Generation of sub-5 fs pulses through cascade of filamentation and hollow fiber compression

A pulse-compression scheme based on cascade of filamentation and hollow fiber has been demonstrated, Pulses with duration of sub-5 fs and energy of 0.2 mJ near 800 nm have been generated by compressing the similar to 40 fs pulses from a commercial laser system. This method is promising to generate near monocycle high energy pulses. [GRAPHICS] Measured autocorrelation curve of the final compressed pulses with duration of sub-5 fs (black solid) and the simulated autocorrelation curve of 4.6 fs pulse near 800 rim (red dash) (C) 2008 by Astro Ltd. Published exclusively by WILEY-VCH Verlag GmbH & Co. KGaA

Synthesis of NaA zeolite membrane on a ceramic hollow fiber

NaA zeolite membrane was successfully synthesized on a ceramic hollow fiber with an outer diameter of 400 mum, a thickness of 100 mum and an average pore radius of 0.1 mum. The as-synthesized membranes were characterized by XRD, SEM as well as gas permeation. A continuous C NaA zeolite membrane formed after a three-stage synthesis. The membrane thickness was similar to5 mum. Gas permeation data indicated that a relatively high quality NaA zeolite membrane formed on the ceramic hollow fiber support. (C) 2003 Elsevier B.V. All rights reserved.

Influence of drying method on morphology and properties of asymmetric cellulose hollow fiber membrane

Using a dry/wet spinning process, asymmetric cellulose hollow fiber membranes (CHFM) were prepared from a dope composed of cellulose/N-methylmorpholine-N-oxide/water. The formation mechanism for the finger-like macrovoids at the inner portion of as-spun fibers was explained. Naturally drying and three solvent exchange drying methods were tried to investigate their influence on morphology and properties of CHFM. It was found that the ethanol-hexane exchange drying was an appropriate method to minimize morphology change of the as-spun CHFM, whereas the naturally drying caused the greatest shrinkage of the fibers that made the porous membrane become dense. The result, CHFM from ethanol-hexane exchange drying performed the highest gas permeation rate but gas permeation of the naturally dried membrane could not be detectable. The resultant CHFM from the ethanol-hexane exchange drying also showed acceptable, mechanical properties, thus it was proposed to be an appropriate method for gas separation purpose. The experimental results supported the proposed drying mechanism of CHFM. The free water would evaporate or be replaced by a solvent that subsequently would evaporate but the bonded water would remain in the membrane. What dominated the changes of membrane morphology during drying should be. the molecular affinities of cellulose-water, water-solvent and solvent-solvent. (C) 2004 Elsevier B.V. All rights reserved.

Gas permeation performance of cellulose hollow fiber membranes made from the cellulose/N-methylmorpholine-N-oxide/H2O system

Cellulose hollow fiber membranes (CHFM) were prepared using a spinning solution containing N-methylmorpholine-N-oxide as solvent and water as a nonsolvent additive. Water was also used as both the internal and external coagulant. It was demonstrated that the phase separation mechanism of this system was delayed demixing. The CHFM was revealed to be homogeneously dense structure after desiccation. The gas permeation properties of CO2, N-2, CH4, and H-2 through CHFM were investigated as a function of membrane water content and operation pressure. The water content of CHFM had crucial influence on gas permeation performance, and the permeation rates of all gases increased sharply with the increase of membrane water content. The permeation rate of CO2 increased with the increase of operation pressure, which has no significant effect on N-2, H-2, and CH4. At the end of this article a detailed comparison of gas permeation performance and mechanism between the CHFM and cellulose acetate flat membrane was given. (C) 2003 Wiley Periodicals, Inc.

Selective hydrogenation of cyclopentadiene in mono- and bimetallic catalytic hollow-fiber reactors

The mono- and bimetallic catalytic polymeric hollow-fiber reactors were established with catalytic polymeric cellulose acetate (CA) hollow fibers prepared by supporting the polymer-anchored mono- or bimetallic catalyst in/on the inner wall of the hollow fibers. The selective hydrogenation of cyclopentadiene to cyclopentene was efficiently carried out in the above catalytic polymeric hollow-fiber reactors, especially in the NaBH4 reduced bimetallic PVP-Pd-0.5Co/CA hollow-fiber reactor under mild conditions of 40 degrees C and 0.1 MPa. It was found that there was a remarkable synergic effect of palladium and cobalt reduced by NaBH4 in the bimetallic PVP-Pd-0.5Co/CA hollow-fiber reactor, which results in a 97.5% conversion of cyclopentadiene and a 98.4% selectivity for cyclopentene. (C) 2000 Elsevier Science B.V. All rights reserved.

Extraction and separation of cadmium(II), iron(III), zinc(II), and europium(III) by Cyanex302 solutions using hollow fiber membrane modules

The mass transfer behaviors of Cd(II), Fe(III), Zn(II), and Eu(III) in sulfuric acid solution using microporous hollow fiber membrane (HFM) containing bis(2,4,4-trimethylpentyl)monothiophosphinic acid (commercial name Cyanex302) were investigated in this paper. The experimental results showed that the values of the mass transfer coefficients (K-w) decreased with an increase of H+ concentration and increased with an increase of extractant Cyanex302 concentration. The mass transfer resistance of Eu3+ was the largest because K-w value of Eu3+ was the smallest. The order of mass transfer rate of metal ions at low pH was Cd > Zn > Fe > Eu. Mixtures of Zn2+ and Eu3+ or of Zn2+ and Cd2+ were well separated in a counter-current circulation experiment using two modules connected in series at different initial acidity and concentration ratio. These results indicate that a hollow fiber membrane extractor is capable of separating the mixture compounds by controlling the acidity of the aqueous solution and by exploiting different mass transfer kinetics. The interfacial activity of Cyanex302 in sulfuric acid solution was measured and interfacial parameters were obtained according to Gibbs adsorption equation.

Vapor permeation separation of MeOH/MTBE through polyimide/sulfonated poly(ether-sulfone) hollow-fiber membranes

Mixtures of methanol/MTBE were separated with polyimide/sulfonated poly(ether-sulfone) hollow-fiber membranes. The separation was attempted by vapor permeation instead of pervaporation, which had been used by most researchers. The separation properties of the hollow-fiber membranes and operating conditions are discussed. The results showed that separation factors of the blended polyimide/sulfonated poly(ether-sulfone) hollow-fiber membranes were extremely high for the methanol/MTBE mixtures.

Extraction and separation of thorium and ytterbium with bis (2,4,4-trimethylpentyl) phosphinic acid using a hollow fiber membrane extractor

The based membrane extraction of Th4+ and Yb3+ was studied in HBTMPP-heptane using a hollow fibber membrane. The separation method of Th4+ and Yb3+ was proposed by kinetics competition. The separation operation of Th4+ and Yb3+ mixture was carried out by two successive extraction and stripping simultaneously. The concentration ratio of Th4+ to Yb3+ is 16.74 in the stripping solution. The recovery and purity of Th4+ are 71.6% and 95.74% respectively.

Effect of polyvinylidene fluoride hollow fiber membranes on mass transfer of samarium

The influence of swelling and stripping acidity on the mass transfer coefficient based on water phase and the inner diameters of membranes were studied with P507-HCl-Sm as working system in the two different kinds of hollow fiber membranes. Effects of extractant concentration, H+ concentration in aqueous phase and Sm3+ concentration on extraction rate were discussed and the corresponding reaction series were obtained. According to the investigations on the interfacial kinetics, the reaction kinetics equation and reaction rate constant were obtained.

Separation of zinc(II) from europium(III) by using hollow fiber membrane

Extraction and separation of Eu3+ and Zn2+ in sulfuric acid solution was investigated by hollow fiber membrane with cyanex 302 (bis (2,4,4-trimethylpentyl) monothiophosphinic acid) in counter-currently circulating operation. Reaction mechanism of membrane extraction and effect of extractant concentration and H+ concentration in aqueous phase on the mass transfer coefficient were discussed. It can be concluded that Zn2+ can be extracted completely from Eu3+ sulfate solution according to the kinetics competing difference. In one extractor process, extraction percentage of Zn2+ was not completely and Eu3+ was not extracted. Extraction percentage of Zn2+ reached 94.92%, but Eu3+ only reached 8.59% after 100 minutes extraction in two series connectors and that of Zn2+ and Eu3+ reached 99.9% and 6.53% respectively after 40 minutes extraction in three series connectors.

Separation of Th4+ and RE3+ with hollow fiber extraction

Separation of Th4+ and RE3+ was investigated by hollow fiber membrane extraction with N1923 in countercurrent recirculating operation. The effect of Hf concentration in aqueous phase and flow rates of aqueous and organic phases on mass transfer coefficient was tested. Then the extraction of Th4+ from RE sulfate obtained from Baotou ore was carried out. The results obtained show that the mass transfer coefficient of Th4+ changes with the flow rate of aqueous phase, but does not change with the flow rate of organic phase and H+ concentration in aqueous phase, which suggests that the mass transfer rate of Th4+ is controlled bg that in the water critical layer, The mass transfer rate of RE3+ does not change with the flow rate of water phase, changes a little with the flow rate of organic phase, and changes with H+ concentration, which suggests that the mass transfer rate is controlled by their reaction rate with N1923. Th4+ could be extracted completely in 8 h from RE sulfate solution of Baotou ore with relatively less extraction of RE3+. So the separation of radioactive element under the sealed condition could be done.

Separation of Ce(IV) and RE(III) with hollow fiber membrane-based extraction

Separation of Ce(IV) and RE(III) was investigated by hollow fiber membrane-based extraction with contercurrent recirculating operation. The mass transfer coefficients of Ce(IV) and RE(III) and the effective factors to them were tested. The results show the mass transfer coefficient of Ce(IV) is larger than that of RE(III), and their mass transfer mechanism is different. The mass transfer of Ce(IV) was controlled by the resistance in water critical layer due to its more rapid interfacial reaction rate and larger distribution coefficient, which was different from RE(III) mass transfer with a slow interfacial reaction rate and small distribution coefficient. Ce(IV) was separated from the mixed solution of Ce(IV) and RE(III) by means of the difference of their mass transfer rates.