Broadband amplification and upconversion luminescence properties of Er3+/Yb3+ co-doped fluorophosphate glass

Broadband and upconversion properties were studied in Er3+/Yb3+ co-doped fluorophosphate glasses. Large Omega(6) and S-ed/(S-ed + S-md) values and the flat gain profile over 1530-1585 nm indicate the good broadband properties of the glass system. And a premise of using Omega(6) as a parameter to estimate the broadband properties of the glasses is proposed for the first time to our knowledge. Results showed that fluorescence intensity, upconversion luminescence intensity, the intensity ratio of red/green light (656 nm/545 nm) are closely related to the Yb3+:Er3+ ratio and Er3+ concentration, and the corresponding calculated lifetime of F-4(9/2) and S-4(3/2) states for red and green upconversion samples proves this conclusion. The upconversion mechanism is also discussed. (c) 2005 Elsevier Ltd. All rights reserved.

Effects of PbF2 on the spectroscopic, lasing and structural properties of Yb3+-doped fluorophosphate glass

Effect of PbF2 on Yb3+ -doped fluorophosphate glasses is studied. Results indicate that proper amount of PbF2 has absolute advantages in improving the crystallization stability of fluorophosphate glasses. T, value performs a decreasing and increasing tendency with 25 mol% PbF2 as the turning-point. And the spectroscopic properties such as absorption and emission cross section, effective fluorescence linewidth are apparently enhanced with PbF2 over 25 mol%. Lasing parameters beta, I-sat and I-min increase slightly with the addition of PbF2. Raman analysis proves that over 20 mol% PbF2, destroys the phosphate vibration groups greatly. (c) 2005 Elsevier Ltd. All rights reserved.

Influence of TeO2, PbF2, ZnF2 on the spectroscopic and lasing properties of Yb3+ doped fluorophosphate glass

The influence of TeO2 on the crystallization stability, thermal stability, spectroscopic and lasing properties of Yb3+ doped fluorophosphate (FP) glass was studied. It is shown that 2 mol% TeO2 is the optimum doping amount which results in better spectroscopic and lasing properties as well as improve the crystallization and thermal stabilities of the glass. In order to enhance the physical and optical properties further, the effect of PbF2 and ZnF2 to the TeO2 contained FP glasses is also investigated, which shows that PbF2 has advantages in improving the crystallization properties while ZnF2 is preferable in enhancing spectroscopic and lasing properties. Results indicate that the co-existence of TeO2, PbF2 or ZnF2 is an effective way to enhance the spectroscopic, lasing and physical properties of Yb3+ doped FP glasses. (c) 2004 Published by Elsevier B.V.

Optical properties and energy transfer processes in (Tm3+, Nd3+) doped tungstate fluorophosphate glass

We investigate the linear optical properties and energy transfer processes in tungstate fluorophosphate glass doped with thulium (Tm3+) and neodymium (Nd3+) ions. The linear absorption spectra from 370 to 3000 nm were obtained. Transitions probabilities, radiative lifetimes, and transition branching ratios were determined using the Judd-Ofelt [Phys. Rev. 127, 750 (1962); J. Chem. Phys. 37, 511 (1962)] theory. Frequency up-conversion to the blue region and fluorescence in the infrared were observed upon pulsed excitation in the range of 630-700 nm. The excitation spectra of the luminescence were obtained to understand the origin of the signals. The temporal decay of the fluorescence was measured for different concentrations of the doping ions. Energy transfer rates among the Tm3+ and Nd3+ ions were also determined.

Influences of radiation trapping on spectroscopic properties of Er3+-doped fluorophosphate glasses

Fluorophosphate glasses with different contents of ErF3 were prepared. Due to the radiation trapping of Er, concentration dependence of the fluorescence lifetime is subject to distortion, and the stimulated-emission cross section calculated by the Fuchtbauer-Ladenburg equation is underestimated. The influence of radiation trapping on the measured fluorescence lifetime and width are investigated quantitatively. By comparing the intensity ratio of the 1556-1532 nm peak in the fluorescence spectrum with that in the stimulated-emission cross-section spectrum obtained according to the McCumber theory, the distortion ratio of fluorescence spectrum due to radiation trapping is obtained. An empirical way to quantitatively evaluate the influences of radiation trapping on fluorescence lifetime and width is proposed. (c) 2007 Optical Society of America.

Stability against crystallization and spectroscopic properties of Tm3+ doped fluorophosphate glasses

Fluorophosphate glasses with various content of Al(PO3)(3) were prepared. With the increment of Al(PO3)(3) content, density decreases while refractive index increases, and transition temperature, crystallization peak temperature and melt temperature increase which were suggested by differential scanning calorimetry. These glasses exhibit the best stability against crystallization with 7-9 mol'Yo Al(PO3)(3) content. Normalized Raman spectra were used to analyze structure and phonon state. The increment of Al(PO3)(3) content does not affect phonon energy but results in the augment of phonon density. Absorption spectra were measured. H-3(6) -> F-3(4) transition exhibits absorption at L band of the third communication window. Compared with the energy of Tm3+ excited states in other glass system, F-3(4) energy of Tm3+ in these glasses is considerable higher and H-3(4) energy is considerable lower, and it can be predicted that emission band of H-3(4) -> F-3(4) transition is close to the amplified band of gain-shift Tm3+ doped fiber amplifier. Analyses of Judd-Ofelt theory suggest when Al(PO3)(3) content is no more than 7 mol%, Judd-Ofelt parameters Omega(t) and the lifetime of H-3(4) energy level of TM3+ vary little with the increment of Al(PO3)(3) content, and when Al(PO3)(3) content is more than 7 mol%, Omega(2) and Omega(6) increase and radiative lifetime of H-3(4) energy level of Tm3+ drops sharply with the increment of Al(PO3)(3) content. (c) 2006 Elsevier B.V. All rights reserved.

Spectroscopic and structural properties of YbF3-doped fluorophosphate glasses

Compositional influences on the spectroscopic properties of Yb3+ and the structural variations with the introduction of YbF3 were studied in fluorophosphate glasses. Emission cross-section (sigma(emi)) and gain coefficient (sigma(emi) x tau(f)) were calculated which exhibit maximum at RF2 = 33 mol%. YbF3 has an important effect on the glass forming ability of fluorophosphate glasses when RF2 is over 36 mol%. The study of Raman spectra showed big differences on the glass structure between non-Yb3+ and Yb3+ -doped glasses. The main building units in Yb3+-doped samples are metaphosphate groups, pyrophosphate groups (P-2(O,F)(7), PO3F), Al[F-6] +Al[O,F](6) and F3Al-O-AlF3 while those of the non-Yb3+-doped glasses are monophosphate group P(O,F)(4), little pyrophosphate group, Al[F-4] + Al[F-6] + Al[O,F](4) + Al[O,F](6) and F3Al-O-AlF3, which means Yb3+ ions contribute to a better glass polymerization and network uniformity. (C) 2004 Elsevier B.V. All rights reserved.

Special effects of YbF3 on the structural changes for fluorophosphate glass

From Raman and IR spectra, obvious differences of the glass structure were observed in non-Yb3+-doped and Yb3+ -doped fluorophosphate glasses. Results showed that Yb3+ ions can induce, in a better glass, polymerization and network uniformity. Compared with the monophosphate-mastered Yb3+-free glass, Yb3+-doped glass has a pyrophosphate environment. The main building blocks in Yb3+ -doped samples are metaphosphate groups, pyrophosphate groups (P-2(O,F)(7),PO3F), Al[F-6]+Al[O,F](6) and F3Al-O-AlF3 while those of the Yb3+ -free glasses are monophosphate groups P(O,F)(4), little pyrophosphate groups, Al[F-4]+Al[F-6]+Al[O,F](4)+Al[O,F](6) and F3Al-O-AlF3. The DSC analysis also showed a slight increase in crystallization stability. (c) 2005 Elsevier B.V. All rights reserved.

Nanoindentation study on germania-doped silica glass preforms: evidence for the compaction-densification model of photosensitivity

Nanoindentation technique was employed to measure the changes in mechanical properties of a glass preform subjected to different levels of UV exposure. The results reveal that short-term exposure leads to an appreciable increase in the Young's modulus (E), suggesting the densification of the glass, confirming the compaction-densification model. However, on prolonged exposure, E decreases, which provides what we believe to be the first direct evidence of dilation in the glass leading into the Type IIA regime. The present results rule out the hypothesis that continued exposure leads to an irreversible compaction and prove that index modulation regimes are intrinsic to the glass matrix.

Direct ultrafast laser written C-band waveguide amplifier in Er-doped chalcogenide glass

This paper reports the fabrication and characterization of an ultrafast laser written Er-doped chalcogenide glass buried waveguide amplifier; Er-doped GeGaS glass has been synthesized by the vacuum sealed melt quenching technique. Waveguides have been fabricated inside the 4 mm long sample by direct ultrafast laser writing. The total passive fiber-to-fiber insertion loss is 2.58 +/- 0.02 dB at 1600 nm, including a propagation loss of 1.6 +/- 0.3 dB. Active characterization shows a relative gain of 2.524 +/- 0.002 dB/cm and 1.359 +/- 0.005 dB/cm at 1541 nm and 1550 nm respectively, for a pump power of 500 mW at a wavelength of 980 nm. (C) 2012 Optical Society of America