Fracture strength of machined ceramic crowns as a function of tooth preparation design and the elastic modulus of the cement

Objectives: To determine, by means of static fracture testing the effect of the tooth preparation design and the elastic modulus of the cement on the structural integrity of the cemented machined ceramic crown-tooth complex. 
Methods: Human maxillary extracted premolar teeth were prepared for all-ceramic crowns using two preparation designs; a standard preparation in accordance with established protocols and a novel design with a flat occlusal design. All-ceramic feldspathic (Vita MK II) crowns were milled for all the preparations using a CAD/CAM system (CEREC-3). The machined all-ceramic crowns were resin bonded to the tooth structure using one of three cements with different elastic moduli: Super-Bond C&B, Rely X Unicem and Panavia F 2.0. The specimens were subjected to compressive force through a 4 mm diameter steel ball at a crosshead speed of 1 mm/min using a universal test machine (Loyds Instrument Model LRX.). The load at the fracture point was recorded for each specimen in Newtons (N). These values were compared to a control group of unprepared/unrestored teeth. 
Results: There was a significant difference between the control group, with higher fracture strength, and the cemented samples regardless of the occlusal design and the type of resin cement. There was no significant difference in mean fracture load between the two designs of occlusal preparation using Super-Bond C&B. For the Rely X Unicem and Panavia F 2.0 cements, the proposed preparation design with a flat occlusal morphology provides a system with increased fracture strength. 
Significance: The proposed novel flat design showed less dependency on the resin cement selection in relation to the fracture strength of the restored tooth. The choice of the cement resin, with respect to its modulus of elasticity, is more important in the anatomic design than in the flat design. © 2013 Academy of Dental Materials.

A method of evaluating psychomotor tooth preparation skills in preclinical dental programs

Preclinical and clinical tooth important and significant aspect of preparation is an a dental student's education. The associated procedures rely heavily on the development of particular psychomotor skills. The most common format of instruction and evaluation in tooth preparation at many Dental Faculties, emphasizes the product (tooth preparation) and associates performance with characteristics of this product. This integrated study examines which skills should be developed and how a course of instruction can best be structured to develop the necessary skills. The skills which are identified are those necessary for tooth preparation are selected from a psychomotor taxonomy. The purpose of evaluating these skills is identified. Behavioral objectives are set for student performance and the advisability of establishing standards of performance is examined. After reviewing studies related to learning strategy for dental psychomotor the most suitable tasks as well as articles on instructor effectiveness a model is proposed. A pilot project at the University of Toronto, based on this proposed model is described. The paper concludes wi th a discussion of the implications of this proposed model.

Influence of convergence angle of tooth preparation on the fracture resistance of Y-TZP-based all-ceramic restorations

Objective: To investigate the influence of the convergence angle of tooth preparation on the fracture load of Y-TZP-based ceramic (YZ-Vita YZ) substructure (SB) veneered with a feldspathic porcelain (VM9-Vita VM9). Methods: Finite element stress analysis (FEA) was performed to examine the stress distribution of the system. Eighty YZ SB were fabricated using a CAD-CAM system and divided into four groups (n = 20), according to the total occlusal convergence (TOC) angle: G6-6° TOC; G12-12° TOC; G20-20° TOC; and G20MOD-20° TOC with modified SB. All SB were veneered with VM9, cemented in a fiber reinforced epoxy resin die, and loaded to failure. Half of the specimens from each group (n = 10) were cyclic fatigued (106 cycles) before testing. Failure analysis was performed to determine the fracture origin. Data were statistically analyzed using Anova and Tukey's tests (α = 0.05). Results: The greatest mean load to fracture value was found for the G20MOD, which was predicted by the FEA. Cyclic fatigue did not significantly affect the load of fracture. Catastrophic failure originating from the internal occlusal surface of the SB was the predominant failure mode, except for G20MOD. Significance: The YZ-VM9 restorations resisted greater compression load than the usual physiological occlusal load, regardless of the TOC angle of preparations. Yet, the G20MOD design produced the best performance among the experimental conditions evaluated. © 2013 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Uso de equipamento auxiliar no preparo dentário para próteses

Trabalho apresentado à Universidade Fernando Pessoa como parte dos requisitos para obtenção do grau de Mestre em Medicina Dentária.

Preparos dentários de dentes pilares em prótese parcial removível

A perda de dentes além de afectar a mastigação e a estética, altera também o equilíbrio do sistema estomatognático, observando-se de imediato alterações na posição dos dentes adjacentes e dos dentes oponentes. Torna-se, portanto, imprescindível para a reposição da saúde oral do paciente a reabilitação com recurso a próteses fixas ou removíveis. No que diz respeito às próteses parciais removíveis (PPR´s) estas visam a substituição dos dentes perdidos, sendo facilmente removidas e inseridas pelo paciente, sem qualquer intervenção do médico dentista e, apoiam-se directamente na mucosa e nos dentes. Enquanto as PPR´s acrílicas são suportadas pela mucosa, mediante uma ampla área de contacto, as próteses esqueléticas são suportadas pelos dentes pilares através da colocação de retentores. No caso específico das PPR´s, é fundamental que o profissional de saúde tenha em consideração a importância do planeamento correcto e adequado da reabilitação oral. Para isso, pode e deve utilizar o paralelómetro, determinando assim correctamente a localização dos planos-guia, dos apoios e retentores necessários. Guiando-se por estes princípios fundamentais, qualquer reabilitação com recurso às PPR´s pode ser bem sucedida quer a nível estético quer a nível funcional.

A new intraoral device to facilitate preparation of the guide plane for removable dental prostheses

The design of the ParalAB device facilitates transfer of the path of insertion from the diagnostic cast to the mouth quickly and efficiently.

Effect of the crown design and interface lute parameters on the stress-state of a machined crown-tooth system: A finite element analysis

The effect of preparation design and the physical properties of the interface lute on the restored machined ceramic crown-tooth complex are poorly understood. The aim of this work was to determine, by means of three-dimensional finite element analysis (3D FEA) the effect of the tooth preparation design and the elastic modulus of the cement on the stress state of the cemented machined ceramic crown-tooth complex. The three-dimensional structure of human premolar teeth, restored with adhesively cemented machined ceramic crowns, was digitized with a micro-CT scanner. An accurate, high resolution, digital replica model of a restored tooth was created. Two preparation designs, with different occlusal morphologies, were modeled with cements of 3 different elastic moduli. Interactive medical image processing software (mimics and professional CAD modeling software) was used to create sophisticated digital models that included the supporting structures; periodontal ligament and alveolar bone. The generated models were imported into an FEA software program (hypermesh version 10.0, Altair Engineering Inc.) with all degrees of freedom constrained at the outer surface of the supporting cortical bone of the crown-tooth complex. Five different elastic moduli values were given to the adhesive cement interface 1.8 GPa, 4 GPa, 8 GPa, 18.3 GPa and 40 GPa; the four lower values are representative of currently used cementing lutes and 40 GPa is set as an extreme high value. The stress distribution under simulated applied loads was determined. The preparation design demonstrated an effect on the stress state of the restored tooth system. The cement elastic modulus affected the stress state in the cement and dentin structures but not in the crown, the pulp, the periodontal ligament or the cancellous and cortical bone. The results of this study suggest that both the choice of the preparation design and the cement elastic modulus can affect the stress state within the restored crown-tooth complex.

High-speed cavity preparation techniques with different water flows

Statement of problem. Cavity and tooth preparations generate heat because the use of rotary cutting instruments on dental tissues creates friction. Dental pulps cannot survive temperature increases greater than 5.5degreesC.Purpose. This study evaluated the efficiency of 3 different water flows for 2 different tooth preparation techniques to determine which are safe for use.Material and methods. Thermocouples were placed in the pulpal chambers of 30 bovine teeth, and 1 of 2 tooth preparation techniques was used: a low-load intermittent tooth preparation technique or a high-load tooth preparation technique without intervals. Water flows of 0, 30, and 45 mL/min were associated with each technique, for a total of 6 different groups. The results were analyzed with a 2-factor analysis of variance (P<.05).Results. Temperature increases with the high-load technique were 16.40&DEG;C without cooling (group 1), 11.68&DEG;C with 30 mL/min air-water spray cooling (group III), and 9.96&DEG;C with 45 mL/min cooling (group V). With the low-load tooth preparation technique, a 9.54&DEG;C increase resulted with no cooling (group II), a 1.56&DEG;C increase with 30 mL/min air-water spray cooling (group TV), and a 0.04&DEG;C decrease with 45 mL/min cooling (group VI). The low-load technique was associated with more ideal temperature changes.Conclusion. The results of this study confirm the necessity of using a low-load technique and water coolants during cavity and tooth preparation procedures.

Method for marginal measurements of restorations: accessory device for toolmakers microscope.

Standardization of measurements for marginal fit of castings is critical. This study describes the fabrication of a device that allowed fixation of specimens on a Toolmakers microscope with identical conditions according to tri-dimensional positioning of specimens, measuring location, and seating force. The device also allows mapping of the marginal discrepancies on the entire marginal perimeter of the tooth preparation.

Aesthetic posts and cores for metal-free restoration of endodontically treated teeth.

Utilization of contemporary post and core systems has facilitated the aesthetic restoration of endodontically treated teeth. Light transmission and biocompatibility have been enhanced by the introduction of metal-free post systems. The periodontal and endodontic status, root length, and histological structure of the devitalized teeth must be considered in order to achieve successful restoration following endodontic treatment. This article presents various restorative criteria for the aesthetic placement and buildup of post and core materials, as well as the preservation of maximum coronal and root structure.

Dual path: A concept to improve the esthetic replacement of missing anterior teeth with a removable partial denture

The dual path of insertion concept for removable partial denture (RPD) design may be used in esthetically demanding situations. When compared to conventional RPDs, the main advantage of this design is the minimal use of clasps. This clinical report describes the treatment of a patient with an anterior maxillary edentulous area using a dual path RPD. The diagnostic cast was surveyed to ensure the adequacy of the undercuts on the mesial surfaces of the anterior abutments, where rigid minor connectors were placed. Inverted V-shaped canine cingulum rest seats were prepared to provide resistance to tooth movement during function. The dual path RPD concept allows excellent esthetic results, minimizes tooth preparation, and reduces the tendency toward plaque accumulation in a Kennedy class IV partially edentulous arch. © 2008 by The American College of Prosthodontists.

Retention strength of cobalt-chromium vs nickel-chromium titanium vs Cp titanium in a cast framework association of removable partial overdenture

Aim: There is little information considering the framework association between cast clasps and attachments. The aim of this study was to evaluate the retention strength of frameworks match circumferential clasps and extra resilient attachment cast in three different alloys (cobalt-chromium, nickel-chromium titanium and commercially pure titanium), using two undercut (0.25 and 0.75 mm) and considering different period of time (0, 1/2, 1, 2, 3, 4 and 5 years). Methods: Using two metallic matrices, representing a partially edentulous mandibular right hemiarch with the first molar crown, canine root and without premolars, 60 frameworks were fabricated. Three groups (n = 20) of each metal were cast and each group was divided into two subgroups (n = 10), corresponding the molar undercut of 0.25 mm and 0.75 mm. The nylon male was positioned at the matrix and attached to the acrylic resin of the prosthetic base. The samples were subjected to an insertion and removal test under artificial saliva environment. Results: The data were analyzed and compared with ANOVAs and Tukey's test at 95% of probability. The groups cast in cobaltchromium and nickel-chromium-titanium had the highest mean retention strength (5.58 N and 6.36 N respectively) without significant difference between them, but statistically different from the group cast in commercially pure titanium, which had the lowest mean retention strength in all the periods (3.46 N). The association frameworks using nickel-chromium-titanium and cobalt-chromium could be used with 0.25 mm and 0.75 mm of undercut, but the titanium samples seems to decrease the retention strength, mainly in the 0.75 mm undercut. The circumferential clasps cast in commercially pure titanium used in 0.75 mm undercuts have a potential risk of fractures, especially after the 2nd year of use. Conclusion: This in vitro study showed that the framework association between cast clasp and an extra resilient attachment are suitable to the three metals evaluated, but strongly suggest extra care with commercially pure titanium in undercut of 0.75 mm. Clinical significance: Frameworks fabricated in Cp Ti tend to decrease in retentive strength over time and have a potential risk of fracture in less than 0.75 mm of undercut.

Considerações gerais sobre prótese fixa adesiva

The success rate of resin-bonded fixed partial dentures is directly related to the adhesive system and the tooth preparation design for good retention. These resin-bonded bridges represent a prosthodontic alternative, based on their costeffectiveness, conservative techniques, and ease of laboratory manufacturing. Through a thorough review of the literature, this study aimed to report on cavity designs, types of materials used, and the advantages and disadvantages of the resin-bonded fixed partial denture. One of significant advantages of the resin-bonded fixed partial dentures is the conservation of the tooth structure, whereas its main disadvantage includes aesthetic limitations, given that the alloy may in fact be visible. Preparation design, cement type, and casting alloy type, as well as surface treatment, are among the factors that influence the longevity of resin-bonded fixed partial dentures. Treatments with resin-bonded fixed partial dentures present a bright outlook regarding the conservation of tooth structures, as well as a high level of success.

A multidisciplinary approach to the functional and esthetic rehabilitation of amelogenesis imperfecta and open bite deformity: a case report

The treatment of amelogenesis imperfecta (AI) with an anterior open bite (AOB) is a challenge for the clinician and often requires a multidisciplinary team of specialists. Most often, patients suffering from these conditions are young and a good functional and esthetic long-term result must be aspired. This clinical report illustrates the orthodontic, maxillofacial, restorative, and prosthodontic rehabilitation of a 20-year-old woman with a hypoplastic form of AI and an AOB malocclusion, having received treatment for the last 6 years. It included adhesive resin composite restorations, orthodontical and maxillofacial surgery with a one-piece Le Fort I osteotomy, and a genioplasty. Subsequent prosthodontic therapy consisted of 28 all-ceramic crowns whereby a solid interdigitation, a canine guidance, and consistent and regular contacts between tooth crowns could be achieved to assure a good functional and esthetic oral situation. The tooth preparation techniques guaranteed minimally invasive treatment. The patient was affected very positively. CLINICAL SIGNIFICANCE: This article describes an interdisciplinary approach to the successful treatment of a patient with a hypoplastic form of amelogenesis imperfecta over a period of 6 years. It starts with a discussion of the conservative steps taken during adolescence and concludes with the final prosthetic rehabilitation with all-ceramic crowns after reaching adulthood.