A novel sheet 4f-3d mixed-metal pyridine dicarboxylate: synthesis, structure, photophysical properties and its transformation to a perovskite oxide

The synthesis, characterization and photophysical properties of a 4f-3d mixed metal compound, Gd(H2O)(3)Co[C5N1H3-(COO)(2)](3), are described; the structure is unique, consisting of sheets with large pores ( ca. 7 angstrom diameter) in the sheets and transforms to a perovskite oxide at moderate temperatures.

K1-xLaxCa2-xNb3O10, a Layered Perovskite Series with Variable Interlayer Cation Density, and LaCaNb3O10, a Novel Layered Perovskite Oxide with No Interlayer Cations

A series of layered perovskite oxides of the formula K1-xLaxCa2-xNb3O10 for 0 < x ≤ 1.0 have been prepared. All the members are isostructural, possessing the structure of KCa2Nb3O10. The interlayer potassium ions in the new series can be ion-exchanged with protons to give H1-xLaxCa2-xNb3O10. The latter readily forms intercalation compounds of the formula (CnH2n+1NH3)1-x LaxCa2-xNb3O10, just as the parent solid acid HCa2Nb3O10. The end member LaCaNb3O10 containing no interlayer cations is a novel layered perovskite oxide, being a n = 3 member of the series An-1BnX3n+1.

Quantum corrections to the conductivity in a perovskite oxide: A low-temperature study of LaNi1-xCoxO3 (0?x?0.75)

In this paper we propose to study the evolution of the quantum corrections to the conductivity in an oxide system as we approach the metal-insulator (M-I) transition from the metallic side. We report here the measurement of the low-temperature (0.1 Kperovskite-structure oxide system LaNi1-x CoxO3 (0?x?0.75). LaNiO3 is a metal and LaCoO3 is an insulator. The system is metallic for x?0.65. For all x, at low temperatures, the conductivity (?) rises with temperature (T). Below 2 K, ? follows a power-law behavior, ?(T)=?(0)+?Tm. For samples in the metallic regime, away from the metal-insulator transition (x?0.4), m?0.3�0.4. As the transition is approached [i.e., ?(0)?0], m increases rapidly; and at the transition [?(0)=0, xc?0.65], m?1. On the insulating side (x>0.65), m takes on large values and ?(0)=0. We explain the temperature dependence of ?(T), for T<2 K, on the metallic side (x?0.4), as arising predominantly from electron-electron interactions, taking into account the diffusion-channel contribution (which gives m=0.5) as well as the Cooper-channel contribution. In this regime, the correction to conductivity, ??(T), is a small fraction of ?(T). However, as the M-I transition is approached (x?xc), ??(T) starts to dominate ?(T) and the above theories fail to explain the observed ?(T).

Magnetoresistance of the metallic perovskite oxide LaNiO3-delta

We report a study of the magnetoresistance (MR) of the metallic perovskite oxide LaNiO3-delta as a function of the oxygen stoichiometry delta (delta less than or equal to 0.14), magnetic field (H less than or equal to 6 T) and temperature (1.5 K less than or equal to T less than or equal to 25 K). We find a strong dependence of the nature of the MR on the oxygen stoichiometry. The MR at low temperatures changes from positive to negative as the sample becomes more oxygen deficient (i.e. delta increases). Some of the samples, which are more resistive, show resistivity minima at T-min approximate to 20 K. We find that in these samples the MR is positive for T > T-min and negative for T < T-min. We conclude that in the absence of strong magnetic interaction, the negative MR in these oxides can arise from weak-localization effects.

Low temperature synthesis of perovskite oxide using the adsorption properties of cellulose

La-0.8Sr(0).2CoO(3) (LSCO) oxide powder was prepared using the adsorption properties of cellulose. The preparation process was studied by XRD, FTIR, TG-DTA and CO2-TPD techniques. The results of XRD, IR and TG-DTA testified that cellulose could successfully reserve the homogeneity of the solution system to the solid precursor. During the early stage of pyrolysis, cellulose was partially oxidized, and some COO- groups appeared in its texture, which were then complexed with the adsorbed metal ions, and effectively suppressed the aggregation of metal ions. Formation of a pure perovskite and the properties of the powder resulted were found to be significantly influenced by the cellulose to metal nitrate ratio. Also the properties of the resulting powder were greatly influenced by the calcination conditions. If the produced carbon dioxide could not be eluted in time, carbonate would be formed in the bulk. Hence, a high calcination temperature (> 800 degreesC) was needed to acquire a pure phase LSCO. At optimized conditions, nano-crystal LSCO could be obtained at as low as 500 degreesC.

Growth and characterization of perovskite oxide ferroelectric thin films and its applications

Department of Physics, Cochin University of Science and Technology

RF magnetron sputtered perovskite oxide electrodes for Ferroelectric RAM

The main objective of this thesis work is to optimize the growth conditions for obtaining crystalline and conducting Lao.5Sro.5Co03 (LSCO) and Lao.5Sro.5Coo.5.5Nio.5O3 (LSCNO) thin films at low processing temperatures. The films are prepared by radio frequency magnetron sputtering under various deposition conditions. The thin films were used as electrodes for the fabrication of ferroelectric capacitors using BaO.7SrO.3 Ti03 (BST) and PbZro.52 Tio.4803 (PZT). The structural and transport properties of the La1_xSrxCo03 and Lao.5Sro.5Co1_xNix03 are also investigated. The characterization of the bulk and the thin films were performed using different tools. A powder X-ray diffractometer was used to analyze the crystalline nature of the material. The transport properties were investigated by measuring the temperature dependence of resistivity using a four probe technique. The magnetoresistance and thermoelectric power were also used to investigate the transport properties. Atomic force microscope was used to study the surface morphology and thin film roughness. The ferroelectric properties of the capacitors were investigated using RT66A ferroelectric tester.

Evaluation of strontium-site-deficient Sr2Fe1.4Co0.1Mo0.5O6-δ-based perovskite oxides as intermediate temperature solid oxide fuel cell cathodes

In this paper strontium-site-deficient Sr₂Fe_1.4Co_0.1Mo_0.5O_6-δ-based perovskite oxides (S_xFCM) were prepared and evaluated as the cathode materials for intermediate temperature solid oxide fuel cells (IT-SOFCs). All samples exhibited a cubic phase structure and the lattice shrinked with increasing the Sr-deficiency as shown in XRD patterns. XPS results determined that the transition elements (Co/Fe/Mo) in S_xFCM oxides were in a mixed valence state, demonstrating the small polaron hopping conductivity mechanism existed. Among the samples, S_1.950FCM presented the lowest coefficient of thermal expansion of 15.62 × 10^-6 K^-1, the highest conductivity value of 28 S cm^-1 at 500 °C, and the lowest interfacial polarization resistance of 0.093 Ω cm² at 800 °C, respectively. Furthermore, an anode-supported single cell with a S_1.950FCM cathode was prepared, demonstrating a maximum power density of 1.16 W cm^-2 at 800 °C by using wet H₂ (3% H₂O) as the fuel and ambient air as the oxidant. These results indicate that the introduction of Sr-deficiency can dramatically improve the electrochemical performance of Sr₂Fe_1.4Co_0.1Mo_0.5O_6-δ, showing great promise as a novel cathode candidate material for IT-SOFCs.

HIGH-Tc superconductivity in perovskite oxides of the Y-Ba-Cu-O system

Several biphasic compositions of the type Y3-xBa3+xCu6O14 show an onset of superconductivity in the 90-115K range, attaining zero resistance in the 70-85K range. The phase responsible for superconductivity in these compositions is a perovskite oxide of composition YBa2Cu3 O7. This oxide annealed in oxygen shows the onset of superconductivity at 120K and zero resistance at 87K. YBa2,Cu3O7 shows the highest Meissner effect of all oxide superconductors. The superconducting behaviour of the two perovskite oxides, Y0.95Ba1.95,Cu3O7 and Y1.05Ba1.95Cu3O7 show interesting features; a marked decrease in resistivity is observed from room temperature itself in the former oxide with zero resistance at 89K. Electron microscopy and infrared spectra of these oxides are briefly discussed.

Single sublattice endotaxial phase separation driven by charge frustration in a complex oxide.

Complex transition-metal oxides are important functional materials in areas such as energy and information storage. The cubic ABO3 perovskite is an archetypal example of this class, formed by the occupation of small octahedral B-sites within an AO3 network defined by larger A cations. We show that introduction of chemically mismatched octahedral cations into a cubic perovskite oxide parent phase modifies structure and composition beyond the unit cell length scale on the B sublattice alone. This affords an endotaxial nanocomposite of two cubic perovskite phases with distinct properties. These locally B-site cation-ordered and -disordered phases share a single AO3 network and have enhanced stability against the formation of a competing hexagonal structure over the single-phase parent. Synergic integration of the distinct properties of these phases by the coherent interfaces of the composite produces solid oxide fuel cell cathode performance superior to that expected from the component phases in isolation.

Characterization and evaluation of BaCo0.7Fe0.2Nb0.1O3−δ as a cathode for proton-conducting solid oxide fuel cells

This study characterizes BaCo0.7Fe0.2Nb0.1O3−δ (BCFN) perovskite oxide and evaluates it as a potential cathode material for proton-conducting SOFCs with a BaZr0.1Ce0.7Y0.2O3-δ (BZCY) electrolyte. A four-probe DC conductivity measurement demonstrated that BCFN has a modest electrical conductivity of 2–15 S cm−1 in air with p-type semiconducting behavior. An electrical conductivity relaxation test showed that BCFN has higher Dchem and Kchem than the well-known Ba0.5Sr0.5Co0.8Fe0.2O3−δ oxide. In addition, it has relatively low thermal expansion coefficients (TECs) with values of 18.2 × 10−6 K−1 and 14.4 × 10−6 K−1 at temperature ranges of 30–900 °C and 30–500 °C, respectively. The phase reaction between BCFN and BZCY was investigated using powder and pellet reactions. EDX and XRD characterizations demonstrated that BCFN had lower reactivity with the BZCY electrolyte than strontium-containing perovskite oxides such as SrCo0.9Nb0.1O3-δ and Ba0.6Sr0.4Co0.9Nb0.1O3−δ. The impedance of BCFN was oxygen partial pressure dependent. Introducing water into the cathode atmosphere reduced the size of both the high-frequency and low-frequency arcs of the impedance spectra due to facilitated proton hopping. The cathode polarization resistance and overpotential at a current density of 100 mA cm−2 were 0.85 Ω cm−2 and 110 mV in dry air, which decreased to 0.43 Ω cm−2 and 52 mV, respectively, in wet air (∼3% H2O) at 650 °C. A decrease in impedance was also observed with polarization time; this was possibly caused by polarization-induced microstructure optimization. A promising peak power density of ∼585 mW cm−2 was demonstrated by an anode-supported cell with a BCFN cathode at 700 °C.

Oxygen reduction reaction activity of La-based perovskite oxides in alkaline medium : a thin-film rotating ring-disk electrode study

In this work, LaMO₃ and LaNi_0.5M_0.5O₃ (M = Ni, Co, Fe, Mn and Cr) perovskite oxide electrocatalysts were synthesized by a combined ethylenediaminetetraacetic acid-citrate complexation technique and subsequent calcinations at 1000 °C in air. Their powder X-ray diffraction patterns demonstrate the formation of a specific crystalline structure for each composition. The catalytic property of these materials toward the oxygen reduction reaction (ORR) was studied in alkaline potassium hydroxide solution using the rotating disk and rotating ring-disk electrode techniques. Carbon is considered to be a crucial additive component because its addition into perovskite oxide leads to optimized ORR current density. For LaMO₃ (M = Ni, Co, Fe, Mn and Cr)), in terms of the ORR current densities, the performance is enhanced in the order of LaCrO₃, LaFeO₃, LaNiO₃, LaMnO₃, and LaCoO3. For LaNi_0.5M_0.5O₃, the ORR current performance is enhanced in the order of LaNi_0.5Fe_0.5O₃, LaNi_0.5Co_0.5O₃, LaNi_0.5Cr_0.5O₃, and LaNi_0.5Mn_0.5O₃. Overall, LaCoO₃ demonstrates the best performance. Most notably, substituting half of the nickel with cobalt, iron, manganese, or chromium translates the ORR to a more positive onset potential, suggesting the beneficial catalytic effect of two transition metal cations with Mn as the most promising candidate. Koutecky–Levich analysis on the ORR current densities of all compositions indicates that the four-electron pathway is favored on these oxides, which are consistent with hydroperoxide ion formation of <2%.

The significant effect of the phase composition on the oxygen reduction reaction activity of a layered oxide cathode

Layered oxides of Sr4Fe4Co2O13 (SFC2) which contains alternating perovskite oxide octahedral and polyhedral oxide double layers are attractive for their mixed ionic and electronic conducting and oxygen reduction reaction properties. In this work, we used the EDTA–citrate synthesis technique to prepare SFC2 and vary the calcination temperature between 900 and 1100 _C to obtain SFC2, containing different phase content of perovskite (denoted as SFC-P) and (Fe,Co) layered oxide phases (SFC-L). Rietveld refinements show that the SFC-P phase content increased from _39 wt% to _50 wt% and _61 wt% as the calcination temperature increased from 900 _C (SFC2-900) to 1000 _C (SFC2-1000) and 1050 _C (SFC2-1050). At 1100 _C (SFC2-1100), SFC-P became the dominant phase. The oxygen transport properties (e.g. oxygen chemical diffusion coefficient and oxygen permeability), electrical conductivity and oxygen reduction reaction activity is enhanced in the order of SFC2-1000, SFC2-1100 and SFC2-1050. The trend established here therefore negates the hypothesis that the perovskite phase content correlates with the oxygen transport property enhancement. The results suggest instead that there is an optimum composition value (e.g. 61 wt% of SFC-L for SFC2-1050 in this work) on which synergistic effects take place between the SFC-P and SFC-L phase.

Enhancing bi-functional electrocatalytic activity of perovskite by temperature shock : a case study of LaNiO3-ᵟ

Perovskite oxide offers an attractive alternative to precious metal electrocatalysts given its low cost and high oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) activity. The results obtained in this work suggest a correlation of crystal structure with ORR and OER activity for LaNiO3-?. LaNiO3-? perovskites with different crystal structure were obtained by heating at different temperatures, e.g., 400, 600, and 800 C followed by quenching into room temperature. Cubic structure (relative to rhombohedral) leads to higher ORR and OER activity as well as enhanced bi-functional electrocatalytic activity, e.g., lower difference in potential between the ORR at -3 mA cm-2 and OER at 5 mA cm -2 (?E). Therefore, this work shows the possibility to adjust bi-functional activity through a simple process. This correlation may also extend to other perovskite oxide systems.