Estudo da flamabilidade e resistência à chama de compósito de poliéster insaturado e fibra da folha do abacaxizeiro (PALF)

In the present research work, composites were prepared using pine apple leaf fibres (PALF) as reinforcement with unsaturated polyester resin as matrix, incorporating with fire retardant at different compositions. The PALF was obtained from the decortication of pine apple leaves obtained from Ramada 4 from Ielmo Marinho in the State of Rio Grande do Norte. The unsaturated polyester resin and the catalyzer were bought from the local establishment. The fire retardant, aluminium tri-hydroxide - Al(OH)3 was donated by Alcoa Alumínio S.A and was used in the proportions of 20%, 40% and 60% w/w. Initially the fibres were treated with 2% NaOH for 1 hour, to remove any impurities present on the fibre surface, such as wax, fat, pectin and pectate, in order to have a better adsorption of the fibres with the matrix as well as the flame retardant. The fibre mat was prepared in a mat preparator by immersion, developed in the Textile Engineering Laboratory, at the UFRN. The composites (300x300x3 mm) were prepared by compression molding and the samples (150x25x3 mm) for analysis of the properties were cut randomly using a laser cutter. Some of the cut samples were used to measure the smoke emission and fire resistance using UL94 standard. Mechanical tension-extension and flexural properties were carried in CTGás RN and the Laboratório de Metais e Ensaios Mecânicos Engenharia de Materiais UFRN , as well as SEM studies were carried out at Núcleo de Estudos em Petróleo e Gás Natural - UFRN . From the observed results, it was noted that, there was no marked influence of the fire retardant on the mechanical properties. Also in the water absorption test, the quantity of water absorbed was less in the sample with higher concentration of fire retardant. It was also observed that the increase in the proportion of the fire retardant increased the time of burning, may be due to the compactness of the composite due to the presence of fire retardant as a filling material even though it was meant to reduce the rate of inflammability of the composite

Comportamento mecânico e de flamabilidade de compósito de polipropileno reclicado com fibra de coco e hidróxido de alumínio

A reciclagem de plásticos tem sido uma possibilidade interessante para minimizar o problema de destino dos resíduos plásticos. O polipropileno (PP) está entre os tipos de polímeros de maior consumo, portanto a reutilização deste material tem possibilitado o desenvolvimento de estudos de grande relevância científica e social. Este polímero apresenta excelente relação custo/benefício, além de ser facilmente conformável e exibir propriedades mecânicas que o torna útil em várias aplicações. Entretanto, esse material ao ser queimado gera produtos que agem como combustíveis de modo que, para alguns usos, boa resistência à chama é necessária. Isso pode ser obtido pela adição de retardante de chama, que tem o propósito de aumentar a resistência desse material à ignição e, ao mesmo tempo, reduzir a velocidade de propagação da chama. O hidróxido de alumínio, ou simplesmente hidrato de alumina, é o agente retardante de chama mais utilizado no mercado, pois, age também como supressor de fumaça e não libera gases tóxicos durante a queima. No entanto, para tais propriedades, altas concentrações de alumina hidratada são necessárias. Isto causa deterioração nas propriedades físicas dos materiais, por não ter caráter reforçante. As fibras naturais possuem boa capacidade de reforço quando combinadas adequadamente com polímeros. Apresentando também vantagens como baixo custo, baixa densidade, biodegradabilidade e na combustão não emana gases tóxicos. Neste trabalho, misturas contendo alumina hidratada e fibras de coco foram incorporadas ao polipropileno com o objetivo de se encontrar um balanço adequado de propriedades para utilização deste compósito com características de resistência à chama e desempenho mecânico. Os compósitos foram moldados por compressão a quente e caracterizados por IV, DRX, MEV, testes mecânicos e de inflamabilidade. Foi observado aumento no módulo de elasticidade dos compósitos em geral, bem como aumento na resistência a tenacidade do compósito PP/fibra de coco em relação ao PP puro. Os resultados indicaram a eficiência da alumina hidratada como antichama, em todos os compósitos, exceto PP/F, classificando os materiais como V-0 segundo a norma internacional UL 94V.

Influência do retardante de chamas nas propriedades mecânicas e flamabilidade em compósitos poliméricos de epóxi/fibra de curauá

Currently, there is a great search for materials derived from renewable sources. The vegetable fibers as reinforcement for polymer matrixes, has been used as an alternative to replace synthetic fibres, being biodegradable and of low cost. The present work aims to develop a composite material with epoxy resin reinforced with curauá fibre with the addition of alumina trihydrate (aluminum hydroxide, Al(OH)3) as a flame retardant, which was used in proportions of 10 %, 20% and 30% of the total volume of the composite. The curauá fibers have gone through a cleaning process with an alkaline bath of sodium hydroxide (NaOH ), parallelized by hand and cut carding according to the default length . They were molded composites with fibers 30cm. Composites were molded in a Lossy Mold with unidirectional fibres in the proportion of 20% of the total volume of the composite. The composites were prepared in the Chemical Processing Laboratory of the Textile Engineering Department at UFRN. To measure the performance of the material, tests for the resistance to traction and flexion were carried out. with samples that were later analyzed in the Electronic Microscopy Apparatus (SEM ). The composites showed good mechanical properties by the addition of flame retardant and in some cases, leaving the composite more vulnerable to breakage. These mechanical results were analyzed by chi-square statistical test at the 5% significance level to check for possible differences between the composite groups. Flammability testing was conducted based on the standard Underwriters Laboratory 94 and the material showed a satisfactory result taking their average burn rate (mm / min) decreasing with increasing addition of the flame retardant composite.

Florística e estrutura de comunidades arbóreas em cerrados de Rondônia,Brasil

O cerrado constitui o segundo maior e mais diverso bioma brasileiro, configurando um heterogêneo mosaico fisionômico e florístico. Mais de seis mil espécies de fanerógamas são reportadas para o cerrado do Brasil Central. Este trabalho teve o objetivo de descrever e analisar a flora e a estrutura de quatro comunidades de árvores dos cerrados sensu latu do município de Vilhena, Rondônia, Brasil. As áreas estudadas foram: cerradão (Área 1), campo sujo (Área 2) e duas comunidades do cerrado sensu stricto (Áreas 3 e 4). Em cada área foi posicionado aleatoriamente um transecto de 10 x 1000 m (1 ha), dividido em 100 parcelas de 10 X 10 m. Todas as plantas vivas e mortas com circunferência do tronco e" 10 cm ao nível do solo foram registradas. O cerradão apresentou a maior riqueza específica, estrutura de tamanho e área basal. As percentagens de árvores mortas foram mais altas nas áreas de cerradão e campo sujo, com ocorrência de fogo recente. As famílias mais importantes foram Vochysiaceae, Ochnaceae, Clusiaceae, Malpighiaceae e Melastomataceae. As espécies mais importantes foram Qualea multiflora, Byrsonima crassifolia (área 1), Eugenia sp., Miconia sp.1 (área 2), Ouratea hexasperma, Caraipa savannarum (área 3), Ouratea hexasperma, Pouteria sp.3 (área 4). A maioria das espécies ocorre somente em uma área, sugerindo que a priorização de áreas para conservação deve envolver todo o mosaico de cerrados existentes. A mortalidade associada ao fogo é diferenciada entre as áreas, talvez induzida pelo grau de flamabilidade, recorrência do fogo e de fatores históricos do uso da terra.