Hydrogen sensing properties of Pt/Lanthanum oxide- molybdenum oxide nanoplatelet/SiC based Schottky diode

An investigation of the electrical and hydrogen sensing properties of a novel Schottky diode based on a nanostructured lanthanum oxide-molybdenum oxide compound is presented herein. Molybdenum oxide (MoO3) nanoplatelets were grown on SiC substrates via thermal evaporation which was then subsequently coated with lanthanum oxide (La2O3) by RF sputtering. The current-voltage characteristics and hydrogen sensing performance (change in barrier height and sensitivity as well as the dynamic response) were examined from 25 to 300°C. At 180°C, a voltage shift of 2.23V was measured from the sensor while exposed to 1% hydrogen gas under a 100 μA constant reverse bias current. The results indicate that the presence of a La2O3 thin layer substantially improves the hydrogen sensitivity of the MoO3 nanoplatelets.

Lanthanum oxide nanostructured films synthesized using hot dense and extremely non-equilibrium plasma for nanoelectronic device applications

Lanthanum oxide (La2O3) nanostructured films are synthesized on a p-type silicon wafer by ablation of La2O3 pellet due to interaction with hot dense argon plasmas in a modified dense plasma focus (DPF) device. The nanostructured films are investigated using scanning electron microscopy (SEM), atomic force microscopy (AFM), and X-ray diffraction (XRD) spectra. SEM study shows the formation of nano-films having nano-size structures with the average nanostructures size ~25, ~53, and ~45 nm for one, two, and three DPF shots, respectively. The nanostructures sizes and morphology of nano-films are consistent between the AFM and SEM analyses. XRD spectra confirms nano-sized La2O3 with an average grain size ~34, ~51, and ~42 nm for one, two, and three DPF shots, respectively. The electrical properties such as current-voltage and capacitance-voltage (C-V) characteristics of the Al-La2O3-Si metal-oxide- semiconductor (MOS) capacitor structure are measured. The current conduction mechanism of the MOS capacitors is also demonstrated. The C-V characteristics are further used to obtain the electrical parameters such as the dielectric constant, oxide thickness, flat-band capacitance, and flat-band voltage of the MOS capacitors. These measurements demonstrate significantly lower leakage currents without any commonly used annealing or doping, thereby revealing a significant improvement of the MOS nanoelectronic device performance due to the incorporation of the DPF-produced La2O3 nano-films.

Investigation of the spectroscopic properties of Yb3+-doped yttrium lanthanum oxide transparent ceramic

Spectroscopic properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic were studied. Two main absorption peaks of the specimen are centered at 940 and 970 nm, which are suitable for InGaAs laser diode pumping. The main emission peaks were located at 1032 and 1075 nm with larger emission cross-section and longer fluorescence lifetime than those of Yb:Y2O3. These properties of (Y0.9-xLa0.1Ybx)(2)O-3 transparent ceramic are favorable to achieve high efficiency and high power laser output. (c) 2007 Elsevier B.V. All rights reserved.

Cooperative up-conversion luminescence of ytterbium doped yttrium lanthanum oxide transparent ceramic

The up-conversion luminescence of Yb3+-doped yttriurn lanthanum oxide transparent ceramic was investigated. It was ascribed to cooperative luminescence originated from the coupled states of the Yb3+ ion pairs. The proper doping of La2O3 can remove the cooperative luminescence of Yb3+ ion. But excessive La2O3 (at least 10 at.%) the cooperative up-conversion of Yb3+:Y2O3 is obtained again, and the intensity of up-conversion luminescence strengthens with the increase of La2O3 content. (c) 2007 Elsevier B.V. All rights reserved.

Fabrication and spectral properties of Nd3+-doped yttrium lanthanum oxide transparent ceramics

Transparent 1 at% Nd3+:Y1.9La0.1O3 ceramics were fabricated with nanopowders prepared by carbonate coprecipitation method. The powder compacts were sintered in H-2 atmosphere at 1550 degrees C for 30 h. The Nd3+:Y1.9La0.1O3 ceramics display uniform grains of about 50 mu m and high transparency. The highest transmittance of the ceramics reaches 67%. The strongest absorption peak is in the wavelength of 820 nm with absorption cross section of 2.48 x 10(-20) cm(2). The absorption is still high at LD wavelength 806 nm with absorption cross section of 1.78 x 10(-20) cm(2) and broad full width at half maximum (FWHM) of about 6.3 nm. The strongest emission peak was centered at 1078 nm with large stimulated emission cross section of 9.63 x 10(-20) cm(2) and broad FWHM of about 7.8 nm. The broad absorption and emission bandwidth of Nd3+:y(1.9)La(0.1)O(3) transparent ceramics are favorable to achieve the miniaturized LD pumping apparatus and ultrashort modelocked pulse laser output, respectively. (c) 2007 Elsevier B.V. All rights reserved.

Luminescence behavior of Yb(3+)heavy-doped yttrium lanthanum oxide transparent ceramics

Yb3+ heavy-doped yttrium lanthanum oxide transparent ceramics were fabricated and their spectroscopic properties were investigated. The absorption bands of (YbxY0.9-xLa0.1)(2)O-3 (x = 0.05-0.15) ceramics are broad at wavelength of 900-1000 nm. The absorption cross-sections centered at 974 nm and the emission cross-sections at 1031 nm of Yb3+ ion are 0.89-1.12 x 10(-20) cm(2) and 1.05 x 10(-20) cm(2) respectively. The up-conversion luminescence intensity of Yb3+-doped yttrium lanthanum oxide ceramics increased firstly, then decreased with the increase of Yb3+ ion content. (C) 2008 Elsevier B.V. All rights reserved.

Remarkable stability of ionic gold supported on sulfated lanthanum oxide

Isolated cationic gold deposited on sulfated lanthanum oxide has been shown to exhibit remarkable stability opening a promising way of stabilising ionic gold for catalytic reactions.

Activation of Alkanes by Gold-Modified Lanthanum Oxide

Functionalization of alkanes is much sought after for the production of fine and bulk chemicals. In particular, the oxidative activation of alkanes and their conversion to ethene and propene has been studied extensively, owing to the use of these alkenes in polymerization reactions. The greater reactivity of the products in comparison with the reactants has proven a major issue in this reaction as this can result in overoxidation, producing CO and CO2 and, therefore, reducing the alkene yield. Herein, the first application of supported gold catalysts for the direct activation of C2+ aliphatic alkanes with oxygen to form alkenes is demonstrated. This catalyst is particularly notable as it is highly active, selective to propene and ethene, and stable on stream over a 48 h period. Maintaining cationic gold is thought to be critical for the stability and this catalyst design provides the possibility of applying gold-based catalysts over a much wider temperature range than has been reported.

Basicity and electron donor properties of lanthanum oxide and its mixed oxides with alumina

The electron donating properties of La2O3 activated at 300, 500 and 800·C and its mixed oxides with alumina are reported from the studies on adsorption of electron acceptors of varying electron affinity on La203. The electron acceptors with their electron affinity values given in parenthesis are: 7,7,8,8-tetracyanoquinodimethane (2.84 eV), 2,3,5,6-tetrachloro-I,4-benzoquinone (2.40 eV) and p-dinitrobenzene(l.77eV). The basicity of the oxide has been determined by titration with n-butylamine and Ho.max values are reported. The limit of electron transfer from the oxide to the electron acceptor is between 2.40 and 1.77 eV. It is observed that La203 promotes the surface electron properties of alumina without changing its limit of electron transfer.

Catalytic activity of lanthanum oxide for the reduction of cyclohexanone

Lanthanum oxide, La2O3 has been found to be an effective catalyst for the liquid phase reduction of cyclohexanone. The catalytic activities of La2O3 activated at 300, 500 and 800·C and its mixed oxides with alumina for the reduction of cyclohexanone with 2-propanol have been determined and the data parallel that of the electron donating properties of the catalysts. The electron donating properties of the catalysts have been determined from the adsorption of electron acceptors of different electron affinities on the surface of these oxides.

CRYSTALLIZATION OF RARE-EARTH OXIDE-FILLED POLYPROPYLENE

A study has been made of the crystallization behavior of polypropylene (PP) filled with rare earth oxides under isothermal conditions. These rare earth oxides include lanthanum oxide (La2O3), yttrium oxide (Y2O3), and a mixture of rare earth oxides containing 70% Y2O3 (Y2O3-0.70). A differential scanning calorimeter was used to monitor the energetics of the crystallization process from the melt. During isothermal crystallization, dependence of the relative degree of crystallinity on time was described by the Avrami equation. It has been shown that the addition of any of the three rare earth oxides causes a considerable increase in the overall crystallization rate of PP but does not influence the mechanism of nucleation and growth of the PP crystals. The analysis of kinetic data according to nucleation theories shows that the increase in crystallization rate of PP in the composites is due to the decrease in surface energy of the extremity surfaces. The relative contents of the beta-form in the composites are somewhat higher than that in the plain PP. However, the contents of the beta-form in the plain PP and the composites are all very low relative to those of the alpha-form and the influence of the formation of the beta-form on the crystallization kinetics can be neglected.

Preparation and structural characterization of rare-earth doped lead lanthanum zirconate titanate ceramics

A new preparation route towards rare-earth (RE) doped polycrystalline lead lanthanum zirconate titanate (PLZT) ceramics (RE = Y(3+), Nd(3+), Yb(3+)), based on the use of doped lanthanum oxide or zirconia, is reported. Structural characterization by X-ray powder diffraction reveals that secondary phase formation can be substantially diminished in comparison to conventional preparation methods. The distribution of the rare-earth dopants was investigated as a function of concentration by static (207)Pb spin echo NMR spectra, using Fourier Transformation of Carr-Purcell-Meiboom-Gill spin echo trains. For the Nd- and Yb-doped materials, the interaction of the (207)Pb nuclei with the unpaired electron spin density results in significant broadening and shifting of the NMR signal, whereas these effects are absent in the diamagnetic Y(3+) doped materials. Based on different concentration dependences of the NMR lineshape parameters, we conclude that the structural role of the Nd(3+) dopants differs significantly from that of Yb(3+). While the Nd(3+) ions appear to be statistically distributed in the PLZT lattice, incorporation of Yb(3+) into PLZT appears to be limited by the appearance of doped cubic zirconia as a secondary phase. (C) 2009 Elsevier Masson SAS. All rights reserved.

Nanosized lead lanthanum titanate (PLT) ceramic powders synthesized by the oxidant peroxo method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of dense lead lanthanum titanate ceramics prepared from powders synthesized by the oxidant peroxo method