Adição de subprodutos da cinza da casca de café (coffea canephora) em massa cerâmica para porcelanato

To produce porcelain tiles fluxing agents are used in order to obtain a liquid phase during firing. This liquid phase fills the pores decreasing porosity, water absorption and contributes to material densification. In the porcelain tiles industry, feldspar is the main flux material used, with quantities ranging between 35 and 50%. Studies focus on the discovery of materials with flux characteristics that can reduce the consumption of feldspar by porcelain tiles industry. In this context, the coffee husk ashes, a residue obtained when coffee husks are burned to produce heat for the dryers during the processing of the green fruit, have as main chemical constituents potassium, calcium and magnesium, giving them characteristics of fluxing material. Brazil is the largest coffee producer in the world and is responsible for over 30% of the world s production. In this work a physical treatment of coffee husk ash was carried out in order to eliminate the organic matter and, after this, two by-products were obtained: residual wastes R1 and R2. Both residues were added separately as single fluxes and also in association with feldspar in mixtures with raw materials collected in a porcelain industry located in Dias d Ávila-Ba. The addition of these residues aimed to contribute to the reduction of the consumption of feldspar in the production of porcelain tiles. Specimens were produced with dimensions of 60 mm x 20 mm x 6 mm in an uniaxial die with compacting pressure of 45 MPa. The samples were heated to a temperature of 1200 °C, for 8 minutes. Tests were performed to characterize the raw materials by XRF, XRD, particle size analysis, DTA and TGA and, additionally, the results of the physical properties of water absorption, apparent porosity, linear shrinkage, density, dilatometry, flexural strength and SEM of sintered body were analyzed. Additions of less than 8% of the residue R1 contributed to the decrease of porosity, but the mechanical strength of the samples was not satisfactory. Additions of 5% the R2 residue contributed significantly to decrease the water absorption and apparent porosity, and also to increase the mechanical strength. Samples with addition of feldspar associated with the R2 residue, in proportions of 6.7% of R2 and 6.7% of feldspar, led to results of water absorption of 0.12% and mechanical strength of 46 MPa, having parameters normalized to the manufacture of porcelain stoneware tiles

Adição de subprodutos da cinza da casca de café (coffea canephora) em massa cerâmica para porcelanato

To produce porcelain tiles fluxing agents are used in order to obtain a liquid phase during firing. This liquid phase fills the pores decreasing porosity, water absorption and contributes to material densification. In the porcelain tiles industry, feldspar is the main flux material used, with quantities ranging between 35 and 50%. Studies focus on the discovery of materials with flux characteristics that can reduce the consumption of feldspar by porcelain tiles industry. In this context, the coffee husk ashes, a residue obtained when coffee husks are burned to produce heat for the dryers during the processing of the green fruit, have as main chemical constituents potassium, calcium and magnesium, giving them characteristics of fluxing material. Brazil is the largest coffee producer in the world and is responsible for over 30% of the world s production. In this work a physical treatment of coffee husk ash was carried out in order to eliminate the organic matter and, after this, two by-products were obtained: residual wastes R1 and R2. Both residues were added separately as single fluxes and also in association with feldspar in mixtures with raw materials collected in a porcelain industry located in Dias d Ávila-Ba. The addition of these residues aimed to contribute to the reduction of the consumption of feldspar in the production of porcelain tiles. Specimens were produced with dimensions of 60 mm x 20 mm x 6 mm in an uniaxial die with compacting pressure of 45 MPa. The samples were heated to a temperature of 1200 °C, for 8 minutes. Tests were performed to characterize the raw materials by XRF, XRD, particle size analysis, DTA and TGA and, additionally, the results of the physical properties of water absorption, apparent porosity, linear shrinkage, density, dilatometry, flexural strength and SEM of sintered body were analyzed. Additions of less than 8% of the residue R1 contributed to the decrease of porosity, but the mechanical strength of the samples was not satisfactory. Additions of 5% the R2 residue contributed significantly to decrease the water absorption and apparent porosity, and also to increase the mechanical strength. Samples with addition of feldspar associated with the R2 residue, in proportions of 6.7% of R2 and 6.7% of feldspar, led to results of water absorption of 0.12% and mechanical strength of 46 MPa, having parameters normalized to the manufacture of porcelain stoneware tiles

Recuperação do cromo contido nas cinzas provenientes da incineração de resíduos sólidos das indústrias coureira e calçadista visando a obtenção de cromato de sódio (VI)

O processo de transformação da pele em couro envolve uma seqüência complexa de reações químicas e processos mecânicos, no qual o curtimento representa fundamental estágio, por propiciar à pele características como qualidade, estabilidade hidrotérmica e excelentes propriedades para uso. O sulfato básico de cromo trivalente é o agente curtente predominantemente empregado no curtimento de peles em todo o mundo. É produzido a partir do cromato de sódio, industrialmente obtido do minério de cromo. Consideráveis quantidades de resíduos sólidos contendo cromo são geradas pelas indústrias coureira e calçadista. Estes resíduos tem sido motivo de preocupação constante, uma vez que são considerados perigosos devido a presença do cromo. O processo de incineração destes resíduos é uma importante alternativa a ser considerada, em decorrência de suas características de redução de massa, volume e possibilidade de aproveitamento da energia térmica dos gases de combustão. O processo de incineração dos resíduos das indústrias coureira e calçadista dá origem a cinzas contendo cerca de 40% de cromo que pode ser submetida a um processo de recuperação. Este trabalho apresenta os resultados da pesquisa sobre a utilização das cinzas, provenientes da incineração dos resíduos sólidos da indústria coureira e da indústria calçadista, para a produção de cromato de sódio(VI). No processo de planejamento e de condução dos experimentos foram utilizadas as técnicas de Planejamento Fatorial 2k, Metodologia de Superfície de Resposta e Análise de Variância na avaliação da produção de cromato de sódio(VI). Os fatores investigados foram: temperatura, taxa de aquecimento, tempo de reação, vazão de ar e quantidade de dolomita. A partir das variáveis selecionadas identificaram-se como parâmetros importantes a temperatura e a taxa de aquecimento. As superfícies de resposta tridimensionais obtidas a partir dos modelos de segunda ordem ajustados aos dados experimentais, apresentaram o comportamento do efeito conjugado dos fatores temperatura e taxa de aquecimento sobre a variável resposta grau de oxidação, desde a temperatura de inicio da reação química até a temperatura limite utilizada industrialmente. As condições de operação do processo de produção de cromato de sódio(VI) foram otimizadas. Os níveis ótimos dos fatores de controle aplicados as cinzas dos resíduos da indústria calçadista, geradas em uma planta piloto com incinerador de leito fixo, com tecnologia de gaseificação e combustão combinadas, apresentaram um grau de oxidação superior a 96% para as cinzas coletadas no ciclone e de 99,5% para as cinzas coletas no reator de gaseificação. Os resíduos sólidos, as cinzas e o produto de reação foram caracterizados por análises químicas, fluorescência de raio-X, microscopia eletrônica de varredura e difração de raio-X.

Uso da cinza do bagaço da cana-de-açúcar como matéria-prima na substituição dos fundentes para aplicações em porcelanato

The present study aims to evaluate the potential use of bagasse ash from sugar cane (CBC) as a flux, replacing phyllite and/or feldspar in standard industrial mass production of enameled porcelain, verifying the possibility of the CBC contribute to the overall reduction of the coefficient of thermal expansion of the ceramic mass. To this end, as a result of the research, we characterized the raw material components of the standard mass (clay, phyllite, kaolin, feldspar, quartz and talc) and the residue of BCC, by testing by XRF, XRD, AG, DTA and ATG. Specimens (CDP) were manufactured in the dimensions of 100 mm x 50 mm x 8 mm in uniaxial matrix under compaction pressure of 33 MPa, assembled in batches of 3 units subsequently sintered at temperatures of 1150°C to 1210°C by varying the Rating Scale at 10°C, heating and cooling ramp of 50°C/min and 25°C/min, with levels of 1 min, 3 min, 5 min, 8 min, 10 min, 15 min, 30 min and 60 min. analyzing the results of the physical properties of water absorption (WA), linear firing shrinkage (LFS), dilatometric analysis (DTA), flexural strain (SFT) and SEM of the sintered bodies in order to verify the adequacy of CDP to ISO 13006, ISO 10545, NBR 13816 standards; NBR 13817 and NBR 13818. The study showed that the formulations that best suit the requirements of the standards are:. G4 - which was applied in 10% of replacing the CBC phyllite, sintering temperature 1210 ° C for 10 min and porch, and F3 - with application of 7.5% of CBC to replace the feldspar in the sintering temperatures of 1190°C, 1200°C and 1210°C for 10 min and porch. These formulations showed better performance regarding the formation of primary and secondary mullite, with considerable reduction of cracks and pores, meeting the prerequisites of standards for glazed porcelain. The results shows that the use of the CBC as a flux in the preparation of porcelain mass meets standard parameters for the manufacture of the product, and thereby can reduce environmental impact and the cost of production. Therefore, it is recommended to use this residue in the ceramics industry, due to its industrial, commercial and collaborative viability for sustainability.

Incorporação de cinzas da casca de café na produção de placas cerâmicas para revestimento

Brazil is the world s leading coffee producer. In 2008, 45.99 million of 60 kg bags of benefited coffee were produced. In the process of improvement 50% is grain and 50% is husk, thus, 1.38 million tons of coffee husk are produced annually. The husk is used as combustible in the drying and improvement ovens in the coffee farms, generating ash as residue. These ashes contain a high concentration of alkaline metals and earth metals, mainly K2O and CaO. This work studies the use of this residue in the ceramic tiles industry, as fluxing agents in substitution to the feldspar. Ten mixtures with equal ratios of clay and kaolin, proceeding from Bahia and the residue (varying from 30 to 5%) were defined and produced in uniaxial tool die of 60x20mm with approximately 5 mm of thickness and 45MPa compacting pressure. The samples were fired in four different temperatures: 1100 °C, 1150 °C, 1185 °C and 1200 °C during 60 minutes and characterized by means of X-ray fluorescence, X-ray diffraction, gravimetric thermal analysis and differential thermal analysis. The results of water absorption, apparent porosity, linear shrinkage, XRD, dilatometry, flexural strength and SEM were also analysed. The test specimen with addition of 10% of ash fired in 1200 °C resulted in 0.18% water absorption and 40.77 MPa flexural strength, being classified as porcelain stoneware tiles according to ABNT, UNI and ISO norms

Análise microestrutural de misturas cerâmicas de grês porcelanato com adição de chamote de telhas cerâmicas

MELO, Maxymme Mendes de ; PINHEIRO, Andrea Santos ; NASCIMENTO, R. M. ; MARTINELLI, Antonio Eduardo ; DUTRA, Ricardo Peixoto Suassuna ; MELO, Marcus Antônio de Freitas . Análise microestrutural de misturas cerâmicas de grês Porcelanato com adição de chamote de telhas cerâmicas. Cerâmica (São Paulo. Impresso), v. 55, p. 356-364, 2009

Uso de resíduos de queima de casca de café e argila da região sul da Bahia na obtenção de isolador elétrico cerâmico

The electrical ceramic insulators industry, uses noble raw materials such as siliceous and aluminous clays of white burning, in order to provide plasticity of the mass and contribute to electrical and mechanical properties required of the product, and feldspar with the flux function In literature references the composition of the masses indicates that the clay participates in percentage between 20 and 32, and feldspar 8 to 35, these materials have significant cost. In this research was performed the total replacement of commercial clay, for white burning clay from Santa Luzia region in southern Bahia and partial replacement of feldspar by ash residue of husk conilon coffee burning, from extreme south of Bahia. The objective of replacement these raw materials is to aver its technical feasibility and call attention for the embryo pole of ceramic industry for the existing in the south and extreme south of Bahia, which has significant reserves of noble raw materials such as clay white burning, kaolin, quartz and feldspar, and generates significant volume of gray husk conilon coffee as alternate flux. Clay Santa Luzia is prima noble material whose current commercial application is the production of white roofing. The residue of coffee husk ash is discarded near of production sites and is harmful to the environment. Phase diagrams and statistic design of experiments, were used for optimization and cost savings in research. The results confirmed the expectations of obtaining electrical ceramic insulators, with white burning clay of Santa Luzia and partial replacement up to 35.4% of feldspar, by treaty residue of conilon ash coffee husk burning. The statistic design that showed best results was for formulation with percentages of: clay 26.4 to 30.4%; kaolin 14.85 to 17.1%; feldspar 12.92 to 16.96%; R2 residue 7.08 to 9.2% and Quartz 32.5 to 38.75%, relative to the total mass of the mixture. The best results indicated; 0.2 to 1.4% apparent porosity , water absorption 0.1 to 0.7%, flexural strength 35 to 45MPa , dielectric strength 35-41 kV/cm , the transverse resistivity 8x109 2.5x1010 Ω.cm and for the dielectric constant ε/ε0 7 to 10.4, specification parameters for manufacturing ceramic electrical insulators of low and medium voltage.

Estudo da adição de resíduos de quartzitos para obtenção de grés porcelanato

In States of Paraíba (PB) and Rio Grande do Norte (RN), northeast of Brazil, the most significant deposits of non-metallic industrial minerals are pegmatites, quartzites and granites, which are located in Seridó region. Extraction of clay, quartz, micas and feldspars occurs mainly in the cities of Várzea (PB), OuroBranco (RN) and Parelhas (RN). Mining companies working in the extraction and processing of quartzite generate large volumes of waste containing about 90% SiO2 in their chemical composition coming from quartz that is one of the basic constituents of ceramic mass for the production of ceramic coating. Therefore, this work evaluates the utilization of these wastes on fabrication of high-quality ceramic products, such as porcelain stoneware, in industrial scale. Characterization of raw materials was based on XRF, XRD, GA, TGA and DSC analysis, on samples composed by 57% of feldspar, 37% of argil and 6% of quartzite residues, with 5 different colors (white, gold, pink, green and black). Samples were synthesized in three temperatures, 1150°C, 1200°C and 1250°C, with one hour isotherm and warming-up tax of 10°C/min. After synthesizing, the specimens were submit to physical characterization tests of water absorption, linear shrinkage, apparently porosity, density, flexural strain at three points. The addition of 6% of quartzite residue to ceramic mass provided a final product with technological properties attending technical norms for the production of porcelain stoneware; best results were observed at a temperature of 1200°C. According to the results there was a high iron oxide on black quartzite, being their use in porcelain stoneware discarded by ethic and structural question, because the material fused at 1250°C. All quartzite formulations had low water absorption when synthesized at 1200°C, getting 0.1% to 0.36% without having gone through the atomization process. Besides, flexural strain tests overcame 27 MPa reaching the acceptance limits of the European Directive EN 100, at 1200°C synthesizing. Thus, the use of quartzite residues in ceramic masses poses as great potential for the production of porcelain stoneware.

Análise microestrutural de misturas cerâmicas de grês porcelanato com adição de chamote de telhas cerâmicas

MELO, Maxymme Mendes de ; PINHEIRO, Andrea Santos ; NASCIMENTO, R. M. ; MARTINELLI, Antonio Eduardo ; DUTRA, Ricardo Peixoto Suassuna ; MELO, Marcus Antônio de Freitas . Análise microestrutural de misturas cerâmicas de grês Porcelanato com adição de chamote de telhas cerâmicas. Cerâmica (São Paulo. Impresso), v. 55, p. 356-364, 2009

Análise microestrutural de misturas cerâmicas de grês porcelanato com adição de chamote de telhas cerâmicas

MELO, Maxymme Mendes de ; PINHEIRO, Andrea Santos ; NASCIMENTO, R. M. ; MARTINELLI, Antonio Eduardo ; DUTRA, Ricardo Peixoto Suassuna ; MELO, Marcus Antônio de Freitas . Análise microestrutural de misturas cerâmicas de grês Porcelanato com adição de chamote de telhas cerâmicas. Cerâmica (São Paulo. Impresso), v. 55, p. 356-364, 2009

Valorização da Borra de Café: Otimização da Produção de Biodiesel por Catálise Enzimática

O decréscimo das reservas de petróleo e as consequências ambientais resultantes do recurso a combustíveis fósseis nos motores a diesel têm levado à procura de combustíveis alternativos. Esta pesquisa alicerçada nas fontes de energia renovável tornou-se essencial, face à crescente procura de energia e ao limitado fornecimento de combustíveis fósseis . Resíduos de óleo de cozinha, gordura animal, entre outros resíduos de origem biológica, tais como a borra de café, são exemplos de matérias-primas para a produção de biodiesel. A sua valorização tem interesse quer pela perspetiva ambiental, quer pela económica, pois aumenta não só a flexibilidade e diversificação das matérias-primas, mas também contribui para uma estabilidade de custos e alteração nas políticas agrícolas e de uso do solo. É neste contexto que se enquadra o biodiesel e a borra de café, pretendendo-se aqui efetuar o estudo da produção, à escala laboratorial, de biodiesel a partir da borra de café, por transesterificação enzimática, visando a procura das melhores condições reacionais. Iniciando-se com a caracterização da borra de café, foram avaliados antes e após a extração do óleo da borra de café, diversos parâmetros, de entre os quais se destacam: o teor de humidade (16,97% e 6,79%), teor de cinzas (1,91 e 1,57%), teor de azoto (1,71 e 2,30%), teor de proteínas (10,7 e 14,4%), teor de carbono (70,2 e 71,7%), teor de celulose bruta (14,77 e 18,48%), teor de lenhina (31,03% e 30,97%) e poder calorifico superior (19,5 MJ/kg e 19,9 MJ/kg). Sumariamente, constatou-se que os valores da maioria dos parâmetros não difere substancialmente dos valores encontrados na literatura, tendo sido evidenciado o potencial da utilização desta biomassa, como fonte calorifica para queima e geração de energia. Sendo a caracterização do óleo extraído da borra de café um dos objetivos antecedentes à produção do biodiesel, pretendeu-se avaliar os diferentes parâmetros mais significativos. No que diz respeito à caracterização do óleo extraído, distingue-se a sua viscosidade cinemática (38,04 mm2/s), densidade 0,9032 g/cm3, poder calorífico de 37,9 kcal/kg, índice de iodo igual a 63,0 gI2/ 100 g óleo, o teor de água do óleo foi de 0,15 %, o índice de acidez igual a 44,8 mg KOH/g óleo, ponto de inflamação superior a 120 ºC e teor em ácidos gordos de 82,8%. Inicialmente foram efetuados ensaios preliminares, a fim de selecionar a lipase (Lipase RMIM, TL 100L e CALB L) e álcool (metanol ou etanol puros) mais adequados à produção de biodiesel, pelo que o rendimento de 83,5% foi obtido através da transesterificação mediada pela lipase RMIM, utilizando como álcool o etanol. Sendo outro dos objetivos a otimização do processo de transesterificação enzimática, através de um desenho composto central a três variáveis (razão molar etanol: óleo, concentração de enzima e temperatura), recorrendo ao software JMP 8.0, determinou-se como melhores condições, uma razão molar etanol: óleo 5:1, adição de 4,5% (m/m) de enzima e uma temperatura de 45 ºC, que conduziram a um rendimento experimental equivalente a 96,7 % e teor de ésteres 87,6%. Nestas condições, o rendimento teórico foi de 99,98%. Procurou-se ainda estudar o efeito da adição de água ao etanol, isto é, o efeito da variação da concentração do etanol pela adição de água, para teores de etanol de 92%, 85% e 75%. Verificou-se que até 92% decorreu um aumento da transesterificação (97,2%) para um teor de ésteres de (92,2%), pelo que para teores superiores de água adicionada (75% e 85%) ocorreu um decréscimo no teor final em ésteres (77,2% e 89,9%) e no rendimento da reação (84,3% e 91,9%). Isto indica a ocorrência da reação de hidrólise em maior extensão, que leva ao desvio do equilíbrio no sentido contrário à reação de formação dos produtos, isto é, dos ésteres. Finalmente, relativamente aos custos associados ao processo de produção de biodiesel, foram estimados para o conjunto de 27 ensaios realizados neste trabalho, e que corresponderam a 767,4 g de biodiesel produzido, sendo o custo dos reagentes superior ao custo energético, de 156,16 € e 126,02 €, respetivamente. Naturalmente que não esperamos que, a nível industrial os custos sejam desta ordem de grandeza, tanto mais que há economia de escala e que as enzimas utilizadas no processo deveriam ser reutilizadas diversas vezes.

Estudo da potencialidade da incorporação de resíduo de granito e da queima da casca do café em cerâmica vermelha

The industrial production of ornamental rocks and the burning of coffee husk generate waste that is discarded into the environment. However, with the study of the incorporation of these residues in ceramic products, may be found an alternative to reducing environmental impacts and detrimental effects on human health caused by its indiscriminate disposal of waste in nature. Thus, this work aimed to study the addition of ashes of the coffee husk and granite residue in matrix of red ceramic. The raw materials were dry milled and sieved to mesh 100. To characterize the raw materials were carried out analyzes of X-ray diffraction (XRD), X-ray fluorescence (XRF), particle size analysis (PSA), differential thermal analysis (DTA) and thermogravimetric analysis (TG). Six formulations were prepared where the clay content was kept constant (70%wt) and ashes contents and granite residue varied from 10, 15, 20 and 30%. Dilatometrics analyzes were performed at four selected formulations, containing them: 100% clay (A100); 70% clay and 30% ashes (A70C30); 70% clay and 30% granite residue (A70G30); and 70% clay, 15% granite residue and 15% ashes (A70G15C15). The samples were prepared by uniaxial compaction with pressure of 25 MPa, and fired at temperatures of 800°C, 850ºC, 900ºC, 950ºC, 1000ºC and 1100°C. Assays were performed to determine the linear shrinkage of burning (LSB), water absorption (WA), apparent porosity (AP), density (D) and tensile bending. Also were performed analyzes of X-ray diffraction (XRD) and scanning electron microscopy (SEM) of the samples fired. The formulations incorporating granite residue and/or ashes reached the required limits of water absorption according to NBR 15270-1 and NBR 15310 and tensile bending according to classical literature (SANTOS, 1989) necessary for the production of tiles and ceramic block for masonry sealing

Avaliação da incorporação combinada dos resíduos de cascalho de perfuração de poço de petróleo e de polimento do porcelanato em cerâmica vermelha

Among the industries, those that produce ceramic porcelain for use in construction industry and oil, during the exploration and production period, play an important role in the production of waste. Much research has been carried out both by academia and the productive sector, sometimes reintroducing them in the same production line that generated them, sometimes in areas unrelated to their generation, as in the production of concrete and mortar for the construction, for example, but each one in an isolated way. In this research, the aim is to study the combined incorporation of the waste drill cuttings of oil well and the residue of the polishing of porcelain, generated in the final stage of finishing of this product in a clay matrix, for the production of red pottery, specifically bricks, ceramic blocks and tiles. The clay comes from the municipality of São Gonçalo, RN, the drilling waste is from the Natal basin, in Rio Grande do Norte, and the residue of the polishing proceeds from a ceramic porcelain of the State of Paraíba. For this purpose, we used a mixture of a plastic clay with a non-plastic, in a ratio of 50% each, settling formulations with the addition of these two residues in this clay matrix. In the formulations, both residues were incorporated with a minimum percentage of 2.5% and maximum of 12.5%, varying from 2.5% each, in each formulation, which the sum of the waste be no more than 15%. It should be noted that the residue of the polishing of ceramic porcelain is a IIa class (not inert). The materials were characterized by XRF, XRD, TG, DTA, laser granulometry and the plasticity index. The technological properties of water absorption, apparent porosity, linear shrinkage of burning, flexural tensile strength and bulk density were evaluated after the sintering of the pieces to 850 °C, 950 °C and 1050 °C, with a burning time of 3 hr, 3 hr and 30 minutes, and 3 hr and 50 minutes, respectively, with a heating rate of 10 °C/minute, for all formulations and landing of 30 minutes. To better understand the influence of each residue and temperature on the evaluated properties, we used the factorial planning and its surfaces of response for the interpretation of the results. It was found that the temperature has no statistical significance at a 95% of reliability level in flexural tensile strength and that it decreases the water absorption and the porosity, but increases the shrinkage and the bulk density. The results showed the feasibility of the desired incorporation, but adjusting the temperature to each product and formulation, and that the temperatures of 850 °C and 950 °C were the one that responded to the largest number of formulations

Aplicação, em pré-colheita, de dessecante em duas cultivares de soja (Glycine max (L. ) Merril) III - Efeitos sobre a composição química (proteína, óleo e cinzas) e resíduos nas sementes

A aplicação pré-colheita do dessecante paraquat, quando real izada a partir das primeiras épocas (75 e 72 dias após o início do florescimento, para a Santa Rosa e IAC-2, respectivamente) não modificaram os teores com que ocorreram normalmente, proteína, extrato etéreo e cinzas nos grãos. As análises do resíduo de paraquat nos grãos colhidos, mostram claramente que não se deve recomendar tal prática às lavouras de soja, cujo objetivo final seja o fornecimento de grãos para a alimentação humana e animal. Entretanto pode ser indicada, sem maiores restrições, àquelas cuja finalidade é a produção de sementes comerciais.

Aproveitamento de resíduos de cinza da cana de açúcar em massas cerâmicas

This study aimed to investigate the use of cane sugar ashes from small-scale stills of Eunápolis region, state of Bahia, in pottery mass that can be developed as porcelain stoneware. Bahia is the second largest producer of rum distillery in Brazil. In the production of rum is produced residue called bagasse, which is used to generate electricity in Power plants and in the distillery itself, generating ashes as residue, which is played in nature, causing environmental damage. We studied 5 (five) formulations of 0% 10% 20%, 30% and 40% by weight of the ash, without ignition and 3 (three) formulations of 10%, 20% and 30% with gray ash temperature of 1250ºC. The formulation at 0% by weight of ash was used for a comparison between the traditional mass of porcelain stoneware and the masses with the addition of ash calcined, replacing feldspar. The percentage by weight of kaolin and of Clay was kept the same, 30%, and all raw materials were derived from the state of Bahia. The samples were made in uniaxial array with dimensions of (60 x 20 x 5) mm and compressed to a pressure of 45 MPa. Assays were performed to characterize the raw by X-ray fluorescence, X-ray diffraction, ATD and ATG and Dilatometric analysis. The samples were sintered at temperatures of 1100°C, 1150°C, 1200°C and 1250°C, for the specimens with the ashes without ash and 1150° C and 1200° C for specimens with the gray level of calcined 60 minutes. and then we made a cooling ramp with the same rate of warming until reach ambient temperature. The sintered bodies were characterized by water absorption, porosity, linear shrinkage, bending strength and XRD of the fracture surface and the results analyzed. It was proven, after results of tests performed, that it is possible to use the ash residue of sugar cane bagasse on ceramic coating with the addition of up to 10% wt of the residue ash