Removal of surface states and recovery of band-edge emission in InAs nanowires through surface passivation.

Surface states in semiconductor nanowires (NWs) are detrimental to the NW optical and electronic properties and to their light emission-based applications, due to the large surface-to-volume ratio of NWs and the congregation of defects states near surfaces. In this paper, we demonstrated an effective approach to eliminate surface states in InAs NWs of zinc-blende (ZB) and wurtzite (WZ) structures and a dramatic recovery of band edge emission through surface passivation with organic sulfide octadecylthiol (ODT). Microphotoluminescence (PL) measurements were carried out before and after passivation to study the dominant recombination mechanisms and surface state densities of the NWs. For WZ-NWs, we show that the passivation removed the surface states and recovered the band-edge emission, leading to a factor of ∼19 reduction of PL linewidth. For ZB-NWs, the deep surface states were removed and the PL peaks width became as narrow as ∼250 nm with some remaining emission of near band-edge surface states. The passivated NWs showed excellent stability in atmosphere, water, and heat environments. In particular, no observable changes occurred in the PL features from the passivated NWs exposed in air for more than five months.

A comparative study of transistors based on wurtzite and zincblende InAs nanowires

We report a comparative study of the electronic properties of nominally identical nanowire field-effect transistor (NW-FET) devices produced using 50 nm diameter InAs nanowires that differ only in phase: ZB on the one hand, and WZ on the other. We find much higher current densities in the ZB NW-FETs, and on/off ratios of up to 100. © 2010 IEEE.

High-density InAs nanowires realized in situ on (100) InP

High-density InAs nanowires embedded in an In0.52Al0.48As matrix are fabricated in situ by molecular beam epitaxy on (100) InP. The average cross section of the nanowires is 4.5 x 10 nm(2). The linear density is as high as 70 wires/mu m. The spatial alignment of the multilayer arrays exhibit strong anticorrelation in the growth direction. Large polarization anisotropic effect is observed in polarized photoluminescence measurements. (C) 1999 American Institute of Physics. [S0003-6951(99)04134-0].

Spin splitting modulated by uniaxial stress in InAs nanowires

We theoretically study the electronic structure, spin splitting, effective mass, and spin orientation of InAs nanowires with cylindrical symmetry in the presence of an external electric field and uniaxial stress. Using an eight-band k center dot p theoretical model, we deduce a formula for the spin splitting in the system, indicating that the spin splitting under uniaxial stress is a nonlinear function of the momentum and the electric field. The spin splitting can be described by a linear Rashba model when the wavevector and the electric field are sufficiently small. Our numeric results show that the uniaxial stress can modulate the spin splitting. With the increase of wavevector, the uniaxial tensile stress first restrains and then amplifies the spin splitting of the lowest electron state compared to the no strain case. The reverse is true under a compression. Moreover, strong spin splitting can be induced by compression when the top of the valence band is close to the bottom of the conductance band, and the spin orientations of the electron stay almost unchanged before the overlap of the two bands.

Electronic properties of GaAs, InAs and InP nanowires studied by terahertz spectroscopy.

We have performed a comparative study of ultrafast charge carrier dynamics in a range of III-V nanowires using optical pump-terahertz probe spectroscopy. This versatile technique allows measurement of important parameters for device applications, including carrier lifetimes, surface recombination velocities, carrier mobilities and donor doping levels. GaAs, InAs and InP nanowires of varying diameters were measured. For all samples, the electronic response was dominated by a pronounced surface plasmon mode. Of the three nanowire materials, InAs nanowires exhibited the highest electron mobilities of 6000 cm² V⁻¹ s⁻¹, which highlights their potential for high mobility applications, such as field effect transistors. InP nanowires exhibited the longest carrier lifetimes and the lowest surface recombination velocity of 170 cm s⁻¹. This very low surface recombination velocity makes InP nanowires suitable for applications where carrier lifetime is crucial, such as in photovoltaics. In contrast, the carrier lifetimes in GaAs nanowires were extremely short, of the order of picoseconds, due to the high surface recombination velocity, which was measured as 5.4 × 10⁵ cm s⁻¹. These findings will assist in the choice of nanowires for different applications, and identify the challenges in producing nanowires suitable for future electronic and optoelectronic devices.

Tailoring GaAs, InAs, and InGaAs nanowires for optoelectronic device applications

GaAs, InAs, and InGaAs nanowires each exhibit significant potential to drive new applications in electronic and optoelectronic devices. Nevertheless, the development of these devices depends on our ability to fabricate these nanowires with tight control over critical properties, such as nanowire morphology, orientation, crystal structure, and chemical composition. Although GaAs and InAs are related material systems, GaAs and InAs nanowires exhibit very different growth behaviors. An understanding of these growth behaviors is imperative if high-quality ternary InGaAs nanowires are to be realized. This report examines GaAs, InAs, and InGaAs nanowires, and how their growth may be tailored to achieve desirable material properties. GaAs and InAs nanowire growth are compared, with a view toward the growth of high-quality InGaAs nanowires with device-accessible properties. © 2011 IEEE.

Understanding the kink formation in GaAs/InAs heterostructural nanowires

The kinks formation in heterostructural nanowires was observed to be dominant when InAs nanowires were grown on GaAs nanowires. Nanowires were grown through vapor-liquid-solid (VLS) mechanism in an MOCVD (metalorganic chemical vapor deposition) reactor. GaAs nanowires were grown in [1 1 1 ]B direction on a GaAs (1 1 1 )B substrate. When InAs nanowires grown on the GaAs nanowires, most of the InAs nanowires changed their growth directions from [1 1 1 ]B to other 〈111〉B directions. The kinks formation is ascribed to the large compressive misfit strain at the GaAs/InAs interface (7.2% lattice mismatch between GaAs and InAs) and the high mobility of indium species during MOCVD growth. The in-depth analysis of the kinks formation was done by growing InAs for short times on the GaAs nanowires and characterizing the samples. The hindrance to compressively strain InAs to form coherent layers with GaAs pushed the InAs/Au interfaces to the sides of the GaAs nanowires growth ends. New InAs/Au interfaces have generated at the sides of GaAs nanowires, due to lateral growth of InAs on GaAs nanowires. These new interfaces led the InAs nanowires growth in other 〈111〉B directions. The morphological and structural features of these heterostructural kinked nanowires were characterized using scanning electron microscopy (SEM) and transmission electron microscopy (TEM) techniques. © 2006 IEEE.

Growth of GaAs/InAs vertical nanowires on GaAs (111)B by metalorganic chemical vapor deposition

The growth mechanism and properties of GaAs/InAs nanowires prepared by metalorganic chemical vapor deposition are investigated. Vertical InAs nanowires on GaAs (111)B substrates are successfully grown despite the large lattice mismatch (-7.2%). The crystallographic perfection of InAs nanowires is confirmed by hexagonal or triangular cross section. An interesting L-shaping of GaAs/InAs heterostructure nanowire which could be useful for novel device application is observed. © 2005 IEEE.

Surface morphology control of strained InAs/GaAs(331)A films: From nanowires to island-pit pairs

We have studied the effect of molecular beam epitaxy growth conditions on the surface morphology of strained InAs/GaAs(331)A films. Our results reveal that InAs nanowires aligned along the [1 (1) over bar0] direction are formed under As-rich conditions, which is explained by the effect of anisotropic buffer layer surface roughing. Under In-rich conditions, however, the surface morphology of the InAs layers is characterized by a feature of island-pit pairs. In this case, cooperative nucleation of islands and pits can lower the activation barrier for domain growth. These results suggest that the surface morphology of strained InAs layers is highly controllable. (C) 2005 American Institute of Physics.

Origin of the vertical-anticorrelation arrays of InAs/InAlAs nanowires with a fixed layer-ordering orientation

InAs/In0.52Al0.48As nanowire multilayer arrays were grown on (001) InP substrate by molecular-beam epitaxy. The structural property of the arrays was investigated by transmission electron microscopy. The results clearly showed the formation of InAs nanowires, evolution of InAs/InAlAs interface, and composition and thickness modulations in the InAlAs spacer layer. A fixed spatial ordering of InAs/InAlAs nanowires was revealed for all the samples. Regardless of the change in InAlAs spacer thickness of different samples, (i) the nanowires of one InAs layer are positioned above the nanowire spacing in the previous InAs layer and (ii) the layer-ordering orientation angle of nanowires is fixed. The results were explained from the viewpoint of the growth kinetics. The effect of InAlAs spacers is suggested to play an important role on the spatial ordering of the nanowire arrays. (C) 2002 American Institute of Physics.

Evolution of Wurtzite Structured GaAs Shells Around InAs Nanowire Cores.

GaAs was radially deposited on InAs nanowires by metal-organic chemical vapor deposition and resultant nanowire heterostructures were characterized by detailed electron microscopy investigations. The GaAs shells have been grown in wurtzite structure, epitaxially on the wurtzite structured InAs nanowire cores. The fundamental reason of structural evolution in terms of material nucleation and interfacial structure is given.

III-V nanowires for optoelectronics

The optical and structural properties of binary and ternary III-V nanowires including GaAs, InP, In(Ga)As, Al(Ga)As, and GaAs(Sb) nanowires by metal-organic chemical vapour deposition are investigated, Au colloidal nanoparticles are employed to catalyze nanowire growth. Zinc blende or wurtzite crystal structures with some stacking faults are observed for these nanowires by high resolution transmission electron microscope. In addition, the properties of heterostructure nanowires including GaAs-AlGaAs core-shell nanowires, GaAs-InAs nanowires, and GaAs-GaSb nanowires are reported. Single nanowire luminescence properties from optically bright InP nanowires are reported. Interesting phenomena such as two-temperature procedure, nanowire height enhancement of isolated ternary InGaAs nanowires, kinking effect of InAs-GaAs heterostructure nanowires, and unusual growth property of GaAs-GaSb heterostructure nanowires are investigated. These nanowires will play an essential role in future optoelectronic devices.

Electronic comparison of InAs wurtzite and zincblende phases using nanowire transistors

We compare the electronic characteristics of nanowire field-effect transistors made using single pure wurtzite and pure zincblende InAs nanowires grown from identical catalyst particles. We compare the transfer characteristics and field-effect mobility versus temperature for these devices to better understand how differences in InAs phase govern the electronic properties of nanowire transistors. © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Probing the critical electronic properties of III-V nanowires using optical pump-terahertz probe spectroscopy

Optical pump-terahertz probe spectroscopy was used to study the key electronic properties of GaAs, InAs and InP nanowires at room temperature. Of all nanowires studied, InAs nanowires exhibited the highest mobilities of 6000 cm2V-1s-1. InP nanowires featured the longest photoconductivity lifetimes and an exceptionally low surface recombination velocity of 170 cm/s. © 2013 IEEE.