Aplicação de Zr/Ti-PILC no processo de adsorção de Cu(II), Co(II) e Ni(II) utilizando modelos físico-químicos de adsorção e termodinâmica do processo

The aim of this investigation is to study how Zr/Ti-PILC adsorbs metals. The physico-chemical proprieties of Zr/Ti-PILC have been optimized with pillarization processes and Cu(II), Ni(II) and Co(II) adsorption from aqueous solution has been carried out, with maximum adsorption values of 8.85, 8.30 and 7.78 x10-1 mmol g-1, respectively. The Langmuir, Freundlich and Temkin adsorption isotherm models have been applied to fit the experimental data with a linear regression process. The energetic effect caused by metal interaction was determined through calorimetric titration at the solid-liquid interface and gave a net thermal effect that enabled the calculation of the exothermic values and the equilibrium constant.

Aplicação de Al-PILC na adsorção de Cu2+, Ni2+e Co2+ utilizando modelos físico-químicos de adsorção

Amostra de esmectita pertencente a Serra de Maicuru (Estado do Pará, Norte do Brasil, região amazônica) foi pilarizada com Al13, A Argila pilarizada com alumínio (Al-PILC) foi caracterizada por DRX, MEV e EDS. Para a análise textural foram utilizadas isotermas de adsorção-desorção utilizando o nitrogênio. Este artigo é dirigido ao estudo da adsorção de metais pesados. A adsorção dos íons de Cu2+, Ni2+e Co2+ foi realizadas com a matriz Al-PILC em temperatura ambiente com soluções aquosas contendo os íons metálicos. Os modelos de adsorção adotados foram os de Langmuir, Freundlich e Temkin que foram aplicados aos valores obtidos experimentalmente com regressão linear. A equação de Langmuir foi o melhor modelo de linearização com r = 0,999. A equação de Freundlich apresentou limitações em altas concentrações, mas foram obtidos valores (Kf e n) bastante aceitáveis utilizando este modelo. Os parâmetros foram utilizados para calcular a quantidade de Nf em função de Cs.

Aplicação de Zr/Ti-PILC no processo de adsorção de Cu(II), Co(II) e Ni(II) utilizando modelos físico-químicos de adsorção e termodinâmica do processo

The aim of this investigation is to study how Zr/Ti-PILC adsorbs metals. The physico-chemical proprieties of Zr/Ti-PILC have been optimized with pillarization processes and Cu(II), Ni(II) and Co(II) adsorption from aqueous solution has been carried out, with maximum adsorption values of 8.85, 8.30 and 7.78 x10^-1 mmol g^-1, respectively. The Langmuir, Freundlich and Temkin adsorption isotherm models have been applied to fit the experimental data with a linear regression process. The energetic effect caused by metal interaction was determined through calorimetric titration at the solid-liquid interface and gave a net thermal effect that enabled the calculation of the exothermic values and the equilibrium constant.

Aplicação de Al-PILC na adsorção de Cu2+, Ni2+ e Co2+ utilizando modelos físico-químicos de adsorção

Amostra de esmectita pertencente a Serra de Maicuru (Estado do Pará, Norte do Brasil, região amazônica) foi pilarizada com Al₁₃, A Argila pilarizada com alumínio (Al-PILC) foi caracterizada por DRX, MEV e EDS. Para a análise textural foram utilizadas isotermas de adsorção-desorção utilizando o nitrogênio. Este artigo é dirigido ao estudo da adsorção de metais pesados. A adsorção dos íons de Cu²⁺, Ni²⁺e Co²⁺ foi realizadas com a matriz Al-PILC em temperatura ambiente com soluções aquosas contendo os íons metálicos. Os modelos de adsorção adotados foram os de Langmuir, Freundlich e Temkin que foram aplicados aos valores obtidos experimentalmente com regressão linear. A equação de Langmuir foi o melhor modelo de linearização com r = 0,999. A equação de Freundlich apresentou limitações em altas concentrações, mas foram obtidos valores (K_f e n) bastante aceitáveis utilizando este modelo. Os parâmetros foram utilizados para calcular a quantidade de N_f em função de Cs.

Role of pili and the phase-variable PilC protein in natural competence for transformation of Neisseria gonorrhoeae.

The Gram-negative bacterial pathogen Neisseria gonorrhoeae is naturally competent for transformation with species-related DNA. We show here that two phase-variable pilus-associated proteins, the major pilus subunit (pilin, or PilE) and PilC, a factor known to function in the assembly and adherence of gonococcal pili, are essential for transformation competence. The PilE and PilC proteins are necessary for the conversion of linearized plasmid DNA carrying the Neisseria-specific DNA uptake signal into a DNase-resistant form. The biogenesis of typical pilus fibers is neither essential nor sufficient for this process. DNA uptake deficiency of defined piliated pilC1,2 double mutants can be complemented by expression of a cloned pilC2 gene in trans. The PilC defect can also be restored by the addition of purified PilC protein, or better, pili containing PilC protein, to the mutant gonococci. Our data suggest that the two phase-variable Pil proteins act on the bacterial cell surface and cooperate in DNA recognition and/or outer membrane translocation.

Controlled doping of transition metal cations in alumina pillared clays

A two-step method of loading controlled amounts of transition metal cations into alumina pillared clays (Al-PILCs) is proposed. First, calcined Al-PILC was dispersed into an aqueous solution of sodium or ammonium ions. Increasing the pH of the dispersion resulted in an increase in the amount of cations loaded into the clay. The ion-doped Al-PILC was then exchanged with an aqueous solution of transition metal salt at a pH of similar to 4.5 to replace Na+ or NH4+ ions by transition metal cations. Analytical techniques such as atomic absorption spectroscopy, X-ray diffraction, diffuse reflectance-ultraviolet-visible spectroscopy, as well as N-2 adsorption were used to characterize the PILC products with and without the loading of metal ions. The introduced transition metal species exist in the forms of hydrated ions in the PILC hosts. The content of transition metal ions in the final product increased with the amount of Na+ or NH4+ loaded in the first step so that by controlling the pH of the dispersion in the first step, one can control the doping amounts of transition metal cations into Al-PILCs. A sample containing 0.125 mmol/g of nickel was thus obtained, which is similar to 3 times of that obtained by directly exchanging Al-PILC with Ni(NO3)(2) solution, while the pillared layered structures of the Al-PILC remained. The porosity analysis using N-2 adsorption data indicated that most of the doped transition metal ions dispersed homogeneously in the micropores of the Al-PILC, significantly affecting the micropore structure.

Porous clays and pillared clays-based catalysts. Part 2: A review of the catalytic and molecular sieve applications

Metal oxide pillared clay (PILC) possesses several interesting properties, such as large surface area, high pore volume and tunable pore size (from micropore to mesopore), high thermal stability, strong surface acidity and catalytic active substrates/metal oxide pillars. These unique characteristics make PILC an attractive material in catalytic reactions. It can be made either as catalyst support or directly used as catalyst. This paper is a continuous work from Kloprogge's review (J.T. Kloprogge, J. Porous Mater. 5, 5 1998) on the synthesis and properties of smectites and related PILCs and will focus on the diverse applications of clay pillared with different types of metal oxides in the heterogeneous catalysis area and adsorption area. The relation between the performance of the PILC and its physico-chemical features will be addressed.

Pore structure characterisation of pillared clays using a modified MP method

The data of nitrogen adsorption on pillared clays (PILC) are converted to comparison plots (t-plots) to derive their pore size distribution (PSD). As in the MP method, the surface area of a group of pores having similar pore sizes is calculated from the slopes of tangent lines at two succeeding points on a comparison plot. By the modified MP method in this work, the tangent line is extrapolated to the adsorption axis on the t-plot, and the difference between intercepts is used to obtain the volume of the group of pores. From the information of surface area and pore volume, the average width of the pore group can be calculated and hence the PSDs of PILCs are obtained by carrying out such calculation procedures from high to low t. With this method, PSDs of several pillared clays are calculated over a wide pore size range, from micropores to mesopores. It is found that the modified MP method could result in the underestimation of the width of ultramicropores due to the enhancement in adsorption energy in these pores. Nevertheless, the method can be very useful in calculating the surface area and pore volume, as well as a mean width of these pores. For super-micropores and mesopores, pore size can also be underestimated, due to deviation of the pore shape from a slit. The principles of the improved MP method, as well as problems associated with it are thoroughly discussed in this paper. In general, this modified method provides practically meaningful results which are consistent with the pore dimension obtained from powder X-ray diffraction measurements, but involves no complicated theoretical treatment or assumptions.

Characterization of pore structure and coordination of titanium in TiO2 and SiO2-TiO2 sol-pillared clays

Titania sol-pillared clay (TiO2 PILC) and silica-titania sol-pillared clay (SiO2-TiO2 PILC) were synthesized by the sol-gel method. Supercritical drying (SCD) and treatment with quaternary ammonium surfactants were used to tailor the pore structure of the resulting clay. It was found that SCD approach increased the external surface area of the PILCs dramatically and that treatment with surfactants could be used to tailor pore size because the mesopore formation in the galleries between the clay layers follows the templating mechanism as observed in the synthesis of MCM-41 materials. Highly mesoporous solids were thus obtained. In calcined TiO2 PILC, ultrafine crystallites in anatase phase, which are active for photocatalytic oxidation of organics, were observed. In SiO2-TiO2 PILCs and their derivatives, titanium was highly dispersed in the matrix of silica and no crystal phase was observed. The highly dispersed titanium sites are good catalytic centers for selective oxidation of organic compounds. (C) 2001 Academic Press.

Argilas pilarizadas - uma introdução

The synthesis, characterization and some applications in catalysis of pillared clays are described at an introductory level. The use of x-ray diffraction, surface area measurements, thermal analysis, IR spectrophotometry and solid-state NMR in the characterization of pillared clays is briefly discussed. Pillarization followed by doping or introduction of metal clusters into clays could lead to the development of selective heterogeneous catalysts.

Influência de argilas pilarizadas na decomposição catalítica do óleo de andiroba

Amostras de esmectitas oriundas do estado do Pará, região amazônica, Brasil, foram usadas em processo de pilarização no presente estudo. As matrizes pilarizadas e natural foram caracterizadas usando DRX e analise textural usando isotermas de adsorção-desorção de nitrogênio. Os íons de intercalação (Al13, Ti, Zr) foram obtidos através de reações químicas com soluções de AlCl(3)6H2O/ NaOH, etoxido de titânio/HCl, acetato de zircônio / HCl. Os resultados obtidos com o processo de pilarização apresentaram aumento do espaçamento basal de 15,6 para 20, 64 Å e área superficial de 44 para 358 m²/g (Zr-PILC). A estabilidade térmica da argila natural foi melhorada com o processo de pilarização. O material resultante foi submetido a um processo catalítico de decomposição do óleo de andiroba em um reator de leito fixo a 673 ± 1 K. A atividade catalítica foi determinada pelo produto de decomposição resultante da reação química. Os parâmetros físico-químicos foram obtidos usando DRX, FTIR e análise textural. As argilas pilarizadas apresentaram alta acidez de Brønsted, com alta concentração de hidrocarbonetos aromáticos e baixa concentração de hidrocarbonetos alifáticos.

Spectroscopic study of the polymerization of intercalated anilinium ions in different montmorillonite clays

The polymerization of the intercalated aniline ions was studied in three different clays, Swy2-montmorillonite (MMT), synthetic mica-montmorillonite (Synl) and pillarized Swy2-montmorillonite (PILC). PANI is formed between the MMT and Syn1 clay layers, being confirmed by the shift of d(001) peak in the X-ray pattern. X-ray Absorption near to Si K edge (Si K XANES) data show that the structures of clays are preserved after the polymerization process and in addition to the SEM images show that morphologies of the clays are maintained after polymerization, indicating no polymerization in their external surface. UV-vis-NIR and resonance Raman data display that the PANI formed in Syn1 galleries has higher amount of phenazinic rings than observed for PANI intercalated in montmorillonite (MMT) clay. No polymer formation was detected in the PILC. N K XANES and EPR spectroscopies show the presence of azo and radical nitrogen in intercalated PAN! chains. Hence, the results are rationalized considering the structural differences between the clays for understanding the role of the anilinium polymerization within the clays galleries. (C) 2011 Elsevier B.V. All rights reserved.

Argilas modificadas como catalisadores ácidos sólidos

Important bentonitic deposits are present in Porto Santo Island, part of the Madeira Archipelago. Several locations were selected and samples were collected and characterised. The bentonite obtained at Serra de Dentro (SD) was selected for further laboratorial work. The fine fraction of SD bentonite was purified using several methods and the sodium homoionic form was prepared. This was the starting material used in the three generic types of modifications: metal exchange, acid activation and pillaring. These modifications produce materials with markedly different acidic (e.g. Brönsted and/or Lewis acidity), textural (e.g. increase of the surface area and active site accessibility) or structural (e.g. creation of permanent porous structures) properties. The wide range of materials obtained (including reference clays counterparts) was characterised in terms of chemical, structural, textural and catalytic properties. Limonene is an important raw material produced in Portugal, and its aromatisation reaction was chosen for the catalytic characterisation of the clay catalysts prepared.

Influência da temperatura de formação do íon de Keggin no processo de pilarização de esmectitas

As amostras de esmectita do estado do Pará, Amazônia, Brasil foram caracterizados utilizando XRD, FTIR e análise textural por curvas isotérmicas adsorpition-desorption nitrogênio. Na produção das argilas pilarizadas foi usado o íon Al,₁₃ (o íon de keggin), este íon foi obtido pela reação das soluções AlC_l36H₂O/aOH, com razão molar OH/Al=2, com intercalação em temperatura ambiente, durante as 3 horas e calcinada em 450ºC (temperatura adequada da calcinação). O material foi preparado utilizando soluções produzidas na faixa de temperatura de 25, 45, 65, 85, 105ºC, o Resultado mostrou que o processo de pilarização aumenta o espaçamento basal da argila natural de 14,02 para 19,74 Å e a área superficial de 44,30 para 198,03m,²/g. a estabilidade térmica da argila natural foi melhorada pelo procedimento de pilarização.

Influência de argilas pilarizadas na decomposição catalítica do óleo de andiroba

Amostras de esmectitas oriundas do estado do Pará, região amazônica, Brasil, foram usadas em processo de pilarização no presente estudo. As matrizes pilarizadas e natural foram caracterizadas usando DRX e analise textural usando isotermas de adsorção-desorção de nitrogênio. Os íons de intercalação (Al₁₃, Ti, Zr) foram obtidos através de reações químicas com soluções de AlCl₃6H₂O/ NaOH, etoxido de titânio/HCl, acetato de zircônio / HCl. Os resultados obtidos com o processo de pilarização apresentaram aumento do espaçamento basal de 15,6 para 20, 64 Å e área superficial de 44 para 358 m²/g (Zr-PILC). A estabilidade térmica da argila natural foi melhorada com o processo de pilarização. O material resultante foi submetido a um processo catalítico de decomposição do óleo de andiroba em um reator de leito fixo a 673 ± 1 K. A atividade catalítica foi determinada pelo produto de decomposição resultante da reação química. Os parâmetros físico-químicos foram obtidos usando DRX, FTIR e análise textural. As argilas pilarizadas apresentaram alta acidez de Brønsted, com alta concentração de hidrocarbonetos aromáticos e baixa concentração de hidrocarbonetos alifáticos.