Perdas na colheita e qualidade da fibra de cultivares de algodão adensado em função de sistemas de colheita

Pós-graduação em Agronomia (Energia na Agricultura) - FCA

Avaliação da degradação fotoquímica de corante alimentício e lixiviação de corantes têxteis de fibras de algodão expostos a suor sintético por método cromatográficos

Pós-graduação em Química - IQ

Reciclagem de poliestireno expandido: compósito com fibras de algodão para a confecção de placas de circuito impresso

In this work polymeric composites reinforced with cotton fibers, from the textile industry, were developed in order to manufacture printed circuit boards. It was used expanded polystyrene (EPS) as a thermoplastic matrix by melting it. For the obtention of 10% and 15% of fiber volume fraction in cotton fibers composites, it was used wasted cotton fibers as an incentive of recycling and reusing of the domestic and industrial wastes as well as for Expanded Polystyrene(EPS). The mechanical properties of the composites were evaluated by tensile and flexural strength from standardized test methods. Composites were characterized by a Scanning Electron Microscopy (SEM), Thermogravimetry (TG/DTG), Differential Scanning Calorimetry (DSC) and dielectric analysis. The analysis of the results showed that fiber in the composite directly influenced in the thermal and mechanical properties

Cinética e modelação da secagem convectiva de papel obtido a partir de fibras de algodão

No presente trabalho pretende-se caraterizar a cinética de secagem de papel obtido partir de fibra de algodão. A componente experimental é executada com recurso a uma estação de secagem, munida com equipamentos de controlo e de leitura. O objetivo é realizar a análise da cinética de secagem, com base nas condições impostas através dos parâmetros de entrada, temperatura a humidade relativa e velocidade do ar de secagem. Os resultados permitem determinar a influência dos parâmetros temperatura, humidade relativa, velocidade do escoamento e espessura do material sobre a cinética de secagem. Foi determinada a difusividade em cada ensaio e desenvolvido e validado um modelo matemático de secagem, com recurso aos valores obtidos experimentalmente. A modelação da secagem é realizada através de um modelo que recorre à segunda lei de Fick. São apresentados os resultados da modelação e respetivos desvio padrão relativamente aos valores experimentais.

Controle de plantas daninhas com cyanazine aplicado em mistura com outros herbicidas, na cultura do algodão (Gossypium hirsutum L.)

Com a finalidade de estudar a mistura de tanque mais eficiente com cyanazine em aplicação de pré-emergência na cultura algodoeira (Gossypium hirsutum L.) , foram estudados os seguintes tratamentos: cyanazine + diuron nas doses de 0,8 + 0,8 kg i.a/ha e 1,0 + 1,0 kg i.a/ha; cyanazine+ oryzalin , nas do sés de 1,2 + 0,8 kg i.a/ha e 1,6 + 1,2 kg i.a/h a; cyanazyne + metol a chlor, nas doses de 1,4 + 2,0 kg i.a/ha e 1,75 + 2,52 kg i.a/ ha;cianazine na dose de 1,75 kg i.a /ha; oryzalin na dose de 1,12 kg i.a/ha; metol achlor na dose de 2,52 kg i.a /ha e diuron na dose de 1,6 kg i.a /ha. Para efeito de comparação, utilizou-se uma testemunha sem capina e outra com capina manual. Nenhum tratamento apresentou injúria para as plantas de algodão e não houve diferenças significativas para o "stand" inicial. Já no "stand" final, a testemunha sem capina apresentou o menor número de plantas, sendo que não houve diferenças significativas dos outros tratamentos com a testemunha capinada. Para o rendimento, a mistura cyanazine + metolachior em ambas as doses estudadas, não apresentaram diferenças significativas da testemunha capinada. Quanto à altura da planta, peso de 100 sementes, porcentagem e índice de fibras não houve diferenças significativas entre os tratamentos estudados, somente o peso do capulho foi afetado pelo oryzalin. Pela avaliação visual (EWRC 1 a 9)*, os herbicidas apres entaram um controle satisfatório somente até os 30 dias após aplicação, sendo que a mistura cyanazine + metolachlor foi efici ente quanto a testemunha capinada. No controle da Portulaca oleracea , a mistura cyanazine + oryzalin na maior dose e oryzalin apresentaram 71,4% de controle ate os 30 dias e 79,4% e 82,4%, respectivamente, até 45 dias da aplicação. Para Amaranthus sp., à exceção da cyanazine e cyanazine + diuron nas doses menores, não apresentaram nenhum controle, sendo que os outros herbicidas controlaram com eficiência superior a 70%. Para Centratherium punctatum, o cyanazine apresentou 78,2% e 73,4%, respectivamente, após 50 e 45 dias da aplicação. Para Cyperus sp e & Brachiaria plantaginea, o metolachlor sozinho ou em mistura com cyanazine, apresentou uma eficiência de 90% para Cyperus sp. e de 70% para B. plantaginea até 45 dias da aplicação. Para as espécies não dominantes (maioria dicotiledôneas), o melhor controle foi de cyanazine + metol achlor na dose maior, com 70,5% e 60,2%, respectivamente, após 30 e 45 dias da aplicação. Para o total das espécies, cyanazine + metolachlor, em ambas doses estudadas, apresentaram controle de 66,2% e 67,3%, respectivamente, após 30 dias e 63,3% e 64,3%, respectivamente, após 45 dias da aplicação. Para as análises tecnológicas da fibra, não houve diferenças significativas na maturação da fibra, uniformidade de comprimento, índice Macronaire e índice Pressley. No comprimento da fibra, a mistura de cyanazine + diuron(0,8+ 0,8 kg ia/h a), apresentou o maior comprimento (26,1 mm) e cyanazine+ metol achlor (1,75 + 2,52 kg i.a / ha),o menor comprimento (24,9 mm), sem diferenças significativas com as testemunhas.

Vigor de sementes e desempenho agronômico de plantas de algodão

O vigor das sementes pode influenciar a emergência, o desempenho e produtividade das plantas, dependendo de cada espécie e de fatores ambientais. Dessa forma, um dos principais desafios das pesquisas com sementes é averiguar a influência do potencial fisiológico das sementes sobre o ciclo das plantas. O objetivo deste trabalho foi avaliar o efeito do vigor de sementes sobre as características morfofisiológicas de plantas de algodão, bem como, sobre o rendimento de caroço e de fibra. Três lotes de sementes da cultivar FMT 701 (safra 2005/2006) foram selecionados com base em resultados de testes realizados em laboratório. O efeito do vigor foi avaliado em campo, nas safras 2006/2007 e 2007/2008, no município de Jaciara, Mato Grosso. Determinou-se a porcentagem de plântulas emergidas, índice de velocidade de emergência, altura das plantas, número de ramos reprodutivos, número de nós, número de posições frutíferas, número de capulhos, rendimento de fibras e caroço. O desempenho inicial e reprodutivo de plantas de algodão em campo depende, além de outros fatores, do nível de vigor das sementes. Plantas com maior vigor apresentam maior rendimento de fibras e de caroço.

Sorção de petróleo por fibras vegetais

Nowadays, when accidents with oil tanker or shore tanks occur and there is oil spill, some arrangements are made in order to repress and to fix the situation. For the containment, barriers or detours are usually made of synthetic materials such as polyurethane foam. In order to clear water away, techniques like in loco burning, biodegradant agents, dispersant agents and sorbent materials application are used. The most of the sorbent materials are also synthetic and they are used because it is easy to store them and their availability in market. This dissertation introduces the study of vegetable fibers of pineapple leaf fibers (Ananas comosus (L.) Merr.), cotton fibers (Gossypium herbaceum L.), kapok fibers (Ceiba pentandra (L.) Gaertn.), curauá fibers (Ananas erectifolius L.B. Sm.) and sisal fibers (Agave sisalana Perrine) related to their capacity of sorption of oil in case of accidental spill in the ocean. This work evaluates the substitution possibility of synthetic materials by natural biodegradable materials with less cost

Extração, caracterização e aplicação do corante de urucum (Bixa orellana L.) no tingimento de fibras naturais

The increasing demand for natural dyes in place of synthetic ones is justified by the non-toxicity or low toxicity of the former. The synthetic dyes are associated with diseases like cancer as well as when released in the environment takes longer to degrade and the intermediates could be still more toxic. The Annatto (Bixa Orellana L.) is a carotenoid and one of the more important natural dyes used in the food industry. In the form of dye, it represents nearly 70% of the world natural dye production and 90% in Brazil. In the present work, annatto seeds were used of the species peruana paulista, which had nearly 2.1% of bixin. The process of dye extraction with ethyl alcohol showed 4% of dye in the form of powder with particle diameter of 28mm. The extraction process did not alter the chemical composition of the dye, which was confirmed by the electronic spectrum of absorption. Dyeings were carried out with different mordents to study the total colour difference as well as the wash fastness properties and friction fastness properties under wet and dry conditions. The samples treated with copper sulphate showed colour difference but at the same time showed better fastness results. The samples treated with resin (no formaldehyde) did not alter the colour significantly still better the fastness properties. From the results, it could be stated that the resin could be an alternative for heavy metallic mordents

Eficácia do cloridrato de tetraciclina em diversas concentrações na remoção de smear layer e exposição de fibras colágenas da superfície radicular

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Obtenção e caracterização de nanocelulose a partir de fibras de Chorisia speciosa St. Hil

Natural fibers have been highlighted as a renewable material that can replace materials from oil and its derivatives. In this context, Brazil becomes the perfect setting because of the diversity of fibers found in its territory, such as sugarcane, sisal, rice, cotton, coconut, pineapple, among others. The paineiras (Chorisia speciosa St. Hil) are typically Brazilian trees, which produce paina as fruit. These fruits are still little studied as a source of lignocellulose by research groups. This project aimed obtaining and characterization of cellulose nanofibers from the fibers from the paina fibers. Obtaining nanocellulose is practically made through simplified chemical processes. First, was performed out pre-treatments to removal of waxes, lignin and hemicellulose. The first stage of pre-treatment was carried out by alkaline aqueous solution of sodium hydroxide (NaOH) at 5wt%, where the fibers were under constant agitation for 1h at 70°C. Through alkali treatment it was possible to remove most of the lignin, hemicellulose, waxes and extractives. After the alkaline treatment was done bleaching with an aqueous solution of sodium hydroxide (NaOH) to 4wt% and hydrogen peroxide (H2O2) to 24wt% 1:1 during 2h with constant stirring to 50 °C. Through bleaching was possibe to remove residual lignin, and got cellulose with 72% of crystallinity. Nanocellulose of paina fibers was extracted using different conditions of acid hydrolysis with sulfuric acid (H2SO4) to 50wt%. After acid hydrolysis, the suspensions were centrifuged during 30 min and dialyzed in water to remove excess acid until neutral pH (6-7). Then the suspensions were passed by ultrasonification in an ultrasound 20 kHz during 1h in an ice bath. Untreated, alkalinized and bleached fibers as well as cellulose nanoparticles were characterized by the techniques of thermogravimetry ... (Complete abastract click electronic access below)

Obtenção e caracterização de nanocelulose a partir de fibras de Chorisia speciosa St. Hil

Natural fibers have been highlighted as a renewable material that can replace materials from oil and its derivatives. In this context, Brazil becomes the perfect setting because of the diversity of fibers found in its territory, such as sugarcane, sisal, rice, cotton, coconut, pineapple, among others. The paineiras (Chorisia speciosa St. Hil) are typically Brazilian trees, which produce paina as fruit. These fruits are still little studied as a source of lignocellulose by research groups. This project aimed obtaining and characterization of cellulose nanofibers from the fibers from the paina fibers. Obtaining nanocellulose is practically made through simplified chemical processes. First, was performed out pre-treatments to removal of waxes, lignin and hemicellulose. The first stage of pre-treatment was carried out by alkaline aqueous solution of sodium hydroxide (NaOH) at 5wt%, where the fibers were under constant agitation for 1h at 70°C. Through alkali treatment it was possible to remove most of the lignin, hemicellulose, waxes and extractives. After the alkaline treatment was done bleaching with an aqueous solution of sodium hydroxide (NaOH) to 4wt% and hydrogen peroxide (H2O2) to 24wt% 1:1 during 2h with constant stirring to 50 °C. Through bleaching was possibe to remove residual lignin, and got cellulose with 72% of crystallinity. Nanocellulose of paina fibers was extracted using different conditions of acid hydrolysis with sulfuric acid (H2SO4) to 50wt%. After acid hydrolysis, the suspensions were centrifuged during 30 min and dialyzed in water to remove excess acid until neutral pH (6-7). Then the suspensions were passed by ultrasonification in an ultrasound 20 kHz during 1h in an ice bath. Untreated, alkalinized and bleached fibers as well as cellulose nanoparticles were characterized by the techniques of thermogravimetry ... (Complete abastract click electronic access below)

Vigor de sementes e desempenho agronômico de plantas de algodão

O vigor das sementes pode influenciar a emergência, o desempenho e produtividade das plantas, dependendo de cada espécie e de fatores ambientais. Dessa forma, um dos principais desafios das pesquisas com sementes é averiguar a influência do potencial fisiológico das sementes sobre o ciclo das plantas. O objetivo deste trabalho foi avaliar o efeito do vigor de sementes sobre as características morfofisiológicas de plantas de algodão, bem como, sobre o rendimento de caroço e de fibra. Três lotes de sementes da cultivar FMT 701 (safra 2005/2006) foram selecionados com base em resultados de testes realizados em laboratório. O efeito do vigor foi avaliado em campo, nas safras 2006/2007 e 2007/2008, no município de Jaciara, Mato Grosso. Determinou-se a porcentagem de plântulas emergidas, índice de velocidade de emergência, altura das plantas, número de ramos reprodutivos, número de nós, número de posições frutíferas, número de capulhos, rendimento de fibras e caroço. O desempenho inicial e reprodutivo de plantas de algodão em campo depende, além de outros fatores, do nível de vigor das sementes. Plantas com maior vigor apresentam maior rendimento de fibras e de caroço.

Avaliação das propriedades das fibras de algodões coloridos naturalmente e ecologicamente corretas cultivados nos assentamentos do município de Guamaré/RN

In this work evaluate the technical characteristics of the fibers grown in settlements Guamaré, colored cotton seeds were donated existing in the Germplasm Bank of Embrapa Cotton. We sought through the breeding program, raising the resistance, fineness, length and uniformity of cotton fibers, as well as stabilize the staining of fibers in the BRS Topaz, BRS Brown and BRS Green shades and raise their productivity in the field. First, the individual selections to test progeny seeds, and thereafter the hybridization method followed by family selection to obtain variations in the color tones were performed. The BRS Topaz, BRS Brown and BRS Green varieties were produced, analyzed and compared with existing cottons in the region which is the White cotton. The properties amount of impurities and neps, length, length uniformity, short fiber content, fineness and tensile strength of the fibers were sized in Classifiber, NATI, Pressley and Micronaire devices. 10 trials each with 10 tests for all four fiber types were carried out. The White and Topaz fibers showed greater length (32-34mm) and greater resistance (7.94 lb/mg and 7.97 lb/mg respectively) and showed finesse with lower micronaire index 3,71μg/inch and 3, 73μg/inch and a low rate of short fibers. The results were very promising for the use of genetically improved cotton in the manufacturing of fabric and yarn in the textile industry. The fibers were brown colored cotton used in the manufacture of a composite fiber with thermoplastic resin

Obtenção e caracterização de um compósito polimérico de matriz poliéster e reforço/carga de tecido plano de algodão

He was obtained and studied the feasibility of using TPA (Tissue Cotton Plan) screen type, for bagging, with a weight of 207.9 g / m2 in a composite of orthophthalic crystal polyester resin matrix. The process for obtaining the composite was tested against the maximum number of layers that could be used without compromising the processability and manufacturing of CPs in compression mold. Five configurations / formulations were selected and tested at 1, 4, 8, 10 and 12 layers of cotton tissue - TPA. TPA was not subjected to chemical treatment, only by passing a mechanical washing process. The composite in its various configurations / formulations was characterized to determine its physical properties. The properties of the composite were higher viability resistance to bending, approaching the matrix and impact resistance, superiority in relation to the polyester resin. Another property that has shown good result compared to other composite has water absorption. Analyzing all the properties set the settings / formulations with higher viability were TA8 and TA10, by combining good processability and higher mechanical strength, with lower loss compared to polyester resin matrix. The composite showed lower mechanical behavior of the resin matrix for all the formulations studied except the impact resistance. The SEM showed a good adhesion between the layers of TPA and polyester resin matrix, without the presence of micro voids in the matrix confirming the efficient manufacturing process of the samples for characterization. The composite proposed proved to be viable for the fabrication of structures with low requests from mechanical stresses, and as demonstrated for the manufacture of solar and wind prototypes, and packaging, shelving, decorative items, crafts and shelves, with good visual appearance.

Obtenção e caracterização de um compósito polimérico de matriz poliéster e reforço/carga de tecido plano de algodão

He was obtained and studied the feasibility of using TPA (Tissue Cotton Plan) screen type, for bagging, with a weight of 207.9 g / m2 in a composite of orthophthalic crystal polyester resin matrix. The process for obtaining the composite was tested against the maximum number of layers that could be used without compromising the processability and manufacturing of CPs in compression mold. Five configurations / formulations were selected and tested at 1, 4, 8, 10 and 12 layers of cotton tissue - TPA. TPA was not subjected to chemical treatment, only by passing a mechanical washing process. The composite in its various configurations / formulations was characterized to determine its physical properties. The properties of the composite were higher viability resistance to bending, approaching the matrix and impact resistance, superiority in relation to the polyester resin. Another property that has shown good result compared to other composite has water absorption. Analyzing all the properties set the settings / formulations with higher viability were TA8 and TA10, by combining good processability and higher mechanical strength, with lower loss compared to polyester resin matrix. The composite showed lower mechanical behavior of the resin matrix for all the formulations studied except the impact resistance. The SEM showed a good adhesion between the layers of TPA and polyester resin matrix, without the presence of micro voids in the matrix confirming the efficient manufacturing process of the samples for characterization. The composite proposed proved to be viable for the fabrication of structures with low requests from mechanical stresses, and as demonstrated for the manufacture of solar and wind prototypes, and packaging, shelving, decorative items, crafts and shelves, with good visual appearance.