Corrosion behavior of Eurofer 97 and ODS-Eurofer alloys compared to traditional stainless steels

In the present work, the corrosion resistance of ferritic-martensitic EUROFER 97 and ODS-EUROFER steels was tested in solutions containing NaCl or H(2)SO(4) and KSCN, both at 25 degrees C. The results were compared to those of AISI 430 ferritic and AISI 410 martensitic conventional stainless steels. The as-received samples were tested by electrochemical techniques, specifically, electrochemical impedance spectroscopy, potentiodynamic polarization curves, and double-loop electrochemical potentiokinetic reactivation tests. The surfaces were observed by scanning electron microscopy after exposure to corrosive media. The results showed that EUROFER 97 and ODS-EUROFER alloys present similar corrosion resistance but lower than ferritic AISI 430 and martensitic 410 stainless steels.

Review of stress corrosion cracking of pipeline steels in "low" and "high" pH solutions

This paper reviews the current understanding of the mechanisms of stress corrosion cracking of pipeline steels. The similarities, the differences and the influencing factors are considered for the high pH stress corrosion cracking caused by a concentrated bicarbonate-carbonate solution, and for the low pH stress corrosion cracking due to a diluter solution. For high pH stress corrosion cracking, it is well accepted that the mechanism involves anodic dissolution for crack initiation and propagation. In contrast, it has been suggested that the low pH stress corrosion cracking is associated with the dissolution of the crack tip and sides, accompanied by the ingress of hydrogen into the pipeline steel. But the precise influence of hydrogen on the mechanism needs to be further studied. (C) 2003 Kluwer Academic Publishers.

Temperature effects on the mechanism of time independent hydrogen assisted fatigue crack propagation in steels

The effects of temperature on hydrogen assisted fatigue crack propagation are investigated in three steels in the low-to-medium strength range; a low alloy structural steel, a super duplex stainless steel, and a super ferritic stainless steel. Significant enhancement of crack growth rates is observed in hydrogen gas at atmospheric pressure in all three materials. Failure occurs via a mechanism of time independent, transgranular, cyclic cleavage over a frequency range of 0.1-5 Hz. Increasing the temperature in hydrogen up to 80°C markedly reduces the degree of embrittlement in the structural and super ferritic steels. No such effect is observed in the duplex stainless steel until the temperature exceeds 120°C. The temperature response may be understood by considering the interaction between absorbed hydrogen and micro-structural traps, which are generated in the zone of intense plastic deformation ahead of the fatigue crack tip. © 1992.

Lujien hitsattavien terästen käyttäytyminen -60 °C:ssa

Opinnäytetyö on osa Arctic Materials Technologies Development -projektia, jonka tavoitteena on kehittää perusteita arktisten alueiden sovelluksiin suunnittelun ja valmistuksen kannalta. Arktisella alueella sijaitsee useita potentiaalisia öljy- ja maakaasuesiintymiä, joiden hyödyn-täminen tulee vuosi vuodelta kannattavammaksi ilmaston lämpenemisestä johtuvan merijään heikkenemisen vuoksi. Alin suunnittelulämpötila arktisilla alueilla on -60 °C, mikä aiheuttaa haasteita sekä materiaalinvalinnalle että hitsaukselle. Ferriittisillä teräksillä esiintyy lämpötilasta riippuvaa sitkeyden vaihtelua, jota kutsutaan transi-tiokäyttäytymiseksi. Lämpötilan laskiessa teräksen iskusitkeys sekä murtumissitkeys laske-vat. Arktisissa sovelluskohteissa käytetään yleisesti niukkaseosteisia, mikroseostettuja hie-noraeteräksiä, joille on ominaista erinomaiset sitkeys-, lujuus- sekä hitsattavuusominaisuudet vaativissakin olosuhteissa. Lujat termomekaanisesti valssatut ja nuorrutetut hienoraeteräkset kattavat myötölujuusluokat 355…700 MPa. Tutkimuksissa on saatu vaihtelevia tuloksia ma-teriaalien isku- ja murtumissitkeydestä -60 °C:ssa. Erityisesti sitkeysominaisuudet hitsiaineen ja muutosvyöhykkeen alueiden välillä ovat vaihtelevia. Pienemmällä lämmöntuonnilla ja seostetuilla lisäaineilla saavutetaan kuitenkin pääsääntöisesti parempia sitkeysarvoja. Asiku-laarinen ferriitti sekä alabainiitti ovat toivottavia mikrorakenteita liitoksessa, niiden pienen raekoon johdosta.

Efeito do fresamento com alta velocidade de corte na integridade superficial de aços ferríticos com grãos ultrafinos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação da tenacidade à fratura na região de transição dúctil-frágil dos aços API 5L X70 e X80 utilizando a metodologia da curva mestra

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo experimental do comportamento à fratura frágil em aços estruturais ferríticos e aplicações à determinação da curva mestra.

Este trabalho apresenta uma investigação experimental sobre o comportamento à fratura frágil de aços estruturais ferríticos, ASTM A285 Gr C e ASTM A515 Gr 65. Os resultados deste trabalho ampliam a base de dados de propriedades mecânicas utilizadas nas análises de integridade de estruturas pressurizadas tais como vasos de pressão e tanques de armazenamento construídos com esta classe de material. O trabalho tem por objetivo também avaliar a aplicabilidade de corpos de prova de dimensões reduzidas, PCVN, na determinação da temperatura de referência, T0, por meio da metodologia da Curva Mestra, a qual define a dependência da tenacidade à fratura do material em função da temperatura. Os ensaios de tenacidade à fratura foram conduzidos utilizando-se corpos de prova solicitados em flexão três pontos com geometria SE(B), PCVN e PCVN com entalhe lateral, extraídos de chapas laminadas. Os resultados dos ensaios foram obtidos em termos de integral J no momento da instabilidade, denotados por Jc. Dados adicionais de resistência à tração e de Impacto Charpy convencional também foram obtidos para caracterizar o comportamento mecânico dos aços utilizados. Os resultados mostraram uma forte influência da geometria dos corpos de prova sobre os valores de Jc, evidenciada pela grande variação nos valores de tenacidade à fratura.

Composition and orientation effects on the final recrystallization texture of coarse-grained Nb-containing AISI 430 ferritic stainless steels

Composition and orientation effects on the final recrystallization texture of three coarse-grained Nb-containing AISI 430 ferritic stainless steels (FSSs) were investigated. Hot-bands of steels containing distinct amounts of niobium, carbon and nitrogen were annealed at 1250 degrees C for 2h to promote grain growth. In particular, the amounts of Nb in solid solution vary from one grade to another. For purposes of comparison, the texture evolution of a hot-band sheet annealed at 1030 degrees C for 1 min (finer grain structure) was also investigated. Subsequently, the four sheets were cold rolled up to 80% reduction and then annealed at 800 degrees C for 15 min. Texture was determined using X-ray diffraction and electron backscatter diffraction (EBSD). Noticeable differences regarding the final recrystallization texture and microstructure were observed in the four investigated grades. Results suggest that distinct nucleation mechanisms take place within these large grains leading to the development of different final recrystallization textures. (c) 2011 Elsevier B.V. All rights reserved.

Effect of alpha prime due to 475 degrees C aging on fracture behavior and corrosion resistance of DIN 1.4575 and MA 956 high performance ferritic stainless steels

The 475 degrees C embrittlement in stainless steels is a well-known phenomenon associated to alpha prime (alpha`) formed by precipitation or spinodal decomposition. Many doubts still remain on the mechanism of alpha` formation and its consequence on deformation and fracture mechanisms and corrosion resistance. In this investigation, the fracture behavior and corrosion resistance of two high performance ferritic stainless steels were investigated: a superferritic DIN 1.4575 and MA 956 superalloy were evaluated. Samples of both stainless steels (SS) were aged at 475 degrees C for periods varying from 1 to 1,080 h. Their fracture surfaces were observed using scanning electron microscopy (SEM) and the cleavage planes were determined by electron backscattering diffraction (EBSD). Some samples were tested for corrosion resistance using electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization. Brittle and ductile fractures were observed in both ferritic stainless steels after aging at 475 degrees C. For aging periods longer than 500 h, the ductile fracture regions completely disappeared. The cleavage plane in the DIN 1.4575 samples aged at 475 degrees C for 1,080 h was mainly {110}, however the {102}, {314}, and {131} families of planes were also detected. The pitting corrosion resistance decreased with aging at 475 degrees C. The effect of alpha prime on the corrosion resistance was more significant in the DIN 1.4575 SS comparatively to the Incoloy MA 956.

High-resolution transmission electron microscopy and electron backscatter diffraction in nanoscaled ferritic and ferritic-martensitic oxide dispersion strengthened-steels

For specific blanket and divertor applications in future fusion power reactors a replacement of presently considered reduced activation ferritic martensitic (RAFM) steels as a structural material by suitable oxide dispersion strengthened ferritic martensitic steels would allow a substantial increase of the operating temperature from similar to 823 to about 923 K. Due to this reason the RAFM-alloy ODS-Eurofer has already been developed and produced with industrial partners. In the He-cooled modular divertor concept, where temperatures above 923 K will arise, an ODS-steel with a purely ferritic matrix is advantageous, because of missing phase transitions. Due to this reason, a special ferritic ODS-steel is being manufactured as well. In this work the microstructures of these two ODS-alloy types, analysed mainly by high resolution TEM are compared, with respect to different manufacturing processes. In addition first results of high resolution EBSD scans together with determined orientation maps of the RAFM steel ODS-Eurofer will also be presented. (C) 2008 Elsevier B.V. All rights reserved.

Damage tolerance of cold drawn ferritic-austenitic stainless steels wires for prestressed concrete

Damage tolerance of high strength cold-drawn ferritic–austenitic stainless steel wires is assessed by means of tensile fracture tests of cracked wires. The fatigue crack is transversally propagated from the wire surface. The damage tolerance curve of the wires results from the empirical failure load when given as a function of crack depth. As a consequence of cold drawing, the wire microstructure is orientated along its longitudinal axis and anisotropic fracture behaviour is found at macrostructural level at the tensile failure of the cracked specimens. An in situ optical technique known as video image correlation VIC-2D is used to get an insight into this failure mechanism by tensile testing transversally fatigue cracked plane specimens extracted from the cold-drawn wires. Finally, the experimentally obtained damage tolerance curve of the cold-drawn ferritic–austenitic stainless steel wires is compared with that of an elementary plastic collapse model and existing data of two types of high strength eutectoid steel currently used as prestressing steel for concrete.

Oxidation and tensile behavior of ferritic/martensitic steels after exposure to lead-bismuth eutectic

Two ferritic/martensitic steels, T91 steel and newly developed SIMP steel, were subject to tensile test after being oxidized in the liquid lead-bismuth eutectic (LBE) at 873 K for 500 h, 1000 h and 2000 h. Tensile tests were also carried out on the steels only thermally aged at 873 K. The result shows that thermal aging has no effect. Exposure to LBE at 873 K leads to a slight decrease in strength, but a large decrease in elongation when tested at 873 K. When tested at 873 K after 2000 h exposure, the tensile strength of T91 decreases slightly, and elongation from 39% to 21%. For SIMP, the decreases are slightly and from 44% to 28%, for tensile strength and elongation, respectively. The room temperature strength has slightly larger percentage reductions after the LBE exposure, but the elongation changes little.

Annealing effects on microstructure and coercive field of ferritic-martensitic ODS Eurofer steel

Oxide dispersion strengthened reduced-activation ferritic-martensitic steels are promising candidates for applications in future fusion power plants. Samples of a reduced activation ferritic-martensitic 9 wt.%Cr-oxide dispersion strengthened Eurofer steel were cold rolled to 80% reduction in thickness and annealed in vacuum for 1 h from 200 to 1350 degrees C to evaluate its thermal stability. Vickers microhardness testing and electron backscatter diffraction (EBSD) were used to characterize the microstructure. The microstructural changes were also followed by magnetic measurements, in particular the corresponding variation of the coercive field (H(c)), as a function of the annealing treatment. Results show that magnetic measurements were sensitive to detect the changes, in particular the martensitic transformation, in samples annealed above 850 degrees C (austenitic regime). (C) 2010 Elsevier B.V. All rights reserved.

X-ray diffraction characterisation of expanded austenite and ferrite in plasma nitrided stainless steels

The S phase, known as expanded austenite, is formed on the surfaces of austenitic stainless steels that are nitrided under low temperature plasma. A similar phase was observed for nitrided ferritic stainless steels and was designed as expanded ferrite or ferritic S phase. The authors treated samples of austenitic AISI 304L and AISI 316L and ferritic AISI 409 stainless steels by plasma nitriding at different temperatures and then studied the structural, morphological, chemical and corrosion characteristics of the modified layers by X-ray diffraction, scanning electron microscopy/energy dispersive spectroscopy and electrochemical tests. For both austenitic AISI 304L and AISI 316L stainless steels, the results showed that a hard S phase layer was formed on the surfaces, promoting an anodic polarisation curve displacement to higher current density values that depend on the plasma nitriding temperature. A layer having a high amount of nitrogen was formed on the ferritic AISI 409 stainless steel. X-ray diffraction measurements indicated high strain states for the modified layers formed on the three stainless steels, being more pronounced for the ferritic S phase.