Knoop Microhardness and FT-Raman Spectroscopic Evaluation of a Resin-Based Dental Material Light-Cured by an Argon Ion Laser and Halogen Lamp: An in Vitro Study

Objective: The purpose of this study was to evaluate in vitro the Knoop microhardness (Knoop hardness number [KHN]) and the degree of conversion using FT-Raman spectroscopy of a light-cured microhybrid resin composite (Z350-3M-ESPE) Vita shade A3 photopolymerized with a halogen lamp or an argon ion laser. Background Data: Optimal polymerization of resin-based dental materials is important for longevity of restorations in dentistry. Materials and Methods: Thirty specimens were prepared and inserted into a disc-shaped polytetrafluoroethylene mold that was 2.0 mm thick and 3 mm in diameter. The specimens were divided into three groups (n = 10 each). Group 1 (G1) was light-cured for 20 sec with an Optilux 501 halogen light with an intensity of 1000 mW/cm(2). Group 2 (G2) was photopolymerized with an argon laser with a power of 150 mW for 10 sec, and group 3 (G3) was photopolymerized with an argon laser at 200 mW of power for 10 sec. All specimens were stored in distilled water for 24 h at 37 degrees C and kept in lightproof containers. For the KHN test five indentations were made and a depth of 100 mu m was maintained in each specimen. One hundred and fifty readings were obtained using a 25-g load for 45 sec. The degree of conversion values were measured by Raman spectroscopy. KHN and degree of conversion values were obtained on opposite sides of the irradiated surface. KHN and degree of conversion data were analyzed by one-way ANOVA and Tukey tests with statistical significance set at p < 0.05. Results: The results of KHN testing were G1 = 37.428 +/- 4.765; G2 = 23.588 +/- 6.269; and G3 = 21.652 +/- 4.393. The calculated degrees of conversion (DC%) were G1 = 48.57 +/- 2.11; G2 = 43.71 +/- 3.93; and G3 = 44.19 +/- 2.71. Conclusions: Polymerization with the halogen lamp ( G1) attained higher microhardness values than polymerization with the argon laser at power levels of 150 and 200 mW; there was no difference in hardness between the two argon laser groups. The results showed no statistically significant different degrees of conversion for the polymerization of composite samples with the two light sources tested.

Scanning electron microscope analysis of internal adaptation of materials used for pulp protection under composite resin restorations

Purpose: The aim of this study was to evaluate the interfacial microgap with different materials used for pulp protection. The null hypothesis tested was that the combination of calcium hydroxide, resin-modified glass ionomer, and dentin adhesive used as pulp protection in composite restorations would not result in a greater axial gap than that obtained with hybridization only. Materials and Methods: Standardized Class V preparations were performed in buccal and lingual surfaces of 60 caries-free, extracted human third molars. The prepared teeth were randomly assessed in six groups: (1) Single Bond (SB) (3M ESPE, St. Paul, MN, USA); (2) Life (LF) (Kerr Co., Romulus, MI, USA) + SB; (3) LF + Vitrebond (VT) (3M ESPE) + SB; (4) VT + SB; (5) SB + VT; (6) SB + VT + SB. They were restored with microhybrid composite resin Filtek Z250 (3M ESPE), according to the manufacturer's instructions. However, to groups 5 and 6, the dentin bonding adhesive was applied prior to the resin-modified glass ionomer. The specimens were then thermocycled, cross-sectioned through the center of the restoration, fixed, and processed for scanning electron microscopy. The specimens were mounted on stubs and sputter coated. The internal adaptation of the materials to the axial wall was analyzed under SEM with × 1,000 magnification. Results: The data obtained were analyzed with nonparametric tests (Kruskal-Wallis, p ≤ .05). The null hypothesis was rejected. Calcium hydroxide and resin-modified glass ionomer applied alone or in conjunction with each other (p < .001) resulted in statistically wider microgaps than occurred when the dentin was only hybridized prior to the restoration. ©2005 BC Decker Inc.

Dental caries-related quality of life and socioeconomic status of preschool children, Bauru, SP

AIM: To evaluate oral health-related quality of life of preschool children of Bauru, State of São Paulo, Brazil, and associate it with socioeconomic profile of households. METHODS: The sample consisted of 229 preschool children between 3 and 5 years and the dmft (decayed, missing due to caries, filled teeth) index was adopted for assessment children's dental caries in accordance with the standards recommended by the World Health Organization. Questionnaires were used for evaluation oral health-related quality of life (Early Childhood Oral Health Impact Scale) and socioeconomic profile of parents or guardians of the preschool children. Statistical analysis was performed descriptively by relative and absolute frequencies and by Spearman's correlation and Kruskal-Wallis test (p <0.05). RESULTS: A dmft of 1.65 (± 2.87) and a Sic Index 4.88 (± 3.20) were found, indicating the polarization of dental caries in the studied group. It was verified low influence of oral health on quality of life of the children examined. With respect to socioeconomic classification, 66.38% of families were in the lower middle class. Linear and statistically significant correlation was found between dmft and oral health-related quality of life for the overall score and domains of the questionnaire (p<0.001). CONCLUSIONS: It was found low influence of oral health on quality of life of the preschool children and the assessment of socioeconomic conditions of the children's families may guide practices aiming to reducing inequalities in the distribution of dental caries in the population.

INFLUENCE OF ROOF MATERIAL ON THERMAL COMFORT IN BROILER HOUSINGS IN THE STATE OF SAO PAULO

This paper presents a different roof tiles influence study on the thermal comfort for broiler housings. The research was conducted at UNESP`s Experimental Campus at Dracena, state of Sao Paulo, Brazil. Four prototypes in real scale were built, each with an area of 28 m(2). The prototype was covered with roof tiles made of recycled long-life packing material, ceramic tiles, ceramic tiles painted with white coating, and fiber/cement tiles. Temperatures inside the structures were recorded in the winter 2007 over a 90-day period. The results obtained indicated that recycled tile thermal behavior was similar to ceramic tiles. However for the winter period all the prototypes had presented comfort thermal index not in the broilers thermo neutral zone.

"Voyage through death/to life upon these shores": the living dead of the Middle Passage

While historical studies of the Atlantic slave trade have amply demonstrated the magnitude of slave mortality during the Middle Passage, only recently have they started to examine how the captives might have endured and coped with this traumatic experience. Although it constitutes a major topos in African diasporic culture, the Middle Passage has only occasionally been represented directly and in details in novels and in films. This article examines three recent narratives of the Middle Passage, Fred D'Aguiar's novel Feeding the Ghosts (1998), Guy Deslauriers's film Passage du milieu (2000), and Stephanie Smallwood's historical study Saltwater Slavery: A Middle Passage from Africa to American Diaspora (2007). Beyond their individual poetic, aesthetic, and scholarly qualities, what is most striking about these three texts is that they all use the figure of the living dead in order to explore the captives' experience of the transatlantic journey. If the ghastly quality of the living dead powerfully captures the life-threatening material and physical conditions the captives endured on the voyage, its dual, liminal character also allows D'Aguiar, Deslauriers, and Smallwood to represent the metaphysical, psychological, social, and cultural journey they were forced to undertake. Through their use of the trope of the living dead, these three texts show that if death is indeed a central aspect of the experience of the Middle Passage, it impacts the captives in ways that go well beyond the issue of mortality.

Fiber-reinforced composite fixed dental prostheses: Studies of the materials used as pontics

Fiber-reinforced composite fixed dental prostheses – Studies of the materials used as pontics University of Turku, Faculty of Medicine, Institute of Dentistry, Department of Biomaterials Science, Finnish Doctoral Program in Oral Sciences – FINDOS, Annales Universitatis Turkuensis, Turku, Finland 2015 Fiber-reinforced composites (FRC), a non-metallic biomaterial, represent a suitable alternative in prosthetic dentistry when used as a component of fixed dental prostheses (FDPs). Some drawbacks have been identified in the clinical performance of FRC restorations, such as delamination of the veneering material and fracture of the pontic. Therefore, the current series of studies were performed to investigate the possibilities of enhancing the mechanical and physical properties of FRC FDPs by improving the materials used as pontics, to then heighten their longevity. Four experiments showed the importance of the pontic design and surface treatment in the performance of FRC FDPs. In the first, the load-bearing capacities of inlay-retained FRC FDPs with pontics of various materials and thicknesses were evaluated. Three different pontic materials were assessed with different FRC framework vertical positioning. Thicker pontics showed increased load-bearing capacities, especially ceramic pontics. A second study was completed investigating the influence of the chemical conditioning of the ridge-lap surface of acrylic resin denture teeth on their bonding to a composite resin. Increased shear bond strength demonstrated the positive influence of the pretreatment of the acrylic surfaces, indicating dissolution of the denture surfaces, and suggesting potential penetration of the monomer systems into the surface of denture teeth. A third study analyzed the penetration depth of different monomer systems on the acrylic resin denture teeth surfaces. The possibility of establishing a durable bond between acrylic pontics and FRC frameworks was demonstrated by the ability of monomers to penetrate the surface of acrylic resin denture teeth, measured by a confocal scanning type microscope. A fourth study was designed to evaluate the load-bearing capacities of FRC FDPs using the findings of the previous three studies. In this case, the performance of pre-shaped acrylic resin denture teeth used as pontics with different composite resins as filling materials was evaluated. The filling material influenced the load-bearing capacities, providing more durable FRC FDPs. It can be concluded that the mechanical and physical properties of FRC FDPs can be improved as has been shown in the development of this thesis. The improvements reported then might provide long lasting prosthetic solutions of this kind, positioning them as potentially permanent rehabilitation treatments. Key words: fiber-reinforced composite, fixed dental prostheses, inlay-retained bridges, adhesion, acrylic resin denture teeth, dental material.

Projecte per a la realització d'un vídeo pel crèdit 9 del cicle formatiu de grau mitjà : cures auxiliars d'infermeria : l'assistència en la clínica dental. 'Proyecto para la realización de un vídeo para el crédito 9 del ciclo formativo de grado medio : curas auxiliares de enfermería : la asistencia en la clínica dental'.

Este documento no está publicado

Science, (grade 3). Life science.

La ciencia no es solo un conjunto de conocimientos acumulados, sino también una forma activa de aprender sobre el mundo que nos rodea. La forma en que se adquieren los conocimientos sobre la naturaleza del mundo está en el fondo del proceso de investigación, y constituye un modelo de aprendizaje recomendado y respaldado por unas normas nacionales sobre educación de la ciencia. En este texto se puede encontrar la secuencia de experiencias que forman la investigación en ciencias.

Deposition of SiOx Thin Films on Y-TZP by Reactive Magnetron Sputtering: Influence of Plasma Parameters on the Adhesion Properties Between Y-TZP and Resin Cement for Application in Dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Spectroscopic study of ejected dental tissue after Er : YAG laser ablation

By means of IR spectroscopy, we determined the teeth ablation mechanism by an Er:YAG laser oscillating at 2.94 mum. Ejected dental material, ablated by the laser from human teeth, was deposited on an IR window and the absorption spectra were measured in the range 2500-20,000 nm. Sound teeth were used, and the corresponding film spectra were compared to spectra obtained by traditional methods. The films spectra obtained do not differ appreciably from those obtained by the traditional method for sound teeth, indicating that the material ejected by an Er:YAG represents the tooth condition.The obtained results confirm that a spectroscopic analysis of a tooth treated with an Er:YAG laser can be done measuring the absorbance of a film composed of ejected material without the need to slice it. In addition, we could determine that the laser absorption occurs mainly by the interstitial water, and the temperature elevation of the ejected material does not exceed 60degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Response of human dental pulp to dentin adhesive systems

Many in vivo studies have stated that the response of the dentin/pulp complex does not depend on the dental material used as the liner or pulp-capping agent. However, several in vitro studies have reported the metabolic cytotoxic effects of resin components applied to fibroblast and odontoblast cell lines. The aim of this study was to evaluate the human pulp response following direct pulp capping with current bonding agents and calcium hydroxide (CH). Sound premolars scheduled for orthodontic extraction had their pulp tissue mechanically exposed. After hemorrhage control and total acid conditioning, the experimental bonding agents, including All Bond 2, Scotchbond MP-Plus, Clearfil Liner Bond 2, and Prime & Bond 2.1 were applied on the pulp exposure site. CH saline paste was used as the control pulp-capping agent. All cavities were restored with Z-100 resin composite according to the manufacturer's instructions. Following extractions, the teeth were processed for microscopic evaluation. In the short term, the bonding agents elicited a moderate inflammatory pulp response with associated dilated and congested blood vessels adjacent to the pulp exposure site. A mild inflammatory pulp response was observed when Clearfil Liner Bond 2 or CH was applied on the pulp exposures. With time, macrophages and giant cells engulfing globules and components of all experimental bonding agents displaced into the pulp space were seen. This chronic inflammatory response did not allow complete pulp repair, which interfered with the dentin bridge formation. Pulp exposures capped with CH exhibited an initial organization of elongated pulp cells underneath the coagulation necrosis. CH stimulated early pulp repair and dentin bridging that extended into the longest period. The bonding agents evaluated in the present study cannot be recommended for pulp therapy on sound human teeth.

Effect of brushing with conventional versus whitening dentifrices on surface roughness and biofilm formation of dental ceramics

The aim of this study was to evaluate the effect of conventional and whitening dentifrices on the weight loss, surface roughness, and early in situ biofilm formation on the surface of dental ceramics. Standardized feldspar ceramic specimens (Vita VM7 and Vita VM13) were submitted to the following experimental conditions: no brushing; brushing without a dentifrice; brushing with a conventional dentifrice; and brushing with a whitening dentifrice. A brushing machine was used to simulate brushing. The mass and surface roughness of all specimens from the test groups were evaluated prior to and after brushing. Ten participants used an oral device for eight hours to evaluate the biofilm formed in situ on the specimens. Scanning electron microscopy was used for qualitative and quantitative analysis of the biofilm. ANOVA and Tukey tests were used to analyze the results of weight loss, surface roughness, and presence of bacteria. A one-way Kruskal-Wallis test was used for bacterial colonization results. For both ceramics, brushing with a whitening dentifrice resulted in weight loss that was significantly greater when compared to brushing without a dentifrice or with a conventional dentifrice. Increased surface roughness was noticed on VM13 ceramic samples with both dentifrices, whereas only conventional dentifrice had a significant effect on the surface roughness of VM7 samples. For both VM7 and VM13, no difference was found between the experimental conditions with regard to the presence or number of bacteria. Cocci and short rods were the predominant microbial morphotypes. Granular or fibrillar acellular material partially covered the specimens. Brushing with a whitening dentifrice resulted in significant weight loss of ceramic restorations, while brushing with both conventional and whitening dentifrices can roughen ceramic surfaces. The increase in roughness was not clinically significant to contribute to increased biofilm formation.

Dental students' familiarity with the medical management of dental patients at Brazilian dental schools

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Desgaste abrasivo e dureza de seis resinas compostas expostas a diferentes tempos de fotopolimerização com aparelhos de LED e lâmpada incandescente

Pós-graduação em Ciência e Tecnologia de Materiais - FC