Influence of fluoride dentifrice on brushing abrasion of eroded human enamel: An in situ/ex vivo study

This in situ/ex vivo study assessed the effect of fluoride dentifrice on eroded enamel subjected to brushing abrasion. In a crossover study performed in 2 phases, 10 volunteers wore acrylic palatal appliances, each containing 3 human enamel blocks. Dentifrice was used to brush the volunteers' teeth and the specimens subjected to abrasion. In phases A and B the dentifrices used had the same formulation, except for the absence or presence of fluoride, respectively. The blocks were subjected to erosion by immersion of the appliances in a cola drink for 5 min, 4 times a day. Then the blocks were brushed, and the appliance was replaced into the mouth. Enamel alterations were determined using profilometry and percentage change in surface microhardness (%SMHC) tests. The data were tested using the paired t test. The mean wear values (+/- SD, mu m) were: group A 6.84 +/- 1.72 and group B 5.38 +/- 1.21 (p = 0.04). The mean %SMHC values (+/- SD) were: group A 54.6 +/- 16.2 and group B 45.7 +/- 6.8 (p = 0.04). Fluoride dentifrice had a protective effect on eroded enamel subjected to brushing abrasion. Copyright (c) 2007 S. Karger AG, Basel.

In situ effect of chewing gum containing CPP–ACP on the mineral precipitation of eroded bovine enamel

Objectives: Stimulation of salivary flow is considered a preventive strategy for dental erosion. Alternatively, products containing calcium phosphate, such as a complex of casein phosphopeptide–amorphous calcium phosphate (CPP–ACP), have also been tested against dental erosion. Therefore, this in situ study analyzed the effect of chewing gum containing CPP–ACP on the mineral precipitation of initial bovine enamel erosion lesions. Methods: Twelve healthy adult subjects wore palatal appliances with two eroded bovine enamel samples. The erosion lesions were produced by immersion in 0.1% citric acid (pH 2.5) for 7 min. During three experimental crossover in situ phases (1 day each), the subjects chewed a type of gum, 3 times for 30 min, in each phase: with CPP–ACP (trident total), without CPP–ACP (trident), and no chewing gum (control). The Knoop surface microhardness was measured at baseline, after erosion in vitro and the mineral precipitation in situ. The differences in the degree of mineral precipitation were analyzed using repeated measures (RM-) ANOVA and post hoc Tukey’s test ( p < 0.05). Results: Significant differences were found among the remineralizing treatments ( p < 0.0001). Chewing gum (19% of microhardness recovery) improved the mineral precipitation compared to control (10%) and the addition of CPP–ACP into the gum promoted the best mineral precipitation effect (30%). Conclusions: Under this protocol, CPP–ACP chewing gum improved the mineral precipitation of eroded enamel. Clinical significance: Since the prevalence of dental erosion is steadily increasing, CPP–ACP chewing gum might be an important strategy to reduce th eprogression of initial erosion lesions.

In Vitro Evaluation of Enamel Erosion After Nd:YAG Laser Irradiation and Fluoride Application

Objective: Previous investigations have demonstrated improved enamel demineralization resistance after laser irradiation. Due to the possibility of a synergistic effect between laser and fluoride, this study investigated the effect of fluoridated agents and Nd:YAG irradiation separately and in combination on enamel resistance to erosion. Methods: One hundred bovine enamel blocks were randomly divided into 10 groups: G1, untreated (control); G2, acidic phosphate fluoride (APF) (1.23% F) for 4 min; G3, fluoride varnish for 6 h (NaF, 2.26%); G4, 0.5 W Nd: YAG laser (250 mm pulse width, 10 Hz, 35 J/cm(2), with uniform velocity for 30 sec in each application); G5, 0.75 W Nd:YAG laser (52.5 J/cm(2)); G6, 1.0 W Nd:YAG laser (70 J/cm(2)); G7, APF + 0.75 W Nd:YAG laser; G8, 0.75 W Nd:YAG laser + APF; G9, fluoride varnish + 0.75 W Nd:YAG laser; and G10, 0.75 W Nd:YAG laser + fluoride varnish. During 10 d the erosive cycle was conducted by immersion of the blocks in Sprite light for 1 min, followed by immersion in artificial saliva for 59 min. This procedure was consecutively repeated four times per day. In each day, during the remaining 20 h, the blocks were maintained in artificial saliva. The wear was evaluated by profilometry (days 5 and 10). Data were tested by two-way ANOVA and Bonferroni's tests (p < 0.05). Results: The mean wear at days 5 and 10 was, respectively: G1, 1.83 and 2.67 mu m; G2, 1.04 and 2.60 mu m; G3, 1.03 and 2.48 mu m; G4, 1.13 and 2.47 mu m; G5, 1.07 and 2.44 mu m; G6, 1.0 and 2.35 mu m; G7, 0.75 and 2.27 mu m; G8, 0.80 and 2.12 mu m; G9, 0.76 and 2.47 mu m; and G10, 1.09 and 2.46 mu m. At day 5, all the experimental groups presented significant lesser wear when compared to control group. However, at 10 d, only G7 and G8 were still different from control. Conclusions: The association between APF application and laser irradiation seems to be an alternative preventive measure against dental erosion.

Prevention of toothbrushing abrasion of acid-softened enamel by CO(2) laser irradiation

Objective: The aim of the present study was to evaluate the effect of CO(2) laser irradiation (10.6 mu m) at 0.3 J/cm(2) (0.5 mu s; 226 Hz) on the resistance of softened enamel to toothbrushing abrasion, in vitro. Methods: Sixty human enamel samples were obtained, polished with silicon carbide papers and randomly divided into five groups (n = 12), receiving 5 different surface treatments: laser irradiation (L), fluoride (AmF/NaF gel) application (F), laser prior to fluoride (LF), fluoride prior to laser (FL), non-treated control (C). After surface treatment they were submitted to a 25-day erosive-abrasive cycle in 100 ml sprite light (90 s) and brushed twice daily with an electric toothbrush. Between the demineralization periods samples were immersed in supersaturated mineral solution. At the end of the experiments enamel surface loss was determined using a contact profilometer and morphological analysis was performed using scanning electron microscopy (SEM). For SEM analysis of demineralization pattern, cross-sectional cuts of cycled samples were prepared. The data were statistically analysed by one-way ANOVA model with subsequent pairwise comparison of treatments. Results: Abrasive surface loss was significantly lower in all laser groups compared to both control and fluoride groups (p < 0.0001 in all cases). Amongst the laser groups no significant difference was observed. Softened enamel layer underneath lesions was less pronounced in laser-irradiated samples. Conclusion: Irradiation of dental enamel with a CO(2) laser at 0.3 J/cm(2) (5 mu s, 226 Hz) either alone or in combination with amine fluoride gel significantly decreases toothbrushing abrasion of softened-enamel, in vitro. (C) 2011 Elsevier Ltd. All rights reserved.

Effect of Different Fluoride Concentrations of Experimental Dentifrices on Enamel Erosion and Abrasion

It has been suggested that fluoride products are able to reduce erosive tooth wear. Thus, the purpose of this in vitro study was to evaluate the effect of dentifrices with different fluoride concentrations as well as of a low-fluoridated dentifrice supplemented with trimetaphosphate (TMP) on enamel erosion and abrasion. One hundred twenty bovine enamel blocks were assigned to the following experimental dentifrices: placebo, 1,100 mu g F/g, 500 mu g F/g plus 3% TMP and 5,000 mu g F/g. The groups of enamel blocks were additionally subdivided into conditions of erosion (ERO) and of erosion plus abrasion (ERO + ABR). For 7 days, the blocks were subjected to erosive challenges (immersion in Sprite (R) 4 times a day for 5 min each time) followed by a remineralizing period (immersion in artificial saliva between erosive challenges for 2 h). After each erosive challenge, the blocks were exposed to slurries of the dentifrices (10 ml/sample for 15 s). Sixty of the blocks were additionally abraded by brushing using an electric toothbrush (15 s). The alterations of the enamel were quantified using the Knoop hardness test and profilometry (measurements in micrometers). The data were analyzed using a 2-way ANOVA test followed by a Bonferroni correction (p < 0.05). In in vitro conditions, the 5,000 mu g F/g and 500 mu g F/g plus 3% TMP dentifrices had a greater protective effect when compared with the 1,100 mu g F/g dentifrice, under both ERO and ERO + ABR conditions. The results suggest that dentifrices alone are not capable of completely inhibiting tooth wear. Copyright (C) 2010 S. Karger AG, Basel

The efficacy of a highly concentrated fluoride dentifrice on bovine enamel subjected to erosion and abrasion

Background. Researchers have proposed the use of fluoride for the prevention of enamel wear; however, only limited information is available about the impact of fluoridated dentifrices. Because tooth wear is a well-recognized dental problem, the authors conducted an in situ, ex vivo study to assess the efficacy of a highly concentrated fluoride dentifrice on bovine enamel subjected to erosion and abrasion. Methods. The authors conducted a double-blind, crossover in situ study consisting of three phases (seven days each). In each phase, the authors tested one of the dentifrices (5,000 parts per million fluoride [F]; 1,100 ppm F; no F). They performed erosive challenges with the use of cola drink (60 seconds, four times per day) and abrasive challenges via toothbrushing (30 seconds, four times per day). The authors determined the enamel loss via profilometry. Results. The authors tested the data by using two-way analysis of variance (P <.05). For the erosion-plus-abrasion condition, the study results showed that enamel wear was significantly higher than that with erosion alone. The findings showed no significant differences between the dentifrices regarding enamel wear. Conclusions. Within the in situ, ex vivo conditions of this study, the authors concluded that the highly concentrated fluoride dentifrice did not have a protective effect on enamel against erosion and erosion plus toothbrushing abrasion. Clinical Implications. Patients at risk of developing enamel erosion should benefit from preventive measures other than fluoride dentifrice, because even a highly concentrated fluoride dentifrice does not appear to prevent enamel erosion.

Probing the Enamel Topography After Acid Erosion by Scanning Electrochemical Microscopy

In this work, we present an investigation on the thickness of the eroded enamel layer in tooth samples after exposure to citric and hydrochloric acid by using Scanning Electrochemical Microscopy (SECM). Approaching curves with typical negative feedback behavior were obtained in enamel samples for evaluation of topographic changes. In a control experiment, SECM images showed no significant difference in the current monitored during the scan, implying that enamel demineralization did not occur in mineral water medium. Topographic SECM images obtained after contact with citric and hydrochloric acid for different periods of time showed a significant increase in the current relative to a previously protected surface, indicating the structural loss of enamel. The thickness of the enamel layer eroded after contact with hydrochloric acid was significantly higher when compared to the one obtained with citric acid. Hence, our results showed that the enamel acid erosion is a relatively fast process, which is strongly dependent on parameters such as pH, time, acid strength and acid concentration.

Application of the specular and diffuse reflection analysis for in vitro diagnostics of dental erosion: correlation with enamel softening, roughness, and calcium release

We present assembly and application of an optical reflectometer for the analysis of dental erosion. The erosive procedure involved acid-induced softening and initial substance loss phases, which are considered to be difficult for visual diagnosis in a clinic. Change of the specular reflection signal showed the highest sensitivity for the detection of the early softening phase of erosion among tested methods. The exponential decrease of the specular reflection intensity with erosive duration was compared to the increase of enamel roughness. Surface roughness was measured by optical analysis, and the observed tendency was correlated with scanning electron microscopy images of eroded enamel. A high correlation between specular reflection intensity and measurement of enamel softening (r(2) ? -0.86) as well as calcium release (r(2) ? -0.86) was found during erosion progression. Measurement of diffuse reflection revealed higher tooth-to-tooth deviation in contrast to the analysis of specular reflection intensity and lower correlation with other applied methods (r(2) = 0.42-0.48). The proposed optical method allows simple and fast surface analysis and could be used for further optimization and construction of the first noncontact and cost-effective diagnostic tool for early erosion assessment in vivo.

Effects of enamel abrasion, salivary pellicle, and measurement angle on the optical assessment of dental erosion

The present study assessed the effects of abrasion, salivary proteins, and measurement angle on the quantification of early dental erosion by the analysis of reflection intensities from enamel. Enamel from 184 caries-free human molars was used for in vitro erosion in citric acid (pH 3.6). Abrasion of the eroded enamel resulted in a 6% to 14% increase in the specular reflection intensity compared to only eroded enamel, and the reflection increase depended on the erosion degree. Nevertheless, monitoring of early erosion by reflection analysis was possible even in the abraded eroded teeth. The presence of the salivary pellicle induced up to 22% higher reflection intensities due to the smoothing of the eroded enamel by the adhered proteins. However, this measurement artifact could be significantly minimized (p<0.05) by removing the pellicle layer with 3% NaOCl solution. Change of the measurement angles from 45 to 60 deg did not improve the sensitivity of the analysis at late erosion stages. The applicability of the method for monitoring the remineralization of eroded enamel remained unclear in a demineralization/remineralization cycling model of early dental erosion in vitro.

Sodium bicarbonate solution as an anti-erosive agent against simulated endogenous erosion

This study investigated whether sodium bicarbonate solution, applied on enamel previously exposed to a simulated intrinsic acid, can control dental erosion. Volunteers wore palatal devices containing enamel slabs, which were exposed twice daily extra-orally to hydrochloric acid (0.01 M, pH 2) for 2 min. Immediately afterwards, the palatal devices were re-inserted in the mouth and volunteers rinsed their oral cavity with a sodium bicarbonate solution or deionized water for 60 s. After the washout period, the palatal devices were refilled with a new set of specimens and participants were crossed over to receive the alternate rinse solution. The surface loss and surface microhardness (SMH) of specimens were assessed. The surface loss of eroded enamel rinsed with a sodium bicarbonate solution was significantly lower than the surface loss of eroded enamel rinsed with deionized water. There were no differences between treatments with sodium bicarbonate and deionized water for SMH measurements. Regardless of the solution used as an oral rinse, eroded enamel showed lower SMH than uneroded specimens. Rinsing with a sodium bicarbonate solution after simulated endogenous erosive challenge controlled enamel surface loss but did not alter the microhardness.

Toothbrushing after an erosive attack: will waiting avoid tooth wear?

The purpose of this study was to determine if storage for up to 4 h in human saliva results in a decrease of erosive tooth wear (ETW) and in an increase of surface microhardness (SMH) of enamel samples after an erosive attack with subsequent abrasion. Furthermore, we determined the impact of individual salivary parameters on ETW and SMH. Enamel samples were distributed into five groups: group 1 had neither erosion nor saliva treatment; groups 2-5 were treated with erosion, then group 2 was placed in a humid chamber and groups 3-5 were incubated in saliva for 30 min, 2 h, and 4 h, respectively. After erosion and saliva treatments, all groups were treated with abrasion. Surface microhardness and ETW were measured before and after erosion, incubation in saliva, and abrasion. Surface microhardness and ETW showed significant changes throughout the experiment: SMH decreased and ETW increased in groups 2-5, regardless of the length of incubation in saliva. The results of groups 3-5 (exposed to saliva) were not significantly different from those of group 2 (not exposed to saliva). Exposure of eroded enamel to saliva for up to 4 h was not able to increase SMH or reduce ETW. However, additional experiments with artificial saliva without proteins showed protection from erosive tooth wear. The recommendation to postpone toothbrushing of enamel after an erosive attack should be reconsidered.

Effect of toothpastes with different abrasives on eroded human enamel: an in situ/ex vivo study

The aim of the present study was to investigate the abrasive effect of CaCO3 and SiO2-based fluoride-free experimental toothpastes on eroded human permanent dental enamel and evaluate the effectiveness of waiting periods between acid exposure and tooth brushing. Twelve volunteers wore palatal appliances containing human enamel blocks for two periods of five days each. The appliances were immersed in a soft drink for five minutes four times a day (9:00 am, 11:00 am, 2:00 pm and 4:00 pm). On two occasions, two blocks were not submitted to additional treatment; two blocks were brushed (30 s) either with a CaCO3 or SiO2 toothpaste immediately after erosion and two blocks were brushed 1 h after erosion. Thus, the sample was divided into six groups: erosion alone (CaCO3 and SiO2 control); brushing with fluoride- free toothpaste (CaCO3 immediate and 1 h after erosion; SiO2 immediate and 1 h after erosion). Significant differences in wear depth were found between the enamel blocks in the CaCO3 immediate and 1 h after erosion groups and the blocks in the CaCO3 control group (p=0.001; p=0.022). No significant differences were found regarding the change in roughness and wear depth between blocks submitted to immediate abrasion and 1 h after erosion (CaCO3 and SiO2). The data revealed that surface roughness and wear depth is increased when erosion is combined with dental abrasion, regardless of the abrasive used. Waiting for 1 h to brush the eroded blocks offered no protective effect.

Effect of a Single Application of TiF(4) and NaF Varnishes and Solutions Combined with Nd:YAG Laser Irradiation on Enamel Erosion in Vitro

Objective: This in vitro study aimed to analyze the influence of neodymium-doped yttrium aluminum garnet (Nd:YAG) laser irradiation on the efficacy of titanium tetrafluoride (TiF(4)) and sodium fluoride (NaF) varnishes and solutions to protect enamel against erosion. Background data: The effect of Nd:YAG laser irradiation on NaF and AmF was analyzed; however, there is no available data on the interaction between Nd:YAG laser irradiation and TiF(4). Methods: Bovine enamel specimens were pre-treated with NaF varnish, TiF(4) varnish, NaF solution, TiF(4) solution, placebo varnish, Nd:YAG (84.9 J/cm(2)), Nd:YAG prior to or through NaF varnish, Nd:YAG prior to or through TiF(4) varnish, Nd:YAG prior to or through NaF solution, Nd:YAG prior to or through TiF(4) solution, and Nd:YAG prior to or through placebo varnish. Controls remained untreated. Ten specimens in each group were then subjected to an erosive demineralization (Sprite Zero, 4x90 s/day) and remineralization (artificial saliva, between the erosive cycles) cycling for 5 days. Enamel loss was measured profilometrically (mu m). Additionally, treated but non-eroded specimens were additionally analyzed by scanning electron microscope (SEM) (each group n-2). The data were statistically analyzed by ANOVA and Tukey's post-hoc test (p < 0.05). Results: Only TiF(4) varnish (1.8 +/- 0.6 mu m), laser prior to TiF(4) varnish (1.7 +/- 0.3 mu m) and laser prior to TiF(4) solution (1.4 +/- 0.3 mu m) significantly reduced enamel erosion compared to the control (4.1 +/- 0.6 mu m). SEM pictures showed that specimens treated with TiF(4) varnish presented a surface coating. Conclusions: Nd:YAG laser irradiation was not effective against enamel erosion and it did not have any influence on the efficacy of F, except for TiF(4) solution. On the other hand, TiF(4) varnish protected against enamel erosion, without the influence of laser irradiation.

Protective effect of different tetrafluorides on erosion of pellicle-free and pellicle-covered enamel and dentine

The aim was to analyze the protective effects of titanium, zirconium and hafnium tetrafluorides on erosion of pellicle-free and pellicle-covered enamel and dentine in vitro. Eight groups of 20 specimens each of bovine enamel and bovine dentine were prepared. Half the specimens in each group were immersed in human saliva for 2 h for pellicle formation. Specimens were then left untreated (controls) or were treated for 120 s with TiF(4), ZrF(4) or HfF(4) solutions (0.4 or 1%) or 1.25% AmF/NaF gel. All specimens were eroded by exposure to hydrochloric acid, pH 2.6, for 25 min. Cumulative calcium release into the acid was monitored in consecutive 30-second intervals for 5 min, then at 2-min intervals up to a total erosion time of 25 min using the Arsenazo III procedure. Data were analyzed by ANOVA. 1% TiF(4) solution offered the best protective effect, especially in dentine (reduction of calcium loss about 50% at 25 min). 1% ZrF 4, 1% HfF 4 and 0.4% TiF(4) also reduced calcium loss, but to a lesser extent. Long-term effects were limited to dentine, while reduction of enamel erosion (about 25%) was restricted to 1-min erosion. The fluoride gel had a protective effect only in dentine. The efficacy of the tetrafluorides was influenced by the presence of the pellicle layer, in that the protection against dentine erosion by TiF(4) and ZrF(4) was greater on pellicle-covered specimens. Tetrafluoride solutions, especially 1% TiF(4), could decrease dental erosion, but were more effective on dentine than on enamel. Copyright (C) 2008 S. Karger AG, Basel.

Potential effect of sodium bicarbonate-containing dentifrice in controlling enamel erosion in situ

Purpose: To assess, by a crossover 2 x 2 in situ study, the speculated protective role of a sodium bicarbonate-containing toothpaste in controlling erosive lesions. Methods: Bovine enamel slabs were sterilized, and submitted to baseline Knoop microhardness measurements. After a 3-day lead-in period, 14 volunteers wore palatal acrylic appliances containing six enamel slabs (three on each side), for 4 consecutive days. On the first day, appliances with contained specimens were placed in the oral cavity to allow salivary pellicle formation. On the subsequent days, half of the enamel slabs were immersed extraorally in a lemonade-like soft drink for 90 seconds, twice daily. On both of these occasions, the appliance was dipped in toothpaste slurry of either a sodium bicarbonate-containing toothpaste or a regular counterpart for 60 seconds. Following a 3-day washout period, a new set of enamel slabs were mounted and the volunteers started the second period using the alternate dentifrice. Results: ANOVA (alpha = 0.05) showed no statistically significant difference between enamel treated with regular and sodium bicarbonate-based dentifrices, regardless of whether specimens were eroded or not (P=0.8430). Acid-challenged specimens revealed lower microhardness values than uneroded samples. (Am J Dent 2008;21:300-302).