Liquid phase epitaxial growth of pure and doped GaSb layers: morphological evolution and native defects

Undoped and Te-doped gallium antimonide (GaSb) layers have been grown on GaSb bulk substrates by the liquid phase epitaxial technique from Ga-rich and Sb-rich melts. The nucleation morphology of the grown layers has been studied as a function of growth temperature and substrate orientation. MOS structures have been fabricated on the epilayers to evaluate the native defect content in the grown layers from the C-V characteristics. Layers grown from antimony rich melts always exhibit p-type conductivity. In contrast, a type conversion from p- to n- was observed in layers grown from gallium rich melts below 400 degrees C. The electron mobility of undoped n-type layers grown from Ga-rich melts and tellurium doped layers grown from Sb- and Ga-rich solutions has been evaluated.

Performance of CMOS Devices in Silicon-on-Sapphire Films After Solid-Phase Epitaxial Growth With Rapid Electron-Beam Heating

The crystal quality of 0.3-μm-thick as-grown epitaxial silicon-on-sapphire (SOS) was improved using solid-phase epitaxy (SPE) by implantation with silicon to 1015 ions/cm2 at 175 keV and rapid annealing using electron-beam heating, n-channel and p-channel transistormobilities increased by 31 and 19 percent, respectively, and a reduction in ring-oscillator stage delay confirmed that crystal defects near the upper silicon surface had been removed. Leakage in n-channel transistors was not significantly affected by the regrowth process but for p-channel transistors back-channel leakage was considerably greater than for the control devices. This is attributed to aluminum released by damage to the sapphire during silicon implantation. © 1985 IEEE

ON THE FORMATION OF THE SBGA HETEROANTISITE IN METALORGANIC VAPOR-PHASE EPITAXIAL GAAS-SB

Metalorganic vapor-phase epitaxial growth of GaAs doped with isovalent Sb is reported. By increasing the trimethylantimony concentration during growth the total Sb concentration was varied between 1 X 10(17)-1 X 10(19) cm-3. A new deep level defect with an activation energy of the thermal emission rates of E(c) - 0.54 eV is observed. The defect concentration increases with increasing As partial pressure and with increasing Sb doping. It is also found that the EL2 concentration decreases with increasing Sb doping. The new energy level is suggested to be the 0/ + transition of the Sb(Ga) heteroantisite defect. No photocapacitance quenching effect, reflecting a metastable state as seen for EL2 (As(Ga)), is observed for Sb(Ga).

Direct epitaxial growth of θ-Ni2Si by reaction of a thin Ni(10 at.% Pt) film with Si(1 0 0) substrate

The reaction between an 11 nm Ni(10 at.% Pt) film on a Si substrate has been examined by in situ X-ray diffraction (XRD), atom probe tomography (APT) and transmission electron microscopy (TEM). In situ XRD experiments show the unusual formation of a phase without an XRD peak through consumption of the metal. According to APT, this phase has an Si concentration gradient in accordance with the θ-Ni2Si metastable phase. TEM analysis confirms the direct formation of θ-Ni2Si in epitaxy on Si(1 0 0) with two variants of the epitaxial relationship. © 2014 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Wurtzite GaN epitaxial growth on a Si(001) substrate using gamma-Al2O3 as an intermediate layer

Wurtzite GaN films have been grown on (001) Si substrates using gamma-Al2O3 as an intermediate layer by low pressure (similar to 76 Torr) metalorganic chemical vapor deposition. Reflection high energy electron diffraction and double crystal x-ray diffraction measurements revealed that the thin gamma-Al2O3 layer of "compliant" character was an effective intermediate layer for the GaN film grown epitaxially on Si. The narrowest linewidth of the x-ray rocking curve for (0002) diffraction of the 1.3 mu m GaN sample was 54 arcmin. The orientation relationship of GaN/gamma-Al2O3/Si was (0001) GaN parallel to(001) gamma-Al2O3 parallel to(001) Si, [11-20] GaN parallel to[110] gamma-Al2O3 parallel to[110] Si. The photoluminescence measurement for GaN at room temperature exhibited a near band-edge peak of 365 nm (3.4 eV). (C) 1998 American Institute of Physics.

Adsorption-controlled molecular-beam epitaxial growth of BiFeO3

BiFeO3 thin films have been deposited on (111) SrTiO3 single crystal substrates by reactive molecular-beam epitaxy in an adsorption-controlled growth regime. This is achieved by supplying a bismuth overpressure and utilizing the differential vapor pressures between bismuth oxides and BiFeO3 to control stoichiometry. Four-circle x-ray diffraction reveals phase-pure, untwinned, epitaxial, (0001)-oriented films with rocking curve full width at half maximum values as narrow as 25 arc sec (0.007 degrees). Second harmonic generation polar plots combined with diffraction establish the crystallographic point group of these untwinned epitaxial films to be 3m at room temperature. (C) 2007 American Institute of Physics.

Evidence of hetero-epitaxial growth of Pb(Mg1/3Nb2/3)O-3 on the BaTiO3 seed particles of a citrate solution

Citrate solution was employed in preparing Pb(Mg1/3Nb1/3)O-3 (PMN) powder from polymeric precursors. BaTiO3 particles of 600 nm average size were used as seed for growing PMN. X-ray diffraction (XRD) indicated the presence of both, pyrochlore Pb6Nb6MgO22 (P6N) and perovskite phases. Transmission electron microscopy (TEM) observations indicated that only the PMN phase has hetero-epitaxially grown on the BaTiO3 seed particles. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Epitaxial growth of Co3O4 films by low temperature, low pressure chemical vapour deposition

The growth of strongly oriented or epitaxial thin films of metal oxides generally requires relatively high growth temperatures or infusion of energy to the growth surface through means such as ion bombardment. We have grown high quality epitaxial thin films of Co3O4 on different substrates at a temperature as low as 400 degreesC by low-pressure metalorganic chemical vapour deposition (MOCVD) using cobalt(II) acetylacetonate as the precursor. With oxygen as the reactant gas, polycrystalline Co3O4 films are formed on glass and Si (100) in the temperature range 400-550 degreesC. Under similar conditions of growth. highly oriented films of Co3O4 are formed on SrTiO3 (100) and LaAlO3 (100). The activation energy for the growth of polycrystalline films on glass is significantly higher than that for epitaxial growth on SrTiO3 (100). The film on LaAlO3 (100) grown at 450 degreesC shows a rocking curve FWHM of 1.61 degrees, which reduces to 1.32 degrees when it is annealed in oxygen at 725 degreesC. The film on SrTiO3 (100) has a FWHM of 0.33 degrees (as deposited) and 0.29 (after annealing at 725 degreesC). The phi -scan analysis shows cube-on-cube epitaxy on both these substrates. The quality of epitaxy on SrTiO3 (100) is comparable to the best of the perovskite-based oxide thin films grown at significantly higher temperatures. A plausible mechanism is proposed for the observed low temperature epitaxy. (C) 2001 Published by Elsevier Science B.V.

Epitaxial Growth of Co3O4 Films by Low Temperature, Low Pressure Chemical Vapor Deposition

The growth of strongly oriented or epitaxial thin films of metal oxides generally requires relatively high growth temperatures or infusion of energy to the growth surface through means such as ion bombardment. We have grown high quality epitaxial thin films of Co3O4 on different substrates at a temperature as low as 450°C by low-pressure metal-organic chemical vapor deposition (MOCVD) using cobalt(II) acetylacetonate as the precursor. With oxygen as the reactant gas, polycrystalline Co3O4 films are formed on glass and Si(100) in the temperature range 350-550°C. Under similar conditions of growth, highly oriented films of Co3O4 are formed on SrTiO3(100) and LaAlO3(100). The film on LaAlO3(100) grown at 450°C show a rocking curve FWHM of 1.61°, which reduces to 1.32° when it is annealed in oxygen at 725°C. The film on SrTiO3(100) has a FWHM of 0.330 (as deposited) and 0.29° (after annealing at 725°C). The ø-scan analysis shows cube-on-cube epitaxy on both these substrates. The quality of epitaxy on SrTiO3(100) is comparable to the best of the pervoskite-based oxide thin films grown at significantly higher temperatures.

Molecular beam epitaxial growth of (11-22) GaN on m-plane sapphire

The structural and optical properties of semipolar (1 1 -2 2) GaN grown on m-plane (1 0 -1 0) sapphire substrates by molecular beam epitaxy were investigated. An in-plane orientation relationship was found to be 1 -1 0 0] GaN parallel to 1 2-1 0] sapphire and -1 -1 2 3] GaN parallel to 0 0 0 1] sapphire for semipolar GaN on m-plane sapphire substrates. The near band emission (NBE) was found at 3.432 eV, which is slightly blue shifted compared to the bulk GaN. The Raman E-2 (high) peak position observed at 569.1 cm(-1), which indicates that film is compressively strained. Schottky barrier height (phi(b)) and the ideality factor (eta) for the Au/semipolar GaN Schottky diode found to be 0.55 eV and 2.11, respectively obtained from the TE model.

Phase evolutions, growth kinetics and diffusion parameters in the Co-Ni-Ta system

Diffusion couple experiments are conducted to study phase evolutions in the Co-rich part of the Co-Ni-Ta phase diagram. This helps to examine the available phase diagram and propose a correction on the stability of the Co2Ta phase based on the compositional measurements and X-ray analysis. The growth rate of this phase decreases with an increase in Ni content. The same is reflected on the estimated integrated interdiffusion coefficients of the components in this phase. The possible reasons for this change are discussed based on the discussions of defects, crystal structure and the driving forces for diffusion. Diffusion rate of Co in the Co2Ta phase at the Co-rich composition is higher because of more number of Co-Co bonds present compared to that of Ta-Ta bonds and the presence of Co antisites for the deviation from the stoichiometry. The decrease in the diffusion coefficients because of Ni addition indicates that Ni preferably replaces Co antisites to decrease the diffusion rate. (C) 2014 Elsevier B.V. All rights reserved.

Liquid phase epitaxy growth of AlxGayIn1-x-yPzAs1-zGaAs with direct band gap up to 2.0 eV

III-V pentenary semiconductor AlGaInPAs with a direct band gap of up to 2.0 eV has been grown successfully on GaAs substrates by liquid phase epitaxy;(LPE). With the introduction of the energy bowing parameters of quaternaries, the theoretical calculations agree well with the measured PL peak energy data from pentenary samples.

Epitaxial growth of ZnO films on (100) and (001) gamma-LiAlO2 substrates by pulsed laser deposition

Structural and optical properties were investigated for ZnO films grown on (100) and (001) gamma-LiAlO2 (LAO) substrates by pulsed laser deposition method. According XRD results, it is intuitionistic that (100) LAO is suitable for fabricating high quality ZnO film, while (001) LAO is unsuitable. The FWHM of XRD, stress in film and FWHM of UV PL spectra for ZnO films on (100) LAO show a decreasing with increasing substrate temperature from 300 to 600 degrees C. ZnO film fabricated at 600 degrees C has the greatest grain size, the smallest stress (0.47 Gpa) and PL FWHM value (similar to 85 meV). This means that the substrate temperature of 600 degrees C is optimum for ZnO film deposited on (100) LAO. Moreover, it was found that the UV PL spectra intensity of ZnO film is not only related to the grain size and stoichiometric, but also depends on the stress in the film.