X-ray-diffraction study of quasipseudomorphic ErSi1.7 layers formed by channeled ion-beam synthesis

ErSi1.7 layers with high crystalline quality (chi(min) of Er is 1.5%) have been formed by 90 keV Er ion implantation to a dose of 1.6X10(17)/cm(2) at 450 degrees C using channeled implantation. The perpendicular and parallel elastic strain e(perpendicular to)=-0.94%+/-0.02% and e(parallel to)=1.24%+/-0.08% of the heteroepitaxial erbium silicide layers have been measured with symmetric and asymmetric x-ray reflections using a double-crystal x-ray diffractometer. The deduced tetragonal distortion e(T(XRD))=e(parallel to)-e(perpendicular to)=2.18%+/-0.10%, which is consistent with the value e(T(RBS))2.14+/-0.17% deduced from the Rutherford backscattering and channeling measurements. The quasipseudomorphic growth of the epilayer and the stiffness along a and c axes of the epilayer deduced from the x-ray diffraction are discussed.

Structural study of YSi1.7 layers formed by channeled ion beam synthesis

High quality YSi1.7 layers (chi(min) of Y is 3.5%) have been formed by 60 keV Y ion implantation in Si (111) substrates to a dose of 1.0 x 10(17)/cm(2) at 450 degrees C using channeled ion beam synthesis (CIBS). It shows that, compared to the conventional nonchanneled ion beam synthesis, CIBS is beneficial in forming YSi1.7 layers with better quality due to the lower defect density created in the implanted layer. Rutherford backscattering/channeling and x-ray diffraction have been used to study the structure and the strain of the YSi1.7 layers. The perpendicular and parallel elastic strains of the YSi1.7 epilayer are e(perpendicular to) = -0.67% +/- 0.02% and e(parallel to) = +1.04% +/- 0.08%. The phenomenon that a nearly zero mismatch of the YSi1.7/Si (111) system results in a nonpseudomorphic epilayer with a rather large parallel strain relative to the Si substrate (epsilon(parallel to) = +1.09%) is explained, and the model is further used to explain the elastic strain of epitaxial ErSi1.7 and GdSi1.7 rare-earth silicides. (C) 1998 American Vacuum Society.

Estudo de microscopia eletronica de varredura e transmissão de pregas vocais de idosos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Tensile properties of Si nanowires with faulted stacking layers

Semiconductor nanowires (NWs) show tremendous applications in micro/nano-electro-mechanical systems. In order to fulfill their promising applications, an understanding of the mechanical properties of NWs becomes increasingly important. Based on the large-scale molecular dynamics simulations, this work investigated the tensile properties of Si NWs with different faulted stacking layers. Different faulted stacking layers were introduced around the centre of the NW by the insertion or removal of certain stacking layers, inducing twins, intrinsic stacking fault, extrinsic stacking fault, and 9R crystal structure. Stress–strain curves obtained from the tensile deformation tests reveal that the presence of faulted stacking layers has induced a considerable decrease to the yield strength while only a minor decrease to Young's modulus. The brittle fracture phenomenon is observed for all tested NWs. In particular, the formation of a monatomic chain is observed for the perfect NW, which exists for a relatively wide strain range. For the defected NW, the monatomic chain appears and lasts shorter. Additionally, all defected NWs show a fracture area near the two ends, in contrast to the perfect NW whose fracture area is adjacent to the middle. This study provides a better understanding of the mechanical properties of Si NWs with the presence of different faulted stacking layers.

Uniformity in Bias Tilt for Nematics Oriented by Polyvinyl Alcohol Surface Layers

Uniformity in bias tilt, for the polyvinyl alcohol(PVA)surface layer induced orientation of nematic liquid crystals, could be achieved for large area display panels, if one of the transparent electrodes is first directionally rubbed with fine abrasive; then both the electrodes coated with PVA, followed by directionally buffing the chemisorbed layers in the same direction. Uniformity may be due to increased 'train' configuration of the adsorbed macromolecule by falling on to microgrooves and maintaining the same sense of asymmetry for the looped segments.

Effects of compressibility and heat release on entrainment processes in mixing layers

Characteristics of the process of entrainment in plane mixing layers, and the changes with compressibility and heat release, were studied using temporal DNS with simultaneous fluid packet tracking. Convective Mach numbers of the simulations are 0.15, 0.7 and 1.1. The Reynolds number is quite high (between 11 000 and 37 000 based on layer width and velocity difference), and is above the mixing transition. The study agrees with recent findings in round jets: first, engulfed fluid volume and its growth rate are both very small compared with the volume of the turbulent region and its growth rate, respectively. Secondly, most often, the process occurs close to the turbulent-nonturbulent boundaries. A new finding is that both compressibility and heat release retard the entrainment process so that it takes an O(1) time for vorticity or scalar levels to grow even after growth has been initiated. This delay is manifested as the fall in mixing layer growth rates as compressibility and heat release levels increase.

The significance of brittle reaction layers in fusing of dental ceramics to titanium

This thesis comprises four intercomplementary parts that introduce new approaches to brittle reaction layers and mechanical compatibility of metalloceramic joints created when fusing dental ceramics to titanium. Several different methods including atomic layer deposition (ALD), sessile drop contact angle measurements, scanning acoustic microscopy (SAM), three-point bending (TPB, DIN 13 927 / ISO 9693), cross-section microscopy, scanning electron microscopy (SEM), and energy dispersive X-ray spectroscopy (EDS) were employed. The first part investigates the effects of TiO2 layer structure and thickness on the joint strength of the titanium-metalloceramic system. Samples with all tested TiO2 thicknesses displayed good ceramics adhesion to Ti, and uniform TPB results. The fracture mode was independent of oxide layer thickness and structure. Cracking occurred deeper inside titanium, in the oxygen-rich Ti[O]x solid solution surface layer. During dental ceramics firing TiO2 layers dissociate and joints become brittle with increased dissolution of oxygen into metallic Ti and consequent reduction in the metal plasticity. To accomplish an ideal metalloceramic joint this needs to be resolved. The second part introduces photoinduced superhydrophilicity of TiO2. Test samples with ALD deposited anatase TiO2 films were produced. Samples were irradiated with UV light to induce superhydrophilicity of the surfaces through a cascade leading to increased amount of surface hydroxyl groups. Superhydrophilicity (contact angle ~0˚) was achieved within 2 minutes of UV radiation. Partial recovery of the contact angle was observed during the first 10 minutes after UV exposure. Total recovery was not observed within 24h storage. Photoinduced ultrahydrophilicity can be used to enhance wettability of titanium surfaces, an important factor in dental ceramics veneering processes. The third part addresses interlayers designed to restrain oxygen dissolution into Ti during dental ceramics fusing. The main requirements for an ideal interlayer material are proposed. Based on these criteria and systematic exclusion of possible interlayer materials silver (Ag) interlayers were chosen. TPB results were significantly better in when 5 μm Ag interlayers were used compared to only Al2O3-blasted samples. In samples with these Ag interlayers multiple cracks occurred inside dental ceramics, none inside Ti structure. Ag interlayers of 5 μm on Al2O3-blasted samples can be efficiently used to retard formation of the brittle oxygen-rich Ti[O]x layer, thus enhancing metalloceramic joint integrity. The most brittle component in metalloceramic joints with 5 μm Ag interlayers was bulk dental ceramics instead of Ti[O]x. The fourth part investigates the importance of mechanical interlocking. According to the results, the significance of mechanical interlocking achieved by conventional surface treatments can be questioned as long as the formation of the brittle layers (mainly oxygen-rich Ti[O]x) cannot be sufficiently controlled. In summary in contrast to former impressions of thick titanium oxide layers this thesis clearly demonstrates diffusion of oxygen from sintering atmosphere and SiO2 to Ti structures during dental ceramics firing and the following formation of brittle Ti[O]x solid solution as the most important factors predisposing joints between Ti and SiO2-based dental ceramics to low strength. This among other predisposing factors such as residual stresses created by the coefficient of thermal expansion mismatch between dental ceramics and Ti frameworks can be avoided with Ag interlayers.

Structure of the Indian southwesterly pre-monsoon and monsoon boundary layers: Observations and numerical simulation

Characteristics of pre-monsoon and monsoon boundary layer structure and turbulence were studied in New Delhi and Bangalore, India during the summer of 1987. Micrometeorological towers were installed and instrumented at these locations to provide mean and turbulent surface layer measurements, while information on the vertical structure of the atmosphere was obtained using miniradiosondes. Thermal structures of the pre-monsoon and monsoon boundary layers were quite distinct. The daytime, pre-monsoon boundary layer observed over New Delhi was much deeper than that of the monsoon boundary layer observed over Bangalore and at times was characterized by multiple inversions. Surface, turbulent sensible heat fluxes at both sites were approximately the same (235 and 200 Wm−2 for New Delhi and Bangalore, respectively). Diurnal variations in the monsoon boundary layer at Bangalore were more regular compared to those under pre-monsoon conditions at New Delhi. One-dimensional numerical simulations of the pre-monsoon boundary layer using a turbulent energy closure scheme show good agreement with observations.

Liquid phase epitaxial growth of pure and doped GaSb layers: morphological evolution and native defects

Undoped and Te-doped gallium antimonide (GaSb) layers have been grown on GaSb bulk substrates by the liquid phase epitaxial technique from Ga-rich and Sb-rich melts. The nucleation morphology of the grown layers has been studied as a function of growth temperature and substrate orientation. MOS structures have been fabricated on the epilayers to evaluate the native defect content in the grown layers from the C-V characteristics. Layers grown from antimony rich melts always exhibit p-type conductivity. In contrast, a type conversion from p- to n- was observed in layers grown from gallium rich melts below 400 degrees C. The electron mobility of undoped n-type layers grown from Ga-rich melts and tellurium doped layers grown from Sb- and Ga-rich solutions has been evaluated.

Effect of Constant and Cyclic Current Stressing on the Evolution of Intermetallic Compound Layers

In this paper the effects of constant and cyclic power loads on the evolution of interfacial reaction layers in lead-free solder interconnections are presented. Firstly, the differences in the growth behavior of intermetallic compound (IMC) layers at the cathode and anode sides of the interconnections are rationalized. This is done by considering the changes in the intrinsic fluxes of elements owing to electromigration as well as taking into account the fact that the growth of Cu3Sn and Cu6Sn5 are coupled via interfacial reactions. In this way, better understanding of the effect of electron flux on the growth of each individual layer in the Cu-Sn system can be achieved. Secondly, it is shown that there is a distinct difference between steady-state current stressing (constant current, constant temperature) and power cycling with alternating on- and off-cycle periods (accompanied by a change of temperature). The reasons behind the observed differences are subsequently discussed. Finally, special care is taken to ensure that the current densities are chosen in such a way that there is no risk for even partial melting of the solder interconnections.

Indium flux, growth temperature and RF power induced effects in InN layers grown on GaN/Si substrate by plasma-assisted MBE

In the present work, we report the growth of wurtzite InN epilayers on GaN/Si (1 1 1) substrate by plasma-assisted molecular beam epitaxy (PAMBE). The growth parameters such as indium flux, substrate temperature and RF power affect the crystallographic and morphological properties of InN layers, which were evaluated using high resolution X-ray diffraction (HRXRD) analysis and atomic force microscopy (AFM). It is found that excess indium (In) concentrations and surface roughness were increased with increase in In flux and growth temperature. The intensity of HRXRD (0 0 0 2) peak, corresponding to c-axis orientation has been increased and full width at half maxima (FWHM) has decreased with increase in RF power. It was found that highly c-axis oriented InN epilayers can be grown at 450 degrees C growth temperature, 450 W RF power and 1.30 x 10(-7) mbar In beam equivalent pressure (BEP). The energy gap of InN layers grown by optimizing growth conditions was determined by photoluminescence and optical absorption measurement. (C) 2011 Elsevier B.V. All rights reserved.