Microstructure and Mechanical Propertiesof a Nitride-Strengthened Reduced ActivationFerritic/Martensitic Steel

Nitride-strengthened reduced activation ferritic/martensitic (RAFM) steels are developed taking advantage of the high thermal stability of nitrides. In the current study, the microstructure and mechanical properties of a nitride-strengthened RAFM steel with improved composition were investigated. Fully martensitic microstructure with fine nitrides dispersion was achieved in the steel. In all, 1.4 pct Mn is sufficient to suppress delta ferrite and assure the steel of the full martensitic microstructure. Compared to Eurofer97, the steel showed similar strength at room temperature but higher strength at 873 K (600 °C). The steel exhibited very high impact toughness and a low ductile-to-brittle transition temperature (DBTT) of 243 K (–30 °C), which could be further reduced by purification.

Nitride-strengthened reduced activation ferritic/martensitic steels

Two nitride-strengthened reduced activation ferritic/martensitic (RAFM) steels with different Mn contents were investigated. The experimental steels were designed based on the chemical composition of Eurofer 97 steel but the C content was reduced to an extremely low level. Microstructure observation and hardness tests showed that the steel with low Mn content (0.47 wt.%) could not obtain a full martensitic microstructure due to the inevitable δ-ferrite independent of cooling rate after soaking. This steel showed similar room temperature strength and higher strength at 600 °C, but lower impact toughness, compared with Eurofer 97 steel. Fractography of the Charpy impact specimen revealed that the low room temperature toughness should be related to the Ta-rich inclusions initiating the cleavage fracture. The larger amount of V-rich nitrides and more dissolved Cr in the matrix could be responsible for the strength being similar to Eurofer 97 steel. In the second steel developed from the first steel by increasing the Mn content from 0.47 wt.% to 3.73 wt.%, a microstructure of full martensite could be obtained.

ANNEALING BEHAVIOR OF RAFM ODS-EUROFER STEEL

Oxide-dispersion-strengthened (ODS) ferritic-martensitic steels are candidates for applications in fusion power plants where micro structural long-term stability at temperatures of 650 degrees C to 700 degrees C are required. The microstructural stability of 80% cold-rolled reduced-activation ferritic-martensitic 9% Cr ODS-Eurofer steel was investigated within a wide range of temperatures (300 degrees C to 1350 degrees C). Fine oxide dispersion is very effective to prevent recrystallization in the ferritic phase field. The low recrystallized volume fraction (<0.1) found in samples annealed at 800 degrees C is associated with the nuclei found at prior grain boundaries and around coarse M23C6 particles. The combination of retarding effects such as Zener drag and concurrent recovery decrease the local stored energy and impede further growth of the recrystallization nuclei. Above 90 degrees C, martensitic transformation takes place with consequent coarsening. Significant changes in crystallographic texture are also reported.