Contribution of solvent effect to the optical spectra of polyanilines: has it been underestimated

The coefficient of thermochromism of polyaniline solutions has been found to be solvent dependent and the solvent effect is not negligible. Hence, thermochromism of polyaniline solutions cannot be explained solely on the basis of conformational change induced by a change in temperature. Further, comparison of the solvatochromism of polyaniline and polytoluidine shows a higher solvatochromic shift for the former. It implies that the higher energy associated with the exciton peak of polytoluidine is not due to the higher ring torsional angle induced by the higher steric repulsion of the methyl group, as widely accepted, but is due to its less solvatochromic red-shift as compared to polyaniline.

Effect of the sulfonic acid group on copolymers of aniline and toluidine with m-aminobenzene sulfonic acid

This article describes the results of the preparation and characterization of self-doped conducting copolymers of aniline and toluidine with m-aminobenzene sulfonic acid. The copolymers have an intrinsic acid group that is capable of doping polyaniline. Spectroscopic, morphological, and electrical conductivity studies have provided insight into the structural and electronic properties of the copolymers. The differences in the properties of polyaniline and polytoluidine due to the sulfonic acid ring substituent on the phenyl ring are discussed. The scanning electron micrographs of the copolymers reveal regions of sharp-edged, needle-shaped structures, whereas the X-ray diffraction patterns show that the copolymers are relatively more crystalline in nature. (C) 2002 Wiley Periodicals, Inc.

THERMAL BEHAVIORS OF INTRINSIC POLYANILINE AND ITS DERIVATIVES

Thermal properties of polyaniline (PAn), polytoluidine(POT) and polyanisidine(PAs) were examined by TG and DSC techniques. The weight-uptake of POT at 200-300 degrees C was observed and carefully discussed.

SOLUBLE POLY-(O,M)-TOLUIDINE

The soluble poly-o-toluidine (POT) and poly-m-toluidine (PMT) have been success- fully prepared under controlled conditions of polymerization and post-treatment, and characterized by IR, VPO and elemental analysis. It is found that the soluble and insol- uble polymers obtained with two different methods (Ⅰ and Ⅱ) have the similar conduc- tivity and molecular chain structure. VPO measurement shows that the number average molecular weight (Mn) of soluble polymers is about 3000. The mole ratio o...