Spectroscopic properties and upconversion mechanisms in Er3+-doped fluoroindate glasses

Fluorindate glasses containing 1,2,3,4 ErF3 mol % were prepared in a dry box under argon atmosphere. Absorption, Stokes luminescence (under visible and infrared excitation), the dependence of 4S3/2, 4I11/2, and 4I13/2 lifetimes with Er concentration, and upconversion under Ti-saphire laser excitation at λ=790 nm were measured, mostly at T=77 and 300 K. The upconversion results in a strong green emission and weaker blue and red emissions whose intensity obeys a power-law behavior I∼Pn, where P is the infrared excitation power and n=1.6, 2.1, and 2.9 for the red, green, and blue emissions, respectively. The red emission exponent n=1.5 can be explained by a cross relaxation process. The green and blue emissions are due to excited state absorption (ESA) and energy transfer (ET) processes that predict a factor n=2 and n=3 for the green and blue emissions, respectively. From transient measurements we concluded that for lightly doped samples the green upconverted emission is originated due to both processes ESA and ET. However, for heavily doped samples ET is the dominant process.

Frequency upconversion in Er3+-doped fluoroindate glasses pumped at 1.48 μm

We report on efficient frequency upconversion in Er3+-doped fluoroindate glass. The process is observed under 1.48 μm laser diode excitation and results in fluorescence generation in the range from ultraviolet to near-infrared radiation. The study was performed for samples containing 1, 2, and 3 ErF3 mol % in the range of temperatures from 24 to 448 K. The upconverted signals were studied as a function of the laser intensity, and their dynamical behavior is described using a rate equation model which allows us to obtain the energy transfer rates between Er3+ ions in pairs and triads.

Optical spectroscopy of Er3+ and Yb3+ co-doped fluoroindate glasses

Optical absorption, Stokes, and anti-Stokes photoluminescence were performed on Er3+-Yb3+ co-doped fluoroindate glasses. For compounds prepared with a fixed 2 mol % ErF3 concentration and YbF3 contents ranging from 0 to 8 mol %, important upconversion processes were observed as a function of temperature and photon excitation energy. Based on the experimental data, two mechanisms for the upconversion (or anti-Stokes photoluminescence) processes were identified and analyzed in detail. At high Yb contents, the upconversion mechanisms are mostly determined by the population of the 2F5/2 levels of Yb3+ ions (or 4I11/2 levels of Er3+ ions, by energy transfer) regardless of the photon excitation energy and temperature of measurement. Moreover, green and red light emission have similar intensities when a large Yb3+ content is present. © 1998 American Institute of Physics.

Negative nonlinear absorption in Er3+-doped fluoroindate glass

We report the observation of negative nonlinear absorption in fluoroindate glasses doped with erbium ions. The pumping wavelength is 800 nm which is doubly resonant with Er3+ ions transitions. A large nonlinear intensity dependence of the optical transmittance and strong upconverted fluorescence are obtained. The dependence of the upconverted fluorescence intensity with the laser power is described by a system of coupled-rate equations for the energy levels' populations. (C) 1998 American Institute of Physics. [S0021-8979(98)07816-5].

Enhanced frequency upconversion in Er3+ doped fluoroindate glass due to energy transfer from Tm3+

Energy transfer processes between Er3+ and Tm3+ were investigated examining the frequency upconversion emissions in a fluoroindate glass pumped at 790 nm. A 60-fold enhancement in the emission at ≈670 nm originating from Er3+ was observed when Tm3+ at concentration of 2% was introduced in a sample containing 2% of Er3+. The results are explained considering the influence of cross-relaxation processes between the active ions. © 2002 Elsevier Science B.V. All rights reserved.

Effect of lithium-potassium mixed alkali on spectroscopic properties of Er3+-doped aluminophosphate glasses

Er3+-doped lithium-potassium mixed alkali aluminophosphate glasses belonging to the oxide system xK(2)O-(15x)Li2O-4B(2)O(3)-11Al(2)O(3)-5BaO-65P(2)O(5) are obtained in a semi-continuous melting quenching process. Spectroscopic properties of Er3+-doped glass matrix have been analysed by fitting the experimental data with the standard Judd-Ofelt theory. It is observed that Judd-Ofelt intensity parameters-Omega(t)(t=2, 4 and 6) of Er3+ change when the second alkali is introduced into glass matrix. The variation of line strength S-ed[I-4(13/2),I-4(15/2)] follows the same trend as that of the Omega(6) parameter. The effect of mixed alkali on the spectroscopic properties of the aluminophosphate glasses, such as absorption cross-section, stimulated emission cross-section, spontaneous emission probability, branching ratio and the radiative lifetime, has also been investigated in this paper.

Influences of radiation trapping on spectroscopic properties of Er3+-doped fluorophosphate glasses

Fluorophosphate glasses with different contents of ErF3 were prepared. Due to the radiation trapping of Er, concentration dependence of the fluorescence lifetime is subject to distortion, and the stimulated-emission cross section calculated by the Fuchtbauer-Ladenburg equation is underestimated. The influence of radiation trapping on the measured fluorescence lifetime and width are investigated quantitatively. By comparing the intensity ratio of the 1556-1532 nm peak in the fluorescence spectrum with that in the stimulated-emission cross-section spectrum obtained according to the McCumber theory, the distortion ratio of fluorescence spectrum due to radiation trapping is obtained. An empirical way to quantitatively evaluate the influences of radiation trapping on fluorescence lifetime and width is proposed. (c) 2007 Optical Society of America.

Er3+-doped germanate glasses for active waveguides prepared by Ag+/K+ <-> Na+ ion-exchange

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Novel fabrication process of planar waveguides in rare-earth doped fluoroindate glasses

We report the successful fabrication of planar waveguides in rare-earth doped fluoroindate glass substrates. A new procedure for waveguide fabrication using a thermally evaporated AgF nonmetallic film was developed. The refractive index changes of more than 0.03, associated to low propagation losses achieved, open new perspectives and show the potentiality of using this glass family toward further developments in fabrication and design of integrated optical devices for optical communication wavelengths.© 1995 American Institute of Physics.

Time-resolved Z-scan and thermal lens measurements in Er+3 and Nd+3 doped fluoroindate glasses

In rare earth ion doped solids, a resonant non-linear refractive index, n2, appears when the laser pumps one of the ion excited states and the refractive index change is proportional to the excited state population. In these solids there are usually thermal and non-thermal lensing effects, where the non-thermal one is due to the polarizability difference, Δα, between excited and ground states of the ions. We have used the time resolved Z-scan and a mode-mismatched thermal lens technique with an Ar+ ion laser in Er+3 (20ZnF2-20SrF2-2NaF-16BaF2-6GaF3-(36 - x)InF3-xErF3, with x= 1, 2, 3 and 4 mol%) and Nd+3 (20SrF2-16BaF2-20ZnF2-2GdF3-2NaF-(40 - x)InF3-xNdF3, with x = 0.1, 0.25, 0.5-1 mol%) doped fluoroindate glasses. In both samples we found that the non-linear refraction is due to the thermal effect, while the non-thermal effect is negligible. This result indicates that in fluoride glasses Δα is very small (less than 10-26 cm3). We also measured the imaginary part of the non-linear refractive index (n″2) due to absorption saturation.

Violet-blue emissions due to frequency up-conversion in Nd3+-doped fluoroindate glasses

We report the observation of intense frequency up-conversion in Nd3+-doped fluoroindate glasses pumped by the second harmonic of a cw mode-locked Nd: YAG laser. Mechanisms for generating the observed emissions are discussed.

Optical properties of chromium-doped fluoroindate glasses

This work reports on the optical properties of Cr3+ ions in the pseudoternary system InF3-GdF3-GaF3. Linear properties, investigated through absorption and emission spectra, provide information on the crystal field, the frequency, and number of phonons emitted during the absorption to the 4T2 band and the emission to the 4A2 ground state, and the Fano antiresonance line shape in the vicinity of the 4A2→2E transition. A study of the nonlinear refractive index as a function of the wavelength, carried out with the Z-scan technique, provides spectroscopic data about electronic transitions starting from the excited state.

Violet and blue light amplification in Nd3+-doped fluoroindate glasses

We report optical gain at 382 and 414 nm from Nd3+-doped fluroindate glasses after excitation with lasers operating either at 583 or 532 nm. Stimulated emission due to a frequency upconversion process results in increase of the emitted violet and blue light intensity and emission line narrowing. Large optical gain is measured by pump-probe spectroscopy using samples with various Nd3+ concentrations. © 1999 American Institute of Physics.

Giant non-linear absorption in Er3+-doped fluoroindate glass

Non-linear absorption is observed in Er3+-doped fluoroindate glass (in mol% 37InF2:20ZnF2:20SrF2:16BaF2:2GdF2: 2NaF:1GaF3:2ErF3) when the sample is irradiated with a CW laser emitting at 650 nm. An intensity dependence of the optical transmittance is detected. Saturation and sequential absorption of two photons are responsible for the decrease of 50% in the transmittance. The results are explained by simple models which are solved based on rate-equations for the populations of energy levels.