Crystal structure of microwave dielectric ceramics Ba[(Mg1-xCdx)(0.33)Nb-0.67]O-3

A series of complex perovskite solid solutions of Ba[(Mg1-xCdx)(0.33)Nb-0.67]O-3 have been synthesized by the columbite method. Detailed Rietveld refinement of their X-ray diffraction data show that Ba[(Mg1-xCdx)0(.33)Nb(0.67)]O-3 has an order trigonal structure. The ordering degree as determined by the B-site occupancies increases with the partial substitution of Cd for Mg.

Microwave Dielectric Properties of RETiTaO6 (RE = La, Ce,Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, Yb, Al, and In) Ceramics

Microwave dielectric ceramics based on RETiTaO6 (RE = La, Cc, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, Yb, Al, and In) were prepared using a conventional solid-state ceramic route. The structure and microstructure of the samples were analyzed using x-ray diffraction and scanning electron microscopy techniques. The sintered samples were characterized in the microwave frequency region. The ceramics based on Ce, Pr, Nd, Sm, Eu, Gd, Tb, and Dy, which crystallize in orthorhombic aeschynite structure, had a relatively high dielectric constant and positive T f while those based on Ho, Er, and Yb, with orthorhombic euxenite structure, had a low dielectric constant and negative Tf. The RETiTaO6 ceramics had a high-quality factor. The dielectric constant and unit cell volume of the ceramics increased with an increase in ionic radius of the rare-earth ions, but density decreased with it. The value of Tf increased with an increase in RE ionic radii, and a change in the sign of Tf occurred when the ionic radius was between 0.90 and 0.92 A. The results indicated that the boundary of the aeschynite to euxenite morphotropic phase change lay between DyTiTaO6 and HoTiTaO6. Low-loss ceramics like ErTiTaO6 (Er = 20.6, Qxf = 85,500), EuTiTaO6 (Er = 41.3, Qxf = 59,500), and YTiTaO6 (Er = 22.1, Q„xf = 51,400) are potential candidates for dielectric resonator applications

Tailoring the Microwave Dielectric Properties of GdTiNb 1 _-xTa,O6 and Sm 1 _X Y,TiTa06 Ceramics

Microwave dielectric ceramics based on GdTiNb,-,.Ta,O6 and Sml _.,Y,TiTa06 have been prepared by conventional solid state method . The GdTiTaO6 and SmTiTaO6 have aeschenite structure with positive rr and GdTiNbO6 and YTiTaO6 have euxenite structure with negative rr. The rr of the ceramics has been tuned by preparing solid solution phases between the aeschynites and euxenites for a possible zero rr material . It is observed that GdTiNbt_YTa.,O6 undergoes a phase transition from aeschynite to euxenite when x=0.75 and in Sml-,YxTiTa06 for x= 0.73. The microwave dielectric properties change abruptly near the transition region . The rr value approaches zero near the phase transition region while the samples have poor sinterability and poor quality factor . The unloaded quality factor, dielectric constant and the sign of rr of the solid solution phases are found to depend on the average ionic radius of the rare earth ion in RE ,-5RE',TiTaO6. The boundary of the euxenite-aeschynite phase transition occurs at an average ( RE) ionic radius of 0.915 A in Sm,_, Y,.TiTaO6 solid solution phases

Improved microwave dielectric properties of (Mg1-(x+y)CaxLay)(Ti1-yAly)O3 ceramics

Phase-singular solids of the composition, (Mg1−(x+y) Cax Lay)(Ti1−yAly)O3 (x = 0 to 0.88; y = 0.05 to 0.35) having the cubic perovskite-type structure were prepared by the substitution of La3+ and Al3+ in equivalent quantities which brought about complete miscibility between MgTiO3 and CaTiO3. These ceramics showed relative permittivities of 16.5 to 50 (at 6 GHz) with increasing Ca content, high Q values of 10 000 to 30 000 and retained near-zero temperature coefficients in permittivity at optimum y values. Their dielectric characteristics are better accountable in terms of the positional disorder rather than the tolerance factor of perovskite structure.

Effect of La3+ on microwave dielectric properties of (Pb0.45Ca0.55) (Fe0.5Nb0.5)O-3 ceramics

In this work, microwave dielectric properties of A-site substitution by La3+ in (Pb0.45Ca0.55) (Fe0.5Nb0.5) 03 system were investigated. Microwave dielectric properties of A-site charge unbalance substitution of [(Pb0.45Ca0.55)(1-x) La-x] (Fe0.5Nb0.5)O-3(+) (P45CLFN) were improved because the solid solution of small amount of surplus La3+ with (Pb, Ca)(2+) could eliminate oxygen vacancies, and the formation of secondary phase (pyrochlore) was also caused by surplus La3+. The decreasing of dielectric constant with the increase of La3+ content is due to the formation of pyrochlore. The grain size is changed slightly and Q(f) values (7000 similar to 7300 GHz) are almost unchanged at x = 0.02 similar to 0.10, but the temperature coefficient of resonant frequency (TCF) are increased and changed from negative to positive. TCF is zero at x 0.075 with Q(f) = 7267 GHz and K = 89. TCF of all specimens are within +/- 5 x 10(-6)degrees C-1.

Tailoring the microwave dielectric properties of BaRE2Ti4O12 and BaRE2Ti5O14 ceramics bycompositional variations

Ceramic dielectric resonators in the BaO-RE2O3-TiO2 (RE=rare earth) system have been prepared by the conventional solid state ceramic route. The dielectric properties have been tailored by substitution of different rare earth oxides and by bismuth oxide addition. The dielectric constants increased with Bi addition whereas the Q decreased. The temperature coeffecient of the resonant frequency improved with bismuth addition.