Obtaining NiAl intermetallic compound using different milling devices

NiAl intermetallic compound was synthesized by mechanical alloying technique in planetary and attritor mills. The starting powders consisted of elemental mixtures of Ni and Al at Ni50Al50(at%) composition. In the planetary mill, compound formation occurred gradually during mechanical alloying, while the occurrence of a mechanically induced self-propagating reaction (MSR) can be suggested in the attritor mill. The NiAl obtained in both mill types was partially disordered with long-range order parameter not inferior to 0.66. Quantitative phase analysis using the Rietveld method was performed in as-milled samples, and this method was also employed to estimate changes in crystallite size and lattice strain of the NiAl produced during mechanical alloying. (C) 2011 The Society of Powder Technology Japan. Published by Elsevier B.V. and The Society of Powder Technology Japan. All rights reserved.

Mean square displacements of hydrogen interstitial and its neighbours in the intermetallic compound Fe0.5Ti0.5

A Green's function technique is used in the scattering matrix formalism to compute the mean square displacement of hydrogen and deuterium interstitials in the intermetallic compound Fe0.5Ti0.5 for low hydrogen/deuterium concentration. The mean square amplitudes of the metal atoms surrounding the interstitial are found to be smaller than those for the host crystal. This anomalous effect is due to the stiffening of the lattice by the dissolved hydrogen or deuterium at low concentration. This type of effect is experimentally observed in the case of NbHx at low hydrogen concentration.

Effect of Constant and Cyclic Current Stressing on the Evolution of Intermetallic Compound Layers

In this paper the effects of constant and cyclic power loads on the evolution of interfacial reaction layers in lead-free solder interconnections are presented. Firstly, the differences in the growth behavior of intermetallic compound (IMC) layers at the cathode and anode sides of the interconnections are rationalized. This is done by considering the changes in the intrinsic fluxes of elements owing to electromigration as well as taking into account the fact that the growth of Cu3Sn and Cu6Sn5 are coupled via interfacial reactions. In this way, better understanding of the effect of electron flux on the growth of each individual layer in the Cu-Sn system can be achieved. Secondly, it is shown that there is a distinct difference between steady-state current stressing (constant current, constant temperature) and power cycling with alternating on- and off-cycle periods (accompanied by a change of temperature). The reasons behind the observed differences are subsequently discussed. Finally, special care is taken to ensure that the current densities are chosen in such a way that there is no risk for even partial melting of the solder interconnections.

Microstructure evolution and metastable phase formation in laser-ablation-deposited films of Ti5Si3 intermetallic compound

Thin films of Ti62.5Si37.5 composition were deposited by the pulsed-laser ablation technique on single-crystal Nad substrates at room temperature and on ′single-crystal′ superalloy substrates at elevated temperatures. Both vapour and liquid droplets generated by pulsed-laser ablation of the target become quenched on the substrate. Amorphization had taken place in the process of quenching of vapour-plasma as well as small liquid droplets on NaCl substrates at room temperature. In addition to the formation of Ti5Si3, a metastable fcc phase (a 0 = 0.433 nm) also forms in micron-sized large droplets as well as in the medium-sized submicron droplets. The same metastable fcc phase nucleates during deposition from the vapour state at 500°C and at 600°C on a superalloy substrate as well as during crystallization of the amorphous phase. The evolution of the metastable fcc phase in the Ti-Si system during non-equilibrium processing is reported for the first time.

Laser synthesizing NiAl intermetallic and TiC reinforced NiAl intermetallic matrix composite

The NiAl intermetallic layers and NiAl matrix composite layers with TiC particulate reinforcement were successfully synthesized by laser cladding with coaxial powder feeding of Ni/Al clad powder and Ni/Al + TiC powder mixture, respectively. With optimized processing parameters and powder mixture compositions, the synthesized layers were free of cracks and metallurgical bond with the substrate. The microstructure of the laser-synthesized layers was composed of 6-NiAl phase and a few gamma phases for NiAl intermetallic; unmelted TiC, dispersive fine precipitated TiC particles and refined beta-NiAl phase matrix for TiC reinforced NiAl intermetallic composite. The average microhardness was 355 HV0.1 and 538 HV0.1, respectively. Laser synthesizing and direct metal depositing offer promising approaches for producing NiAl intermetallic and TiC-reinforced NiAl metal matrix composite coatings and for fabricating NiAl intermetallic bulk structure. (C) 2004 Laser Institute of America.

Microstructural evolution and formation of nanocrystalline intermetallic compound during surface mechanical attrition treatment of cobalt

Nanocrystalline intermetallic Co3Fe7 was produced on the surface of cobalt via surface mechanical attrition (SMA). Deformationinduced diffusion entailed the formation of a series of solid solutions. Phase transitions occurred depending on the atomic fraction of Fe in the surface solid solutions: from hexagonal close-packed (<4% Fe) to face-centered cubic (fcc) (4-11% Fe), and from fcc to body-centered cubic (>11% Fe). Nanoscale compositional probing suggested significantly higher Fe contents at grain boundaries and triple junctions than grain interiors. Short-circuit diffusion along grain boundaries and triple junctions dominate in the nanocrystalline intermetallic compound. Stacking faults contribute significantly to diffusion. Diffusion enhancement due to high-rate deformation in SMA was analyzed by regarding dislocations as solute-pumping channels, and the creation of excess vacancies. Non-equilibrium, atomic level alloying can then be ascribed to deformation-induced intermixing of constituent species. The formation mechanism of nanocrystalline intermetallic grains on the SMA surface can be thought of as a consequence of numerous nucleation events and limited growth. (C) 2007 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer During Surface Mechanical Attrition Treatment of Zirconium

The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC) layer on the surface of metallic materials for upgrading their overall properties and performance. In this paper, by means of SMAT to a pure zirconium plate at the room temperature, repetitive multidirectional peening of steel shots (composition (wt%): 1C, 1.5Cr, base Fe) severely deformed the surface layer. A NC surface layer consisting of the intermetallic compound FeCr was fabricated on the surface of the zirconium. The microstructure characterization of the surface layer was performed by using X-ray diffraction analysis, optical microscopy, scanning and transmission electron microscopy observations. The NC surface layer was about 25 mu m thick and consisted of the intermetallic compound FeCr with an average grain size of 25 +/- 10 nm. The deformation-induced fast diffusion of Fe and Cr from the steel shots into Zr occurred during SMAT, leading to the formation of intermetallic compound. In addition, the NC surface layer exhibited an ultrahigh nanohardness of 10.2 GPa.

Formation and structure of LaNi2 intermetallic compound under high pressure

The Cubic LaNi2 Laves phase has been synthesized under high pressure. The effects of temperature and pressure on the stability of the Laves phase have been studied. High pressure also induces the phase transitions from intermetallic compounds La2Ni3 and LaNi2.286 to the Laves phase.

ELECTROCHEMICAL FORMATION OF NI-Y INTERMETALLIC COMPOUND LAYER IN MOLTEN CHLORIDE

The reduction of Y(III) ions in molten chloride is known to be a one-step three electron reaction [1, 2, 3], but a voltammogram of YCl3 in molten LiCl-KCl-NaCl at a nickel electrode shows at least two reduction peaks of Y(III) ions, indicating the possibility of formation of Ni-Y intermetallic compounds. Using a galvanostatic electrolysis method, samples were prepared at several current densities at 450, 500, 600 and 700-degrees-C, respectively, and were identified with X-ray diffraction (XRD) and electron probe microanalysis (EPMA) methods. The results show that Ni2Y, Ni2Y3 and NiY can be produced by electrolysis and Ni2Y is found to be the predominant Ni-Y intermetallic compound under the experimental conditions. Nickel appears to diffuse in Ni2Y faster than yttrium, and the diffusion process is the rate determining step during Ni2Y formation.

Microstructure, properties and application of YAl2 intermetallic compound as particle reinforcements

An yttrium aluminum (YAl2) intermetallic compound ingot was prepared in an induction furnace under vacuum. The microstructure of YAl2 ingot was characterized by optical microscopy, scanning electron microscopy, and X-ray diffraction. The load bearing response of YAl2 intermetallic was investigated and compared with SiC ceramic by indentation combined with optical microscopy and scanning electron microscopy. Additionally, the tensile properties of the Mg–Li matrix composites reinforced with ultrafine YAl2 particles fabricated by planet ball milling were tested. The results show that the intermetallic compound ingot in this experiment is composed of a main face-centered-cubic structure YAl2 phase, a small amount of YAl phase, and minor Y and Al-rich phases. YAl2 intermetallic compound has excellent stability and shows better capability in crack resistance than SiC ceramic. The YAl2 intermetallic compound has better deformation compatibility with the Mg–14Li–3Al matrix than SiC reinforcement with the matrix, which leads to the superior resistance to crack for YAl2p/Mg–14Li–3Al composite compared to SiCp/Mg–14Li–3Al composite.

The atomic structure of low-index surfaces of the intermetallic compound InPd

The intermetallic compound InPd (CsCl type of crystal structure with a broad compositional range) is considered as a candidate catalyst for the steam reforming of methanol. Single crystals of this phase have been grown to study the structure of its three low-index surfaces under ultra-high vacuum conditions, using low energy electron diffraction (LEED), X-ray photoemission spectroscopy (XPS), and scanning tunneling microscopy (STM). During surface preparation, preferential sputtering leads to a depletion of In within the top few layers for all three surfaces. The near-surface regions remain slightly Pd-rich until annealing to ∼580 K. A transition occurs between 580 and 660 K where In segregates towards the surface and the near-surface regions become slightly In-rich above ∼660 K. This transition is accompanied by a sharpening of LEED patterns and formation of flat step-terrace morphology, as observed by STM. Several superstructures have been identified for the different surfaces associated with this process. Annealing to higher temperatures (≥750 K) leads to faceting via thermal etching as shown for the (110) surface, with a bulk In composition close to the In-rich limit of the existence domain of the cubic phase. The Pd-rich InPd(111) is found to be consistent with a Pd-terminated bulk truncation model as shown by dynamical LEED analysis while, after annealing at higher temperature, the In-rich InPd(111) is consistent with an In-terminated bulk truncation, in agreement with density functional theory (DFT) calculations of the relative surface energies. More complex surface structures are observed for the (100) surface. Additionally, individual grains of a polycrystalline sample are characterized by micro-spot XPS and LEED as well as low-energy electron microscopy. Results from both individual grains and “global” measurements are interpreted based on comparison to our single crystals findings, DFT calculations and previous literature.

Fabrication of porous TiAl intermetallic compound by self-propagating high temperature synthesis

The present paper describes processing of a lotus-structured porous Ti-Al/Ti composite by SHS with Ti powder and Al rods. Ti-Al intermetallic compound was formed in a range of 200-300μm around the pore by SHS of reaction between Ti and Al, resulting in formation of a lotus-structured porous Ti-Al/Ti composite.

Study of elastic properies of Ti3Al intermetallic compound using the ab initio calculation

The elastic properties of a Ti3Al intermetallic compound were studied using full potential (FP LAPW ) with the APW+lo method. The FP-LAPW is among the most accurate band structure calculations currently available and is based on the density functional theory with general gradient approximation for the exchange and correlation potential. This method provides the structural properties of the ground state as bulk modulus, equilibrium lattice parameter, and equilibrium minimum energy, and the elastic properties as shear modulus, young modulus, Zener coefficient (anisotropy), and Poisson coefficient. The calculated elastic properties are coherent with the elastic properties of the material.