Dentin bond strength: Influence of laser irradiation, acid etching, and hypermineralization

Objective: the purpose of the present study was to investigate the effects of ND:YLF laser irradiation (1.31 J/cm(2); 250 mJ per pulse), acid etching, and hypermineralization on the shear bond strength (SBS) of the Scotchbond Multi-Purpose Plus (3M Dental Products) bonding system. Summary Background Data: Previous studies had shown that the pretreatment of the dentin substrate with laser irradiation can influence the SBS, Methods: Sixty bovine incisors were selected and stored at -18 degrees C, Dentinal buccal surface was exposed and radiographs were taken to control dentin thickness, the specimens were separated into 2 groups: (1) the control, which was kept in distilled water at 4 degrees C; (2) the hypermineralized, which was kept in hypermineralizing solution at 4 degrees C for 14 days, Each group was divided into 3 subgroups according to the type of dentin pretreatment used: M (acid etching + primer + bond); AL (acid etching + primer + bond + laser); and LA (laser + acid etching + primer + bond). A standard composite resin cylinder (Z100-3M) was bonded to the dentinal surface and the SBS performed on an Instron machine (500 Kg load cell at 0.5 mm/min), followed by scanning electron microscopy (SEM) and x-ray diffraction analysis. Results: Analysis of variance (ANOVA) determined that the pretreatments influenced the SBS values (p < 0.05): AL (9.96 MPa), M (7.28 MPa), and LA (4.87 MPa), the interaction between the group and pretreatment factors also influenced the SBS (p < 0.05). The highest values were obtained for the interaction control/AL (11.64 MPa), Conclusion: the results suggested that dentin treatment with laser after the application of the adhesive system is efficient in achieving higher bond strength and is promising as a possible new adhesive substrate.

Influence of dental exposure to oral environment on smear layer removal and collagen exhibition after using different conditioning agents

Although in vitro studies have shown encouraging results for root surface conditioning with demineralizing agents, in vivo studies have failed to show its benefits in periodontal healing. This can be attributed to several factors, among which, the hypermineralization of dental surface. Therefore, this in vitro study compared, using scanning electron microscopy (SEM), the effect of root surface conditioning with different conditioners (1% and 25% citric acid, 24% EDTA and 50 mg/mL tetracycline hydrochloride) in impacted teeth and in teeth that had their roots exposed to the oral environment. One trained examiner assessed the SEM micrographs using a root surface modification index. There was a tendency of more root surface modification in the group of impacted teeth, suggesting that the degree of root mineralization influences its chemical demineralization.

Biomodificação radicular em dentes expostos e não expostos à placa bacteriana

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Resistência de união ao microcisalhamento de sistemas adesivos autocondicionates com graus de acidez distintos: efeito de diferentes tratamentos em substrato dentinário normal e hipermineralizado artificialmente

Pós-graduação em Ciências Odontológicas - FOAR

Pré tratamento dentinário influência do condicionamento ácido, irradiação laser e hipermineralização na resistência ao cisalhamento de sistema adesivo multi uso

The disadvantages generated by the acid etching of the dentin, such as an increase in its permeability, in the surface moisture and in the potential to denature the external dentinal collagen, the formation of a fragility zone and the citotoxicity of the adhesive monomers; which are all aggravated by the depth of the dentin, have stimulated new and different treatment philosophies of the dentin. The purpose of the present study, therefore, was to investigate the effects of three dentin treatments: laser irradiation, acid etching and hypermineralization, in the shear bond strength of the SMP Plus bonding system. Sixty bovine incisors were extracted and randomly selected immediatly alter the animal's death. They were kept frozen (-18°C) for no longer than 14 days. After buccal dentinal surface had been exposed, X-Rays were taken to control the dentin thickness. The specimens were separated into two groups: (1) Control, kept in distilled water at 4ºC; (2) Mineralized, kept in hypermineralized solution at 4°C for 14 days. Each group was divided into three sub-groups according to the type of dentin treatment used: group F - followed the manufacturer instructions (acid-etching + primer + bond), group AL (acid-etching + primer + bond + laser) and group LA (laser + (laser + acid-etching + primer + bond). A composite resin standard cylinder (Z100-3M) was bond to the dentinal surface and the shear bond strength performed on a Universal lnstron machine 4301, with 500 Kg load and at 0,5mm/min. speed. The analysis of variance (ANOVA) determined that the treatments influenced the shear bond strength values (p<0,05) with the following average shearing load at failure: AL (9,96 MPa), F (7,28MPa) e LA (4,87 MPa). The interaction between the two factors analyzed Group (control and mineralized) and treatment (F, AL, LA) also influenced the shear bond strength (p<0,05). The highest values were obtained...