Magnetoelectric coefficient in strontium ruthenate buffered lanthanum modified bismuth ferrite thin films grown by chemical method

This paper focuses on the magnetoelectric coupling (ME) at room temperature in lanthanum modified bismuth ferrite thin film (BLFO) deposited on SrRuO 3-buffered Pt/TiO 2/SiO 2/Si(100) substrates by the soft chemical method. BLFO film was coherently grown at a temperature of 500 °C. The magnetoelectric coefficient measurement was performed to evidence magnetoelectric coupling behavior. Room temperature magnetic coercive field indicates that the film is magnetically soft. The maximum magnetoelectric coefficient in the longitudinal direction was close to 12 V/cmOe. Dielectric permittivity and dielectric loss demonstrated only slight dispersion with frequency due the less two-dimensional stress in the plane of the film. Polarization reversal was investigated by applying dc voltage through a conductive tip during the area scanning. We observed that various types of domain behavior such as 71 ° and 180° domain switching, and pinned domain formation occurred. Copyright © 2009 American Scientific Publishers All rights reserved.

Lanthanum cobaltite black pigments with perovskite structure

In this work La1-xCaxCoO3 (x = 0-0.4) pigments were synthesized by the polymeric precursor method with heat treatments at 700, 800 and 900 C for 4 h. The powders were characterized by colorimetry, UV-vis spectroscopy and powder X-ray diffraction (XRD). The X-ray diffraction patterns showed the presence of a single phase perovskite, changing its structure from rhombohedral to cubic, when calcium was added to the lattice. All of the pigments had a black colour with a strong absorption over the whole of the visible spectrum as a consequence of the different oxidation states of cobalt and the high short-range disorder. The substitution of Ca2+ for La3+ did not influence the pigment colour but decreased its final cost. © 2013 Elsevier Ltd. All rights reserved.

Effect of substituting cerium-rich mischmetal with lanthanum on microstructure and mechanical properties of die-cast Mg-Al-RE alloys

Die-cast Mg-4Al-4RE-0.4Mn (RE = Ce-rich mischmetal) and Mg-4Al-4La-0.4Mn magnesium alloys were prepared successfully and their microstructure, tensile and creep properties have been investigated. The results show that two binary Al-RE phases, Al11RE3 and Al2RE, are formed along grain boundaries in Mg-4Al-4RE-0.4Mn alloy, while the phase compositions of Mg-4Al-4La-0.4Mn alloy mainly consist of alpha-Mg phase and Al11La3 phase. And in Mg-4Al-4La-0.4Mn alloy the Al11La3 phase occupies a large grain boundary area and grows with complicated morphologies, which is characterized by scanning electron microscopy in detail. Changing the rare earth content of the alloy from Ce-rich mischmetal to lanthanum gives a further improvement in the tensile and creep properties, and the later could be attributed to the better thermal stability of Al11La3 phase in Mg-4Al-4La-0.4Mn alloy than that of Al11RE3 phase in Mg-4Al-4RE-0.4Mn alloy.

Lanthanum zirconate ceramic toughened by BaTiO3 secondary phase

La2Zr2O7 (LZ) is a promising thermal barrier coating material for the high-temperature applications, which could be significantly toughened by the BaTiO3 piezoelectric phase incorporated into the matrix. The composites of xBaTiO(3)/(l-x)LZ (x=5, 10, 15, 20 vol%, LZ-x-BaTiO3) were densified by means of high-pressure sintering (HPS) under a pressure of 4.5 GPa at 1450 degrees C for 10 min, by which a high relative density above 93% could be obtained.

Effects of Y2O3 addition on the phase evolution and thermophysical properties of lanthanum zirconate

Lanthanum zirconate (La2Zr2O7, LZ) powders with the addition of various Y2O3 contents for potential thermal barrier coatings (TBCs) application were synthesized by solid-state reaction. The structure evolution, sintering-resistance and thermophysical properties of the synthesized powders and sintered ceramics were systematically studied. X-ray diffraction (XRD) results indicate that LZ containing 3-12 wt.% Y2O3 mainly keeps a pyrochlore-type structure, and two new phases of LaYO3 and Y0.18Zr0.82O1.91 are also detected. Raman spectra confirm that the higher the Y2O3 content, the easier is the formation of LaYO3.

Thermal barrier coating of lanthanum-zirconium-cerium composite oxide made by electron beam-physical vapor deposition

Lanthanum-zirconium-cerium composite oxide (La-2(Zr0.7Ce0.3)(2)O-7, LZ7C3) as a candidate material for thermal barrier coatings (TBCs) was prepared by electron beam-physical vapor deposition (EB-PVD). The composition, crystal structure, thermophysical properties, surface and cross-sectional morphologies and cyclic oxidation behavior of the LZ7C3 coating were studied. The results indicated that LZ7C3 has a high phase stability between 298 K and 1573 K, and its linear thermal expansion coefficient (TEC) is similar to that of zirconia containing 8 wt% yttria (8YSZ). The thermal conductivity of LZ7C3 is 0.87 W m(-1) K-1 at 1273 K, which is almost 60% lower than that of 8YSZ. The deviation of coating composition from the ingot can be overcome by the addition of excess CeO2 and ZrO2 during ingot preparation or by adjusting the process parameters.

Solvent extraction of scandium(III), yttrium(III), lanthanum(III) and gadolinium(III) using Cyanex 302 in heptane from hydrochloric acid solutions

The extractions of the selected rare earths (Sc, Y, La and Gd) from hydrochloric acid solutions have been investigated using bis(2,4,4-trimethylpentyl)-mono thiophosphinic acid (Cyanex 302, HL) in heptane as an extractant. The results demonstrate that the extractions of rare earths occur via the following reaction: Sc(OH)(2+) + 2[(HL)(2)]((O)) double left right arrow [Sc(OH)L-2 (.) 2(HL)]((O)) + 2H(+) Y3+ + 3[(HL)(2)]((O)) double left right arrow [Y(HL2)(3)]((O)) + 3H(+) La(OH)(2)(+) + 3[(HL)(2)](O) double left right arrow [La(OH)(2)L (.) 5(HL)]((O)) + H+ Gd(OH)(2+) + 3[(HL)(2)]((O)) double left right arrow [Gd(OH)L-2 (.) 4(HL)]((O)) + 2H(+) The pH(1/2) values and equilibrium constants of the extracted complexes have been deduced by taking into account the aqueous phase complexation of the metal ion with hydroxyl ligands and plausible complexes extracted into the organic phase. According to the pH(1/2) values, it is possible to realize mutual separation among Sc(III), Y(III), La(III) and Gd(III) with Cyanex 302 by controlling aqueous acidity.

MAGNETIC-PROPERTIES OF LANTHANUM MANGANITE AND VALENCE EQUILIBRIA OF MANGANESE

The paramagnetic susceptibility of lanthanum manganite has been measured over a wide temperature range (100-1073 K). On the basis of the thermodynamic equilibria between the various manganese ions with different valence and spin states and the magnetic interactions between the various manganese ions, a semiempirical formula has been proposed to calculate the paramagnetic susceptibilities of lanthanum manganite at different temperatures. The results indicate that most of the discrepancies between the calculated and experimental reciprocal susceptibilities of lanthanum manganite are less than 10% and that the relative contents of the various manganese ions in lanthanum manganite vary with temperature. The relative content of the trivalent manganese ion with a high spin state is dominant over the whole temperature range, while be relative content of the tetravalent manganese ion with a high spin state decreases monotonously with increasing temperature. At 300 K the calculated relative content of the tetravalent manganese ion in lanthanum manganite is about 34%, which is in good agreement with the experimental result (30%). There are some divalent manganese ions present in lanthanum manganite from low temperature to high temperature. The ratio of the relative contents of the tetravalent and divalent manganese ions in the compound varies with temperature. Above 750 K the relative content of the tetravalent manganese ion is less than that of the divalent manganese ion. The variation in the electrical resistivity of lanthanum manganite with temperature has also been interpreted reasonably.

Remarkable stability of ionic gold supported on sulfated lanthanum oxide

Isolated cationic gold deposited on sulfated lanthanum oxide has been shown to exhibit remarkable stability opening a promising way of stabilising ionic gold for catalytic reactions.

Nanosized lead lanthanum titanate (PLT) ceramic powders synthesized by the oxidant peroxo method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Lanthanum doped BiFeO3 powders: Syntheses and characterization

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Dielectric properties of pure and lanthanum modified bismuth titanate thin films

We investigated the dielectric properties of pure and lanthanum modified bismuth titanate thin films obtained by the polymeric precursor method. X-ray diffraction of the film annealed at 300 degrees C for 2h indicates a disordered structure. Lanthanum addition increases gradually the dielectric permittivity of films, keeping unchanged their loss tangent. From C-V curve we can see no hysteresis behavior indicating the absence of domain structure. The decrease in the conductivity for the heavily doped Bi4Ti3O12 (BIT) must be associated to the unidentified crystal defects. For comparison, dielectric properties of crystalline BIT film were also investigated. (C) 2007 Published by Elsevier B.V.