Preparation of porous nanofibers from electrospun polyacrylonitrile/calcium carbonate composite nanofibers using porogen leaching technique

Production of nanofibrous polyacrylonitrile/calcium carbonate (PAN/CaCO3) nanocomposite web was carried out through solution electrospinning process. Pore generating nanoparticles were leached from the PAN matrices in hydrochloric acid bath with the purpose of producing an ultimate nanoporous structure. The possible interaction between CaCO3 nanoparticles and PAN functional groups was investigated. Atomic absorption method was used to measure the amount of extracted CaCO3 nanoparticles. Morphological observation showed nanofibers of 270–720 nm in diameter containing nanopores of 50–130 nm. Monitoring the governing parameters statistically, it was found that the amount of extraction (ε) of CaCO3was increased when the web surface area (a) was broadened according to a simple scaling law (ε = 3.18 a0.4). The leaching process was maximized in the presence of 5% v/v of acid in the extraction bath and 5 wt % of CaCO3 in the polymer solution. Collateral effects of the extraction time and temperature showed exponential growth within a favorable extremum at 50°C for 72 h. Concentration of dimethylformamide as the solvent had no significant impact on the extraction level.

On Coloration of Polyacrylonitrile: A Nuclear Magnetic Resonance Study

Coloration in polyacrylonitrile can be induced in three distinct ways: by heat treatment, by treatment with base, or during synthesis of the polymer itself using ionic initiators at relatively higher temperatures. The present investigation employing 'H and NMR spectroscopy has revealed some common features in colored polyacrylonitrile irrespective of ita mode of coloration. All colored polyacrylonitriles give an additional peak around S 2.7 in 'H NMR spectra and, except for heat-treated polyacrylonitrile, one extra group of peaks in the region 8 12-16 in 13C NMR spectra. The former peak has been attributed to methine and/or methylene protons in branched and/or cyclized structures, while the latter peak has been attributed to methylene carbon atoms in the branched structure. Colorless polyacrylonitriles have been found to be predominantly heterotactic, while colored polyacrylonitriles have been found to have appreciable isotactic contribution.

Well-defined higher-molecular-weight polyacrylonitrile via RAFT technique in the presence of disulfide compounds as a source of chain transfer agent

Well-defined polyacrylonitrile with a higher number-average molecular weight (R.) up to 200,000 and a lower polydispersity index (PDI, 1.7-2.0) was firstly obtained via reversible addition-fragmentation chain transfer (RAFT) process. This was achieved by selecting a stable, easy way to prepare disulfide compound intermediates including bis(thiobenzoyl) disulfide (BTBDS) and bis(thiophenylacetoyl) disulfide (BTPADS) to react with azobis(isobutyronitrile) to directly synthesize RAFT agents in situ.

A Novel Strategy to Branched Polyacrylonitrile Via One-Pot RAFT Copolymerization of Acrylonitrile and an Asymmetrical Divinyl Monomer

Branched polyacrylonitriles were prepared via the one-pot radical copolymerization of acrylonitirle and an asymmetric divinyl monomer (allyl methacrylate) that possesses both a higher reactive methacrylate and a lower reactive allyl. RAFT technique was used to keep a low-propagation chain concentration via a fast reversible chain transfer euilibration and thus the cross-linking was prevented until a high level of monomer conversions. This novel strategy was demonstrated to engenerate a branched architecture with abundant pendant functional vinyl and nitrile groups, and controlled molecular weight as a behavior of controlled/living radical polymerization characteristics. The effect of the various experimental parameters, including temperature, brancher to monomer molar ratio, and chain transfer agent to initiator molar ratio, on the control Of moleculer dimension (molecular weight and polydispersity indices) and the degree of branching were investigated in detail. Moreover, H-1 NMR and gel permeation chromatography confirm the branched architecture of the resultant polymer. The intrinsic viscosity of the copolymer is also lower than the linear counterpart.