A qualidade de placas de circuito impresso confeccionadas a partir de poliestireno reciclado

Pós-graduação em Engenharia Mecânica - FEG

Reciclagem de poliestireno expandido: compósito com fibras de algodão para a confecção de placas de circuito impresso

In this work polymeric composites reinforced with cotton fibers, from the textile industry, were developed in order to manufacture printed circuit boards. It was used expanded polystyrene (EPS) as a thermoplastic matrix by melting it. For the obtention of 10% and 15% of fiber volume fraction in cotton fibers composites, it was used wasted cotton fibers as an incentive of recycling and reusing of the domestic and industrial wastes as well as for Expanded Polystyrene(EPS). The mechanical properties of the composites were evaluated by tensile and flexural strength from standardized test methods. Composites were characterized by a Scanning Electron Microscopy (SEM), Thermogravimetry (TG/DTG), Differential Scanning Calorimetry (DSC) and dielectric analysis. The analysis of the results showed that fiber in the composite directly influenced in the thermal and mechanical properties

Uso da avaliação do ciclo de vida para a determinação na redução de emissões de gases do efeito estufa e do consumo de energia associados a reciclagem de EPS

Pós-graduação em Engenharia Mecânica - FEG

Reciclagem de poliestireno expandido: compósito com fibras de sisal para confecção de placas de circuito impresso

In this work polystyrene composites reinforced with recycled sisal fibers were processed, in order to apply in the manufacture of printed circuit boards. A thermoplastic matrix of recycled polystyrene was used, this material came from waste expanded polystyrene (EPS) used in appliance's packages. Composites were prepared with 15% and 25% of sisal fibers. To obtain the composites, wasted EPS and natural sisal fibers were chosen, to encourage recycling and reuse of household waste and also the use of renewable resources. The composites were analyzed by standard tensile and flexural test, in order to verify the mechanical properties of the material. The characterization of the composite was done by scanning electron microscopy (SEM) , thermogravimetry (TGA / DTG) , differential scanning calorimetry (DSC) and dielectric analysis . The analysis of the results showed that the percentage of fibers in the composite influences directly the thermal and mechanical properties. Plates with a lower percentage of fibers showed superior properties at a higher percentage. The composite material obtained is easy to process and it's use is feasible for the confection of printed circuit boards, considering it's mechanical, thermal and insulative properties

Reaproveitamento de óxidos de manganês de pilhas descartadas para eletrocatálise da reação de redução de oxigênio em meio básico

The oxygen reduction reaction was studied in alkaline media using manganese oxides obtained from spent batteries as electrocatalysts. Three processes were used to recover manganese oxides from spent batteries. The particles obtained were in the range from 8 to 11 nm. The electrochemical experiments indicated a good electrocatalytic activity toward oxygen reduction using the different samples and showing approximately a direct transference of 4 electrons during the process. Even though all the processes were efficient, the best result was observed for the prepared sample using reactants of low cost.

Produção de substratos sers eficientes através da deposição de ouro sobre um molde de microesferas de poliestireno

This work reports on the SERS activity of a nanostructured substrate that was obtained by electrodepositing gold over a template consisting of polystyrene microspheres. This substrate displayed superior SERS performance for the detection of 4-merctaptopyridine as compared to a conventional roughened Au electrode. In order to investigate the substrate capability for the detection at low concentration limits, a series of Rhodamine 6G (1 nM) spectra were registered. Our spectral dynamics data is in agreement with single-molecule behavior, showing that the control over the substrate morphology is crucial to enable the production of highly reproducible and sensitive SERS substrates.

Estudo do reaproveitamento energético de ar quente numa Olaria

Como o sector cerâmico é um consumidor intensivo de energia, este trabalho teve como objectivo principal a elaboração de um plano de optimização do desempenho energético da olaria número três da Fábrica Cerâmica de Valadares. Para o efeito, efectuou-se o levantamento energético desta fracção autónoma. O valor total obtido para os ganhos térmicos foi de 8,7x107 kJ/dia, sendo 82% desta energia obtida na combustão do gás natural. Por outro lado, as perdas energéticas rondam os 8,2x107 kJ/dia, sendo o ar de exaustão e a envolvente os principais responsáveis, com um peso de 42 % e 38%, respectivamente. Tendo em conta estes valores, estudaram-se várias medidas de isolamento da cobertura, pavimento, paredes e saída de ar através de fendas do edifício. No caso do isolamento da cobertura sugeriu-se a substituição das telhas de fibrocimento e do isolamento actualmente existentes por painéis sandwich de cobertura. Esta acção permite uma poupança de 64.796€/ano, com um investimento de 57.029€ e o seu período de retorno de 0,9 anos. O Valor Actualizado Líquido (VAL) no 5º ano foi de 184.069€, com uma Taxa Interna de Rentabilidade (TIR) de 92%. Para isolar o pavimento, sugeriu-se a utilização de placas de poliuretano expandido (PU) de 20mm de espessura. Assim, consegue-se uma poupança de 7.442 €/ano, com um investimento de 21.708€, e um tempo de retorno 2,9 anos. No final do 5º ano de vida útil do projecto, o VAL é de 4.070€ e a TIR 7%. Relativamente ao isolamento das paredes e pilares, sugeriu-se a utilização de placas de PU (30mm), recobertas com chapa de ferro galvanizado. O tempo de retorno do investimento é de 1,5 anos, uma vez que, o investimento é de 13.670€ e a poupança anual será de 9.183€. Esta solução apresenta no último ano um VAL de 12.835€ e uma TIR de 22%. No isolamento das fendas do edifício, sugeriu-se a redução de 20% da sua área livre. Esta medida de optimização implica um investimento de 8.000€, revelando-se suficientemente eficaz, pois apresenta um tempo de retorno de 0,67 anos. O VAL e a TIR da solução no último ano de vida útil do projecto de investimento são de 36.835€ e 35%, respectivamente. Por fim, sugeriu-se ainda a instalação de um sistema de controlo que visa o aproveitamento de ar quente proveniente do forno, instalado no piso inferior à olaria, para pré-aquecer o ar alimentado aos geradores de calor. Esta medida implicaria um investimento de 4.000€, com um tempo de retorno de 2,4 anos e uma poupança anual é de 1.686€. O investimento é aconselhável, já que, no 5º ano, o VAL é de 1.956€ e a TIR é de 17%.

Síntese de poliestireno sulfonado para aplicações no tratamento de água produzido a partir de copos e bandejas descartadas de poliestireno

In the present paper, the use of poly(styrene sulfonate) (PSS), produced from discarded polystyrene materials through heterogeneous and homogeneous processes, was investigated. The use of PSS for water treatment, using a kaolin suspension as wastewater model, reduced water turbidity for all the employed materials when compared to the blank analysis, without PSS. The most efficient polyelectrolyte was PSS cups obtained by homogeneous route. The same behavior was observed for real system. The homogeneous PSS cups showed a balance between a moderate molecular weight and high anionic character that improved flocks formation and water removal turbidity.

Reaproveitamento de óxidos de manganês de pilhas descartadas para eletrocatálise da reação de redução de oxigênio em meio básico

The oxygen reduction reaction was studied in alkaline media using manganese oxides obtained from spent batteries as electrocatalysts. Three processes were used to recover manganese oxides from spent batteries. The particles obtained were in the range from 8 to 11 nm. The electrochemical experiments indicated a good electrocatalytic activity toward oxygen reduction using the different samples and showing approximately a direct transference of 4 electrons during the process. Even though all the processes were efficient, the best result was observed for the prepared sample using reactants of low cost.

Produção de substratos sers eficientes através da deposição de ouro sobre um molde de microesferas de poliestireno

This work reports on the SERS activity of a nanostructured substrate that was obtained by electrodepositing gold over a template consisting of polystyrene microspheres. This substrate displayed superior SERS performance for the detection of 4-merctaptopyridine as compared to a conventional roughened Au electrode. In order to investigate the substrate capability for the detection at low concentration limits, a series of Rhodamine 6G (1 nM) spectra were registered. Our spectral dynamics data is in agreement with single-molecule behavior, showing that the control over the substrate morphology is crucial to enable the production of highly reproducible and sensitive SERS substrates.

Síntese e caracterização de nanocompósitos de poliestireno/hidroxissal lamelar

Polystyrene/layered hydroxide salt (LHS) modified with sodium dodecyl sulfate was synthesized by in situ polymerization. The materials synthesized were characterized by gravimetry, X-ray diffraction (XRD), thermogravimetry analyses (TGA), differential scanning calorimetry (DSC) and the flammability test (FT). XRD demonstrated that synthesized nanocomposites in all compositions studied showed poor global dispersion of LHS in polystyrene. TGA showed a slight decrease in thermal stability. DSC curves showed that the glass transition temperature of polystyrene and nanocomposites were similar. The FT showed that the nanocomposite with low load of LHS exhibited good results.

Painéis de partículas aglomeradas de madeira de Pinus elliottii Engelm., poliestireno (PS) e polietileno tereftalato (PET)

O objetivo deste trabalho foi avaliar as propriedades de painéis fabricados com partículas de madeira, poliestireno (PS) e polietileno tereftalato (PET). Foram utilizadas três proporções, em relação à massa seca de madeira, de poliestireno (0, 25 e 50%) e duas proporções de PET/PS (5/20 e 10/40%), combinadas com 50, 75 ou 100% de partículas de madeira de Pinus elliottii. Os painéis foram produzidos com adesivos à base de uréia-formaldeído ou de fenol-formaldeído, em três teores (0, 4 ou 6%) e três níveis de solução de poliestireno em tolueno (0 , 4 e 6%), todos calculados em relação à massa seca total dos painéis. Foram produzidos painéis de aproximadamente 400 x 400 x 10 mm, em camada única, com densidade aproximada de 0,6 g/cm³. Determinou-se a resistência dos painéis à tração perpendicular à superfície, à flexão estática (módulos de ruptura (MOR) e elasticidade (MOE)), ao arrancamento de parafusos, bem como a absorção de água e o inchamento em espessura, após 24 horas de imersão. Todas as propriedades mecânicas dos painéis foram superiores às exigidas pela norma ANSI/A 208.1-1993. Contudo, todos os painéis absorveram água em valores superiores àqueles normalmente observados em painéis comerciais. Apesar disto, o inchamento em espessura foi compatível com o dos painéis de partículas de madeira existentes no mercado. Os painéis nos quais se aplicou a solução de poliestireno foram, de modo geral, os que apresentaram os melhores valores para todas as propriedades.

Entre el juego y la Geometría : posibilidad pedagógica del poliestireno expandido.

Utilización del poliestireno expandido para el aprendizaje de la geometría. Se pretende que los alumnos tengan por la vía sensitiva un conocimiento de las formas geométricas. Se proponen una serie de ejercicios a realizar.

Influencia del proceso de reciclado sobre las propiedades de los materiales compuestos obtenidos por inyección de poliestireno reforzado con fibras lignocelulósicas

The objective of this research is to study the influence of several recycling cycles on the mechanical properties of four different materials made by the injection of polystyrene. The four materials studied have different characteristics. The first one is polystyrene (PS), the second one is polystyrene reinforced with hemp fibers (PSf), the third one is polystyrene reinforced with hemp fibers modified with AKD (PSft) and the last one is polystyrene reinforced with fiberglass (PSfv). With all these materials tensile strength, bending, hardness and impact is measured. After the measurement of these physical properties, materials are recycled to obtain new injection samples, and its physical properties are measured again. This process is repeated during 24 cycles. After each recycling cycle material physical properties are related with polystyrene molecular weight, melt flow, FTIR spectra and DSC. From reinforced materials, fibers are recovered and through microscopy and image analysis they are characterized to study the influence that recycling has on its structure.

Estudo da agregação de copolímeros anfifílicos de poliestireno e Poli[5-(N,N-Dialquilamino) Isopreno]

As propriedades em solução e a auto-associação de copolímeros em bloco de estireno e 5- (N,N-dialquilamino)isopreno foram estudados. Copolímeros di e tribloco são formados por um longo bloco de poliestireno, com um ou dois blocos menores de poli[5-(N,Ndialquilamino) isopreno] em uma ou ambas as extremidades. A polaridade do solvente é determinante na afinidade deste com um ou ambos blocos constituintes do polímero e, conseqüentemente, afetará as propriedades dinâmicas e estruturais do mesmo. Após a quaternização dos sistemas com dimetil sulfato, os agregados foram preparados pela prévia dissolução dos polímeros em um solvente orgânico e subsequente adição de água para induzir a agregação das cadeias insolúveis de PS. Solventes puros (DMF, THF e dioxano), bem como misturas de DMF e THF foram empregados como solvente comum. A concentração crítica de água (cwc) e as morfologias foram estudadas em função da natureza do solvente comum, da concentração inicial, arquitetura e massa molecular do copolímero, por espalhamento de luz estático e microscopia eletrônica de transmissão (MET), respectivamente. Determinou-se que tanto a cwc quanto as morfologias, são predominantemente influenciadas pela natureza do solvente comum. Alguns resultados inesperados foram encontrados para os copolímeros tribloco, incluindo a descoberta de uma nova morfologia formada a partir desse tipo de copolímero- a morfologia bowl-shape. Os agregados bowl-shaped, são essencialmente esferas bastante polidispersas, contendo um vazio alocado assimetricamente em seu interior. A fase contínua é composta de um arranjo de micelas inversas (núcleo de PAI e coroa de PS), sendo que as cadeias hidrofílicas de PAI circundam toda a estrutura na interface polímero/água. Acredita-se que a formação desta morfologia está sob controle cinético e não representa uma estrutura de equilíbrio. Foi proposto um possível mecanismo para a formação deste novo tipo de agregado.