Fe K-edge X-ray absorption spectroscopy study of Pb(Fe2/3W 1/3)O3-PbTiO3 multiferroic ceramics

The present paper is a comprehensive study concerning Fe K-edge X-ray absorption spectroscopy (XAS) measurements, which were performed to characterize the local structure of (1 - x)Pb(Fe2/3W1/3)O 3-xPbTiO3 samples as a function of temperature and PbTiO3 content. Results obtained by the fits of extended X-ray absorption fine structure consist with rhombohedral symmetry for Pb(Fe 2/3W1/3)O3 composition at temperatures lower than room temperature. This result is in apparent disagreement with X-ray and neutron diffraction characterization which have been reported. This apparent disagreement is related to the fact that XAS probes the short-range order, whereas X-ray diffraction provides structural information about the average structure. Moreover, as the PbTiO3 content increases, a disorder has been detected at local structure of the FeO6 octahedron. Analysis of X-ray absorption near edge structure spectra did not show modifications in intensity nor energy of transitions. © 2013 American Institute of Physics.

Relaxor behavior in multiferroic BiMn2O5 ceramics

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Local structure around Fe ions on multiferroic Pb(Fe1/2Nb1/2)O-3 ceramics probed by x-ray absorption spectroscopy

Local structure around Fe ions on Pb(Fe1/2Nb1/2)O-3 ceramics was probed by x-ray absorption spectroscopy in order to settle the controversies about its structure. It is observed that the shell structure around Fe atoms exhibits a monoclinic local symmetry at 130 and 230 K, tetragonal local symmetry at room temperature, and cubic local symmetry at 410 K. Independently of the coordination, temperature, or symmetry, Fe-O mean bond-length does not vary significantly. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4709490]

High-voltage electrophoretic deposition of preferentially oriented films from multiferroic YMn2O5 nanopowders

Processing of the YMn2O5 powder is very challenging, since it decomposes to YMnO3 and Mn3O4 at temperatures close to 1180 °C, while samples consolidation commonly demands high temperatures. The main goal of this work is to investigate a possibility to prepare thick films of YMn2O5, since their deposition generally requires significantly lower temperatures. Multiferroic YMn 2O5 was synthesized by the hydrothermal method from Y(CH3COO)3·xH2O, Mn(CH 3COO)2·4H2O and KMnO4 precursors. XRD, FE-SEM and TEM analysis showed that the obtained powder was monophasic, with orthorhombic crystal structure and columnar particle shape with mean diameter and length of around 20 and 50 nm, respectively. The obtained powder was suspended in isopropyl alcohol with addition of appropriate binder and deflocculant. This suspension was used for electrophoretic deposition of YMn2O5 thick films under the high-voltage conditions and electric fields ranging from 250 to 2125 V/cm. The films obtained at 1000 V/cm and higher electric fields showed good adhesion, particle packing, homogeneity and very low porosity. It was shown that the deposition in extremely high electric fields (KC=2125 V/cm) can influence the crystal orientation of the films, resulting in formation of preferentially oriented films. © 2012 Elsevier Ltd and Techna Group S.r.l.

Mechanosynthesis of the multiferroic cubic spinel Co2MnO4: Influence of the calcination temperature

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Investigation of the dielectric relaxation processes in PbZr0.65Ti0.35O3-BaFe12O19 multiferroic ceramic composites

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Coupling of magnetic, strain and electric polarization fields in the structure of multiferroic material

The comprehensive study on the coupling of magnetism, electrical polarization and the crystalline lattice with the off-stoichiometric effects in self-doped multiferroic hexagonal h-LuMnxO3±δ (0.92≤x≤1.12) ceramic oxides was carried out for the PhD work. There is a complex coupling of the three ferroic degrees. The cancelation of the magnetic moments of ions in the antiferromagnetic order, electric polarization with specific vortex/antivortex topology and lattice properties have pushed researchers to find out ways to disclose the underlying physics and chemistry of magneto-electric and magneto-elastic couplings of h-RMnO3 multiferroic materials. In this research work, self-doping of Lu-sites or Mn-sites of h-LuMnxO3±δ ceramics prepared via solid state route was done to pave a way for deeper understanding of the antiferromagnetic transition, the weak ferromagnetism often reported in the same crystalline lattices and the ferroelectric properties coupled to the imposed lattice changes. Accordingly to the aim of the PhD thesis, the objectives set for the sintering study in the first chapter on experimental results were two. First, study of sintering off-stoichiometric samples within conditions reported in the bibliography and also extracted from the phase diagrams of the LuMnxO3±δ, with a multiple firings ending with a last high temperature step at 1300ºC for 24 hours. Second, explore longer annealing times of up to 240 hours at the fixed temperature of 1300 ºC in a search for improving the properties of the solid solution under study. All series of LuMnxO3±δ ceramics for each annealing time were characterized to tentatively build a framework enabling comparison of measured properties with results of others available in literature. XRD and Rietveld refinement of data give the evolution the lattice parameters as a function to x. Shrinkage of the lattice parameters with increasing x values was observed, the stability limit of the solid solution being determined by analysis of lattice parameters. The evolution of grain size and presence of secondary phases have been investigated by means of TEM, SEM, EDS and EBSD techniques. The dependencies of grain growth and regression of secondary phases on composition x and time were further characterized. Magnetic susceptibility of samples and magnetic irreversibility were extensively examined in the present work. The dependency of magnetic susceptibility, Neel ordering transition and important magnetic parameters are determined and compared to observation in other multiferroics in the following chapter of the thesis. As a tool of high sensitivity to detect minor traces of the secondary phase hausmannite, magnetic measurements are suggested for cross-checking of phase diagrams. Difficulty of previous studies on interpreting the magnetic anomaly below 43 K in h-RMnO3 oxides was discussed and assigned to the Mn3O4 phase, with supported of the electron microscopy. Magneto-electric coupling where AFM ordering is coupled to dielectric polarization is investigated as a function of x and of sintering condition via frequency and temperature dependent complex dielectric constant measurements in the final chapter of the thesis. Within the limits of solid solubility, the crystalline lattice of off-stoichiometric ceramics was shown to preserve the magneto-electric coupling at TN. It represents the first research work on magneto-electric coupling modified by vacancy doping to author’s knowledge. Studied lattices would reveal distortions at the atomic scale imposed by local changes of x dependent on sintering conditions which were widely inspected by using TEM/STEM methods, complemented with EDS and EELS spectroscopy all together to provide comprehensive information on cross coupling of distortions, inhomogeneity and electronic structure assembled and discussed in a specific chapter. Internal interfaces inside crystalline grains were examined. Qualitative explanations of the measured magnetic and ferroelectric properties were established in relation to observed nanoscale features of h-LuMnxO3±δ ceramics. Ferroelectric domains and topological defects are displayed both in TEM and AFM/PFM images, the later technique being used to look at size, distribution and switching of ferroelectric domains influenced by vacancy doping at the micron scale bridging to complementary TEM studies on the atomic structure of ferroelectric domains. In support to experimental study, DFT simulations using Wien2K code have been carried out in order to interpret the results of EELS spectra of O K-edge and to obtain information on the cation hybridization to oxygen ions. The L3,2 edges of Mn is used to access the oxidation state of the Mn ions inside crystalline grains. In addition, rehybridization driven ferroelectricity is also evaluated by comparing the partial density of states of the orbitals of all ions of the samples, also the polarization was calculated and correlated to the off-stoichiometric effect.

Mechanical properties and porosity of dental glass-ceramics hot-pressed at different temperatures

The objective of this work was to evaluate biaxial-flexural-strength (σf), Vickers hardness (HV), fracture toughness (K Ic), Young's modulus (E), Poisson's ratio (ν) and porosity (P) of two commercial glass-ceramics, Empress (E1) and Empress 2 (E2), as a function of the hot-pressing temperature. Ten disks were hot-pressed at 1065, 1070, 1075 and 1080 °C for E1; and at 910, 915, 920 and 925 °C for E2. The porosity was measured by an image analyzer software and s f was determined using the piston-on-three-balls method. K Ic and HV were determined by an indentation method. Elastic constants were determined by the pulse-echo method. For E1 samples treated at different temperatures, there were no statistical differences among the values of all evaluated properties. For E2 samples treated at different temperatures, there were no statistical differences among the values of σf, E, and ν, however HV and K Ic were significantly higher for 910 and 915 °C, respectively. Regarding P, the mean value obtained for E2 for 925 °C was significantly higher compared to other temperatures.

Cation size effects-modified phase and PTCR development in Er3+ and Ca2+ co-doped BaTiO3 ceramics during sintering

Development of the positive temperature coefficient of resistivity (PTCR) in Er3+ and Ca2+ co-doped ferroelectric BaTiO3 was studied in this work, with Er3+ being used to act as a donor doping. Irrespective of all the materials showing high densities after sintering at 1200 to 1300 ºC, these revealed insulator at the lowest sintering temperature, changing to semiconducting and PTCR-type materials only when the sintering temperature was further increased. Observations from X-ray diffraction help correlating this effect with phase development in this formulated (Ba,Ca,Er)TiO3 system, considering the formation of initially two separated major (Ba,Ca)TiO3- and minor (Ca,Er)TiO3-based compounds, as a consequence of cation size-induced stress energy effects. Thus, appearance and enhancement here of the semiconducting and PTCR responses towards higher sintering temperatures particularly involve the incorporation of Er3+ into the major phase, rendering finally possible the generation and "percolative-like" migration of electrons throughout the whole material.

Spontaneous long and short-range ferroelectric ordering in Pb(0.55)La(0.30)TiO(3) ceramics

In this work, we investigated the temperature dependence of short and long-range ferroelectric ordering in Pb(0.55)La(0.30)TiO(3) relaxor composition. High-resolution x-ray powder diffraction measurements revealed a clear spontaneous macroscopic cubic-to-tetragonal phase transition in the PLT relaxor sample at similar to 60 K below the maximum of the dielectric constant peak (T(m)). Indeed, the x-ray diffraction (XRD) data showed that at 300 K (above T(m) but below the Burns temperature, T(B)) the long-range order structure corresponds to a macroscopic cubic symmetry, space group number 221 (Pm-3m), whereas the data collected at 20 K revealed a macroscopic tetragonal symmetry, space group number 99 (P4mm) with c/a=1.0078, that is comparable to that of a normal ferroelectric. These results show that for samples with tetragonal composition, the long-range ferroelectric order may be recovered spontaneously at cryogenics temperatures, in contrast to ferroelectric samples with rhombohedral symmetry. On the other hand, x-ray absorption spectroscopy investigations intriguingly revealed the existence of local tetragonal disorder around Ti atoms for temperatures far below T(m) and above T(B), for which the sample presents macroscopic tetragonal and cubic symmetries, respectively. (C) 2010 American Institute of Physics. [doi: 10.1063/1.3431024]

Microstructuration induced differences in the thermo-optical and luminescence properties of Nd:YAG fine grain ceramics and crystals

The temperature and compositional dependences of thermo- optical properties of neodymium doped yttrium aluminum garnet (YAG) crystals and fine grain ceramics have been systematically investigated by means of time- resolved thermal lens spectrometry. We have found that Nd:YAG ceramics show a reduced thermal diffusivity compared to Nd:YAG single crystals in the complete temperature range investigated (80-300 K). The analysis of the time- resolved luminescent properties of Nd(3+) has revealed that the reduction in the phonon mean free path taking place in Nd:YAG ceramics cannot be associated with an increment in the density of lattice defects, indicating that phonon scattering at grain boundaries is the origin of the observed reduction in the thermal diffusivity of Nd: YAG ceramics. Finally, our results showed the ability of the time- resolved thermal lens to determine and optimize the thermo- optical properties of Nd: YAG ceramic based lasers. (C) 2008 American Institute of Physics. [DOI: 10.1063/1.2975335]

Mechanical properties of Y-TPZ ceramics obtained by liquid phase sintering using bioglass as additive

Yttria stabilized tetragonal zirconia (Y-TZP) ceramics were sintered by liquid phase sintering at low temperatures using bioglass as sintering additive. ZrO2-bioglass ceramics were prepared by mixing a ZrO2 stabilized with 3 Mol%Y2O3 and different amounts of bioglass based on 3CaO center dot P2O5-MgO-SiO2 system. Mixtures were compacted by uniaxial cold pressing and sintered in air, at 1200 and 1300 degrees C for 120 min. The influence of the bioglass content on the densification, tetragonal phase stability, bending strength, hardness and fracture toughness was investigated. The ceramics sintered at 1300 degrees C and prepared by addition of 3% of bioglass, exhibited the highest strength of 435 MPa, hardness of 1170 HV and fracture toughness of 6.3 MPa m(1/2). These results are related to the low monoclinic phase content, high relative density and the presence of the thermal residual stress generated between the ZrO2-matrix and bioglass grain boundary, contributing to the activation of the toughening mechanisms. (c) 2007 Elsevier B.V. All rights reserved.

Spontaneous infiltrations of compound systems of Y(2)O(3), Sm(2)O(3), RE(2)O(3), Al(2)O(3) and AIN in SiC ceramics

Silicon carbide ceramics (SiC) are used in different applications in the engineering area due to the excellent properties, mainly in high temperatures. They are usually obtained by liquid-phase sintering enabling to form volatile products and, consequently, defects. The present work aims at studying the obtention of SiC ceramics by spontaneous infiltration using a eutectic composition of the Al(2)O(3)/Y(2)O(3), AIN/Y(2)O(3), Al(2)O(3)/Sm(2)O(3), AlN/Sm(2)O(3), Al(2)O(3)/RE(2)O(3) and AlN/RE(2)O(3) Systems. RE(2)O(3) is the concentrate of the rare-earth oxide obtained from Xenotime ore. Infiltration tests were carried out in argon atmosphere, graphite crucibles, in several temperatures near the melting point of each system, varying from 2.5 to 60 min. It was observed that Al(2)O(3)/Y(2)O(3), Al(2)O(3)/SM(2)O(3), AlN/SM(2)O(3) and Al(2)O(3)/RE(2)O(3) systems do not infiltrate appropriately and the AlN/Y(2)O(3) and AlN/RE(2)O(3) systems infiltrated spontaneously more than 20 mm; however, the first one presented a higher degree of infiltration, approximately 97%. (C) 2009 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Crystallographic characterization of silicon nitride ceramics sintered with Y(2)O(3)-Al(2)O(3) or E(2)O(3)-Al(2)O(3) additions

Silicon nitride ceramics were sintered using Y(2)O(3)-Al(2)O(3) or E(2)O(3)-Al(2)O(3) (E(2)O(3) denotes a mixed oxide Of Y(2)O(3) and rare-earth oxides) as sintering additives. The intergranular phases formed after sintering was investigated using high-resolution X-ray diffraction (HRXRD). The use of synchrotron radiation enabled high angular resolution and a high signal to background ratio. Besides the appearance Of beta-Si(3)N(4) phase the intergranular phases Y(3)Al(5)O(12) (YAG) and Y(2)SiO(5) were identified in both samples. The refinement of the structural parameters by the Rietveld method indicated similar crystalline structure Of beta-Si(3)N(4) for both systems used as sintering additive. On the other hand, the intergranular phases Y(3)Al(5)O(12) and Y(2)SiO(5) shown a decrease of the lattice parameters, when E(2)O(3) was used as additive, indicating the formation of solid solutions of E(3)Al(5)O(12) and E(2)SiO(5), respectively. (C) 2007 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Toughened ZrO2 ceramics sintered with a La2O3-rich glass as additive

In this study, the influence of the glass addition and sintering parameters on the densification and mechanical properties of tetragonal zirconia polycrystals (3Y-TZP) ceramics were evaluated. High-purity tetragonal ZrO2 powder and La2O3-rich glass were used as starting powders. Two compositions based on ZrO2 and containing 5wt.% and 10wt.% of La2O3-rich glass were studied in this work. The starting powders were mixed/milled by planetary milling, dried at 90 degrees C for 24 h, sieved through a 60 mesh screen and uniaxially cold pressed under 80 MPa. The samples were sintered in air at 1200 degrees C, 1300 degrees C, 1400 degrees C for 60 min and at 1450 degrees C for 120 min, with heating and cooling rates of 10 degrees C/min. Sintered samples were characterized by relative density, X-ray diffraction (XRD) and scanningelectron microscopy (SEM). Hardness and fracture toughness were obtained by Vickers indentation method. Dense sintered samples were obtained for all conditions. Furthermore, only tetragonal-ZrO2 was identified as crystalline phase in sintered samples, independently of the conditions studied. Samples sintered at 1300 degrees C for 60 min presented the optimal mechanical properties with hardness and fracture toughness values near to 12 GPa and 8.5 MPa m(1/2) respectively. (c) 2007 Elsevier B.V, All rights reserved.