Microstructural and mechanical characteristics of W-2Ti and W-1TiC processed by Hot Isostatic Pressing

It has been demonstrated that mechanical alloying and subsequent consolidation by hot isostatic pressing (HIP) is a successful route to produce dispersion strengthened W alloys with properties satisfying the design requirements of particular plasma facing components in the fusion reactor. However, the presence of the alloying element as a phase filling large interstices between W particles appears to reduce the mechanical properties of these alloys. In order to limit this phase separation induced by the HIP treatment and the detrimental effects on the mechanical properties, the enhancement of the mechanical alloying process, and the effect of a postconsolidation heat treatment in an reducing atmosphere, have been investigated.

Microstructural and mechanical characteristics of W-2Ti and W-1TiC processed by hot isostatic pressing

W–2Ti and W–1TiC alloys were produced by mechanical alloying and consolidation by hot isostatic pressing. The composition and microstructural characteristics of these alloys were studied by X-ray diffraction, energy dispersion spectroscopy and scanning electron microscopy. The mechanical behavior of the consolidated alloys was characterized by microhardness measurements and three point bending tests. The mechanical characteristics of the W–2Ti alloy appear to be related to solution hardening. In W–1TiC, the residual porosity should be responsible for the poor behavior observed in comparison with W–2Ti.

Bonding of various metals and alloys by isostatic pressing at elevated temperatures /

Work performed at the Sylvania-Corning Nuclear Corporation under contract AT-30 GEN-366.

Ceramic fuel elements made by hot isostatic pressing /

Work performed at the Sylvania-Corning Nuclear Corporation under contract AT-30-1 GEN-366 with the Division of Reactor Development.

Isostatic pressing of UO₂ in high temperature metals /

The hot isostatic pressing process has been applied at temperatures up to 1500°C for the fabrication of high temperature fuel rods composed of UO₂ clad in columbium and UO₂ in iron-aluminum type alloy. The fused UO₂ powder apparently becomes quite plastic at temperatures above 1200°C and can be isostatically compacted at 1500°C to 98% of its theoretical density. Columbian tubes particularly lend themselves to the fabrication of fuel rods by simultaneously compacting and cladding UO₂ powders in the tubes, but the cast iron-aluminum type alloy that was used was unsatisfactory because of its brittleness.

alpha-SiAlON-SiC composites obtained by gas-pressure sintering and hot-pressing

The objective of this work was the obtaining in situ of alpha-SiAlON-SiC composite, using an alternative rare-earth oxide mixture, RE2O3, as sintering additive, by two different sintering processes. As sintering additive, 20 vol.% of AlN-RE2O3 in a molar ratio of 90: 10 was mixed to the alpha-Si3N4 powder. In the Si3N4-AlN-RE2O3 powder mixture, 0, 10, 15 and 20wt.% of SiC were added. The powder batches were milled, dried and compacted by cold isostatic pressing. Two different sintering processes were used: gas-pressure sintering at 1950 degrees C for 1 h under 1.5 MPa of N-2 atmosphere, or uniaxial hot-pressing at 1750 degrees C, for 30 min under pressure of 20 MPa. The sintered samples were characterized by X-ray diffraction, scanning electron microscopy and mechanical properties. XRD patterns indicate only alpha-SiAlON (alpha') and beta-SiC as crystalline phases. It was observed that the SiC addition did not influence the alpha-SiAlON formation, although the growth of elongated alpha'-grains is substantially decreased. The hot-pressed composites presented better mechanical properties, exhibiting fracture toughness of 5 MPa m(1/2) and hardness around 21.5 GPa. (c) 2007 Elsevier B.V. All rights reserved.

Hot isostatic compaction of graphite /

"October 5, 1965."

Structural, mechanical and biocompatibility studies of hydroxyapatite-derived composites toughened by zirconia addition

Hydroxyapatite(OHAp)-based ceramic composites with added ZrO2 have been prepared both by sintering at 1400 °C and by hot isostatic pressing (HIP) at 1450 °C and 140 MPa pressure (argon atmosphere). The development of the crystalline phases and the microstructure of the composites have been examined using X-ray diffraction, electron microscopy, infrared and magic-angle spinning nuclear magnetic resonance (MASNMR) spectroscopic techniques. The fracture toughness and biocompatibility of the composites have also been studied. The effect of the addition of CeO2- and Y2O3-stabilized ZrO2 and of simple monoclinic ZrO2 to the initial physical mixture, on the structure and properties of the resulting composites has been investigated. In most of the sintered or HIP samples, the OHAp decomposes into tricalcium phosphate (β-TCP). CaO, which forms as a product of decomposition, dissolves completely in ZrO2 and stabilizes the latter in its cubic/tetragonal phase. Presence of the β-TCP phase in the product seems to be the result of a structural synergistic effect of hexagonal OHAp. Two structurally distinct orthophosphate groups have been identified in the composites by MASNMR of 31P and attributed to decomposition products of OHAp at higher temperatures. The composites possess high KIC values (2–3 times higher than that of pure OHAp). Decomposition of hydroxyapatite gives rise to differences in microstructure between HIP and simply sintered composites although fracture toughness values are similar in magnitude indicating the presence of several toughening mechanisms. The in vitro SP2-O cell test suggests that these composites possess good biocompatibility. The combination of good biocompatibility, desirable microstructure and easy availability of initial reactants indicates that the simply sintered composite of OHAp and monoclinic ZrO2(ZAP-30) appears to be the most suitable for prosthetic applications.

Sintering of nanopowders of amorphous silicon nitride under ultrahigh pressure

Nanopowders of amorphous silicon nitride were densified and sintered without additives under ultrahigh pressure (1.0-5.0 GPa) between room temperature and 1600 degrees C. The powders had a mean diameter of 18 nm and contained similar to 5.0 wt% oxygen that came from air-exposure oxidation, Sintering results at different temperatures were characterized in terms of sintering density, hardness, phase structure, and grain size. It was observed that the nanopowders can be pressed to a high density (87%) even at room temperature under the high pressure. Bulk Si3N4 amorphous and crystalline ceramics (relative density: 95-98%) were obtained at temperatures slightly below the onset of crystallization (1000-1100 degrees C and above 1420 degrees C, respectively. Rapid grain growth occurred during the crystallization leading to a grain size (>160 nm) almost 1 order of magnitude greater than the starting particulate diameters, With the rise of sintering temperature, a final density was reached between 1350 and 1420 degrees C, which seemed to be independent of the pressure applied (1.0-5.0 GPa), The densification temperature observed under the high pressure is lower by 580 degrees C than that by hot isostatic pressing sintering, suggesting a significantly enhanced low-temperature sintering of the nanopowders under a high external pressure.

Development of sialons colloidally processed in aqueous medium

Desenvolveu-se um novo método de processamento coloidal em meio aquoso para consolidar cerâmicos de α-Y-SiAlON, os quais foram sinterizados por prensagem isostática a quente (HIP) e por spark plasma sintering (SPS). Preparou-se com sucesso uma suspensão aquosa de pós precursores de YSiAlON (Si3N4, Al2O3, Y2O3 e AlN), temporariamente estável, usando Dolapix PC21 como dispersante, permitindo a fabricação de pós granulados pela técnica de aspersão-congelamento-liofilização e a consolidação de corpos em verde por enchimento por barbotina. Avaliou-se o efeito do excesso de oxigénio introduzido pelo processamento aquoso no desenvolvimento microestrutural e nas propriedades mecânicas. Os corpos de Y-SiAlON consolidados por enchimento por barbotina e sinterizados por HIP a 1800ºC apresentaram microestruturas e propriedades mecânicas similares a corpos consolidados por prensagem a seco. Estes materiais exibiram densificação completa, dureza Vickers máxima de 2003 e tenacidade à fractura (método SEVNB) máxima de 5.20 MPam1/2. Foi ainda possível estabelecer uma relação estreita entre o aumento do conteúdo em oxigénio das amostras sinterizadas e a diminuição da tenacidade à fractura. Na tentativa de melhorar a tenacidade à fractura dos materiais, procedeu-se à incorporação nas suspensões de sementes de Ca-α-SiAlON de geometria alongada produzidas por síntese por combustão, adicionadas como agentes de reforço. A síntese por combustão realizada em larga escala (cargas até 1 kg) não produziu efeitos negativos óbvios nos produtos da reacção. Investigara-se os efeitos da adição de 5 % em peso de sementes nas propriedades mecânicas e no desenvolvimento microestrutural de amostras densificadas por HIP. Em comparação com os materiais sem sementes, a tenacidade à fractura (método SEVNB) aumentou 13%, mas a dureza Vickers resultou 14,5% inferior. A sinterização por SPS permitiu obter densificação completa a temperaturas tão baixas como 1600ºC a partir dos pós granulados de Y-SiAlON sem a adição extra de Y2O3 para aumentar o teor de fase líquida. Os materiais sinterizados a 1700ºC e 1600ºC mostraram valores máximos de tenacidade à fractura de 4.36 e 4.20 MPam1/2 (método SEVNB), e de dureza Vickers de 2089 e 2084, respectivamente. Esta técnica de sinterização permitiu ainda obter corpos sinterizados translúcidos com uma transmitância máxima de 61% numa amostra de 2mm de espessura. Os corpos translúcidos apresentaram dureza Vickers de 2154 e tenacidade à fractura 3.74 MPam1/2 (método SEVNB).

Silicon carbide surface modification by nitrogen plasma expander

Silicon carbide (SiC) has been employed in many different fields such as ballistic armor, thermal coating, high performance mirror substrate, semiconductors devices, among other things. Plasma application over the silicon carbide ceramics is relatively recent and it is able to promote relevant superficial modifications. Plasma expander was used in this work which was supplied by nitrogen and switched by a capacitor bank. Nitrogen plasma was applied over ceramic samples for 20 minutes, in a total medium of 1440 plasma pulses. SiC ceramics were produced by uniaxial pressing method (40 MPa) associated to isostatic pressing (300 MPa) and sintered at 1950 degrees C under argon gas atmosphere. Silicon carbide (beta-sic - BF-12) supplied by HC-Starck and sintering additive (7.6% YAG - Yttrium Aluminum Garnet) were used in order to obtain the ceramics. Before and after the plasma application, the samples were characterized by SEM, AFM, contact angle and surface energy measurement.

Production of a low young modulus titanium alloy by powder metallurgy

Titanium alloys have several advantages over ferrous and non-ferrous metallic materials, such as high strengthto-weight ratio and excellent corrosion resistance. A blended elemental titanium powder metallurgy process has been developed to offer low cost commercial products. The process employs hydride-dehydride (HDH) powders as raw material. In this work, results of the Ti-35Nb alloy sintering are presented. This alloy due to its lower modulus of elasticity and high biocompatibility is a promising candidate for aerospace and medical use. Samples were produced by mixing of initial metallic powders followed by uniaxial and cold isostatic pressing with subsequent densification by isochronal sintering between 900 up to 1600 °C, in vacuum. Sintering behavior was studied by means of microscopy and density. Sintered samples were characterized for phase composition, microstructure and microhardness by X-ray diffraction, scanning electron microscopy and Vickers indentation, respectively. Samples sintered at high temperatures display a fine plate-like alpha structure and intergranular beta. A few remaining pores are still found and density above 90% for specimens sintered in temperatures over 1500 °C is reached.

Obtenção in situ do compósito alfa-SiAlON-SiC

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Sintering of tin oxide using zinc oxide as a densification aid

The physicochemical electronic characteristics of SnO2 render it useful in many technical applications, including ceramic varistors, stable electrodes used in electric glass-melting furnaces and electrometallurgy of aluminum, transparent windows and chemical sensors. The use of ZnO as a sintering aid was explored in this study to obtain SnO2 as a dense ceramic. Compacts were obtained by mechanical mixing of oxides, isostatic pressing at 210 MPa and sintering in situ inside a dilatometer at heating rates of 10degreesC/min. The grain size and microstructure were investigated by scanning and transmission electron microscopy (SEM/TEM). The phases and chemical composition were analyzed by energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The results indicated that ZnO acts as a densification aid for SnO2, improving its grain growth with additions of up to 2 mol%. ZnO forms a solid solution with SnO2 UP to 1 mol%, above which SnZnO3 precipitates in the grain boundary, potentially inhibiting shrinkage and grain growth. (C) 2004 Kluwer Academic Publishers