed a satisfactory performance by the implemented control strategy for the drying air temperature of the rotary system

Síntese e caracterização de analcina obtida a partir de rejeito caulim com aplicação em adsorção

Neste trabalho foi utilizado rejeito de caulim da região do Ipixuna-PA, com objetivo de sintetizar zeólita tipo analcina na forma sódica como fase cristalina predominante, através do processo hidrotérmico. O rejeito foi submetido à calcinação por 4 horas a 700°C, para conversão em metacaulinita. A partir desta metacaulinita foi preparada uma mistura reacional contendo diatomito e hidróxido de sódio, que foi levada à autoclave a uma temperatura de 215°C por 24 horas. Diversas variáveis do processo de síntese foram investigadas, entre elas destacam-se: disponibilidade de sódio, proporção de silício, natureza da fonte de sílica, pH na mistura reacional e tempo de autoclavagem. Isso com o intuito de se determinar quais asalterações que os produtos reacionais sofrem com tais modificações, definindo desta forma a condição ideal de síntese da analcina. Foram avaliadas também algumas propriedades importantes do adsorvente, tais como: estabilidade térmica, onde foi aplicado o método de Rietveld para identificar as modificações na estrutura cristalina; estabilidade em presença ácida; cinética de dessorção gerada pelo íon hidrogênio; comportamento das isotermas de adsorção de cobre, cádmio, zinco e níquel bem como avaliar a seletividade de tais cátions no adsorvente. A síntese de analcina mostrou-se possível usando rejeito de caulim. Quando analcina foi calcinada a 400°C foi observado deslocamento nos planos (h,k,l) e manteve-se constante até 600°C, gerado pela saída de oxigênio da posição 1/8 da analcina, isso gera uma diminuição na célula unitária provocando uma diminuição nos canais e sítios ativos da zeólita o que afetou a capacidade de adsorção.

Influência da granulometria e de aditivos no comportamento reológico do rejeito de lavagem da bauxita

Na mineração da bauxita no município de Paragominas-PA, são descartados no processo de beneficiamento rejeitos com teor de sólido de 33,5 % e granulometria muito fina com D₅₀ abaixo de 5 μm. Esses fatores contribuem para que esta suspensão formada basicamente por silico aluminatos, com elevada concentração de argila caulinita, apresente alta viscosidade e alta tensão inicial de escoamento. Foi realizada análise granulométrica e determinadas as composições químicas e mineralógicas do material. A análise granulométrica foi feita por peneiramento a úmido e as frações finas foram determinadas pela técnica da difração a laser. A determinação da composição química foi feita por Espectrometria de Fluorescência de Raios-X, obtendo-se considerável teor de alumina aproveitável, 21, 28%. A composição mineralógica foi determinada por Difração de Raios-X (DRX), obtendo-se gibsita, hematita, quartzo e caulinita. Realizou-se a determinação dos fatores de atrito da polpa, utilizando equação para fluidos que seguem o modelo de Herschel-Bulkley e utilizando as correlações de Dodge e Metzner. Utilizou-se o viscosímetro VT550, com sensor tipo cilindros coaxiais SV1, para realizar testes de defloculação e floculação utilizando diferentes aditivos reológicos. Os aditivos utilizados foram: hexametafosfato de sódio, hidroxamato, sulfato de alumínio, poliacrilato de sódio e poliacrilamida 25% aniônica. A programação foi taxa de cisalhamento de 100 s^-1, tempo de 20s e temperatura de 32ºC. Os defloculantes podem ser utilizados para melhorar o processo de bombeamento e os floculantes podem ser utilizados como auxiliadores no processo de sedimentação nos espessadores, auxiliando no processo de separação sólido-líquido. Foram realizadas ainda, análises de viscosidade em polpas com diferentes pH e em amostras passante a 400# Tyler, com o objetivo de avaliar se a granulometria e o pH influenciavam no comportamento dos aditivos. Pelo estudo observou-se que a granulometria e o pH influenciam no comportamento dos aditivos, pois quanto menor a granulometria mais eficiente é a atuação do aditivo e o seu comportamento como floculante ou defloculante está condicionado ao ajuste do pH.

Especiação e quimissorção de Pb(II) em rejeito de caulim

This study assesses the adsorption of Pb(II) on natural kaolin waste (KR_natural) and on that treated with 3 mol L^-1 H₂SO₄ and HCl. Equilibrium and thermodynamic parameters were determined. The results indicate that the values of CEC, specific area and SiO₂/Al₂O₃ ratio (4.6-6.0 cmol kg^-1, 14.0-16.0 m² g^-1 and 1.16-1.30, respectively) vary only slightly for the adsorbents; the concentration of Pb²⁺ is much higher than that of other species (PbOH⁺ and Pb(OH) ₂). The values of R_L, ΔGº, ΔHº and ΔSº are typical of feasible, spontaneous, exothermic and ordered adsorption. The chemisorption on KR _natural is more feasible and ordered.

Adsorção de nitrato em caulinita a partir de rejeito de caulim modificado com uréia

Este estudo avalia a eficiência, viabilidade e espontaneidade de processos de adsorção do íon nitrato em caulinita sem tratamento e modificada com uréia, empregando como material de partida o rejeito de processamento de caulim do rio Jari. Os materiais foram caracterizados por difração de raios X, fluorescência de raios X e espectroscopia IV (DRX, FRX e FTIR). As medidas de pH de equilíbrio foram efetuadas por potenciometria e as concentrações de equilíbrio (Ce) de nitrato medidas por cromatografia iônica. Quantidades adsorvidas no equilíbrio (qe), constantes de distribuição (K_d=qe/Ce), fator de separação (R_L) e variação de energia livre de Gibbs (ΔGº), foram calculados com base nos dados experimentais de adsorção. Os resultados de DRX e FTIR confirmaram a formação do complexo caulinita-uréia a partir do tratamento efetuado no rejeito de caulim. Os seguintes dados foram obtidos nos processos de adsorção de nitrato, no rejeito de caulim natural e tratado com uréia: q_Max= 18,17 e 14,1 mmol kg^-1; K_d=0,7-2,2 e 0,45-1,5 L Kg^-1; R^L= 0,35-0,85 e 0,25-0,80; ΔGº= -9,3 a -5,8 e -9,1 a -5,4 kJ mol^-1, respectivamente. Os valores de K_d, ΔGº e R_L são típicos de processos de adsorção física (fisissorção), viáveis e espontâneos e os de q_Max indicam que a retenção de nitrato em rejeito de caulim natural é mais eficiente do que em rejeito modificado com uréia.

Síntese hidrotermal de sodalita básica a partir de um rejeito de caulim termicamente ativado

Basic sodalite was successfully synthesized by hydrothermal method using kaolin waste as source of Aluminum and Silicon. This waste is mainly composed by kaolinite and is produced in large amount by kaolin processing industries for paper coating from the Amazon region. Initially, the waste has been calcined at 700 ºC for 2 h and then reacted with the following solutions: Na₂CO₃ and mixture of Na₂CO₃ + NaOH to 150 ºC with autogenous pressure for 24 h. The raw materials and transformed materials were characterized by XRD, FTIR and SEM. In both studied media, well-crystallized, basic sodalite was the only phase synthesized, while in the literature usually a mixture of zeolites is obtained.

Síntese de zeólita do tipo faujasita a partir de um rejeito de caulim

Materiais zeolíticos foram sintetizados utilizando como fonte principal de silício e alumínio um rejeito industrial gerado durante o beneficiamento do caulim para cobertura de papel; o material de partida e as fases formadas como produtos de reação foram caracterizados por difração de raios X, microscopia eletrônica de varredura e espectroscopia de refletância difusa no infravermelho com transformada de Fourier. O processo de síntese ocorreu em condições hidrotermais através de autoclavagem estática e os efeitos tempo-temperatura, assim como também as relações Si/Al e Na/Al foram considerados. Os resultados mostram que na metodologia desenvolvida com o rejeito de caulim, inicialmente calcinado a 700 ºC por 2 h, submetido em seguida à reação em meio alcalino a 90 ºC por 48 h na presença de uma fonte adicional de sílica foi obtida zeólita do tipo faujasita com boa cristalinidade como fase predominante no produto de síntese.

Estabilidade térmica da zeólita A sintetizada a partir de um rejeito de caulim da Amazônia

Zeólita A foi calcinada nas temperaturas de 200, 400, 600, 800 e 1000 °C/2 h para estudar sua estabilidade térmica. A síntese foi feita a partir de um rejeito de beneficiamento de caulim para a produção de papel de uma empresa mineradora localizada na região Amazônica. A caracterização da zeólita A calcinada nas diferentes temperaturas foi realizada por difração de raios X e microscopia eletrônica de varredura. A zeólita A permaneceu estável até 600 °C, havendo apenas variações nas intensidades dos picos em função da temperatura. A 800 °C o padrão de difração apresentado pelo material continuava sendo da zeólita A mas com ausência de alguns picos. A 1000 °C foi constatado que o produto de calcinação era constituído de nefelina, mulita e provavelmente sodalita. Essa zeólita também foi aquecida em mais duas temperaturas, 900 e 950 °C, com o objetivo de confirmar os dois picos exotérmicos observados em curva de análise térmica diferencial. Os produtos de calcinação nessas temperaturas eram constituídos de nefelina, sodalita e mulita.