On Coloration of Polyacrylonitrile: A Nuclear Magnetic Resonance Study

Coloration in polyacrylonitrile can be induced in three distinct ways: by heat treatment, by treatment with base, or during synthesis of the polymer itself using ionic initiators at relatively higher temperatures. The present investigation employing 'H and NMR spectroscopy has revealed some common features in colored polyacrylonitrile irrespective of ita mode of coloration. All colored polyacrylonitriles give an additional peak around S 2.7 in 'H NMR spectra and, except for heat-treated polyacrylonitrile, one extra group of peaks in the region 8 12-16 in 13C NMR spectra. The former peak has been attributed to methine and/or methylene protons in branched and/or cyclized structures, while the latter peak has been attributed to methylene carbon atoms in the branched structure. Colorless polyacrylonitriles have been found to be predominantly heterotactic, while colored polyacrylonitriles have been found to have appreciable isotactic contribution.

A Novel Strategy to Branched Polyacrylonitrile Via One-Pot RAFT Copolymerization of Acrylonitrile and an Asymmetrical Divinyl Monomer

Branched polyacrylonitriles were prepared via the one-pot radical copolymerization of acrylonitirle and an asymmetric divinyl monomer (allyl methacrylate) that possesses both a higher reactive methacrylate and a lower reactive allyl. RAFT technique was used to keep a low-propagation chain concentration via a fast reversible chain transfer euilibration and thus the cross-linking was prevented until a high level of monomer conversions. This novel strategy was demonstrated to engenerate a branched architecture with abundant pendant functional vinyl and nitrile groups, and controlled molecular weight as a behavior of controlled/living radical polymerization characteristics. The effect of the various experimental parameters, including temperature, brancher to monomer molar ratio, and chain transfer agent to initiator molar ratio, on the control Of moleculer dimension (molecular weight and polydispersity indices) and the degree of branching were investigated in detail. Moreover, H-1 NMR and gel permeation chromatography confirm the branched architecture of the resultant polymer. The intrinsic viscosity of the copolymer is also lower than the linear counterpart.