Electrocatalytic oxidation of C-3-aliphatic alcohols on electrodeposited Pd-PEDOT nanodendrites in Alkaline medium

Nanodendritic Pd is electrodeposited on poly(3,4-ethylenedioxythiophene) (PEDOT) coated carbon paper electrode. Electrodeposited Pd is non-dendritic in the absence of PEDOT. The electrooxidation of C-3-aliphatic alcohols, namely, propanol (PA), 1,2- propanediol (1, 2-PD), 1, 3-propanediol (1, 3-PD), and glycerol (GL) is studied in 1.0 M NaOH. The catalytic activity of nanodendritic Pd is greater than that of non-dendritic Pd for oxidation of the four alcohols molecules. Among those molecules the oxidation rate increases as: PA< 1, 2-PD < 1, 3-PD < GL. The cyclic voltammetric oxidation current peak appearing in the reverse direction of the sweep is greatly influenced by the nature of alcohol. The reduction of oxide film on Pd surface is attributed to affect the magnitude of backward peak current density. The amperometry and repeated cyclic voltammetry data suggest a high stability of nanodendritic Pd in alkaline medium. Glycerol is expected to be an appropriate alcohol for application as a fuel in alkaline fuel cells at nanodendritic electrodeposited Pd.

Nitrogen-assisted electroless assembling of 3D nanodendrites consisting of Pd and N-doped carbon nanoparticles as bifunctional catalysts

We report a facile synthesis of three-dimensional (3D) nanodendrites of Pd nanoparticles (NPs) and nitrogen-doped carbon NPs (N-CNPs) by electroless deposition of Pd2+ ions. N-CNPs being an electron-enriched material act as a reducing agent. Moreover, the availability of a variety of nitrogen species in N-CNPs promotes the open arm structure as well as stabilizes the oriented 3D assembly of primary Pd NPs. The dendrites exhibit superior catalytic activity for methanol (0.5 M) oxidation in alkaline media (1 M NaOH) which is ascribed to the large electrochemical active surface area and the enhanced mass activity with repeated use. Further mass activity improvement has been realized after acid-treatment of dendrites which is attributed to the increment in the -OH group. The dendrites show higher mass activity (J(f) similar to 653 A g(-1)) in comparison with a commercial Pt-carbon/Pd-carbon (Pt-C/Pd-C) catalyst (J(f) similar to 46 and 163 A g(-1), respectively), better operational stability, superior CO tolerance with I-f/I-b (similar to 3.7) over a commercial Pt-C/Pd-C catalyst (I-f/I-b similar to 1.6 and 1.75, respectively) and may serve as a promising alternative to commercial Pt-C catalysts for anode application in alkaline fuel cells. To ensure the adaptability of our 3D-nanodendrites for other catalytic activities, we studied 4-nitrophenol reduction at room temperature. The 3D-nanodendrites show excellent catalytic activity toward 4-nitrophenol reduction, as well.

Carboxyl-cored dendrimer and toluene-assisted fabrication of uniform platinum nanodendrites at a water/oil interface and their potential application as a catalyst

Uniform platinum nanodendrites have been prepared at a water/oil interface by a facile catalyst-free method at room temperature. This is carried out by introducing NaBH4 into the platinum precursor solution in the presence of the second generation of carboxyl-cored dendrimer ([G-2]-CO2H dendrimer) and toluene to act as a protective agent and a linker, respectively. The average fractal dimension of 1.61 of the obtained platinum nanodendrites is calculated by analysing the transmission electron micrographs using the programs Fractal Dimension Version 1.1 and Fractal Dimension Calculator. Control experiments show that the fabrication of platinum nanodendrites can be operated with a wide parameter window, which undoubtedly raises the degree of control of the synthesis process. The potential application of such a nanostructure as a catalyst is investigated, and the results reveal that they show highly efficient catalytic properties for the typical redox reaction between hexacyanoferrate (III) and thiosulfate ions at 301 K.

Platinum dendritic nanoparticles with magnetic behavior

Magnetic nanoparticles have attracted increasing attention for biomedical applications in magnetic resonance imaging, high frequency magnetic field hyperthermia therapies, and magnetic-field-gradient-targeted drug delivery. In this study, three-dimensional (3D) platinum nanostructures with large surface area that features magnetic behavior have been demonstrated. The well-developed 3D nanodendrites consist of plentiful interconnected nano-arms ∼4 nm in size. The magnetic behavior of the 3D dendritic Pt nanoparticles is contributed by the localization of surface electrons due to strongly bonded oxygen/Pluronic F127 and the local magnetic moment induced by oxygen vacancies on the neighboring Pt and O atoms. The magnetization of the nanoparticles exhibits a mixed paramagnetic and ferromagnetic state, originating from the core and surface, respectively. The 3D nanodendrite structure is suitable for surface modification and high amounts of drug loading if the transition temperature was enhanced to room temperature properly.

Effect of methanol concentration on oxygen reduction reaction activity of Pt/C catalysts

The oxygen reduction reaction (ORR) activity of Pt/C catalysts was investigated in electrolytes of 0.5 mol/L H2SO4 containing varying concentrations of methanol in a half-cell. It was found that the ORR activity was improved notably in an electrolyte of 0.5 mol/L H2SO4 containing 0.1 mol/L CH3OH as compared with that in 0.5 mol/L H2SO4, 0.5 mol/L H2SO4 containing 0.5 mol/L CH3OH, or 0.5 mol/L H2SO4 containing 1.0 mol/L CH3OH electrolytes. The same tendency for improved ORR activity was also apparent after commercial Nafion (R) NRE-212 membrane was hot-pressed onto the catalyst layers. The linear sweep voltammetry results indicate that the ORR activities of the Pt/C catalyst were almost identical in the 0.5 mol/L H2SO4 + 0.1 mol/L CH3OH solution before and after coated with the Nafion (R) membrane. Electrochemical impedance spectroscopy results demonstrated that the resistance of the Nafion (R) membrane is smaller in the electrolyte of 0.5 mol/L H2SO4 + 0.1 mol/L CH3OH than in other electrolytes with oxygen gas feed. This exceptional property of the Nafion (R) membrane is worth investigating and can be applied in fuel cell stacks to improve the system performance. (c) 2013, Dalian Institute of Chemical Physics, Chinese Academy of Sciences. Published by Elsevier B.V. All rights reserved.