Unusual carrier thermalization in a dilute GaAs1-xNx alloy

Photoluminescence (PL) properties of the E-0, E-0+Delta(0), and E+ bands in an x=0.62% GaAs1-xNx alloy were investigated in detail, including their peak position, linewidth, and line shape dependences on the excitation energy, excitation power, and temperature, using micro-PL. The hot electrons within the E+ band are found to exhibit highly unusual thermalization, which results in a large blueshift in its PL peak energy by >2k(B)T, suggesting peculiar density of states and carrier dynamics of the E+ band.

Photoluminescence from the nitrogen-perturbed above-bandgap states in dilute GaAs1-xNx alloys: A microphotoluminescence study

Using microphotoluminescence (mu-PL), in dilute N GaAs1-xNx alloys, we observe a PL band far above the bandgap E-0 with its peak energy following the so-called E+ transition, but with contribution from perturbed GaAs host states in a broad spectral range (> 100 meV). This finding is in sharp contrast to the general understanding that E+ is associated with a well-defined conduction band level (either L-1c or N-x). Beyond this insight regarding the strong perturbation of the GaAs band structure caused by N incorporation, we demonstrate that a small amount of isoelectronic doping in conjunction with mu-PL allows direct observation of above-bandgap transitions that are not usually accessible by PL.

Lifetime study of N impurity states in GaAs1-xNx (x=0.1%) under hydrostatic pressure

The lifetimes of a series of N-related photoluminescence lines (A(2)-A(6)) in GaAs1-xNx (x=0.1%) were studied under hydrostatic pressures at similar to 30 K. The lifetimes of A(5) and A(6) were found to increase rapidly with increasing pressure: from 2.1 ns at 0 GPa to more than 20 ns at 0.92 GPa for A(5) and from 3.2 ns at 0.63 GPa to 10.8 ns at 0.92 GPa for A(6). The lifetime is found to be closely correlated with the binding energy of the N impurity states, which is shown either in the pressure dependence for a given emission line or in the lifetime variation from A(2) to A(6). (c) 2006 American Institute of Physics.

Selectively excited photoluminescence of GaAs1-xNx single quantum wells

GaAsN bulk and GaAsN/GaAs single quantum wells grown by molecular beam epitaxy are studied by selectively excited photoluminescence (PL) measurements. A significant difference is observed in the PL spectra when the excitation energy is set below or above the band gap of GaAs for the GaAsN/GaAs quantum well samples, while the spectral features of GaAsN bulk are not sensitive to the excitation energy. The observed difference in PL of the GaAsN/GaAs quantum well samples is attributed to the exciton localization effect at the GaAsN/GaAs interfaces, which is directly correlated with the transfer and trap processes of the photogenerated carriers from GaAs into GaAsN through the heterointerfaces. This interface-related exciton localization effect can be greatly reduced by a rapid thermal annealing process, making the PL be dominated by the intrinsic delocalized transition in GaAsN/GaAs. (C) 2003 American Institute of Physics.

Alloy states in dilute GaAs1-xNx alloys (x < 1%)

A set of GaAs1-xNx samples with small nitrogen composition (x<1%) were investigated by continuous-wave photoluminescence (PL), pulse-wave excitation PL, and time-resolved PL. In the PL spectra, an extra transition located at the higher-energy side of the commonly reported N-related emissions was observed. By measuring the PL dependence on temperature and excitation power, the PL peak was identified as a transition of alloy band edge-related recombination in GaAsN. The PL dynamics further confirms its intrinsic nature as being associated with the band edge rather than N-related bound states. (C) 2003 American Institute of Physics.

Electron spin quantum beats and room temperature g factor in GaAsN

We report on the investigation of electron spin quantum beats at room temperature in GaAsN thin films by time-resolved Kerr rotation technique. The measurement of the quantum beats, which originate from the Larmor precession of electron spins in external transverse magnetic field, yields an accurate determination of the conduction electron g factor. We show that the g factor of GaAs1-xNx thin films is significantly changed by the introduction of a small nitrogen fraction.

Phonon-induced Raman scattering in GaNAs

The Raman scattering spectra of MBE-grown GaNAs epilayers were investigated. The resonant enhancement of Raman scattering due to the E+ states in the conduction band was observed and the Raman peaks related to the phonons at non-Gamma points of the Brillouin Zone were detected. II was clearly seen that the local vibrational mode induced by nitrogen impurities evolves to the GaN-like lattice phonon mode when the nitrogen content increases. By comparing the Raman spectra measured before and after 850 degreesC rapid thermal annealing, it was tentatively suggested that two weak peaks were induced by the pairing or clustering effect of nitrogen.

X-ray double-crystal characterization of the strain relaxation in GaAs/GaNxAs1-x/GaAs(001) sandwiched structures

An X-ray diffraction method, estimating the strain relaxation in an ultrathin layer, has been discussed by using kinematic and dynamical X-ray diffraction (XRD) theory. The characteristic parameter Delta Omega, used as the criterion of the strain relaxation in ultrathin layers, is deduced theoretically. It reveals that Delta Omega should be independent of the layer thickness in a coherently strained layer. By this method, we characterized our ultrathin GaNxAs1-x samples with N contents up to 5%. XRD measurements show that our GaNxAs1-x layers are coherently strained on GaAs even for such a large amount of N. Furthermore, a series of GaNxAs1-x samples with same N contents but different layer thicknesses were also characterized. It was found that the critical thickness (L-c) of GaNAs in the GaAs/GaNAs/GaAs structures determined by XRD measurement was 10 times smaller than the theoretical predictions based on the Matthews and Blakeslee model. This result was also confirmed by in situ observation of reflection high-energy electron diffraction (RHEED) and photoluminescence (PL) measurements. RHEED observation showed that the growth mode of GaNAs layer changed from 2D- to 3D-mode as the layer thickness exceeded L-c. PL measurements showed that the optical properties of GaNAs layers deteriorated rapidly as the layer thickness exceeded L-c. (C) 2000 Elsevier Science B.V. All rights reserved.

Epitaxial growth of GaNAs/GaAs heterostructure materials

A series of systematic experiments on the growth of high quality GaNAs strained layers on GaAs (001) substrate have been carried out by using DC active Nz plasma, assisted molecular beam epitaxy. The samples of GaNAs between 3 and 200 nm thick were evaluated by double crystal X-ray diffraction (XRD) and photoluminescence (PL) measurements. PL and XRD measurements for these samples are in good agreement. Some material growth and structure parameters affecting the properties of GaNAs/GaAs heterostructure were studied; they were: (1) growth temperature of GaNAs epilayer; (2) electrical current of active N-2 plasma; (3) Nz flow rate; (4) GaNAs growth rate; (5) the thickness of GaNAs strained layer. XRD and PL measurements showed that superlattice with distinct satellite peaks up to two orders and quantum well structure with intensity at 22 meV Fourier transform infrared spectroscopy (FWHM) can be achieved in molecular beam epitaxy (MBE) system. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

Growth and characterization of strained superlattices delta-GaNxAs1-x/GaAs by molecular beam epitaxy

A series of superlattices delta-GaNxAs1-x/GaAs were grown by a DC plasma-N-2-assisted molecular beam epitaxy. The evolution of the surface reconstruction during the growth has been studied with the use of in situ reflection high-energy electron diffraction. The superlattices have been characterized by high-resolution X-ray diffraction measurements. Distinct satellite peaks indicate that the superlattices are of good quality. The N compositions in strained GaNxAs1-x monolayers are obtained from the dynamical simulations of the measured X-ray diffraction patterns. The periodicity fluctuations of N composition are obtained from a kinematical method dependent on the broadening of the satellite peaks of the X-ray diffraction. (C) 2000 Elsevier Science B.V. All rights reserved.

Band crossing in isovalent semiconductor alloys with large size mismatch: First-principles calculations of the electronic structure of Bi and N incorporated GaAs

For large size- and chemical-mismatched isovalent semiconductor alloys, such as N and Bi substitution on As sites in GaAs, isovalent defect levels or defect bands are introduced. The evolution of the defect states as a function of the alloy concentration is usually described by the popular phenomenological band anticrossing (BAC) model. Using first-principles band-structure calculations we show that at the impurity limit the N-(Bi)-induced impurity level is above (below) the conduction- (valence-) band edge of GaAs. These trends reverse at high concentration, i.e., the conduction-band edge of GaAs1-xNx becomes an N-derived state and the valence-band edge of GaAs1-xBix becomes a Bi-derived state, as expected from their band characters. We show that this band crossing phenomenon cannot be described by the popular BAC model but can be naturally explained by a simple band broadening picture.

Optical study of localized and delocalized states in GaAsN/GaAs

Taking advantages of short pulse excitation and time-resolved photoluminescence (PL), we have studied the exciton localization effect in a number of GaAsN alloys and GaAsN/GaAs quantum wells (QWs). In the PL spectra, an extra transition located at the higher energy side of the commonly reported N-related emissions is observed. By measuring PL dependence on temperature and excitation power along with PL dynamics study, the new PL peak has been identified as a transition of the band edge-related recombination in dilute GaAsN alloy and delocalized transition in QWs. Using selective excitation PL we further attribute the localized emission in QWs to the excitons localized at the GaAsN/GaAs interfaces. This interface-related exciton localization could be greatly reduced by a rapid thermal annealing.

Optical study of electronic states in GaAsN

GaAs1-xNx alloys with small N composition (x<1%) and GaAsN/GaAs quantum wells (QWs) were studied by continuous wave photoluminescence (PL), pulse wave excitaiton PL and time-resolved PL. In the PL spectra an extra transition located at the higher energy side of the commonly reported N-related emissions was observed. By measuring the PL dependence on temperature and excitation power, the new PL peak was identified as a transition of alloy band edge-related recombination in GaAsN and delocalized transition in QWs. The PL dynamics further confirms its intrinsic nature of band edge states rather than N-related bound states.

Epitaxial growth of GaNAs/GaAs heterostructure materials

A series of systematic experiments on the growth of high quality GaNAs strained layers on GaAs (001) substrate have been carried out by using DC active Nz plasma, assisted molecular beam epitaxy. The samples of GaNAs between 3 and 200 nm thick were evaluated by double crystal X-ray diffraction (XRD) and photoluminescence (PL) measurements. PL and XRD measurements for these samples are in good agreement. Some material growth and structure parameters affecting the properties of GaNAs/GaAs heterostructure were studied; they were: (1) growth temperature of GaNAs epilayer; (2) electrical current of active N-2 plasma; (3) Nz flow rate; (4) GaNAs growth rate; (5) the thickness of GaNAs strained layer. XRD and PL measurements showed that superlattice with distinct satellite peaks up to two orders and quantum well structure with intensity at 22 meV Fourier transform infrared spectroscopy (FWHM) can be achieved in molecular beam epitaxy (MBE) system. (C) 2000 Published by Elsevier Science S.A. All rights reserved.

Metalorganic chemical vapor deposition of GaAsN epilayers: microstructures and optical properties

In this article, we investigate the parameters used in the MOCVD growth of GaAsN epilayers on GaAs substrates and some of their microstructures and optical properties. The N incorporation was found to mainly depend on the growth temperature and the fractional 1,1-dimethylhydrazine molar flow. A thin highly strained interface layer was observed between GaAsN and GaAs, which, contrary to previously published results, was not N enriched. The low-temperature (10 K) photoluminescence spectra were composed of several emissions that we attribute to a combination of interband transition and transitions involving localized defect states. (C) 2004 Elsevier B.V. All rights reserved.