In Vitro Evaluation of Bacterial Leakage Along the Implant-Abutment Interface of an External-Hex Implant After Saliva Incubation

The aim of this in vitro study was to evaluate bacterial leakage along the implant-abutment interface under unloaded conditions. Twelve premachined abutments with plastic sleeves and 12 dental implants were used in this study. Prior to tests of bacterial leakage, samples from the inner parts of the implants were collected with sterile microbrushes to serve as negative controls for contamination. After casting, the abutments were tightened to 32 Ncm on the implants. The assemblies were immersed in 2.0 mL of human saliva and incubated for 7 days. After this period, possible contamination of the internal parts of the implants was evaluated using the DNA Checkerboard method. Microorganisms were found in the internal surfaces of all the implants evaluated. Aggregatibacter actinomycetemcomitans and Capnocytophaga gingivalis were the most incident species. No microorganisms were found in the samples recovered from the implants before contamination testing (negative control). Bacterial species from human saliva may penetrate the implant-abutment interface under unloaded conditions. INT J ORAL MAXILLOFAC IMPLANTS 2011;26:782-787

Biomechanical evaluation of internal and external hexagon platform switched implant-abutment connections: An in vitro laboratory and three-dimensional finite element analysis

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Relation between implant/abutment vertical misfit and torque loss of abutment screws

This study investigated whether there is a direct correlation between the level of vertical misfit at the abutment/implant interface and torque losses (detorque) in abutment screws. A work model was obtained from a metal matrix with five 3.75 x 9 mm external hex implants with standard platform (4.1 mm). Four frameworks were waxed using UCLA type abutments and one-piece cast in commercially pure titanium. The misfit was analyzed with a comparator microscope after 20 Ncm torque. The highest value of misfit observed per abutment was used. The torque required to loose the screw was evaluated using a digital torque meter. The torque loss values, measured by the torque meter, were assumed as percentage of initial torque (100%) given to abutment screws. Pearson's correlation (α=0.05) between the misfit values (29.08 ± 8.78 µm) and the percentage of detorque (50.71 ± 11.37%) showed no statistically significant correlation (p=0.295). Within the limitations of this study, it may be concluded that great vertical misfits dot not necessarily implies in higher detorque values.

Influence of microgap location and configuration on the periimplant bone morphology in submerged implants. An experimental study in dogs

Objectives: The vertical location of the implant-abutment connection influences the periimplant bone morphology. It is unknown, however, whether different microgap configurations cause different bone reactions. Therefore, in this study the bone morphologies of two different implant systems were compared.Material and methods: Three months after tooth extraction in eight mongrel dogs, two grit-blasted screw implants with internal Morse taper connection (ANK group) were placed on one side whereas the contralateral side received two oxidized screw implants with external hex (TIU group). One implant on each side was placed level with the bone (equicrestal), the second implant was inserted 1.5mm below bone level (subcrestal). After 3 months the implants were uncovered. Three months after stage two surgery, histometrical evaluations were performed in order to assess the periimplant bone levels (PBL), the first bone-to-implant contact points (BICP), the width (HBD) and the steepness (SLO) of the bone defect.Results: All implants osseointegrated clinically and histologically. Bone overgrowth of the microgap was seen in ANK implants only. No significant differences between ANK and TIU could be detected in neither vertical position for PBL and BICP. However, a tendency in favor of ANK was visible when the implants were placed subcrestally. In the parameters HBD (ANK equicrestal -0.23mm; TIU equicrestal -0.51mm; ANK subcrestal +0.19mm; TIU subcrestal -0.57mm) and SLO (ANK equicrestal 35.36 degrees; TIU equicrestal 63.22 degrees; ANK subcrestal 20.40 degrees; TIU subcrestal 44.43 degrees) more pronounced and significant differences were noted.Conclusions: Within the limits of this study, it is concluded that different microgap designs cause different shapes and sizes of the periimplant ('dish-shaped') bone defect in submerged implants both in equicrestal and subcrestal positions.

Influence of Microgap Location and Configuration on Radiographic Bone Loss Around Submerged Implants: An Experimental Study in Dogs

Purpose: The vertical location of the implant-abutment connection influences the subsequent reaction of the peri-implant bone. It is not known, however, whether any additional influence is exerted by different microgap configurations. Therefore, the radiographic bone reactions of two different implant systems were monitored for 6 months. Materials and Methods: In eight mongrel dogs, two implants with an internal Morse-taper connection (INT group) were placed on one side of the mandible; the contralateral side received two implants with an external-hex connection (EXT group). on each side, one implant was aligned at the bone level (equicrestal) and the second implant was placed 1.5 mm subcrestal. Healing abutments were placed 3 months after submerged healing, and the implants were maintained for another 3 months without prosthetic loading. At implant placement and after 1, 2, 3, 4, 5, and 6 months, standardized radiographs were obtained, and peri-implant bone levels were measured with regard to microgap location and evaluated statistically. Results: All implants osseointegrated clinically and radiographically. The overall mean bone loss was 0.68 +/- 0.59 mm in the equicrestal INT group, 1.32 +/- 0.49 mm in the equicrestal EXT group, 0.76 +/- 0.49 mm in the subcrestal INT group, and 1.88 +/- 0.81 mm in the subcrestal EXT group. The differences between the INT and EXT groups were statistically significant (paired t tests). The first significant differences between the internal and external groups were seen at month 1 in the subcrestal groups and at 3 months in the equicrestal groups. Bone loss was most pronounced in the subcrestal EXT group. Conclusions: Within the limits of this study, different microgap configurations can cause different amounts of bone loss, even before prosthetic loading. Subcrestal placement of a butt-joint microgap design may lead to more pronounced radiographic bone loss. INT J ORAL MAXILLOFAC IMPLANTS 2011;26:941-946

Influence of Microgap Location and Configuration on Radiographic Bone Loss in Nonsubmerged Implants: An Experimental Study in Dogs

Purpose: The implant-abutment connection (microgap) influences the pen-implant bone morphology. However, it is unclear if different microgap configurations additionally modify bone reactions. This preliminary study aimed to radiographically monitor pen-implant bone levels in two different microgap configurations during 3 months of nonsubmerged healing. Materials and Methods: Six dogs received two implants with internal Morse taper connection (INT group) on one side of the mandible and two implants with external-hex connection (EXT group) on the other side. One implant on each side was positioned at bone level (equicrestal); the second implant was inserted 1.5 mm below the bone crest (subcrestal). Healing abutments were attached directly after implant insertion, and the implants were maintained for 3 months without prosthetic loading. At implant placement and 1, 2, and 3 months, standardized radiographs were taken to monitor pen-implant bone levels. Results: All implants osseointegrated. A total bone loss of 0.48 +/- 0.66 mm was measured in the equicrestal INT group, 0.69 +/- 0.43 mm in the equicrestal EXT group, 0.79 +/- 0.93 mm in the subcrestal INT group, and 1.56 +/- 0.53 mm in the subcrestal EXT group (P>.05, paired t tests). Within the four groups, bone loss over time became significantly greater in the EXT groups than in the INT groups. The greatest bone loss was noted in the subcrestal EXT group. Conclusion: Within the limits of this animal study, it seems that even without prosthetic loading, different microgap configurations exhibit different patterns of bone loss during nonsubmerged healing. Subcrestal positioning of an external butt joint microgap may lead to faster radiographic bone loss. Int J Prosthodont 2011;24:445-452.

Influence of Microgap Location and Configuration on Peri-implant Bone Morphology in Nonsubmerged Implants: An Experimental Study in Dogs

Purpose: It is unknown whether different micro gap configurations can cause different pen-implant bone reactions. Therefore, this study sought to compare the peri-implant bone morphologies of two implant systems with different implant-abutment connections. Materials and Methods: Three months after mandibular tooth extractions in six mongrel dogs, two oxidized screw implants with an external-hex connection were inserted (hexed group) on one side, whereas on the contralateral side two grit-blasted screw implants with an internal Morse-taper connection (Morse group) were placed. on each side, one implant was inserted level with the bone (equicrestal) and the second implant was inserted 1.5 mm below the bony crest (subcrestal). Healing abutments were inserted immediately after implant placement. Three months later, the peri-implant bone levels, the first bone-to-implant contact points, and the width and steepness of the peri-implant bone defects were evaluated histometrically. Results: All 24 implants osseointegrated clinically and histologically. No statistically significant differences between the hexed group and Morse group were detected for either the vertical position for peri-implant bone levels (Morse equicrestal -0.16 mm, hexed equicrestal -0.22 mm, Morse subcrestal 1.50 mm, hexed subcrestal 0.94 mm) or for the first bone-to-implant contact points (Morse equicrestal -2.08 mm, hexed equicrestal -0.98 mm, Morse subcrestal -1.26 mm, hexed subcrestal -0.76 mm). For the parameters width (Morse equicrestal -0.15 mm, hexed equicrestal -0.59 mm, Morse subcrestal 0.28 mm, hexed subcrestal -0.70 mm) and steepness (Morse equicrestal 25.27 degree, hexed equicrestal 57.21 degree, Morse subcrestal 15.35 degree, hexed subcrestal 37.97 degree) of the pen-implant defect, highly significant differences were noted between the Morse group and the hexed group. Conclusion: Within the limits of this experiment, it can be concluded that different microgap configurations influence the size and shape of the peri-implant bone defect in nonsubmerged implants placed both at the crest and subcrestally. INT J ORAL MAXILLOFAC IMPLANTS 2010;25:540-547

Biomechanical Evaluation of Platform Switching in Different Implant Protocols: Computed Tomography-Based Three-Dimensional Finite Element Analysis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Implant Connection Type on the Biomechanical Environment of Immediately Placed Implants - CT-Based Nonlinear, Three-Dimensional Finite Element Analysis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Effectiveness of Screw Surface Coating on the Stability of Zirconia Abutments After Cyclic Loading

Purpose: Different surface treatments have been developed in attempts to prevent the loosening of abutment screws. The aim of the current study was to compare the effectiveness of titanium alloy screws with tungsten-doped diamond-like carbon (W-DLC) coating and uncoated screws in providing stability to zirconia (ZrO2) ceramic abutments after cyclic loading. Materials and Methods: Twenty prefabricated ZrO2 ceramic abutments on their respective external-hex implants were divided into two groups of equal size according to the type of screw used: uncoated titanium alloy screw (Ti) or titanium alloy screw with W-DLC coating (W-DLC/Ti). The removal torque value (preload) of the abutment screw was measured before and after loading. Cyclic loading between 11 and 211 N was applied at an angle of 30 degrees to the long axis of the implants at a frequency of 15 Hz. A target of 0.5 x 10(6) cycles was defined. Group means were calculated and compared using analysis of variance and the F test (alpha=.05). Results: Before cyclic loading, the preload for Ti screws was significantly higher than that for W-DLC/Ti screws (P=.021). After cyclic loading, there was no significant difference between them (P=.499). Conclusions: Under the studied conditions, it can be concluded that, after cyclic loading, both abutment screws presented a significant reduction in the mean retained preload and similar effectiveness in maintaining preload. INT J ORAL MAXILLOFAC IMPLANTS 2012;27:1061-1067

Strain Gauge Analysis of the Effect of Porcelain Firing Simulation on the Prosthetic Misfit of Implant-Supported Frameworks

Objectives: This study investigated the effect of porcelain firing on the misfit of implant-supported frameworks and analyzed the influence of preheat treatment on the dimensional alterations.Materials and Methods: Four external-hex cylindrical implants were placed in polyurethane block. Ten frameworks of screw-retained implant-supported prostheses were cast in Pd-Ag using 2 procedures: (1) control group (CG, n = 5): cast in segments and laser welded; and test group (TG, n = 5): cast in segments, preheated, and laser welded. All samples were subjected to firing to simulate porcelain veneering firing. Strain gauges were bonded around the implants, and microstrain values (mu epsilon = 10(-6)epsilon) were recorded after welding (M1), oxidation cycle (M2), and glaze firing (M3). Data were statistically analyzed (2-way analysis of variance, Bonferroni, alpha = 0.05).Results: The microstrain value in the CG at M3 (475.2 mu epsilon) was significantly different from the values observed at M1 (355.6 mu epsilon) and M2 (413.9 mu epsilon). The values at M2 and M3 in the CG were not statistically different. Microstrain values recorded at different moments (M1: 361.6 mu epsilon/M2: 335.3 mu epsilon/M3: 307.2 mu epsilon) did not show significant difference.Conclusions: The framework misfit deteriorates during firing cycles of porcelain veneering. Metal distortion after porcelain veneering could be controlled by preheat treatment. (Implant Dent 2012;21:225-229)

Photoelastic comparison of single tooth implant-abutment-bone of platform switching vs conventional implant designs

Objectives: The maintenance and stability of peri-implantar soft tissue seem to be related to the crestal bone around the implant platform and different implant designs connections might affect this phenomenon. The aim of this study was to evaluate by photoelastic analysis the stress distribution in the cervical and apical site of implant-abutment interface of conventional implant joints (external hex, internal hex and cone morse) and compare to the novel platform switching design. Materials and methods: It was fabricated photoelastic models using five different implant-abutment connection, one set of external hex (Alvim Ti, Neodent, Curitiba, Brazil), one set of internal hex (Full Osseotite, Biomet 3i, Florida, USA), one cone morse set (Alvim CM, Neodent, Curitiba, Brazil), and two sets of internal hex plus platform switching concept (Alvim II Plus, Neodent, Curitiba, Brazil) (Certain Prevail, Biomet 3i, Florida, USA). These models were submitted to two compressive loads, axial from 20 kgf (load I) and another (load II), inclined 45° from 10 kgf. During the qualitative analysis, digital pictures were taken from a polariscope, for each load situation. For the quantitative analyses in both situations of load, the medium, minimum and maximum in MPa values of shear strain were determined in the cervical and apical site. The Kruskal-Wallis test was used to compare the results between the different systems and between cervical and apical site were compared using Mann-Whitney U test. Results: The results from qualitative analysis showed less concentration of strain in the cervical area to the internal hex plus platform switching (Certain Prevail), in both situation of load. The same results were get in the quantitative analysis, showing less stress concentrations around the implant Certain Prevail with internal hex plus the novel design (17.9 MPa to load I and 29.5 MPa to load II), however, without statistical significant difference between the systems. Conclusion: The minor stress concentration strongly suggest the use of platform switching design as a manner to prevent bone loss around the implant-abutment platform. Clinical Significance: From the result of this study its possible to make clinical decision for implant system which provides implant components with platform switching characteristics.

Efetividade de parafusos com tratamento de superfície na estabilidade de pilares em zircônia após carga cíclica

Pós-graduação em Reabilitação Oral - FOAR

Influência do tipo de pilar de resistência mecânica pré-ciclagem, quantidade de toque retido e desajuste vertical pré e pós-ciclagem, com análise estrutural em MEV

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo do comportamento biomecânico em protocolos modificados de Branemark (conceito All-on-Four): análise por extensometria linear elétrica

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)