Synthesis and enhanced green photoluminescence emission from BCT ZnS nanocrystals

Body-centered-tetragonal (BCT) ZnS nanocrystals have been synthesized, for the first time to the best of our knowledge, by using the chemical coprecipitation method at higher synthesis temperatures of 65 and 95 degrees C. It is confirmed from X-ray diffraction (XRD) studies that in the high-temperature-synthesized samples, cubic and BCT phases coexist, in contrast to the room-temperature-synthesized sample, which consists of only cubic phase with sizes of the particles lying between 2 and 3 nm. The sizes of BCT phase nanocrystals are bigger than those of cubic phase of ZnS. The presence of BCT phase of ZnS in the samples is increased from 40 to 90% when the temperature of synthesis is increased from 65 to 95 degrees C. The nanocrystalline nature and UV-Vis absorption characteristics of the prepared samples have been studied with a transmission electron microscope (TEM) and a UV-Visible pectrophotometer, respectively. The room-temperature-synthesized ZnS sample shows photoluminescence (PL) emission in the blue region with multiple peaks, whereas the high-temperature-synthesized samples show PL emissions in the visible region. The Gaussian fittings of the measured PL spectra shows that three PL peaks at 429, 477, and 525 nm are appeared in the 65 degrees C sample and two peaks at 491 and 540 nm appear in the 95 degrees C sample with the enhanced PL intensity of the green peak at 540 nm. (C) 2010 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Experimental and theoretical correlation of very intense visible green photoluminescence in BaZrO3 powders

Very intense visible green photoluminescence (PL) was observed at room temperature in structurally ordered-disordered BaZrO3 powders. Ab initio calculations, ultraviolet-visible absorption spectroscopy, electron paramagnetic resonance, and PL were performed. Theoretical and experimental results showed that local defects in the cubic structure caused by [ZrO5 center dot V-O(z)] complex clusters, where V-O(z) = V-O(x), V-O(center dot), and V-O(center dot center dot), play an important role in the formation of hole-electron pairs, giving rise to a charge gradient in the structure which is responsible for PL emission. (c) 2008 American Institute of Physics.

Intense blue and green photoluminescence emissions at room temperature in barium zirconate powders

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Contribution of structural order-disorder to the green photoluminescence of PbWO4

An intense and broad visible photoluminescence (PL) band was observed at room temperature in structurally disordered PbWO4 thin films. The scheelite lead tungstate (PbWO4) films prepared by the polymeric precursor method and annealed at different temperatures were structurally characterized by means of x-ray diffraction and atomic force microscopy analysis. Quantum-mechanical calculations showed that the local disorder of the network modifier (Pb) has a very important role in the charge transfer involved in the green PL emission. The experimental and theoretical results are in good agreement, both indicating that the generation of the intense visible PL band is related to simultaneous structural order and disorder in the scheelite PbWO4 lattice.

The Role of Short-Range Disorder in BaWO4 Crystals in the Intense Green Photoluminescence

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Synthesis, Characterization, Anisotropic Growth and Photoluminescence of BaWO4

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis of wurtzite-phase ZnS nanocrystal and its optical properties

The wurtzite phase of ZnS nanocrystal has been prepared by annealing in 200-600 degrees C temperature range, its cubic phase of 2-3 nm size. prepared through soft chemical method. Results of isochronal experiments of 2 h at different temperatures indicate that visible transformation to wurtzite from cubic ZnS appears at a temperature of 400 degrees C, which is about three times smaller than that of bulk ZnS phase transition temperature. The phases, nanostructures, and optical absorption characteristics are obtained through X-ray diffraction. transmission electron microscopy, and UV-visible absorption spectroscopy. A stable and green photoluminescence emission peaked at 518 nm is observed from the 600 degrees C annealed samples, under ultraviolet light excitation.

Defect induced optical bandgap narrowing in undoped SnO2 nanocrystals

Unusual optical bandgap narrowing is observed in undoped SnO2 nanoparticles synthesized by the solution combustion method. The estimated crystallite size is nearly 7 nm. Though the quantum confinement effect predicts a larger optical bandgap for materials with small crystallite size than the bulk, the optical bandgap in the as synthesized materials is found to be 2.9 eV compared to the reported value of 3.6 eV for bulk SnO2 particles. The yellow-green photoluminescence emissions and the observed narrowing of the bandgap can be attributed to the deep donor levels of oxygen vacancies, owing to the high exothermicity of the combustion reaction and the faster cooling rates involved in the process.

Defect induced optical bandgap narrowing in undoped SnO2 nanocrystals

Unusual optical bandgap narrowing is observed in undoped SnO2 nanoparticles synthesized by the solution combustion method. The estimated crystallite size is nearly 7 nm. Though the quantum confinement effect predicts a larger optical bandgap for materials with small crystallite size than the bulk, the optical bandgap in the as synthesized materials is found to be 2.9 eV compared to the reported value of 3.6 eV for bulk SnO2 particles. The yellow-green photoluminescence emissions and the observed narrowing of the bandgap can be attributed to the deep donor levels of oxygen vacancies, owing to the high exothermicity of the combustion reaction and the faster cooling rates involved in the process. (C) 2013 Author(s). All article content, except where otherwise noted, is licensed under a Creative Commons Attribution 3.0 Unported License.

Investigation of native defects and property of bulk ZnO single crystal grown by a closed chemical vapor transport method

Hall effect, Raman scattering, photoluminescence spectroscopy (PL), optical absorption (OA), mass spectroscopy, and X-ray diffraction have been used to study bulk ZnO single crystal grown by a closed chemical vapor transport method. The results indicate that shallow donor impurities (Ga and Al) are the dominant native defects responsible for n-type conduction of the ZnO single crystal. PL and OA results suggest that the as-grown and annealed ZnO samples with poor lattice perfection exhibit strong deep level green photoluminescence and weak ultraviolet luminescence. The deep level defect in as-grown ZnO is identified to be oxygen vacancy. After high-temperature annealing, the deep level photoluminescence is suppressed in ZnO crystal with good lattice perfection. In contrast, the photoluminescence is nearly unchanged or even enhanced in ZnO crystal with grain boundary or mosaic structure. This result indicates that a trapping effect of the defect exists at the grain boundary in ZnO single crystal. (C) 2007 Elsevier B.V. All rights reserved.

In situ preparation and luminescent properties of LaPO4:Ce3+, Tb3+ nanoparticles and transparent LaPO4:Ce3+, Tb3+/PMMA nanocomposite

LaPO4:Ce3+, Tb3+ nanoparticles were prepared by the reverse microemulsion with functional monomer, methyl methacrylate (MMA) as oil phase, and LaPO4:Ce3+, Tb3+/poly(methyl methacrylate) (PMMA) nanocomposite was obtained via polymerization of MMA monomer. The nanoparticles and nanocomposite have been well characterized by XRD, SEM, TEM, UV/vis spectrum, photoluminescence excitation and emission spectra and luminescence decays. The obtained solid nanocomposite LaPO4:Ce3+, Tb3+/PMMA is highly transparent and exhibits strong green photoluminescence upon UV excitation, due to the integration of luminescent LaPO4:Ce3+, Tb3+ nanoparticles. The luminescent lifetime of Tb3+ is determined to be 1.25 ms in the nanocomposite. (C) 2009 Elsevier Inc. All rights reserved.

Tunable photoluminescent and cathodoluminescent properties of ZnO and ZnO : Zn phosphors

ZnO and ZnO: Zn powder phosphors were prepared by the polyol-method followed by annealing in air and reducing gas, respectively. The samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), X-ray photoelectron spectra (XPS), electron paramagnetic resonance (EPR), and photoluminescence (PL) and cathodoluminescence ( CL) spectra, respectively. The results indicate that all samples are in agreement with the hexagonal structure of the ZnO phase and the particle sizes are in the range of 1-2 mu m. The PL and CL spectra of ZnO powders annealed at 950 degrees C in air consist of a weak ultraviolet emission band ( similar to 390 nm) and a broad emission band centered at about 527 nm, exhibiting yellow emission color to the naked eyes. When the sample was reduced at the temperatures from 500 to 1050 degrees C, the yellow emission decreased gradually and disappeared completely at 800 degrees C, whereas the ultraviolet emission band became the strongest. Above this temperature, the green emission ( similar to 500 nm) appeared and increased with increasing of reducing temperatures.

Strutural and optical approach of CdS@ZnS core-shell system

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Photoluminescent properties of lead zirconate powders obtained by the polymeric precursor method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Entwicklung neuartiger stickstoffreicher Polyphenylene

Im Rahmen dieser Arbeit wurden Darstellung und elektronische Anwendungsmöglichkeiten von neuartigen stickstoff- und damit elektronenreichen Poly(para-phenylenen) untersucht. Der Teilbereich „Polycarbazole“ befasst sich mit der Synthese von konjugierten (Stufen)leiterpolymeren auf der Basis von Carbazol. Dazu wurde ein neuer und effizienter Syntheseweg zur Gewinnung von 2,7-Dibromcarbazol entwickelt. Durch die weitere Funktionalisierung von 2,7-Dibromcarbazol gelang es, elektronenreiche Leiterpolymere zu gewinnen, die eine grüne Emissionsfarbe aufwiesen. Mit der Verwendung von R = 2-Decyltetradecyl als löslichkeitsfördernder Seitenkette in einem Poly(2,7-carbazol) konnte erstmals ein hochmolekulares Polycarbazol gewonnen werden. Dieses gut lösliche Poly(2,7-carbazol) erwies sich als ein exzellentes Donatormaterial in Solarzellen, welches in Kombination mit dem Farbstoff PDI eine effiziente Solarzelle ergab. Eine OLED mit einem neuartigen arylierten Polycarbazol als Emittermaterial zeigte eine sehr niedrige Turn-on-Spannung und eine intensive blaue EL-Emission. Das Kapitel über imidazolhaltige Poly(para-phenylene) und Discoten stellt die Darstellung von planarisierten Bisimidazolen vor, welche in hohen Ausbeuten durch eine intramolekulare Buchwald-Reaktion zwischen den Imidazolringen und der zentralen Terphenyleinheit durchgeführte wurde. Die dreistufige Darstellung der Discoten aus einem Terephthalaldehyd-Derivat und einem Benzil erlaubt eine einfache sowie variable Einführung von löslichkeitsfördernden Alkylsubstituenten. Auf diese Weise ist der Zugang zu einer völlig neuartigen Klasse an discotischen Materialien möglich, die eine Kombination aus Discoten auf der Basis von Benzolringen (wie z.B. HBC) mit Heteroaromaten darstellen. Die gewonnenen scheibenförmigen Bisimidazole wiesen dementsprechend auf Selbstanordnung zurückzuführende kolumnare Anordnungen und hexagonale Überstrukturen auf. Im dritten Themengebiet wird der Einbau eines Phthalimidchromophors direkt in das Rückgrad von Polyanilin vorgestellt. Da jegliche Veränderung des Oxidationsgrades zu einer unterschiedlichen Donatorfähigkeit des Polyanilinhauptkette führt, variiert in Abhängigkeit davon das Absorptionsverhalten des eingebauten Farbstoffes. Durch die Einführung des Phthalimidchromophores war es zudem möglich, ein leitfähiges Polymer zu erhalten, das im Gegensatz zum nicht-fluoreszierenden Polyanilin eine intensive gelbe Fluoreszenz (lmax = 547 nm) aufweist.