Deposition of carbon nitride films using an electron cyclotron wave resonance plasma source

Hydrogenated amorphous carbon nitride (a-C:N:H) has been synthesized using a high plasma density electron cyclotron wave resonance (ECWR) technique using N2 and C2H2 as source gases, at different ratios and a fixed ion energy (80 eV). The composition, structure and bonding state of the films were investigated and related to their optical and electrical properties. The nitrogen content in the film rises rapidly until the N2/C2H2 gas ratio reaches 2 and then increases more gradually, while the deposition rate decreases steeply, placing an upper limit for the nitrogen incorporation at 30 at%. For nitrogen contents above 20 at%, the band gap and sp3-bonded carbon fraction decrease from 1.7 to 1.1 eV and approximately 65 to 40%, respectively. Films with higher nitrogen content are less dense than the original hydrogenated tetrahedral amorphous carbon (ta-C:H) film but, because they have a relatively high band gap (1.1 eV), high resistivity (109 Ω cm) and moderate sp3-bonded carbon fraction (40%), they should be classed as polymeric in nature.

Effect of deposition conditions on the chemical bonding in sputtered carbon nitride films

A balanced planar r.f. powered magnetron sputter source has been used to deposit carbon nitride films from a graphite target under various conditions. Sample temperature, bias voltage and nitrogen content in the gas mixture were varied. The effects of oxygen, methane and ammonia on the film growth were also studied. Special attention was paid to the effects of the deposition parameters on the structure of the films, in particular the hybridisation of the carbon and nitrogen bonding. The chemical bonding of the carbon and nitrogen atoms was studied by electron energy loss spectroscopy (EELS). The chemical composition was evaluated by Rutherford back-scattering. The intensity of transitions to π antibonding orbitals, as revealed by EELS, was found to increase with the nitrogen content in the films. Ion bombardment of the films during growth and the addition of oxygen or hydrogen-rich gases further increased the proportion of π bonds of both the carbon and nitrogen atoms. It is suggested that the increase in the transitions to μ antibond orbitals is to be explained by increased sp2 or possibly sp hybridisation of the carbon and nitrogen. Also, the effect of annealing on the bonding of nitrogen rich films after deposition was tested. The changes caused by nitrogen and deposition conditions are consistent with previous reports on the formation of paracyanogen structures.

Optical gap in carbon nitride films

In this paper we study the effect of introducing nitrogen into different carbon networks. Two kinds of carbon nitride films were deposited: (a) Using a DC-magnetron sputtering system sp2 bonded carbon nitride (a-CN) films were deposited and (b) Using a combination of filtered cathodic vacuum arc and a low-pressure N2 plasma source, N was introduced into sp3 carbon networks (ta-C), leading to the formation of a more dense CN film named ta-CN. For ta-CN films we found that the optical gap initially decreases as the N content and the sp2 fraction rises, but above a certain N quantity there is a level-off of the value, and the gap then remains constant despite further increases in the fraction and clustering of the sp2 phase. However, for a-CN films the optical gap increases with the nitrogen content. These two different trends are not easily explained using the same framework as that for carbon films, in which any decrease in the band gap is associated to an increase in the sp2 fraction or its clustering. Here we discuss the conditions that lead to high optical gap in sp2-bonded carbon nitride samples, which are clearly not associated to the presence of any crystalline super-hard phase. We also compared other differences in properties observed between the two films, such as deposition rate, infrared and Raman spectra. © 2003 Elsevier Science B.V. All rights reserved.