Effect of the bath pH on the electrodeposition of nanocrystalline Pd-Co alloys and their magnetic properties

The effect of the bath pH on the electrodeposition of nanocrystalline Pd-Co alloys and on their magnetic properties was studied. The pH practically did not affect the alloy composition. Conversely, the pH showed a significant influence on the shape and size of crystallites. Two different crystallites morphology were observed depending on the bath pH. A crystallite size ranging from 18.2 to 30 nm was obtained from X-ray diffractometry (XRD) patterns using the Scherrer's method. Also from the XRD patterns the lattice strain percentage was calculated and correlated with the residual stress, which probably originated during the film electrodeposition on the substrate. Some alloy magnetic properties showed small variations. In contrast, high and unexpected coercivities were obtained reaching a maximum of 1.69 kOe at pH 5.5. The high coercivity values were attributed to the presence of residual stress at the film-substrate interface, which increased as the bath pH and crystallite size decrease, both of them contributing simultaneously to increase in coercivity. (C) 2006 Elsevier B.V. All rights reserved.

The influence of residual stress and crystallite size on the magnetic properties of electrodepo sited nanocrystalline Pd-Co alloys

Nanocrystalline Pd-Co alloys were obtained by electrodeposition from an ammoniacal chloride bath. The influence of the crystallite size and the residual stress on the magnetic properties of the alloys was investigated. The residual stress increased as the applied current density was increased. It was associated to the high nucleation rate during electrodeposition and correlated to the lattice strain, estimated from the XRD patterns. Also from the XRD patterns the average crystallite size and the lattice constant were determined by Scherrer's and Rietveld's methods, respectively. Both parameters were directly influenced by the applied current density. Magnetic properties such as coercivity, remanence, saturation magnetization and squareness showed strong dependence on the residual stress and crystallite size. Coercivity higher than 1 kOe was achieved when a high current density was applied. High coercivity was attributed to the presence of residual stress and to the small crystallite size of deposits. (C) 2007 Elsevier B.V. All rights reserved.

Influence of composition on the structure, electric and magnetic properties of Pd-Mn-P and Pd-Co-P amorphous alloys

The influence of composition on the structure and on the electric and magnetic properties of amorphous Pd-Mn-P and Pd-Co-P prepared by rapid quenching techniques were investigated in terms of (1) the 3d band filling of the first transition metal group, (2) the phosphorus concentration effect which acts as an electron donor and (3) the transition metal concentration.

The structure is essentially characterized by a set of polyhedra subunits essentially inverse to the packing of hard spheres in real space. Examination of computer generated distribution functions using Monte Carlo random statistical distribution of these polyhedra entities demonstrated tile reproducibility of the experimentally calculated atomic distribution function. As a result, several possible "structural parameters" are proposed such as: the number of nearest neighbors, the metal-to-metal distance, the degree of short-range order and the affinity between metal-metal and metal-metalloid. It is shown that the degree of disorder increases from Ni to Mn. Similar behavior is observed with increase in the phosphorus concentration.

The magnetic properties of Pd-Co-P alloys show that they are ferromagnetic with a Curie temperature between 272 and 399°K as the cobalt concentration increases from 15 to 50 at.%. Below 20 at.% Co the short-range exchange interactions which produce the ferromagnetism are unable to establish a long-range magnetic order and a peak in the magnetization shows up at the lowest temperature range . The electric resistivity measurements were performed from liquid helium temperatures up to the vicinity of the melting point (900°K). The thermomagnetic analysis was carried out under an applied field of 6.0 kOe. The electrical resistivity of Pd-Co-P shows the coexistence of a Kondo-like minimum with ferromagnetism. The minimum becomes less important as the transition metal concentration increases and the coefficients of ℓn T and T^2 become smaller and strongly temperature dependent. The negative magnetoresistivity is a strong indication of the existence of localized moment.

The temperature coefficient of resistivity which is positive for Pd- Fe-P, Pd-Ni-P, and Pd-Co-P becomes negative for Pd-Mn-P. It is possible to account for the negative temperature dependence by the localized spin fluctuation model and the high density of states at the Fermi energy which becomes maximum between Mn and Cr. The magnetization curves for Pd-Mn-P are typical of those resulting from the interplay of different exchange forces. The established relationship between susceptibility and resistivity confirms the localized spin fluctuation model. The magnetoresistivity of Pd-Mn-P could be interpreted in tenns of a short-range magnetic ordering that could arise from the Rudennan-Kittel type interactions.

First order reversal curve analysis of nanocrystalline Pd(80)Co(20) alloy films

Films of isotropic nanocrystalline Pd(80)Co(20) alloys were obtained by electrodeposition onto brass substrate in plating baths maintained at different pH values. Increasing the pH of the plating bath led to an increase in mean grain size without inducing significant changes in the composition of the alloy. The magnetocrystalline anisotropy constant was estimated and the value was of the same order of magnitude as that reported for samples with perpendicular magnetic anisotropy. First order reversal curve (FORC) analysis revealed the presence of an important component of reversible magnetization. Also, FORC diagrams obtained at different sweep rate of the applied magnetic field, revealed that this reversible component is strongly affected by kinetic effect. The slight bias observed in the irreversible part of the FORC distribution suggested the dominance of magnetizing intergrain exchange coupling over demagnetizing dipolar interactions and microstructural disorder. (c) 2009 Elsevier B.V. All rights reserved.

Análise química, microestrutural, determinação das propriedades mecânicas e dureza de ligas odontológicas (Ag Pd,Co Cr e NiCr) fundidas em diferentes temperaturas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Pretreatment of polymer-supported Pd-Co and its catalytic activity

Various pretreatments of poly (N-vinyl-2-pyrrolidone) (PVP) protected palladium-cobalt system result in different catalytic activities in the hydrodechlorination of chlorobenzene.

Crystallographic and electrochemical characteristics of Ti-Zr-Ni-Pd quasicrystalline alloys

Ti45Zr35Ni20-xPdx (x = 0, 1, 3, 5 and 7, at%) alloys were prepared by melt-spinning. The phase structure and electrochemical hydrogen storage performances of melt-spun alloys were investigated. The melt-spun alloys were icosahedral quasicrystalline phase, and the quasi-lattice constant increased with increasing x value. The maximum discharge capacity of alloy electrodes increased from 79 mAh/g (x = 0) to 148 mAh/g (x = 7). High-rate dis-chargeability and cycling stability were also enhanced with the increase of Pd content. The improvement in the electrochemical hydrogen storage characteristics may be ascribed to better electrochemical activity and oxidation resistance of Pd than that of Ni.

Dynamic, in situ optical, magnetic and magneto-optical monitoring of the growth of Co/Au and Pd/Co/Au multilayer systems

The growth of magnetron sputtered Co/Au and Pd/Co/Au superlattices on Au and Pd buffer layers, deposited onto glass substrates, has been monitored optically and magneto-optically in real time, using rotating analyser ellipsometry and Kerr polarimetry, at a wavelength of 633 nm. The magneto-optical traces, combined with ex situ and in situ hysteresis loops, provide a detailed and informative fingerprint of the optical and magnetic properties of the films as they evolve during growth. For Co/Au, oscillations in the polar magneto-optical effect developed during the deposition of An overlayers on Co and these may be attributed to quantum well states. However, the hysteresis measurements show that the magnetic field required to maintain saturation magnetization throughout the experiment was larger than available in situ, introducing a degree of confusion concerning the interpretation of the data. This problem was overcome by the incorporation of Pd layers into the Co/Au structure, thereby eliminating variation in magnetic orientation during growth of the Au layers as a contributory factor to the observations.

Surface segregation and oxidation studies of Cu-Sn and Cu-Pd alloys by x-ray photoelectron and auger spectroscopy

X-ray photoelectron and Auger spectroscopic techniques have been employed to study surface segregation and oxidation of Cu-1 at%Sn, Cu-9at%Pd and Cu-25at%Pd alloys. Both Cu-Pd(9%) and Cu-Pd(25%) alloys show segregation of Cu when heated above 500 K. The Pd concentration was reduced by 50% at 750 K compared to the bulk composition; the enthalpy of segregation of Cu is around - 6kJ/mol. Sn segregation is seen from 470 to 650 K in the Cu-Sn(1%) alloy, and a saturation plateau of Sn concentration above 650 K is observed. Surface oxidation of Cu-Sn(1%) and Cu-Pd(9%) alloys at 500 K showed the formation of Cu2O on the surface with total suppression of Sn or Pd on the respective alloy surfaces. On vacuum annealing the oxidised Cu-Sn alloy surface at 550 K, a displacement reaction 2Cu2O+Sn→4Cu+SnO2 was observed. However, under similar annealing of the oxidised Cu-Pd(9%) alloy surface at 500 K, oxide oxygen was totally desorbed leaving the Cu-Pd alloy surface clean. In the case of the Cu-Pd(25%) alloy, only dissociatively chemisorbed oxygen was seen at 500 K which desorbed at the same temperature. Oxygen spill-over from copper to palladium is suggested as the mechanism of oxygen desorption from the oxidised Cu-Pd alloy surfaces.

Influence of composition on the structure and properties of Fe-Pd-P and Ni-Pd-P amorphous alloys

Ternary alloys of nickel-palladium-phosphorus and iron-palladium- phosphorus containing 20 atomic % phosphorus were rapidly quenched from the liquid state. The structure of the quenched alloys was investigated by X-ray diffraction. Broad maxima in the diffraction patterns, indicative of a glass-like structure, were obtained for 13 to 73 atomic % nickel and 13 to 44 atomic % iron, with palladium adding up to 80%.

Radial distribution functions were computed from the diffraction data and yielded average interatomic distances and coordination numbers. The structure of the amorphous alloys could be explained in terms of structural units analogous to those existing in the crystalline Pd₃P, Ni₃P and Fe₃P phases, with iron or nickel substituting for palladium. A linear relationship between interatomic distances and composition, similar to Vegard's law, was shown for these metallic glasses.

Electrical resistivity measurements showed that the quenched alloys were metallic. Measurements were performed from liquid helium temperatures (4.2°K) up to the vicinity of the melting points (900°K- 1000°K). The temperature coefficient in the glassy state was very low, of the order of 10^-4/°K. A resistivity minimum was found at low temperature, varying between 9°K and 14°K for Ni_x-Pd_80-x -P₂₀ and between 17°K and 96°K for Fe_x-Pd_80-x -P₂₀, indicating the presence of a Kondo effect. Resistivity measurements, with a constant heating rate of about 1.5°C/min,showed progressive crystallization above approximately 600°K.

The magnetic moments of the amorphous Fe-Pd-P alloys were measured as a function of magnetic field and temperature. True ferromagnetism was found for the alloys Fe₃₂-Pd₄₈-P₂₀ and Fe₄₄-Pd₃₆-P₂₀ with Curie points at 165° K and 380° K respectively. Extrapolated values of the saturation magnetic moments to 0° K were 1.70 µ_B and 2.10 µ_B respectively. The amorphous alloy Fe₂₃-Pd₅₇-P₂₀ was assumed to be superparamagnetic. The experimental data indicate that phosphorus contributes to the decrease of moments by electron transfer, whereas palladium atoms probably have a small magnetic moment. A preliminary investigation of the Ni-Pd-P amorphous alloys showed that these alloys are weakly paramagnetic.

Conduction-electron localized-moment interaction in palladium-silicon base amorphous alloys containing transition metals

The electrical and magnetic properties of amorphous alloys obtained by rapid quenching from the liquid state have been studied. The composition of these alloys corresponds to the general formula M_xPd_80-xSi₂₀, in which M stands for a metal of the first transition series between chromium and nickel and x is its atomic concentration. The concentration ranges within which an amorphous structure could be obtained were: from 0 to 7 for Cr, Mn and Fe, from 0 to 11 for Co and from 0 to 15 for Ni. A well-defined minimum in the resistivity vs temperature curve was observed for all alloys except those containing nickel. The alloys for which a resistivity minimum was observed had a negative magnetoresistivity approximately proportional to the square of the magnetization and their susceptibility obeyed the Curie-Weiss law in a wide temperature range. For concentrated Fe and Co alloys the resistivity minimum was found to coexist with ferromagnetism. These observations lead to the conclusion that the present results are due to a s-d exchange interaction. The unusually high resistivity minimum temperature observed in the Cr alloys is interpreted as a result of a high Kondo temperature and a large s-d exchange integral. A low Fermi energy of the amorphous alloys (3.5 eV) is also responsible for the anomalies due to the s-d exchange interaction.

Magnetic moments in amorpous palladium-cobalt-silicon alloys

The magnetic moments of amorphous ternary alloys containing Pd, Co and Si in atomic concentrations corresponding to Pd_(80-x)Co_xSi_(20) in which x is 3, 5, 7, 9, 10 and 11, have been measured between 1.8 and 300°K and in magnetic fields up to 8.35 kOe. The alloys were obtained by rapid quenching of a liquid droplet and their structures were analyzed by X-ray diffraction. The measurements were made in a null-coil pendulum magnetometer in which the temperature could be varied continuously without immersing the sample in a cryogenic liquid. The alloys containing 9 at.% Co or less obeyed Curie's Law over certain temperature ranges, and had negligible permanent moments at room temperature. Those containing 10 and 11 at.% Co followed Curie's Law only above approximately 200°K and had significant permanent moments at room temperature. For all alloys, the moments calculated from Curie's Law were too high to be accounted for by the moments of individual Co atoms. To explain these findings, a model based on the existence of superparamagnetic clustering is proposed. The cluster sizes calculated from the model are consistent with the rapid onset of ferromagnetism in the alloys containing 10 and 11 at.% Co and with the magnetic moments in an alloy containing 7 at.% Co heat treated in such a manner as to contain a small amount of a crystalline phase. In alloys containing 7 at.% Co or less, a maximum in the magnetization vs temperature curve was observed around 10°K. This maximum was eliminated by cooling the alloy in a magnetic field, and an explanation for this observation is suggested.