Fire behaviour of lightweight concrete units based on corn cob aggregate

Recent research works have concluded that corn cob may have interesting material properties, in particular, lightness, and thermal and sound insulation abilities. In this research work, corn cob is proposed as an alternative sustainable aggregate for lightweight concrete masonry unit (CMU) manufacturing. The corn cob requires to be granulated previously in order to obtain adequate particle size grade. Subsequently, the particles are wrapped in a cement paste with the purpose of reducing their water abortion and adherent capacities. CMU are current applied in the building of partition walls. The main goal of this research work consists on studying the fire behaviour of partition walls built with CMU of processed corn cob granulate (CMU-PCC).

Estudo da aderência entre o concreto celular e as barras de aço

Pós-graduação em Engenharia Civil - FEIS

Estimation Of concrete resistance To chloride-ion penetration based On water accessible porosity and unit weight Of concrete

To ensure better concrete quality and long-term durability, there has been an increasing focus in recent years on the development of test methods for quality control of concrete. This paper presents a study to evaluate the effect of water accessible porosity and oven-dry unit weight on the resistance of concrete to chloride-ion penetration. Based on the experimental results and regression analyses, empirical relationships of the charge passed (ASTM C 1202) and chloride migration coefficient (NT Build 492) versus the water accessible porosity and oven dry unit weight of the concrete are established. Using basic physical properties of water accessible porosity and oven dry unit weight which can be easily determined, total charge passed and migration coefficient of the concrete can be estimated for quality control and for estimating durability of concrete.

Simulation of retrofitted unreinforced concrete masonry unit walls under blast loading

This paper describes an investigation into the effectiveness of using spray-on nano-particle reinforced polymer and aluminium foam as new types of retrofit material to prevent the breaching and collapse of unreinforced concrete masonry walls subjected to blast over a whole range of dynamic and impulsive regimes. Material models from the LSDYNA material library were used to model the behaviors of each of the materials and its interface for retrofitted and unretrofitted masonry walls. Available test data were used to validate the numerical models. Using the validated LS-DYNA numerical models, the pressure-impulse diagrams for retrofitted concrete masonry walls were constructed. The efficiency of using these retrofits to strengthen the unreinforced concrete masonry unit (CMU) walls under various pressures and impulses was investigated using pressure-impulse diagrams. Comparisons were made to find the most efficient retrofits for masonry walls against blasts.

Tests of concrete beams reinforced with unit frames.

Thesis (B.S.)--University of Illinois at Urbana-Champaign, 1910.

Unit, direct support and general support maintenance repair parts and special tools list for saw, concrete, self propelled, abrasive disk, model C-3000-30, NSN 3895-01-303-8909.

"October 1991."

Unit, direct support, and general support maintenance repair parts and special tools lists : drier-mixer, bituminous, concrete material, wheel mounted, GED, 2-wheel, pneumatic tires, 3 to 10 tons per hour (NSN 3895-00-832-6230).

"June 1992."

The provision of patient personal hygiene in the intensive care unit : a descriptive exploratory study of bed-bathing practice

Background/objectives The provision of the patient bed-bath is a fundamental nursing care activity yet few quantitative data and no qualitative data are available on registered nurses’ (RNs) clinical practice in this domain in the intensive care unit (ICU). The aim of this study was to describe ICU RNs current practice with respect to the timing, frequency and duration of the patient bed-bath and the cleansing and emollient agents used. Methods The study utilised a two-phase sequential explanatory mixed method design. Phase one used a questionnaire to survey RNs and phase two employed semi-structured focus group (FG) interviews with RNs. Data was collected over 28 days across four Australian metropolitan ICUs. Ethical approval was granted from the relevant hospital and university human research ethics committees. RNs were asked to complete a questionnaire following each episode of care (i.e. bed-bath) and then to attend one of three FG interviews: RNs with less than 2 years ICU experience; RNs with 2–5 years ICU experience; and RNs with greater than 5 years ICU experience. Results During the 28-day study period the four ICUs had 77.25 beds open. In phase one a total of 539 questionnaires were returned, representing 30.5% of episodes of patient bed-baths (based on 1767 bed occupancy and one bed-bath per patient per day). In 349 bed-bath episodes 54.7% patients were mechanically ventilated. The bed-bath was given between 02.00 and 06.00 h in 161 episodes (30%), took 15–30 min to complete (n = 195, 36.2%) and was completed within the last 8 h in 304 episodes (56.8%). Cleansing agents used were predominantly pH balanced soap or liquid soap and water (n = 379, 71%) in comparison to chlorhexidine impregnated sponges/cloths (n = 86, 16.1%) or other agents such as pre-packaged washcloths (n = 65, 12.2%). In 347 episodes (64.4%) emollients were not applied after the bed-bath. In phase two 12 FGs were conducted (three FGs at each ICU) with a total of 42 RN participants. Thematic analysis of FG transcripts across the three levels of RN ICU experience highlighted a transition of patient hygiene practice philosophy from shades of grey – falling in line for inexperienced clinicians to experienced clinicians concrete beliefs about patient bed-bath needs. Conclusions This study identified variation in process and products used in patient hygiene practices in four ICUs. Further study to improve patient outcomes is required to determine the appropriate timing of patient hygiene activities and cleansing agents used to improve skin integrity.

Characterisation of flexural bond strength in thin bed concrete masonry

This paper presents an experimental investigation of the flexural bond strength of thin bed concrete masonry. Flexural bond strength of masonry depends upon the mortar type, the techniques of dispersion of mortar and the surface texture (roughness) of concrete blocks. There exists an abundance of literature on the conventional masonry bond containing 10mm thick mortar; however, the 2mm polymer flue mortar bond is not yet well researched. This paper reports a study on the examination of the effect of mortar compositions, dispersion methods and unit surface textures to the flexural bond strength of thin bed concrete masonry. Three types of polymer modified glue mortars, three surface textures and four techniques of mortar dispersion have been used in preparing 108 four point flexural test specimens. All mortar joints have been carefully prepared to ensure achievement of 2mm layer polymer mortar thickness on average. The results exhibit the flexural bond strength of thin bed concrete masonry much is higher than that of the conventional masonry; moreover the unit surface texture and the mortar dispersion methods are found to have significant influence on the flexural bond strength.

Development of lightweight concrete with high resistance to water and chloride-ion penetration

This paper presents an experimental study to evaluate the influence of coarse lightweight aggregate (LWA), fine LWA and the quality of the paste matrix on water absorption and permeability, and resistance to chloride-ion penetration in concrete. The results indicate that incorporation of pre-soaked coarse LWA in concrete increases water sorptivity and permeability slightly compared to normal weight concrete (NWC) of similar water-to-cementitious materials ratio (w/cm). Furthermore, resistance of the sand lightweight concrete (LWC) to water permeability and chloride-ion penetration decreases with an increase in porosity of the coarse LWA. The use of fine LWA including a crushed fraction <1.18 mm reduced resistance of the all-LWC to water and chloride-ion penetration compared with the sand-LWC which has the same coarse LWA. Overall, the quality of the paste matrix was dominant in controlling the transport properties of the concrete, regardless of porosity of the aggregates used. With low w/cm and silica fume, low unit weight LWC (_1300 kg/m3) was produced with a higher resistance to water and chloride-ion penetration compared with NWC and LWC of higher unit weights.

Permeability of high-performance concrete incorporating presoaked lightweight aggregates for internal curing

This paper presents an experimental study on the effect of presoaked lightweight aggregates (LWAs) for internal curing on water permeability, water absorption and resistance of concrete to chloride-ion penetration in comparison with those of a control concrete and a concrete with shrinkage reducing admixture (SRA) of similar water/cement ratios (w/c). In general, the concretes with LWA particles had initial water absorption, sorptivity and water permeability similar to or lower than those of the control concrete and the concrete with SRA. The charges passed, chloride migration coefficient and chloride diffusion coefficient of such concretes were in the same order as those of the control concrete and the concrete with SRA. However, the incorporation of the LWAs for internal curing reduced unit weight, compressive strength and elastic modulus of the concrete. Comparing the LWAs of different sizes for internal curing, finer particles were more efficient in reducing the shrinkage and generally resulted in less reduction in the unit weight, compressive strength, and elastic modulus. However, the increase in the more porous crushed LW particles in concrete seems to increase the penetration of chloride ions in the concrete. The concrete with SRA had initial water absorption, sorptivity, water permeability and resistance to chloride ion penetration comparable with those of the control concrete. The use of SRA in concrete does not affect the elastic modulus of the concrete, except for a minor influence on the compressive strength of the concrete.

High-strength high-performance lightweight concrete : a review (Invited)

In the last two decades, there are developments that lead to greater understanding on how and why lightweight concretes (LWC) may achieve similar or higher performance than their normal weight counterparts. The present paper reviews some of these aspects beginning with basic properties such as unit weight, compressive strength and specific strength (strength/ unit weight). Stability and workability of LWC is discussed from rheological perspective. The volumetric stability of LWC in terms of shrinkage and creep are presented with some recent published data. Transport properties of the LWC in terms of sorptivity, water permeability and resistance to chloride-ion penetration are reviewed in comparison with normal weight concrete. Fire resistance of LWC and some current measures used to improve the resistance are discussed. With continual research and development, the performance of LWC is being enhanced to provide new opportunities for practical applications.

Development of lightweight aggregate concrete with high resistance to water and chloride-ion penetration

This paper presents an experimental study to evaluate the effect of coarse and fine LWA in concrete on its water absorption and permeability, and resistance to chloride-ion penetration. In additions, LWC with lower unit weight of about 1300 kg/m3 but high resistance to water and chloride-ion penetration was developed and evaluated. The results indicate that the incorporation of coarse LWA in concrete increases water sorptivity and permeability slightly compared to NWC of similar w/c. The resistance of the sand-LWC to chloride-ion penetration depends on porosity of the coarse LWA. Fine LWA has more influence on the transport proper-ties of concrete than coarse LWA. Use of lightweight crushed sand <1.18 mm reduced the resistance of the LWC to water and chloride-ion penetration to some extent. With low w/cm and silica fume, low unit weight LWC (~1300 kg/m3) was produced with higher resistance to water and chloride ion penetration compared with concretes of higher unit weights.

Flexural and shear bond characteristics of thin layer polymer cement mortared concrete masonry

This paper presents an experimental investigation of the flexural and shear bond characteristics of thin layer polymer cement mortared concrete masonry. It is well known that the bond characteristics of masonry depend upon the mortar type, the techniques of dispersion of mortar and the surface texture of concrete blocks; there exists an abundance of literature on the conventional 10 mm thick cement mortared masonry bond; however, 1-4 mm thick polymer cement mortared masonry bond is not yet well researched. This paper reports a study on the examination of the effect of mortar compositions, dispersion methods and unit surface textures to the flexural and shear bond characteristics of thin layer mortared concrete masonry. A non-contact digital image correlation method was adopted for the measurement of strains at the unit-mortar interface in this research. All mortar joints have been carefully prepared to ensure achievement of the desired thin layer mortar thickness on average. The results exhibit that the bond strength of thin mortar layered concrete masonry with polymer cement mortar is higher than that of the conventional masonry; moreover the unit surface texture and the mortar dispersion methods are found to have significant influence on the flexural and shear bond characteristics. From the experimental results, a correlation between the flexural and the shear bond strengths has been determined and is presented in this paper.

A model to estimate the durability performance of both normal and light-weight concrete

There has been an increasing focus on the development of test methods to evaluate the durability performance of concrete. This paper contributes to this focus by presenting a study that evaluates the effect of water accessible porosity and oven-dry unit weight on the resistance of both normal and light-weight concrete to chloride-ion penetration. Based on the experimental results and regression analyses, empirical models are established to correlate the total charge passed and the chloride migration coefficient with the basic properties of concrete such as water accessible porosity, oven dry unit weight, and compressive strength. These equations can be broadly applied to both normal and lightweight aggregate concretes. The model was also validated by an independent set of experimental results from two different concrete mixtures. The model provides a very good estimate on the concrete’s durability performance in respect to the resistance to chloride ion penetration.