Shear bond strength fatigue limit of rest seats made with dental restoratives

Purpose: This study compared the shear bond strength (SBS) to enamel of rest seats made with a glass-ionomer cement (Fuji IX GP Fast), a resin-modified glass-ionomer cement (Fuji II LC), and a composite resin (Z100 MP) under monotonic and cyclic loading. Materials and Methods: Rest seats were built up onto the lingual surfaces of 80 intact human mandibular incisors. Specimens (n=10) were stored in distilled water at 37°C for 30 days and subjected to shear forces in a universal testing machine (0.5 mm/min) until fracture. The SBS values were calculated (MPa) using the bonding area (9.62 mm2) delimited by adhesive tags. A staircase approach was used to determine the SBS fatigue limit of each material. Specimens were submitted to either 10,000 cycles (5 Hz) or until specimen fracture. A minimum of 15 specimens was tested for each material. Scanning electron microscopy was used to examine the mode of failure. Data were statistically analyzed with one-way ANOVA and Tukey HSD tests (α = 0.05). Results: Z100 MP yielded higher (p < 0.05) SBS (12.25 MPa) than Fuji IX GP Fast (7.21 MPa). No differences were found between Fuji II LC (10.29 MPa) and the other two materials (p > 0.05). Fuji II LC (6.54 MPa) and Z100 MP (6.26 MPa) had a similar SBS limit. Fuji IX GP Fast promoted the lowest (p < 0.05) SBS fatigue limit (2.33 MPa). All samples showed cohesive failure patterns. Conclusion: Fatigue testing can provide a better means of estimating the performance of rest seats made with dental restoratives.

Aspecto histológico do esmalte decíduo e influência do material restaurador após a indução de formação de lesão artificial de cárie por diferentes métodos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Comportamento do esmalte de dentes decíduos após desafio desmineralizante em função de materiais restauradores: estudo ao microscópio de luz polarizada

Pós-graduação em Biopatologia Bucal - ICT

Shear bond strengths of glass-ionomer cements to sound and to prepared carious dentine

The aim of this study was determine whether bonding of glass-ionomer cements to non-carious dentine differed from that to carious dentine. Five commercial cements were used, namely Fuji IX GP, Fuji IX capsulated, Fuji IX Fast capsulated (all GC, Japan), Ketac-Molar and Ketac-Molar Aplicap (both 3M-ESPE, Germany). Following conditioning of the substrate with 10% poly (acrylic acid) for 10 s, sets of 10 samples of the cements were bonded to prepared teeth that had been removed for orthodontic reasons. The teeth used had either sound dentine or sclerotic dentine. Shear bond strengths were determined following 24 h storage. For the auto-mixed cements, shear bond strength to sound dentine was found not to differ statistically from shear bond strength to sclerotic dentine whereas for hand-mixed cements, shear bond to sound dentine was found to be higher than to carious dentine (to at least p < 0.05). This shows that the chemical effects arising from interactions of glass-ionomer cements with the mineral phase of the tooth are the most important in developing strong bonds, at least in the shorter term.

In vitro cytotoxicity of five glass-ionomer cements

To evaluate the cytotoxic effects of five glass-ionomer cements (GICs) on an odontoblast cell line (MDPC-23), disks of every material were prepared and divided into Group 1: Vitrebond, Group 2: Vitremer, Group 3: Fuji IILC, Group 4: Fuji IX GP, Group 5: Ketac-Molar, Group 6: Z-100 (positive control). In Group 7, phosphate-buffered saline solution (negative control) was applied on filter paper. After placing the samples in the bottom of wells, the cells (30,000 cells/cm(2)) were plated and incubated for 72 h. The cell number was counted, the cell morphology was assessed by scanning electron microscopy and the cell metabolism was evaluated using methyltetrazolium assay. The statistical analysis of Kruskal-Wallis was used to determine if the scores obtained for the cell metabolism and number of cells were different at the 95% confidence level. In groups 1, 2, 3, 4, 5, and 6 the materials decreased the cell number by 74.5% 75.5%, 45.5%, 29.5%, 32.5%, and 88.5%, respectively. In groups 1, 2, 3, 4, and 5, the experimental GICs reduced the cell metabolism by 79%, 84%, 54%, 40%, and 42.5%, respectively. Despite the fact that all experimental materials were cytotoxic to the MDPC-23 cells, the GICs were the least cytotoxic. on the other hand, the RMGICs caused the highest cytophatic effects. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

Effect of Ultrasonic Excitation on the Porosity of Glass Ionomer Cement: A Scanning Electron Microscope Evaluation

Background: Ultrasonic excitation (US) was applied to glass ionomer cement (GIC) during early set time to increase the advantageous properties of this material. Purpose: The aim of this in vitro study was to assess the inner porosity of GIC after US. Study design: A total of 16 specimens, for each material, were prepared from high-viscosity GIC Fuji IX GP, Ketac Molar, and Ketac Molar Easymix. Half of these specimens (n = 8) received 30 s of US during the initial cement setting. After completion of the material setting, specimens were fractured and observed by scanning electronic microscopy to quantitatively assay porosity inside the material using Image J software. Results: Statistical data analysis revealed that US reduced the porosity for all tested materials (P <= 0.05). The following reductions (expressed in percentages) were achieved: Fuji IX-from 3.9% to 2.8%; Ketac Molar Easy Mix-from 4.4% to 2.6%, and Ketac Molar-from 2.4% to 1.6%. Conclusion: Under the tested conditions, US was an effective method for porosity reduction inside the material. Microsc. Res. Tech. 74:54-57, 2011. (C) 2010 Wiley-Liss, Inc.

EFFECT of ULTRASONIC EXCITATION on THE MICROTENSILE BOND STRENGTH of GLASS IONOMER CEMENTS TO DENTIN AFTER DIFFERENT WATER STORAGE TIMES

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Características bioquímicas e microbiológicas do biofilme dentário formado in situ sobre materiais que contêm flúor ou fosfato de cálcio amorfo

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Aplicação de ondas de ultra-som sobre cimentos de ionômero de vidro: rugosidade superficial e perda de massa após ensaio de escovação

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Efeito da excitação ultrasônica na resistência máxima à tração e de união à dentina de cimentos de ionômero de vidro, após diferentes períodos de armazenamento

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Biochemical and microbiological characteristics of in situ biofilm formed on materials containing fluoride or amorphous calcium phosphate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação da aplicação de ondas de ultra-som sobre cimentos de ionômero de vidro: rugosidade superficial e dureza

The application of ultrasonic waves during the initial setting of the glass ionomer cements (GIC) has demonstrated increase of the cure speed, reduction of air bubbles and improves in some mechanical properties. The aim of this study was to evaluate the effect of the ultrasound on the microhardness and the superficial roughness in two GICs (FUJI IX GP (GC Corporation) and Ketac Molar EasyMix (3M ESPE)). Forty specimens were confectioned, twenty for evaluation of the superficial roughness and twenty for evaluation of the microhardness. Half of them received for thirty seconds the ultrasonic waves application. The readings of the roughness had been carried before and after the toothbrushing test. The twenty remaining specimens had been polished with abrasive sandpapers of decreasing granulations and submitted to the hardness test. The results, analyzed for the variance analysis (ANOVA) (p<0,05), had demonstrated increase of the hardness for all the groups with the application of ultrasonic waves, being bigger for the Ketac Molar EasyMix. The ultrasound application also caused significant reduction of the superficial roughness for the Ketac Molar EasyMix. After the toothbrushing test, this last property increased for all the materials. It could be concluded that the application of ultrasonic waves was effective in increasing the superficial hardness of the materials and that it improved the roughness of the Ketac Molar EasyMix before the toothbrushing test.

Effect of ultrasonic ecxitation on the ultimate tensili strength of glass ionomer cements after different water storage times

The application of ultrasound waves with a conventional dental ultrasonic scaler on glass ionomer cements surface accelerated initial setting reaction and improved the mechanical properties. Objective: This study evaluated the ultimate tensile strength of glass ionomer cements after ultrasonic excitation and different water storage times. Material and method: Twelve specimens of each material (Fuji IX GP, Ketac Molar Easymix and Vitremer) were prepared, and six of each received a 30-second ultrasound application during initial setting of the cements. After storage of the 24 hours or 30 days, the specimens were sectioned into stick to microtensile testing and the mean ultimate tensile strength values were submitted to Welch’s ANOVA and Tamhane’s test. Result: The results showed that the Vitremer presented the highest mean tensile strength. The chemically set Fuji IX GP presented significantly higher mean tensile strength after 30 days than after 24 hours of storage (p < 0.05). At 24 hours, the ultrasonically set Fuji IX GP presented significantly higher mean tensile strength than their counterparts set under standard conditions (p < 0.05). Conclusion: Treatment with ultrasound increased the tensile strength of Fuji IX GP in the early period of maturation.

Kinetic studies of the effect of varnish on water loss by glass-ionomer cements

OBJECTIVES: This paper reports a study of the water loss behaviour of two commercial glass-ionomer cements coated with varnishes. METHODS: For each cement (Fuji IX Fast or Chemflex), specimens (6mmdiameterx2mm depth) were prepared and cured for 10min at 37 degrees C. They were exposed to a desiccating environment over H(2)SO(4) either uncoated or coated with the appropriate varnish (Fuji Varnish, a solvent-based lacquer, or Fuji Coat, a light-cured varnish). Four specimens were prepared for each material. They were weighed at hourly intervals for 6h, daily for up to 5 days, then weekly thereafter until equilibration. RESULTS: Unlike the uncoated specimens, water loss from varnished cements was not Fickian, but followed the form: mass loss=A/t+B, where t is time, A and B are constants specific to each cement/varnish combination. A varied from 1.22 to 1.30 (mean 1.26, standard deviation 0.04), whereas B varied from 1.54 to 2.09 (mean -1.83, standard deviation 0.29). At equilibrium, varnished specimens lost much less water than unvarnished ones (p>0.01) but there was no significant difference between the solvent-based and the light-cured varnishes. SIGNIFICANCE: Varnishes protect immature glass-ionomer cements from drying out by altering the mechanism of water loss. This slows the rate of drying but does not necessarily change the total amount of water retained. It confirms that, in clinical use, glass-ionomer restoratives should be varnished to allow them to mature satisfactorily.

Avaliação da microinfiltração marginal em cavidades classe II de molares decíduos restauradas com diferentes cimentos de ionômero de vidro

O objetivo desta pesquisa foi avaliar a microinfiltração em restaurações classe II realizadas com diferentes cimentos de ionômero de vidros em molares decíduos. Para tal, foram selecionados quarenta molares decíduos humanos a partir de um Banco de Dentes. Nas faces mesial e distal de cada dente foram preparadas cavidades classe II com dimensões padronizadas. Em seguida, os dentes foram divididos em oito grupos experimentais correspondentes ao material restaurador utilizado: grupo MXR (Maxxion R); grupo VDR (Vidrion R); grupo VTR (Vitremer); grupo VTF (Vitro Fill LC); grupo FUJ (Fuji IX); grupo KTM (Ketac Molar); grupo VMO (Vitro Molar); grupo MGS (Magic Glass ART). Ao término de vinte e quatro horas de imersão em água destilada, os dentes foram mantidos em solução de nitrato de prata a 50% pelo mesmo período e, então, em solução reveladora de radiografias (hidroquinona, Kodak) por quinze minutos. Os dentes foram então seccionados através do centro das restaurações, e observados em lupa estereoscópica sob o aumento de quarenta vezes. A microinfiltração foi graduada co base em escores relacionados à penetração do nitrato de prata na interface adesiva. Os resultados, após submetidos à análise estatística, demonstraram que nenhum dos materiais testados impediu completamente a microinfiltração. No entanto, o Vitremer apresentou os escores mais baixos, seguido do Ketac Molar e do Fuji IX. Os materiais Magic Glass ART, Vitro Molar, Vitro Fill LC e Vidrion R apresentaram comportamento intermediário em relação aos demais, enquanto o Maxxion R apresentou os piores resultados. Com base na metodologia empregada e nos resultados obtidos, pode-se concluir que nenhum dos materiais testados foi capaz de impedir completamente a microinfiltração, apesar de apresentarem graus varáveis de suscetibilidade a esse fenômeno, destacando-se, entre eles o Vitremer, o Ketac Molar e o Fuji IX por apresentarem baixos níveis de microinfiltração, seguidos do Magic Glass ART, Vitro Molar, Vitro Fill LC e Vidrion R. Em contrapartida, o Maxxion R apresentou os piores resultados, fato constatado pelos altos escores de microinfiltração registrados.