Evaluation of piezoelectric PVDF polymers for use in space environments. III. Comparison of the effects of vacuum UV and gamma radiation

Films of piezoelectric PVDF and P(VDF-TrFE) were exposed to vacuum UV (115-300 nm VUV) and -radiation to investigate how these two forms of radiation affect the chemical, morphological, and piezoelectric properties of the polymers. The extent of crosslinking was almost identical in both polymers after -irradiation, but surprisingly, was significantly higher for the TrFE copolymer after VUV-irradiation. Changes in the melting behavior were also more significant in the TrFE copolymer after VUV-irradiation due to both surface and bulk crosslinking, compared with only surface crosslinking for the PVDF films. The piezoelectric properties (measured using d33 piezoelectric coefficients and D-E hysteresis loops) were unchanged in the PVDF homopolymer, while the TrFE copolymer exhibited more narrow D-E loops after exposure to either - or VUV-radiation. The more severe damage to the TrFE copolymer in comparison with the PVDF homopolymer after VUV-irradiation is explained by different energy deposition characteristics. The short wavelength, highly energetic photons are undoubtedly absorbed in the surface layers of both polymers, and we propose that while the longer wavelength components of the VUV-radiation are absorbed by the bulk of the TrFE copolymer causing crosslinking, they are transmitted harmlessly in the PVDF homopolymer.

Effects of gamma radiation on nutritional and microbial quality of Pampus chinensis (Euphrasen 1788)

To evaluate the efficiency of gamma radiation in combination with low temperature Chinese pomfret, Pampus chinensis were preserved by the treatment of different doses of gamma radiation (3, 5 and 8 KGy) at freezing temperature (-20°C) during 90 days of storage period. Quality assessments for fish were carried out at an interval of 15 days during the storage period. Quality assessments were done by organoleptic, chemical (Total Volatile Nitrogen, TVN and Trimethylamine, TMA) and microbiological (Total Bacterial Count, TBC and Total Mould Count, TMC) evaluation. From the analysis of all parameters, maximum shelf-life was observed for irradiated (8 KGy) sample. It remained acceptable up to 75 days and that was the highest duration among 4 types of samples.

Effects of gamma radiation and -20°C temperatures on the shelf life of Hilsa, Tenualosa ilisha (ham.-Buch. 1822)

The combined effect of radiation and refrigeration on the shelf life of hilsa, Tanualosa ilisha was studied by monitoring the microbiological, chemical and sensory changes of unirradiated and irradiated fish samples using low dose irradiation, doses of 300 krad, 600 krad and 900 krad. Irradiation (900 krad) dramatically reduced population of bacteria, namely total viable counts 48.850cfu per gm for unirradiated, 31.850cfu per gm and 19.600cfu per gm of 300 krad and 600 krad, respectively. The effect was more pronounced at the higher dose (900 krad), total viable count were 14.100cfu per gm. Another microbial indicator total mould counts (TMC) was 8.750cfu per gm, 6.350cfu per gm, and 19.600cfu per gm for 300 krad and 600 krad, respectively. The effect was more pronounced at the higher dose (900 krad) where total viable counts were 14,100cfu per gm. Total volatile nitrogen values increased slowly attaining a value of 101.02mgN per 100gm for unirradiated T. ilisha during refrigerated storage, whereas for irradiated fish, lower values of 71.13, 59.33 and 47.03mgN per 100gm muscle were recorded. Sensory evaluation showed a good correlation with bacterial populations on the basis of overall acceptability scores.

Effects of gamma radiation and freezing on the chemical and sensory changes in shrimp Penaeus monodon (Fabricius, 1978)

Gamma radiation (3, 6 and 9 kGy) in combination with low temperature (-20°C) were applied to retain the quality and shelf-life of shrimp, Penaeus monodon for a longer period. The quality was assessed by monitoring the chemical (TVN, TMA) and sensory changes in irradiated and non-irradiated (control) samples. Among chemical indicators of spoilage, total volatile nitrogen (TVN) values for irradiated shrimps were found to be 2.26, 2.18 and 1.57 mg N/100g of sample at 3, 6 and 9 kGy respectively after 90 days whereas for non-irradiated samples it was found 2.45mg N/100 g of sample. Trimethylamine (TMA) value for non-irradiated samples after 90 days were found 2.30mg N/100 g sample whereas that for irradiated shrimps at 3, 6 and 9 kGy were found to be 2.10, 2.08 and 1.98 mg N/100 g sample respectively. The sensory scores of control sample were gradually decreased with the progress of storage period. From this study, it was clear that gamma radiation in combination with low temperature showed shelf-life extension (90 days) in each dose of radiation used but during the use of 9 kGy radiation, P. monodon showed best quality.

Effect of gamma radiation in combination with freezing on the microbiological changes in frozen shrimp Penaeus monodon

In this study gamma radiation (3, 6 and 9 kGy) in combination with low temperature (-20°C) were applied to retain the quality and shelf-life of shrimp, Penaeus monodon for a longer period. The quality was assessed by monitoring microbiological changes (TBC, TMC, TYC, TCC and Salmonella count) in irradiated and non-irradiated (control) samples. Among microbiological indicators of spoilage, total bacterial count (TBC) values for irradiated shrimps were found to be 1875, 1625 and 1525 cfugˉ¹ of sample at 3, 6 and 9 kGy respectively after 90 days whereas for non-irradiated samples it was found 2475 cfugˉ¹ of sample. Total moulds count (TMC) value for non-irradiated samples after 90 days were found 425 cfugˉ¹ sample whereas that for irradiated shrimps at 3, 6 and 9 kGy were found to be 275, 250 and 200 cfugˉ¹ sample respectively. Total yeast count (TYC) value for non-irradiated samples after 90 days were found 4125 cfugˉ¹ sample whereas that for irradiated shrimps at 3, 6 and 9 kGy were found to be 2850, 2150 and 1725 cfugˉ¹ sample respectively. Total coliform count and Salmonella count showed that those were absent during 90 days storage period. From this study, it was clear that gamma radiation in combination with low temperature showed shelf-life extension (90 days) in each dose of radiation used but during the use of 9 kGy radiation, Penaeus monodon showed best quality.

JFET SOS devices: Processing and gamma radiation effects

A process for fabricating n channel JFET/SOS (junction field-effect transistors on silicon-on-sapphire) has been researched. The gate p(+)n junction was obtained by diffusion, and the conductive channel was gotten by a double ion implantation. Both enhancement and depletion mode transistors were fabricated in different processing conditions. From the results of the Co-50 gamma ray irradiation experimental we found that the devices had a good total dose radiation-hardness. When the tot;ll dose was 5Mrad(Si), their threshold voltages shift was less than 0.1V. The variation of transconductance and the channel leakage current were also little.

Vulcanization of polybutadiene latex induced by Co-60 gamma radiation

Polybutadiene latex (PBL) vulcanization induced by Co-60 radiation and the influence of dose on crosslinking were investigated. Morphology and particle size distribution were examined by AFM and a particle size analyzer. The casting films were characterized for their swelling and mechanical properties as a function of dose.

Effect of gamma-radiation on the thermal and mechanical properties of a commercial poly(butylene adipate-co-terephthalate)

BACKGROUND: Poly(butylene adipate-co-terephthalate) (PBAT) has attracted wide interest as a biodegradable polymer. However, its use is restricted in certain applications due to its low melting point.RESULTS: PBAT was treated using gamma-radiation. The radiation features were analyzed using Soxhlet extraction, and the ratio of chain scission and crosslinking and gelation dose were determined using the classical Charlesby-Pinner equation. The results showed that PBAT is a radiation-crosslinkable polymer. The degree of crosslinking increased with increasing radiation dose; the relation between sol fraction and dose followed the Charlesby-Pinner equation. Differential scanning calorimetry analyses showed that the melting temperature (T-m) and the heat of fusion (Delta H-m) of PBAT exhibited almost no change in the first scan. The second scan, however, showed a decrease in T-m and Delta H-m. The glass transition temperature of irradiated PBAT increased with increasing radiation dose.

Thermal and mechanical properties of poly(epsilon-caprolactone) crosslinked with gamma radiation in the presence of triallyl isocyanurate

Poly(epsilon-caprolactone) was crosslinked by gamma radiation in the presence of triallyl isocyanurate. The influence of gamma-radiation crosslinking on the thermal and mechanical properties of poly(epsilon-caprolactone)/triallyl isocyanurate was investigated. Differential scanning calorimetry analyses showed differences between the first and second scans. Dynamic mechanical analysis showed an increase in the glass-transition temperature as a result of the radiation crosslinking of poly(epsilon-caprolactone). Thermogravimetric analysis showed that gamma-radiation crosslinking slightly improved the thermal stability of poly(epsilon-caprolactone). The 7 radiation also strongly influenced the mechanical properties. At room temperature, crosslinking by radiation did not have a significant influence on the Young's modulus and yield stress of poly(E-caprolactone). However, the tensile strength at break and the elongation at break generally decreased with an increase in the crosslinking level. When the temperature was increased above the melting point, the tensile strength at break, elongation at break, and Young's modulus of poly(epsilon-caprolactone) were also reduced with an increase in the crosslinking level. The yield stress disappeared as a result of the disappearance of the crystallites.

A novel route for the preparation of CdS nanocrystal-poly(acrylic acid) composites using gamma-radiation

CdS nanocrystals were synthesized through AOT/heptane/H2O reverse micelles. New stable reverse mikelles were obtained by adding an appropriate amount of acrylic. acid monomer, CdS nanocrystal-poly(acrylic acid) composites were synthesized by gamma-radiation with a reverse mi'celle route at room temperature. The US nanocrystals with narrow size distribution were, found to be dispersed homogeneously in the poly(acrylic acid) matrix. (C) 2002 Elsevier Science B.V. All rights reserved.

Thermal, mechanical and ionic conductive behaviour of gamma-radiation induced PEO/PVDF(SIN)-LiClO4 polymer electrolyte system

An effort has been made to modify the mechanical behaviour of our previously reported gel-type gamma-radiation crosslinked polyethylene oxide (PEO)-LiClO4 polymer electrolyte. A highly polar and gamma-radiation crosslinkable crystalline polymer, polyvinylidene fluoride (PVDF), was selected to blend with PEO and then subjected to gamma-irradiation in order to make an simultaneous interpenetrating network (SIN), which was used as a polymer host to impart stiffness to the plasticized system. Experimental results have shown that the presence of PVDF in the system, through gamma-radiation induced SIN formation, could not only give a rather high mechanical modulus of 10(7) Pa at ambient temperature, but also maintain the room temperature ionic conductivity at a high level (greater than 10(-4) S/cm). DSC, DMA and conductivity measurement techniques were used to examine the effects of blending, gamma-irradiation and plasticization on the variations of glass transition and melting endotherm, on the appearance of high elastic plateau and on the temperature dependence of ionic conductivity: In addition, it was found that, in contrast with the unplasticized system, the ionic conductivity mechanism of this gel-type electrolyte seems to conform to the Arrhenius model, suggesting that, as a result of the high degree of plasticization, the polymer chains act mainly as the skeleton of the networks or polymer cages to immobilize the liquid electrolyte solution, whereas the ionic species migrate as if they were in a liquid medium. (C) 1997 Elsevier Science Ltd.

gamma-Radiation damage to nylon 1010 containing neodymium oxide

A comparison of radiation damage to nylon 1010 (denoted nylon-a) and nylon 1010 containing neodymium oxide (Nd2O3) (denoted nylon-b) was made by DSC, WAXD, ESR and the determination of gel fractions. The results show that radiation damage to nylon-b is delayed, and radiation damage to nylon-a is more severe than that to nylon-b, due to the protection of the fold surface of the lamellae. Furthermore, the fact that the damage begins with the fold surface of the lamellae is confirmed. (C) 1996 Elsevier Science Limited

WAXD and SAXS study on gamma-radiation damage to polyamide-1010 crystal structure

In the present work we attempt to settle the controversy on the district wherein the radiation induced reaction preferentially occurs through examining the structural changes of the irradiated polyamide-1010 specimens on both the crystallographic and the supermolecular level by using WAXD and SAXS techniques. Experimental results indicated that the chain crosslinking and scission of the irradiated specimens occur mainly in the amorphous region and on the crystal surface (or interphase), and extend into the inner portion of the crystal with increasing radiation dose.

THE INFLUENCE OF GAMMA-RADIATION ON POLYAMIDE-1010 AGGREGATE STRUCTURES

The influence of gamma-radiation on polyamide 1010 aggregate structures and crystal damage were examined by using wide angle X-ray diffraction (WAXD) and small angle X-ray scattering (SAXS) techniques. The results revealed that some structural parameters of the aggregated state, the density differences and the degree of crystallinity W-c,W-x, essentially decreased with increasing radiation dose, but the specific surface O-s increased. Crosslinking and scission of irradiated polyamide 1010 samples occurred mainly in amorphous and interphase regions, and crystal damage and amorphization induced by gamma-radiation spread from the interphase and extended into the crystal phase with increasing radiation dose. This result also indicated that the (010) reflection with the hydrogen bond was more susceptible to the action of radiation.