Gamma-ray induced color centers in Yb : YAG crystals grown by Czochralski method

20 at.% Yb:YAG single crystals have been grown by the CZ method and gamma-ray irradiation induced color centers and valence change of Fe3+ and Yb3+ ions in Yb:YAG have been studied. One significant 255 nm absorption band was observed in as-grown crystals and was attributed to Fe3+ ions. Two additional absorption (AA) bands located at 255 nm and 345 nm, respectively, were produced after gamma irradiation. The changes in the AA spectra after gamma irradiation and air annealing are mainly related to the charge exchange of the Fe3+, Fe2+, oxygen vacancies and F-type color centers. Analysis shows that the broad AA band is associated with Fe2+ ions and F-type color centers. The transition Yb3+ Yb2+ takes place as an effect of recharging of one of the Yb3+ ions from a pair in the process of gamma irradiation. (C) 2006 Elsevier Ltd. All rights reserved.

Phi 140 mm sapphire crystal growth by temperature gradient techniques and its color centers

Sapphire crystals, 140 mm in diameter and 90 turn in height, have been grown by temperature gradient techniques (TGT). The growth direction of the boule was fixed by means of Lane X-ray diffraction. A prominent 204 nm absorption band in TGT-Al2O3. which does not appear in single crystals grown by Czochralski method has been studied. Analysis further substantiates the F-center model of this band. Two relatively weaker bands absorbing at 232 nm and 254 nm were ascribed to F+ centers. F-type centers concentration was determined using Smakula's equation. (c) 2005 Elsevier B.V. All rights reserved.

Color centers and charge state change in Ce : YAG crystals grown by temperature gradient techniques

Color centers and impurity defects of Ce:YAG crystals grown in reduction atmosphere by temperature gradient techniques have been investigated by means of gamma irradiation and thermal treatments. Four absorption bands associated with color centers or impurity defects at 235, 255, 294 and 370 nm were observed in as-grown crystals. Changes in optical intensity of the 235 and 370 nm bands after gamma irradiation indicate that they are associated with F+-type color center. Charge state change processes of Fe3+ impurity and Ce3+ ions take place in the irradiation process. The variations of Ce3+ ions concentration clearly indicate that Ce4+ ions exist in Ce:YAG crystals and gamma irradiations could increase the concentration of Ce3+ ions. Annealing treatments and the changes in optical density suggest that a heterovalent impurity ion associated with the 294 nm band seems to be present in the crystals. (c) 2005 Elsevier B.V. All rights reserved.

Color centers and charge state recharge in gamma-irradiated Yb : YAP

Gamma-ray irradiation induced color centers and charge state recharge of impurity and doped ion in 10 at.% Yb:YAP have been studied. The change in the additional absorption (AA) spectra is mainly related to the charge exchange of the impurity Fe2+, Fe3+ and Yb3+ ions. Two impurity color center bands at 255 and 313 nm were attributed to Fe3+ and Fe2+ ions, respectively. The broad AA band centered at 385 nm may be associated with the cation vacancies and F-type center. The transition Yb3+ -> Yb2+ takes place in the process of gamma-irradiation. Oxygen annealing and gamma-ray irradiation lead to an opposite effect on the absorption properties of the Yb:YAP crystal. In the air annealing process, the transition Fe2+ -> Fe3+ and Yb2+ -> Yb3+ take place and the color centers responsible for the 385 nm band was destroyed. (c) 2005 Elsevier B.V. All rights reserved.

Ternary copper(II) complexes of thiosemicarbazones and heterocyclic bases showing N3OS coordination as models for the type-2 centers of copper monooxygenases

Six ternary copper(II) complexes of general formulation [CuLB] (1-6), where L is dianionic ONS-donor thiosemicarbazones derived from the condensation of salicylaldehyde with thiosemicarbazides and B is NN-donor heterocyclic bases like 2,2'-bipyridine, 1,10-phenanthroline and 2,9-dimethyl-1,10-phenanthroline, are prepared from a reaction of copper(II) acetate hydrate with the heterocyclic base (B) and the thiosemicarbazone (H2L) in MeOH, and structurally characterized by X-ray diffraction technique. Crystal structures of the complexes display a distorted square-pyramidal (4 + 1) coordination geometry having the ONS-donor thiosemicarbazone bonded at the basal plane. The chelating heterocyclic bases exhibit axial-equatorial mode of bonding. The complexes are one-electron paramagnetic and they show axial X-band EPR spectra in DMF-toluene glass at 77 K giving g(parallel to)(A(parallel to)) and g(perpendicular to) values of similar to2.2 (175 x 10(-4) cm(-1)) and similar to2.0 indicating a {d(x2-y2)}(1) ground state. The complexes show a d-d band near 570 nm and a charge transfer band near 400 nm in DMF. The complexes are redox active and exhibit a quasireversible Cu(II)-Cu(I) couple in DMF-0.1 M tetrabutylammonium perchlorate near 0.1 V vs. SCE. They are catalytically active in the oxidation of ascorbic acid in presence of dioxygen. The complexes with a CuN3OS coordination model the ascorbate oxidation property of dopamine beta-hydroxylase and peptidylglycine a-hydroxylating monooxygeanase. (C) 2003 Elsevier Science B.V. All rights reserved.

Color centers in Yb : YAG crystals grown by temperature-gradient techniques

Yb: YAG (Yb: Y3Al5O12) crystals have been grown by temperature-gradient techniques (TGT) and their color centers and impurity defects were investigated by means of gamma irradiations and thermal treatment. Two color centers located at 255 and 290 nm were observed in the as-grown TGT-Yb: YAG. Analysis shows that the 255 nm band may be associated with Fe3+ ions. Absorption intensity changes of the 290 nm band after gamma irradiation and thermal treatment indicate that this band may be associated with oxygen-vacancy defects. (c) 2006 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

New color centers and photostimulated luminescence of BaFCl : Eu2+

Three new absorption bands, appearing around 670, 865 and 980 nm, are observed in BaFCl:Eu2+ phosphors. They are ascribed to F aggregates formed by association of F centers or by trapping of electrons to the primary F-n(+) (n = 2,3,4) centers. The growth curves of F and F-aggregated centers are similar and may be divided into three stages. The photostimulated luminescence (PSL) decays by stimulation into the absorption bands of F centers and of F aggregates are different; the former decay logarithmically and the latter decay hyperbolically. Some non-radiative processes related to F aggregates, such as electron migration, occur accompanying the PSL process, which may reduce the PSL efficiency and sensitivity of the phosphors. (C) 1997 Published by Elsevier Science Ltd. All rights reserved.

Study of color centers and trace oxygen in KMgF3 : Eu single crystal

Using the Bridgeman-Stockbarger method, the KMgF3:EU2+ single crystal was grown. The color centers in unirradiated KMgF3:Eu crystal were studied. By thermal annealing, we confirmed the 422-nm emission resulted from color centers and oxygen centers, and we proved the energy transfer from EU2+ to color centers. From spectra, the relative oxygen content in crystal was calculated, and the relationships of oxygen displacing fluorine were studied.

Effect of air annealing on the spectral properties of Ce : Y3Al5O12 single crystals grown by the temperature gradient technique

Five absorption hands, at 227, 300 340, 370 and 457nm, were observed in the optical absorption spectrum of Ce:Y3Al5O12 (Ce:YAG) crystals grown by the temperature gradient technique (TGT). The absorption bands at 227, 340, and 457 nm were identified Lis belonging to the Ce3+ -ion in the YAG crystal. A near UV optical emission band at 398nm was observed. with an excitation spectrum containing two bands, at 235 and 370nm. No fluorescence was detected under 300 nm excitation. The pair of absorption bands at 235 and 370 nm and the absorption band at 300 nm were attributed to the F- and F+-type color centers, respectively. The color centers model was also applied to explain the spectral changes in the Ce:YAG (TGT) crystal, including the reduction in the Ce 31 -ion absorption intensity, after annealing in an oxidizing atmosphere (air). (C) 2004 Elsevier B.V. All rights reserved.

Color center formation in alpha-Al2O3 induced by high energy heavy ions

Single crystals of alpha-alumina were irradiated at room temperature with 1.157 (GeVFe)-Fe-56, 1.755 (GeVXe)-Xe-136 and 2.636 (GeVU)-U-238 ions to fluences range from 8.7 x 10(9) to 6 x 10(12) ions/cm(2). Virgin and irradiated samples were investigated by ultraviolet visible absorption measurements. The investigation reveals the presence of various color centers (F, F+, F-2(2+), F-2(+) and F-2 centers) appearing in the irradiated samples. It is found that the ratio of peak absorbance of F-2 to F centers increases with the increase of the atomic numbers of the incident ions from Fe, Xe to U ions, so do the absorbance ratio of F-2(2+) to F+ centers and of large defect cluster to F centers, indicating that larger defect clusters are preferred to be produced under heavier ion irradiation. Largest color center production cross-section was found for the U ion irradiation. The number density of single anion vacancy scales better with the energy deposition through processes of nuclear stopping, indicating that the nuclear energy loss processes determines the production of F-type defects in heavy ion irradiated alpha-alumina.

Effects of annealing on the color, absorption spectra, and light yield of Ce : YAlO3 single crystal grown by the temperature gradient technique

YAlO3 single crystal doped with Ce3+ at concentration 1% was grown by the temperature gradient technique. The as-grown crystal was pink. After H-2 annealing or air annealing at 1400degreesC for 20 h, the crystal was turned into colorless. We concluded there were two kinds of color centers in the as-grown crystal. One is F+ center attributed to absorption band peaking at about 530 nm, the other is O- center attributed to absorption band peaking at about 390 nm. This color centers model can be applied in explaining the experiment phenomena including the color changes, the absorption spectra changes, and the light yield changes of Ce:YAP crystals before and after annealing. (C) 2004 American Institute of Physics.

钛宝石中子辐照色心的研究

研究了中子辐照下钛宝石单晶体缺陷的形成及光学性能的变化。对温度梯度法(TGT)生长的钛宝石晶体进行中子辐照。中子能量为1．5MeV，剂量为4．32×10^18 neutrons／cm^2。辐照后194nm吸收峰强度增加,268nm吸收峰强度则降低。荧光谱检测中发现辐照使得420nm荧光峰强度明显降低，荧光峰位置也蓝移至414nm处。分析表明辐照使得钛宝石晶体内形成F^+缺陷，同时Ti^4+离子则转化成Ti^3+离子。辐照后的钛宝石在247C处有热释光TL出现，通过初始上升法计算出其陷阱深度为0．63eV。

Defects in U3+: CaF2 single crystals grown under different conditions by the temperature gradient technique

Defects in as-grown U3+ : CaF2 crystals grown with or without PbF2 as an oxygen scavenger were studied using Raman spectra, thermoluminescence glow curves, and additional absorption (AA) spectra induced by heating and gamma-irradiation. The effects of heating and irradiation on as-grown U3+: CaF2 crystals are similar, accompanied by the elimination of H-type centers and production of F-type centers. U3+ is demonstrated to act as an electron donor in the CaF2 lattice, which is oxidized to the tetravalent form by thermal activation or gamma-irradiation. In the absence of PbF(2)as an oxygen scavenger, the as-grown U3+:CaF2 crystals contain many more lattice defects in terms of both quantity and type, due to the presence of O2- impurities. Some of these defects can recombine with each other in the process of heating and gamma-irradiation. (c) 2005 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.