Ratchetting of railhead in the vicinity of the gap of the insulated rail joints

Insulated Rail Joints (IRJs) are designed to electrically isolate two rails in rail tracks to control the signalling system for safer train operations. Unfortunately the gapped section of the IRJs is structurally weak and often fails prematurely especially in heavy haul tracks, which adversely affects service reliability and efficiency. The IRJs suffer from a number of failure modes; the railhead ratchetting at the gap is, however, regarded as the root cause and attended to in this thesis. Ratchetting increases with the increase in wheel loads; in the absence of a life prediction model, effective management of the IRJs for increased wagon wheel loads has become very challenging. Therefore, the main aim of this thesis is to determine method to predict IRJs' service life. The distinct discontinuity of the railhead at the gap makes the Hertzian theory and the rolling contact shakedown map, commonly used in the continuously welded rails, not applicable to examine the metal ratchetting of the IRJs. Finite Element (FE) technique is, therefore, used to explore the railhead metal ratchetting characteristics in this thesis, the boundary conditions of which has been determined from a full scale study of the IRJ specimens under rolling contact of the loaded wheels. A special purpose test set up containing full-scale wagon wheel was used to apply rolling wheel loads on the railhead edges of the test specimens. The state of the rail end face strains was determined using a non-contact digital imaging technique and used for calibrating the FE model. The basic material parameters for this FE model were obtained through independent uniaxial, monotonic tensile tests on specimens cut from the head hardened virgin rails. The monotonic tensile test data have been used to establish a cyclic load simulation model of the railhead steel specimen; the simulated cyclic load test has provided the necessary data for the three decomposed kinematic hardening plastic strain accumulation model of Chaboche. A performance based service life prediction algorithm for the IRJs was established using the plastic strain accumulation obtained from the Chaboche model. The predicted service lives of IRJs using this algorithm have agreed well with the published data. The finite element model has been used to carry out a sensitivity study on the effects of wheel diameter to the railhead metal plasticity. This study revealed that the depth of the plastic zone at the railhead edges is independent of the wheel diameter; however, large wheel diameter is shown to increase the IRJs' service life.

Predicting crack initiation due to ratchetting in rail heads using critical element analysis

This paper presents a strategy to predict the lifetime of rails subjected to large rolling contact loads that induce ratchetting strains in the rail head. A critical element concept is used to calculate the number of loading cycles needed for crack initiation to occur in the rail head surface. In this technique the finite element method (FEM) is used to determine the maximum equivalent ratchetting strain per load cycle, which is calculated by combining longitudinal and shear stains in the critical element. This technique builds on a previously developed critical plane concept that has been used to calculate the number of cycles to crack initiation in rolling contact fatigue under ratchetting failure conditions. The critical element concept simplifies the analytical difficulties of critical plane analysis. Finite element analysis (FEA) is used to identify the critical element in the mesh, and then the strain values of the critical element are used to calculate the ratchetting rate analytically. Finally, a ratchetting criterion is used to calculate the number of cycles to crack initiation from the ratchetting rate calculated.

Investigation of surface ratchetting due to rail/wheel contact

This project advances the knowledge of rail wear and crack formation due to rail/wheel contact in Australian heavy-haul railway lines. This comprehensive study utilised numerous techniques including: simulation using a twin-disk test-rig, scanning electron microscope particle analysis and finite element modeling for material failure prediction. Through this work, new material failure models have been developed which may be used to predict the lifetime and reliability of materials undergoing severe contact conditions.

Sub-modelling for the ratchetting failure of insulated rail joints

Insulated rail joints are critical for train safety as they control electrical signalling systems; unfortunately they exhibit excessive ratchetting of the railhead near the endpost insulators. This paper reports a three-dimensional global model of these joints under wheel–rail contact pressure loading and a sub-model examining the ratchetting failures of the railhead. The sub-model employs a non-linear isotropic–kinematic elastic–plastic material model and predicts stress/strain levels in the localised railhead zone adjacent to the endpost which is placed in the air gap between the two rail ends at the insulated rail joint. The equivalent plastic strain plot is utilised to capture the progressive railhead damage adequately. Associated field and laboratory testing results of damage to the railhead material suggest that the simulation results are reasonable.

Experimental investigation into the failure behaviour of insulated rail joints

Ratchetting failure of railhead material adjacent to endpost which is placed in the air gap between the two rail ends at insulated rail joints causes significant economic problems to the railway operators who rely on the proper functioning of these joints for train control using the signalling track circuitry. The ratchetting failure is a localised problem and is very difficult to predict even when complex analytical methods are employed. This paper presents a novel experimental technique that enables measurement of the progressive ratchetting. A special purpose test rig was developed for this purpose and commissioned by the Centre for Railway Engineering at Central Queensland University. The rig also provides the capability of testing of the wheel/rail rolling contract conditions. The results provide confidence that accurate measurement of the localised failure of railhead material can be achieved using the test rig.

Experimental investigation of wheel/rail rolling contact at railhead edge

Wheel-rail rolling contact at railhead edge, such as a gap in an insulated rail joint, is a complex problem; there are only limited analytical, numerical and experimental studies available on this problem in the academic literature. This paper describes experimental and numerical investigations of railhead strains in the vicinity of the edge under the contact of a loaded wheel. A full-scale test rig was developed to cyclically apply wheel/rail rolling contact load to the edge zone of the railhead. An image analysis technique was employed to determine the railhead vertical, lateral and shear strain components. The vertical strains determined using the image analysis method have been validated with the strain gauge measurements and used for the calibration of a 3D nonlinear Finite Element Model (FEM) that simulates the wheel/rail contact at the railhead edge and use suitable boundary conditions commensurate to the experimental setup. The FEM was then used to determine other states of strains.

Characterisation of head-hardened rail steel in terms of cyclic plasticity response and microstructure for improved material modelling

Stress- and strain-controlled tests of heat treated high-strength rail steel (Australian Standard AS1085.1) have been performed in order to improve the characterisation of the said material׳s ratcheting and fatigue wear behaviour. The hardness of the rail head material has also been studied and it has been found that hardness reduces considerably below four-millimetres from the rail top surface. Historically, researchers have used test coupons with circular cross-sections to conduct cyclic load tests. Such test coupons, typically five-millimetres in gauge diameter and ten‐millimetres in grip diameter, are usually taken from the rail head sample. When there is considerable variation of material properties over the cross-section it becomes likely that localised properties of the rail material will be missed. In another case from the literature, disks 47 mm in diameter for a twin-disk rolling contact test machine were obtained directly from the rail sample and used to validate ratcheting and rolling contact fatigue wear models. The question arises: How accurate are such tests, especially when large material property gradients exist? In this research paper, the effects of rail sampling location on the ratcheting behaviour of AS1085.1 rail steel were investigated using rectangular-shaped specimens obtained at four different depths to observe their respective cyclic plasticity behaviour. The microstructural features of the test coupons were also analysed, especially the pearlite inter-lamellar spacing which showed strong correlation with both hardness and cyclic plasticity behaviour of the material. This work ultimately provides new data and testing methodology to aid the selection of valid parameters for material constitutive models to better understand rail surface ratcheting and wear.