A new inexpensive method for the preparation of acicular precursors for magnetic recording media

Magnetic materials meant for audio/video recording applications necessitate that polycrystalline materials be in acicular shape. So preparation of acicular precursors for magnetic storage materials assumes significance. The employment of aqueous solutions do not produce needle shape crystallites. Glycerol is one of the complexing media used for the precipitation of ferrous oxalate dihydrate. An inexpensive method using starch for preparation of acicular particles is described. The influence of an additive namely Gd on acicularity is also investigated

The tribology of laminated magnetic recording heads

This thesis investigates the mechanisms that lead to pole tip recession (PTR) in laminated magnetic recording heads (also known as "sandwich heads"). These heads provide a platform for the utilisation of advanced soft magnetic thin films in practical recording heads suitable for high frequency helical scan tape recording systems. PTR results from a differential wear of the magnetic pole piece from the tape-bearing surface of the head. It results in a spacing loss of the playback or read signal of 54.6dB per recording wavelength separation of the poles from the tape. PTR depends on the material combination used in the head, on the tape type and the climate - temperature and relative humidity (r.h.). Five head materials were studied: two non-magnetic substrate materials- sintered multi granular CaTi03 and composite CaTi03/ZrTi04/Ti02 and three soft magnetic materials- amorphous CoNbZr, and nanocrystalline FeNbSiN and FeTaN. Single material dummy heads were constructed and their wear rates measured when cycling them in a Hi-8 camcorder against commercially available metal particulate (MP) and metal evaporated (ME) tapes in three different climates: 25°C/20%r.h., 25°C/80%r.h. and 40°C/80%r.h. X-ray photoelectron spectroscopy (XPS) was used to examine changes the head surface chemistry. Atomic force microscopy (AFM) was used to examine changes in head and tape surface topography. PTR versus cycling time of laminated heads of CaTi03/ZrTiO4/Ti02 and FeTaN construction was measured using AFM. The principal wear mechanism observed for all head materials was microabrasion caused by the mating body - the tape surface. The variation in wear rate with climate and tape type was due to a variation in severity in this mechanism, except for tape cycling at 40°C in which gross damage was observed to be occurring to the head surface. Two subsidiary wear mechanisms were found: third body scratching (all materials) and grain pullout (both ceramics and FeNbSiN). No chemical wear was observed, though tribochemical reactions were observed on the metal head surfaces. PTR was found to be caused by two mechanisms - the first differential microabrasion of the metal and substrate materials and which was characterised by a low (~10nm) equilibrium value. The second was by deep ploughing by third body debris particles, thought mainly to be grain pullout particles. This level of PTR caused by this mechanism was often more severe, and of a non-equilibrium nature. It was observed more for ME tape, especially at 40°C/80%r.h. and 25°c/20%r.h. Two other phenomena on the laminated head pole piece were observed and commented upon: staining and ripple texturing.

An investigation of thin film magnetic recording media

Mechanical, physical and chemical changes in the surface of commercial thin film metal evaporated magnetic recording media have been correlated to recording error and signal degradation measurements. Modified and adapted commercial Hi-8 video recorders have been used for sample generation whilst analytical techniques such as SXPS,IMS and SEM have been employed in the surface characterisation. The durability of the media was assessed through stop motion (still frame) and cycling tests, where error growth and signal degradation were measured as a function of running time. The tests were performed under ambient (22°C, 40% RH) and high humidity (22°C, 80% RH) conditions. Characterisation of the lubricant layer on each tape was performed through models based on XPS and angle resolved XPS. The lubricant thickness can significantly affect the durability and signal output level of a thin film tape and thus it is important that reliable quantification can be achieved. Various models were considered for determining the lubricant thickness although ultimately, the most suitable technique was deemed to be a model that assumed a uniform layer structure. In addition to thin film metal evaporated media, equivalent durability tests and surface analysis experiments were performed using a commercial metal particle tape in order that comparisons could be made between the two types of recording media. The signal performance of the thin film metal evaporated media was found to be quite different from that for the metal particle tape since dropout errors and signal degradation increased at a much earlier stage. Extensive surface analyses enabled the mechanisms responsible for media failure and error growth to be identified in the ME and MP tapes and these were found to result from cyclic stressing and fatigue on the immediate substrate of the media.

Next generation high density three-dimensional magnetic recording systems

This work is the first work using patterned soft underlayers in multilevel three-dimensional vertical magnetic data storage systems. The motivation stems from an exponentially growing information stockpile, and a corresponding need for more efficient storage devices with higher density. The world information stockpile currently exceeds 150EB (ExaByte=1x1018Bytes); most of which is in analog form. Among the storage technologies (semiconductor, optical and magnetic), magnetic hard disk drives are posed to occupy a big role in personal, network as well as corporate storage. However; this mode suffers from a limit known as the Superparamagnetic limit; which limits achievable areal density due to fundamental quantum mechanical stability requirements. There are many viable techniques considered to defer superparamagnetism into the 100's of Gbit/in2 such as: patterned media, Heat-Assisted Magnetic Recording (HAMR), Self Organized Magnetic Arrays (SOMA), antiferromagnetically coupled structures (AFC), and perpendicular magnetic recording. Nonetheless, these techniques utilize a single magnetic layer; and can thusly be viewed as two-dimensional in nature. In this work a novel three-dimensional vertical magnetic recording approach is proposed. This approach utilizes the entire thickness of a magnetic multilayer structure to store information; with potential areal density well into the Tbit/in2 regime. ^ There are several possible implementations for 3D magnetic recording; each presenting its own set of requirements, merits and challenges. The issues and considerations pertaining to the development of such systems will be examined, and analyzed using empirical and numerical analysis techniques. Two novel key approaches are proposed and developed: (1) Patterned soft underlayer (SUL) which allows for enhanced recording of thicker media, (2) A combinatorial approach for 3D media development that facilitates concurrent investigation of various film parameters on a predefined performance metric. A case study is presented using combinatorial overcoats of Tantalum and Zirconium Oxides for corrosion protection in magnetic media. ^ Feasibility of 3D recording is demonstrated, and an emphasis on 3D media development is emphasized as a key prerequisite. Patterned SUL shows significant enhancement over conventional "un-patterned" SUL, and shows that geometry can be used as a design tool to achieve favorable field distribution where magnetic storage and magnetic phenomena are involved. ^

Stripe domains formation and their affect on three-dimensional and perpendicular magnetic recording

In this study, the formation of stripe domains in permalloy (NisoFe20) thin films was investigated mainly utilizing magnetic force microscopy. Stripe domains are a known phenomenon, which reduces the "softness" of magnetic material and introduces a significant source of noise when used in perpendicular magnetic media. For the particular setup mentioned in this report, a critical thickness for stripe domains initiation depended on the sputtering rate, the substrate temperature, and the film thickness. Beyond the stripe domain formation, an increase in the periodicity of highly ordered stripe domains was evident with increasing film thickness. Above a particular thickness, stripe domains periodicity decreased along with magnetic domain randomization. The results led to the inference that the perpendicular anisotropy responsible for the formation of stripe domains originated mainly from magnetostriction.

Development of pure and doped gamma ferric oxide

Optimum conditions and experimental details for the formation of v-Fe203 from goethite have been worked out. In another method, a cheap complexing medium of starch was employed for precipitating acicular ferrous oxalate, which on decomposition in nitrogen and subsequent oxidation yielded acicular y-Fe203. On the basis of thermal decomposition in dry and moist nitrogen, DTA, XRD, GC and thermodynamic arguments, the mechanism of decomposition was elucidated. New materials obtained by doping ~'-Fe203 with 1-16 atomic percent magnesium, cobalt, nickel and copper, were synthesised and characterized

Magnetic properties of acicular Fe1-xREx (RE = Nd, Sm, Eu, Tb; x=0, 0.05, 0.10) metallic nanoparticles

Acicular monodispersed Fe1-xREx (RE= Nd, Sm,Eu,Tb;x=0, 0.05, 0.10) metallic nanoparticles (60 +/- 5 nm in length and axial ratio similar to6) obtained by reduction of alumina-coated goethite nanoparticles-containing rare earth (RE) under hydrogen flow are reported. Alumina and maghemite thin layers on particle surface were used to protect the goethite particles against sintering and oxidation, respectively. Al and RE additions were obtained by successive heterocoagulation reactions. Aluminum sulfate (10 at.% based on Fe) was dissolved in water and the pH adjusted to 12.5 with NaOH solution. Goethite particles were suspended in this solution and CO2 gas was blown into the slurry to neutralize it to a pH 8.5 or less. Particles were purified and dehydrated to effect transformation to alumina-coated hematite nanoparticles, which were re-suspended in aqueous solution in which RE sulfate (0-0.15 at.% based on Fe) has been dissolved, and the pH increased by ammonia aqueous solution addition. Resulted alumina-coated RE-doped hematite nanoparticles were reduced to metal at 450 degreesC/12 h under hydrogen flow and passivated with nitrogen-containing ethanol vapor at room temperature. Acicular monodispersed metallic nanoparticle systems were obtained and the presence of Al and RE were confirmed by induced-coupled plasma spectrometry analysis. X-ray diffraction, Mossbauer spectroscopy, and magnetization data are in agreement with the nanosized alpha-Fe core in a bcc structure, having a spinel structure, gammaFe(2)O(3), with thickness similar to1.5 run on particle surface. Main magnetic parameters showed saturation magnetization decreases and significant increasing in the coercive field with the RE composition increases. Magnetic properties of these particles, similar to40% smaller than those commercially available, suggest a decrease in the bit-size for high-density magnetic or magneto-optics recording media application. (C) 2004 Published by Elsevier B.V.

Magnetic properties of spindle-type iron fine particles obtained from hematite

Spindle-type iron fine particles have been prepared by reduction of silica-coated-hematite particles. Hydrogen reduction of the coated-hematite cores yielded uniform spindle-type iron particles, which were stabilized by surface oxidation. Narrow particle distributions are observed from TEM measurements. X-ray, Mössbauer and magnetization data are in agreement with the presence of nanosized α-Fe particles, having surface layer of spinel structure oxide. Mössbauer spectra show that the oxide surface is superparamagnetic at room temperature. © 2001 Elsevier Science B.V. All rights reserved.

Design studies of the magnetic properties of structural materials affecting the magnetic field of high-homogeneity superconducting magnets

Austenitic stainless steel presents phase changes caused by heat treatment and welding processes. Because it represents a problem in the design of high-homogeneity magnets, we have been studying the magnetic properties of Ti alloys for their use instead of stainless steel as structural material for superconducting magnet construction. In this work, we present the comparative study of the influence of magnetic properties of steel and Ti alloys on the magnetic-field homogeneity of a superconducting coil through numerical calculation using the measured magnetic properties. © 2001 Elsevier Science B.V. All rights reserved.

Continuous/Cluster-Pinned Recording Media

We propose and theoretically investigate a new class of nanostructured magnetic recording films, cluster-pinned recording media. The films consist of magnetic clusters exchange coupled to a continuous hard layer with perpendicular anisotropy and low coercivity. Our calculations yield the coercivity and the cross-track correlation length as a function of film thickness and pinning density and strength. The mechanism is very similar to the Gaunt–Friedel pinning in bulk magnets, which differs from ordinary strong pinning by the selfconsistent dependence of wall curvature and coercivity on defect concentration. The main difference is the exponent for the coercivity as a function of the pinning strength, which is equal to 2 in the bulk but equal to 3/2 in thin films. The pinning strength is estimated for various regimes, and it is shown that the diminished domain-wall curvature reduces jitter.

Focused ion beam manufacturing of magnetic nanostructures

A number of patterning methods including conventional photo-lithography and E-beam lithography have been employed to pattern devices with critical dimensions of submicrometer levels. The methods of device fabrication by lithography and multilevel processing are usually specific to the chemical and physical properties of the etchants and materials used, and require a number of processing steps. As an alternative, focused ion beam (FIB) lithography is a unique and straightforward tool to rapidly develop nanomagnetic prototyping devices. This feature of FIB is critical to conduct the basic study necessary to advance the state-of-the-art in magnetic recording. ^ The dissertation develops a specific design of nanodevices and demonstrates FIB-fabricated stable and reproducible magnetic nanostructures with a critical dimension of about 10 nm. The project included the fabrication of a patterned single and multilayer magnetic media with areal densities beyond 10 Terabit/in 2. Each block had perpendicular or longitudinal magnetic anisotropy and a single domain structure. The purpose was to demonstrate how the ability of FIB to directly etch nanoscale patterns allowed exploring (even in the academic environment) the true physics of various types of nanostructures. ^ Another goal of this study was the investigation of FIB patterned magnetic media with a set of characterization tools: e.g. Spinstand Guzik V2002, magnetic force microscopy, scanning electron microscopy with energy dispersive system and wavelength dispersive system. ^ In the course of this work, a unique prototype of a record high density patterned magnetic media device capable of 10 terabit/in 2 was built. The read/write testing was performed by a Guzik spinstand. The readback signals were recorded and analyzed by a digital oscilloscope. A number of different configurations for writing and reading information from a magnetic medium were explored. The prototype transducers for this work were fabricated via FIB trimming of different magnetic recording heads. ^

Magnetization reversal and magnetic anisotropies in epitaxial Fe/MgO and Fe/MgO/Fe heterostructures grown on Si(001)

Epitaxial Fe/MgO heterostructures have been grown on Si(001) by a combination of sputtering and laser ablation deposition techniques. The growth of MgO on Si(001) is mainly determined by the nature of the interface, with large lattice mismatch and the presence of an amorphous layer of unclear origin. Reflection high energy electron diffraction patterns of this MgO buffer layer are characteristic of an epitaxial, but disordered, structure. The structural quality of subsequent Fe and MgO layers continuously improves due to the better lattice match and the burial of defects. A weak uniaxial in-plane magnetic anisotropy is found superimposed on the expected cubic biaxial anisotropy. This additional anisotropy, of interfacial nature and often found in Fe/MgO and Fe/MgO/GaAs(001) systems, is less intense here due to the poorer MgO/Si interface quality compared with that of other systems. From the evolution of the anisotropy field with film thickness, magnetic anisotropy is also found to depend on the crystal quality. Kerr measurements of a Fe/MgO multilayered structure grown on Si show two different switching fields, suggesting magnetic coupling of two of the three Fe layers. Nevertheless, due to the little sensitivity to the bottom Fe film, independent switching of the three layers cannot be ruled out.

Magnetic properties and martensitic transition in annealed Ni50Mn30Al20

We have studied the effect of heat treatment on the magnetic properties and on the martensitic transition of the Ni50Mn30Al20 alloy. A mixed L21+B2 state is obtained in the as-prepared sample, while no L21 order is retained in the sample quenched from high temperature. For the two heat treatments, the samples order antiferromagnetically, but there is evidence of coexisting ferromagnetic interactions. A martensitic transition occurs below the magnetic one for quenched samples. However, the martensitic transition is inhibited in the as-prepared sample.

Magnetic hardening mechanisms in Nd-Fe-B nanocrystalline material

Microstructural and magnetic measurements of the evolution by heat treatment of initially amorphous Nd16Fe76B8 alloys prepared by melt spinning are presented. Evidence of magnetic hardening above a threshold temperature induced by magnetic isolation of the Nd2Fe14B grains is provided. A thermodynamic and kinetic explanation of local melting of the intergranular nanostructured Nd¿rich eutectic phase at temperatures below 900 K based on capillary effects is presented. A subsequent Ostwald ripening process moves Nd to wet intimately the hard magnetic grains, becoming, on cooling, a real paramagnetic isolating thin film (~2.5 nm). By using a simple analogy, it is shown that the switching magnetization field in a single¿domain crystal can be drastically affected through the exchange coupling to neighboring grains with different orientation of the easy axis. This effect should be important enough to reinforce the coercive field of polycrystalline hard magnetic materials and explains the observed enhancement from 0.9 to 1.9 T.

Unconventional magnetic behavior of iron-oxide nanoparticles in polymeric matrices

We report the results of magnetization and 57Fe Mössbauer spectroscopy measurements performed in the temperature range 5-300 K on composites containing iron¿oxide nanoparticles encased in polystyrene type resins. After carrying out a suitable field treatment in order to decouple the particles from the matrix, a fraction of the particles freely rotate in response to an applied magnetic field