Grain Refinement at the Nanoscale Via Mechanical Twinning and Dislocation Interaction in a Nickel-Based Alloy

A nanostructured surface layer was formed on an Inconel 600 plate by subjecting it to surface mechanical attrition treatment at room temperature. Transmission electron microscopy and high-resolution transmission electron microscopy of the treated surface layer were carried out to reveal the underlying grain refinement mechanism. Experimental observations showed that the strain-induced nanocrystallization in the current sample occurred via formation of mechanical microtwins and subsequent interaction of the microtwins with dislocations in the surface layer. The development of high-density dislocation arrays inside the twin-matrix lamellae provides precursors for grain boundaries that subdivide the nanometer-thick lamellae into equiaxed, nanometer-sized grains with random orientations.

A rationale for the strong dependence of mechanical twinning on grain size

In metals that yield as a consequence of mechanical twinning, the yield stress is a function of the grain size in much the same way as it is for dislocation glide. However, the sensitivity to grain size is typically greater. The intent of the present communication is to show that this can be understood, at least in part, in terms of a size effect that accompanies twinning. Some confirmatory data from a magnesium alloy are presented.

Temperature and grain orientation dependence of mechanical twinning in a high manganese TWIP steel

 This thesis contains fundamental studies of the deformation mechanisms of the third generation steel at different deformation temperatures. To analyse the microstructure of the steel a unique characterisation technique was implemented for the first time. These analyses provided with vital parameters for modelling the stress-strain behaviour of the steel at different deformation temperatures.

Observation of {1121}twinning in a Mg-based alloy

The magnesium alloy Mg–5%Y–2%Nd–2%RE–0.5Zr, known as WE54, was heat treated to produce different particle dispersions. Specimens were then compressed to a strain of 8%, and this resulted in prolific mechanical twinning.EBSD analysis revealed that {1121} twins were operative in this alloy, a twinning mode not reported before in magnesium alloys. Activation of this twinning mode is ascribed to the presence of alloying elements in solution. Removal of alloying elements from solution by precipitation treatments completely inhibited this twin mode.

Effect of temperature on mechanical behaviour of high manganese TWIP steel

The aim of the present study was to investigate the role of deformation temperature on the active deformation mechanisms in a 0.6C-18Mn-1.5Al (wt%) TWIP steel. The tensile testing was performed at different temperatures, ranging from ambient to 400°C at a constant strain rate of 10-3 S-1. The microstructure characterization was carried out using a scanning electron microscopy. The deformation temperature revealed a significant effect on the active deformation mechanisms (i.e. slip versus twinning), resulting in different microstructure evolution and mechanical properties. At the room temperature, the mechanical twinning was the dominant deformation mechanism, enhancing both the strength and ductility. Dynamic strain aging (DSA) effect was observed at different deformation temperatures, though it was more pronounced at higher temperatures. The volume fraction of deformation twins significantly reduced with an increase in the deformation temperature, deteriorating the mechanical behavior. There was a transition temperature (~300°C), above which the mechanical twinning was hardly observed in the microstructure even at fracture, resulting in low ductility and strength. The current observation can be explained through the change in the stacking fault energy with the deformation temperature. © (2014) Trans Tech Publications, Switzerland.

The correlation between stacking fault energy and the work hardening behaviour of high-mn twinning induced plasticity steel tested at various temperatures

High-Mn Twinning Induced Plasticity (TWIP) steels have superior mechanical properties, which make them promising materials in automotive industry to improve the passenger safety and the fuel consumption. The TWIP steels are characterized by high work hardening rates due to continuous mechanical twin formation during the deformation. Mechanical twinning is a unique deformation mode, which is highly governed by the stacking fault energy (SFE). The composition of steel alloy was Fe-18Mn-0.6C-1Al (wt.%) with SFE of about 25-30 mJ/m2 at room temperature. The SFE ensures the mechanical twinning to be the main deformation mechanism at room temperature. The microstructure, mechanical properties, work hardening behaviour and SFE of the steel was studied at the temperature range of ambient ≤T[°C]≤ 400°C. The mechanical properties were determined using Instron tensile testing machine with 30kN load cell and strain rate of 10-3s-1 and the work hardening behaviour curves were generated using true stress and true strain data. The microstructure after deformation at different temperatures was examined using Zeiss Supra 55VP SEM. It was found that an increase in the deformation temperature raised the SFE resulting in the deterioration of the mechanical twinning that led to decrease not only in the strength but also in the total strain of the steel. A correlation between the temperature, the SFE, the mechanical twinning, the mechanical properties and the work hardening rate was also found. © (2014) Trans Tech Publications, Switzerland.

Processing map for hot working of as cast magnesium

The constitutive flow behaviour in hot working of as cast magnesium has been studied with the help of a processing map developed in the temperature range 300-550°C and strain rate range 0·001-100 s−1. The map, interpreted using the dynamic materials model, revealed that the material undergoes dynamic recrystallisation at 425°C and 0·3 s−1, which are the optimum parameters for hot working. Ai temperatures higher than 450°C and strain rates lower than about 0·1 s−1, wedge cracking occurs in as cast magnesium. The wedge cracking domain has a high efficiency of power dissipation (60%), whereas the dynamic recrystallisation domain has a value of 34%. At temperatures below 450°C and strain rates above 10 s−1, the material exhibits flow instability in the form of mechanical twinning. At higher temperatures and strain rates, instability is manifested by flow localisation.

Processing map for hot working of stainless steel type AISI 316L

Processing and instability maps using a dynamic materials model have been developed for stainless steel type AISI 316L in the temperature range 600-1250-degrees-C and strain rate range 0.001-100 s-1 with a view to optimising its hot workability. Stainless steel type AISI 316L undergoes dynamic recrystallisation, with a peak efficiency of 35% at 1250-degrees-C and 0.05 s-1, which are the optimum parameters for hot working this material. The material undergoes dynamic recovery at 900-degrees-C and 0.001 s-1. The increase in the dynamic recrystallisation and dynamic recovery temperatures in comparison with stainless steel type AISI 304L is attributed to the presence of a backstress caused by the molybdenum additions. These results are in general agreement with those reported elsewhere on stainless steel type 316 deformed in hot extrusion and hot torsion. At temperatures < 850-degrees-C and strain rates > 10 s-1, the material exhibits flow localisation owing to adiabatic shear band formation, whereas at higher temperatures (> 850-degrees-C) and strain rates (> 10 s-1) mechanical twinning and wavy slip bands are observed. (C) 1993 The Institute of Materials.

Atom probe tomography of solute distributions in mg-based alloys

Atom probe tomography (APT) has been carried out on three magnesium-based alloys: M1 (Mg-1 wt pct Mn), AZ31(Mg-3 pct Al-1 pct Zn), and ME10 (Mg-1 pct Mn- 0.4 pct misch metal). The aims of this experiment were to measure the composition of the matrix and to investigate solute clustering in the matrix of the three different alloys. For AZ31, the matrix composition was variable but close to the bulk composition. For ME10 and M1, the matrix was depleted in alloying additions, with the remainder residing in precipitates. Most alloying additions were found to exhibit clustering to some extent, with misch metal having the strongest partitioning behavior to clusters. Solute clusters did not appear to affect mechanical twinning. It has been proposed that the clustering behavior of misch metal contributes to its ability to modify the recrystallization texture.

On the work-hardening behaviour of a high manganese TWIP steel at different deformation temperatures

In the current study, the work-hardening behaviour of a high manganese TWIP steel was investigated at different deformation temperatures. At room temperature, the steel exhibited an excellent combination of mechanical properties due to a unique work-hardening behaviour. There were four distinct stages observed in the work-hardening behaviour as a result of complex dynamic strain induced microstructural reactions consisted of dynamic recovery, dislocation dissociation, stacking fault formation, mechanical twining and dynamic strain aging. An increase in the deformation temperature significantly influenced the microstructure evolution, resulting in a remarkable alteration in the work-hardening behaviour. Consequently, the mechanical properties of the TWIP steel were gradually deteriorated with the deformation temperature. The mechanical twins appeared to have a restricted influence on the work-hardening behaviour of the TWIP steel at room temperature and remarkably diminished with the temperature. The enhanced work-hardening behaviour was mostly attributed to the interaction of glide dislocations with stacking faults.

Gamma -> Epsilon Martensite Transformation and Twinning Deformation in fcc Cobalt During Surface Mechanical Attrition Treatment

The deformation microstructure of face-centered cubic cobalt subjected to surface mechanical attrition treatment was studied as a function of strain levels. Strain-induced gamma --> epsilon transformation and twinning deformation were evidenced by transmission electron microscopy and were found to progress continuously in ultrafine and nanocrystalline grains as the strain increased.

Equal-channel angular pressing and annealing of a twinning-induced plasticity steel : microstructure, texture, and mechanical properties

In this work, a high-manganese Fe-23Mn-1.5Al-0.3C Twinning-Induced Plasticity (TWIP) steel was subjected to plastic shear deformation using Equal-Channel Angular Pressing (ECAP) at 300 °C following route BC and additional annealing. The microstructure evolution during both deformation by ECAP and subsequent annealing was investigated and correlated with the mechanical properties. The successive grain refinement during ECAP was promoted by two parallel mechanisms, namely dislocation driven grain fragmentation and twin fragmentation, and accounted for the ultra-high strength. In addition, due to the relatively low volume fraction of deformation twins after ECAP at 300 °C, further contribution of deformation twinning during room temperature deformation allowed additional work-hardening capacity and elongation. During subsequent recovery annealing the ultra-fine grains and deformation twins were thermally stable, which supported retainment of the high yield strength along with regained uniform elongation. For the first time, the texture evolution during ECAP and during the following heat treatment was analyzed. After 1, 2, and 4 ECAP passes a transition texture with the characteristic texture components of both high- and low-SFE materials developed. During the following heat treatment the texture evolution proceeded similar to that observed in the same material after cold rolling. Retaining of the ECAP texture components due to oriented nucleation at grain boundaries and triple junctions as well as annealing twinning accounted for the formation of a weak, retained ECAP texture after recrystallization.

Asymmetry in structural and thermo-mechanical behavior of intermetallic NiAl nanowire under tensile/compressive loading: A molecular dynamics study

The asymmetric stress strain behavior under tension/compression in an initial < 100 > B-2-NiAl nanowire is investigated considering two different surface configurations i.e., < 100 >/(0 1 0) (0 0 1) and < 100 >/(0 1 1) (0 - 1 1). This behavior is attributed to two different deformation mechanisms namely a slip dominated deformation under compression and a known twinning dominated deformation under tension. It is also shown that B2 -> BCT (body-centered-tetragonal) phase transformation under tensile loading is independent of the surface configurations for an initial < 100 > oriented NiAl nanowire. Under tensile loading, the nanowire undergoes a stress-induced martensiticphase transformation from an initial B2 phase to BCT phase via twinning along {110} plane with failure strain of similar to 0.30. On the other hand, a compressive loading causes failure of these nanowires via brittle fracture after compressive yielding, with a maximum failure strain of similar to-0.12. Such brittle fracture under compressive loading occurs via slip along {110} plane without any phase transformations. Softening/hardening behavior is also reported for the first time in these nanowires under tensile/compressive loadings, which cause asymmetry in their yield strength behavior in the stress strain space. Result shows that a sharp increase in energy with increasing strain under compressive loading causes hardening of the nanowire, and hence, gives improved yield strength as compared to tensile loading. (C) 2010 Elsevier Ltd. All rights reserved.

Deformation-induced grain growth and twinning in nanocrystalline palladium thin films

The microstructure and mechanical properties of nanocrystalline Pd films prepared by magnetron sputtering have been investigated as a function of strain. The films were deposited onto polyimide substrates and tested in tensile mode. In order to follow the deformation processes in the material, several samples were strained to defined straining states, up to a maximum engineering strain of 10%, and prepared for post-mortem analysis. The nanocrystalline structure was investigated by quantitative automated crystal orientation mapping (ACOM) in a transmission electron microscope (TEM), identifying grain growth and twinning/detwinning resulting from dislocation activity as two of the mechanisms contributing to the macroscopic deformation. Depending on the initial twin density, the samples behaved differently. For low initial twin densities, an increasing twin density was found during straining. On the other hand, starting from a higher twin density, the twins were depleted with increasing strain. The findings from ACOM-TEM were confirmed by results from molecular dynamics (MD) simulations and from conventional and in-situ synchrotron X-ray diffraction (CXRD, SXRD) experiments.