通过显微镜聚焦近红外超快强激光作用在垂直于激光束移动的LiF晶体样品上，在LiF晶体中连续地诱导产生色心。以一定的间隔．反复移动该激光束的焦斑可在LiF晶体内空间选择性地诱导产生稳定的色心区。测定了不同条件下形成的色心区的吸收光谱，结果表明用近红外超快强激光可在LiF晶体中诱导产生具有激光效应的色心。

超短脉冲照射下氟化锂的烧蚀机理及其超快动力学研究

研究了超短脉冲激光照射下LiF晶体的破坏机理及其超快动力学过程，利用扫描电镜和原子力显微镜等测试手段，观测了飞秒激光照射下LiF晶体的烧蚀形貌。利用烧蚀面积与激光脉冲能量的对数关系确定了LiF晶体的破坏阈值，并利用非线性玻璃棒展宽脉宽，得到了800nm激光作用下LiF破坏阈值对激光脉宽（50～1000fs）的依赖关系；利用抽运一探针超快探测平台，探测了LiF烧蚀过程中反射率的变化。采用雪崩击穿模型，并根据晶体材料反射率与材料的介电常量的依赖关系，通过数值计算，模拟了材料烧蚀阈值与脉宽的依赖关系及材料激发过

Role of Crystal Field in Mixed Alkali Metal Effect: Electron Paramagnetic Resonance Study of Mixed Alkali Metal Oxyfluoro Vanadate Glasses

The mixed alkali metal effect is a long-standing problem in glasses. Electron paramagnetic resonance (EPR) is used by several researchers to study the mixed alkali metal effect, but a detailed analysis of the nearest neighbor environment of the glass former using spin-Hamiltonian parameters was elusive. In this study we have prepared a series of vanadate glasses having general formula (mol %) 40 V2O5-30BaF(2)-(30 - x)LiF-xRbF with x = 5, 10, 15, 20, 25, and 30. Spin-Hamiltonian parameters of V4+ ions were extracted by simulating and fitting to the experimental spectra using EasySpin. From the analysis of these parameters it is observed that the replacement of lithium ions by rubidium ions follows a ``preferential substitution model''. Using this proposed model, we were able to account for the observed variation in the ratio of the g parameter, which goes through a maximum. This reflects an asymmetric to symmetric changeover of. the alkali metal ion environment around the vanadium site. Further, this model also accounts for the variation in oxidation state of vanadium ion, which was confirmed from the variation in signal intensity of EPR spectra.

Color center conversion by femtosecond pulse laser irradiation in LiF : F-2 crystals

We report the observation of intense spontaneous emission of green light from LiF:F-2:F-3(+) centers in active channel waveguides generated in lithium fluoride crystals by near-infrared femtosecond laser radiation. While irradiating the crystal at room temperature with 405 nm light from a laser diode, yellow and green emission was seen by the naked eye. Stripe waveguides were fabricated by translating the crystal along the irradiated laser pulse, and their guiding properties and fluorescence spectra at 540 nm demonstrated. This single-step process inducing a waveguide structure offers a good prospect for the development of a waveguide laser in bulk LiF crystals.

Thermoluminescence, structural and magnetic properties of a Li(2)O-B(2)O(3)-Al(2)O(3) glass system doped with LiF and TiO(2)

A Li(2)O-B(2)O(3)-Al(2)O(3) glass system, un-doped and doped with LiF, and/or TiO(2) was synthesized by the fusion method and its physical properties were investigated by thermoluminescence (TL), X-ray diffraction (XRD), electron paramagnetic resonance (EPR), atomic force microscopy (AFM) and differential thermal analysis (DTA). The samples were subjected to gamma-rays from a colbalt-60 ((60)Co) source. These techniques provided evidence of LiF and LiF doped with Ti crystal formation in the glass system. A TL glow peak at about 433 K was sensitive to (60)Co gamma-rays and showed good linearity with doses and consequently could be used to quantify radiation doses. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved.

Micropillar compression of LiF [111] single crystals: effect of size, ion irradiation and misorientation

The mechanical response under compression of LiF single crystal micropillars oriented in the [111] direction was studied. Micropillars of different diameter (in the range 1–5 lm) were obtained by etching the matrix in directionally-solidified NaCl–LiF and KCl–LiF eutectic compounds. Selected micropillars were exposed to high-energy Ga+ ions to ascertain the effect of ion irradiation on the mechanical response. Ion irradiation led to an increase of approximately 30% in the yield strength and the maximum compressive strength but no effect of the micropillar diameter on flow stress was found in either the as-grown or the ion irradiated pillars. The dominant deformation micromechanisms were analyzed by means of crystal plasticity finite element simulations of the compression test, which explained the strong effect of micropillar misorientation on the mechanical response. Finally, the lack of size effect on the flow stress was discussed to the light of previous studies in LiF and other materials which show high lattice resistance to dislocation motion.

Effect of misorientation on the compression of highly anisotropic single-crystal micropillars

The effect of crystal misorientation, geometrical tilt, and contact misalignment on the compression of highly anisotropic single crystal micropillars was assessed by means of crystal plasticity finite element simulations. The investigation was focused in single crystals with the NaCl structure, like MgO or LiF, which present a marked plastic anisotropy as a result of the large difference in the critical resolved shear stress between the “soft” {110}〈110〉 and the “hard” {100}〈110〉 active slip systems. It was found that contact misalignment led to a large reduction in the initial stiffness of the micropillar in crystals oriented in the soft and hard direction. The crystallographic tilt did not modify, however, the initial crystal stiffness. From the viewpoint of the plastic response, none of the effects analyzed led to significant differences in the flow stress when the single crystals were oriented along the “soft” [100] direction. Large differences were found, however, if the single crystal was oriented in the “hard” [111] direction as a result of the activation of the soft slip system. Numerical simulations were in very good agreement with experimental literature data.

Towards a single crystal Raman spectrum of kaolinite at 77 K

The Raman spectra at 77 K of the hydroxyl stretching of kaolinite were obtained along the three axes perpendicular to the crystal faces. Raman bands were observed at 3616, 3658 and 3677 cm−1 together with a distinct band observed at 3691 cm−1 and a broad profile between 3695 and 3715 cm−1. The band at 3616 cm−1 is assigned to the inner hydroxyl. The bands at 3658 and 3677 cm−1 are attributed to the out-of-phase vibrations of the inner surface hydroxyls. The Raman spectra of the in-phase vibrations of the inner-surface hydroxyl-stretching region are described in terms of transverse and longitudinal optic splitting. The band at 3691 cm−1 is assigned to the transverse optic and the broad profile to the longitudinal optic mode. This splitting remained even at liquid nitrogen temperature. The transverse optic vibration may be curve resolved into two or three bands, which are attributed to different types of hydroxyl groups in the kaolinite.

Azo-linked corner porphyrin systems: synthesis, crystal structures and spectroscopic investigation

1,2-Bis[10,15-di(3,5-di-tert-butyl)phenylporphyrinatonickel(II)-5-yl]diazene was synthesised via copper catalysed coupling of aminated nickel(II) 5,10-diarylporphyrin (“corner porphyrin”) and its X-ray crystal structure was determined. Two different crystals yielded different structures, one with the free meso positions in a trans-like orientation, and the other with a cis-like disposition. The free meso positions of the obtained dimer have been further functionalised while the synthesis of a zinc analogue has so far been unsuccessful. The X-ray crystal structure of the dinitro derivative of the dinickel(II) azoporphyrin was determined, and the structure showed a cis-like disposition of the nitro groups.